CN103772757A - 一种高硬度o型圈复配橡胶材料 - Google Patents

一种高硬度o型圈复配橡胶材料 Download PDF

Info

Publication number
CN103772757A
CN103772757A CN201310680826.2A CN201310680826A CN103772757A CN 103772757 A CN103772757 A CN 103772757A CN 201310680826 A CN201310680826 A CN 201310680826A CN 103772757 A CN103772757 A CN 103772757A
Authority
CN
China
Prior art keywords
parts
powder
raw material
modified filler
rubber
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310680826.2A
Other languages
English (en)
Inventor
韦中祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu Jinying Machinery Science & Technology Development Co Ltd
Original Assignee
Wuhu Jinying Machinery Science & Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu Jinying Machinery Science & Technology Development Co Ltd filed Critical Wuhu Jinying Machinery Science & Technology Development Co Ltd
Priority to CN201310680826.2A priority Critical patent/CN103772757A/zh
Publication of CN103772757A publication Critical patent/CN103772757A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种高硬度O型圈复配橡胶材料，其是由下述重量份的原料制得:防老剂MB0.8-1.6、氯化橡胶40-59、六甲基磷酰三胺2-3，二甲基硅油2-4，二乙基二硫代氨基甲酸银1-2、促进剂TMTD1-2，快压出炭黑N55020-25、莱茵蜡2-4、氧化铈1-2，硫酸钡3-5、纳米碳化硅0.2-0.4，DCP硫化剂1-2、促进剂DM0.5-1、天然橡胶60-70，改性填料40-50；本发明的橡胶漆具有高硬度、耐酸碱腐蚀的特点、同时使用简单。

Description

一种高硬度O型圈复配橡胶材料
技术领域
本发明涉及橡胶材料领域，确切地说是一种高硬度O型圈复配橡胶材料。
背景技术
O型密封圈O型圈(O-rings)是一种截面为圆形的橡胶密封圈，因其截面为O型，故称其为O型密封圈，也叫O型圈。开始出现在19世纪中叶，当时用它作蒸汽机汽缸的密封元件。
O型密封圈适用于装在各种机械设备上，在规定的温度、压力、以及不同的液体和气体介质中，于静止或运动状态下起密封作用。在机床、船舶、汽车、航空航天设备、冶金机械、化工机械、工程机械、建筑机械、矿山机械、石油机械、塑料机械、农业机械、以及各类仪器仪表上，大量应用着各种类型的密封元件。O型密封圈主要用于静密封和往复运动密封。用于旋转运动密封时，仅限于低速回转密封装置。O型密封圈一般安装在外圆或内圆上截面为矩形的沟槽内起密封作用。 O型密封圈在耐油、酸碱、磨、化学侵蚀等环境依然起到良好密封、减震作用。因此，O型密封圈是液压与气压传动***中使用最广泛的一种密封件。
发明内容
本发明的目的在于提供一种高硬度O型圈复配橡胶材料。
上述目的通过以下方案实现：
    一种高硬度O型圈复配橡胶材料，其特征在于：其是由下述重量份的原料制得：防老剂MB 0.8-1.6、氯化橡胶40-59、六甲基磷酰三胺2-3，二甲基硅油2-4，二乙基二硫代氨基甲酸银1-2、促进剂TMTD 1-2，快压出炭黑N550 20-25、莱茵蜡2-4、氧化铈1-2，硫酸钡3-5、纳米碳化硅0.2-0.4，DCP硫化剂 1-2、促进剂DM0.5-1、天然橡胶60-70，改性填料40-50；
　　所述的改性填料由下述重量份的原料制得：
环氧亚麻籽油1-2、亚磷酸二苯一异辛酯0.2-0.4、云母粉5-8、钾长石粉10-15、透闪石粉30-40、萤石矿渣20-30、硅烷偶联剂KH550  1-2、抗氧剂168 2-4、氯化石蜡2-4，机油1-2，脂肪酸0.8-1.5。　　
所述的改性填料的制备方法为：
将萤石矿渣破碎后，用浓度为15-20%的氢氧化钠泡4-6小时后，再用去离子水洗涤至中性，烘干；再将烘干后的萤石矿渣粉与云母粉、钾长石粉、透闪石粉混匀，于600-790℃下煅烧1-2小时，取出冷却后，与其余原料混匀后，加入适量的水，在900-1800转/分下搅拌20-30分钟后，烘干粉碎即得。
    所述的一种高硬度O型圈复配橡胶材料，其特征在于：
制备方法为：将各原料混匀后，110-120摄氏度下混炼完全，再经硫化，即得。
本发明的有益效果为：本发明的橡胶漆具有高硬度、耐酸碱腐蚀的特点、同时使用简单。
具体实施方式
 一种高硬度O型圈复配橡胶材料，其是由下述重量kg的原料制得：防老剂MB 0.8、氯化橡胶45、六甲基磷酰三胺3，二甲基硅油4，二乙基二硫代氨基甲酸银2、促进剂TMTD  2，快压出炭黑N550  25、莱茵蜡 4、氧化铈2，硫酸钡5、纳米碳化硅0.4，DCP硫化剂 2、促进剂DM0.7、天然橡胶70，改性填料50；
　　所述的改性填料由下述重量kg的原料制得：
环氧亚麻籽油2、亚磷酸二苯一异辛酯0.4、云母粉8、钾长石粉15、透闪石粉33、萤石矿渣30、硅烷偶联剂KH550  1.5、抗氧剂168  2.4、氯化石蜡2，机油1，脂肪酸1.5。　　
所述的改性填料的制备方法为：
将萤石矿渣破碎后，用浓度为15%的氢氧化钠泡5小时后，再用去离子水洗涤至中性，烘干；再将烘干后的萤石矿渣粉与云母粉、钾长石粉、透闪石粉混匀，于600℃下煅烧2小时，取出冷却后，与其余原料混匀后，加入适量的水，在1200转/分下搅拌20分钟后，烘干粉碎即得。
    所述的一种高硬度O型圈复配橡胶材料，
制备方法为：将各原料混匀后，110摄氏度下混炼完全，再经硫化，即得。
 性能测试：
拉伸强度：17.2MPa；
断裂伸长率：428%；
耐油性：20#机油100℃×70h，断裂伸长率保持率80.8%、抗拉强度保持率83.1%；
耐臭氧：26℃、24h、臭氧浓度0.026%，无开裂；
耐老化：120℃、150h，抗拉强度保持率81.2%，断裂伸长率保持率83.7%；
压缩耐寒系数（-32℃）0.59。

Claims (2)

1.一种高硬度O型圈复配橡胶材料，其特征在于：其是由下述重量份的原料制得：防老剂MB 0.8-1.6、氯化橡胶40-59、六甲基磷酰三胺2-3，二甲基硅油2-4，二乙基二硫代氨基甲酸银1-2、促进剂TMTD 1-2，快压出炭黑N550  20-25、莱茵蜡2-4、氧化铈1-2，硫酸钡3-5、纳米碳化硅0.2-0.4，DCP硫化剂 1-2、促进剂DM0.5-1、天然橡胶60-70，改性填料40-50；
所述的改性填料由下述重量份的原料制得：
环氧亚麻籽油1-2、亚磷酸二苯一异辛酯0.2-0.4、云母粉5-8、钾长石粉10-15、透闪石粉30-40、萤石矿渣20-30、硅烷偶联剂KH550  1-2、抗氧剂168 2-4、氯化石蜡2-4，机油1-2，脂肪酸0.8-1.5；　　
所述的改性填料的制备方法为：
将萤石矿渣破碎后，用浓度为15-20%的氢氧化钠泡4-6小时后，再用去离子水洗涤至中性，烘干；再将烘干后的萤石矿渣粉与云母粉、钾长石粉、透闪石粉混匀，于600-790℃下煅烧1-2小时，取出冷却后，与其余原料混匀后，加入适量的水，在900-1800转/分下搅拌20-30分钟后，烘干粉碎即得。
2.根据权利要求1所述的一种高硬度O型圈复配橡胶材料，其特征在于：
制备方法为：将各原料混匀后，110-120摄氏度下混炼完全，再经硫化，即得。
CN201310680826.2A 2013-12-13 2013-12-13 一种高硬度o型圈复配橡胶材料 Pending CN103772757A (zh)