CN103613963A - Nano inorganic anti-oxidation water-based paint - Google Patents
Nano inorganic anti-oxidation water-based paint Download PDFInfo
- Publication number
- CN103613963A CN103613963A CN201310593916.8A CN201310593916A CN103613963A CN 103613963 A CN103613963 A CN 103613963A CN 201310593916 A CN201310593916 A CN 201310593916A CN 103613963 A CN103613963 A CN 103613963A
- Authority
- CN
- China
- Prior art keywords
- parts
- auxiliary agent
- stirring
- raw material
- nano inorganic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a nano inorganic anti-oxidation water-based paint which consists of the following raw materials in parts by weight: 46-50 parts of silicon oxide sol, 1-2 parts of tragacanth gum, 0.65-1 part of polyethylene ester, 1-2 parts of potassium hydrogen sulfate, 0.1-0.3 part of polyvinylpyrrolidone, 0.7-1 part of ethylene glycol dimethacrylate, 1-2 parts of diethanol amine, 2-3 parts of diphenyl imidazoline, 2-3 parts of polyisobutene, 4-5 parts of silicon carbide, 0.8-2 parts of antioxidant 1010, 10-13 parts of sepiolite powder, 5-6 parts of auxiliary and 10-25 parts of deionized water. The coating of the waterproof paint disclosed by the invention has good smoothness and density; the added auxiliary remarkably improves the adhesive property and enhances the protectiveness on a base material; the paint disclosed by the invention has strong weather resistance as well as perfect heat preservation and heat insulation properties.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to the anti-oxidant water-borne coatings of a kind of nano inorganic.
Background technology
Coating is a kind of product that defencive function has again beautifying articles that has, and visible everywhere in the middle of people live, it is widely used in all respects such as building, steel product, woodenware, has become the indispensable product of society.
In the middle of a large amount of coating using and paint; different due to the quality of product and cost performance; also expose many problems; for example a lot of products use just there is not for a long time efflorescence, come off, the phenomenon of variable color (fading); its due defencive function is reduced greatly, lost the decoration function to object and article.Effect attractive in appearance and work-ing life are not long, have wasted greatly resource.
Its reason is exactly that people just think that coating, paint just can play the protection of object and increase gorgeous color for a long time, has ignored the Nature they are destroyed, and does not also understand coating and also needs protection with paint.
To the destruction of coating and paint, be mainly the cold and hot variation that derives from weather, the impact of dust storm, the infringement to it of environmental pollution and sunlight.If for the reason that causes coating with paint infringement, to its protection, just can make extend its work-ing life.
The annual production of domestic 2010 at present statistics building coatings is 5,000,000 tons of left and right, and the output of common paint, at-ten thousand tons, if can extend coating and the work-ing life of painting 10%, just means can reduce every year and produces 500,000 tons of building coatings, paint-ton.By 30,000 yuan/ton of calculating of middle-grade building coating, 1 year will reduce the use of 15,000,000,000 yuan of coating.This is a huge amount of money, if can reduce input, economize on resources, makes great efforts exactly to facilitate the concrete manifestation of conservation-minded society.Just can economize on resources with the energy, cut the waste and pollute, increase the economic benefit of user's use and the effect of social benefit.
Our company utilizes a kind of of high-tech approach research and production to have being applied to the existing coating such as building, steel-product, timber and plastics, painting the ultraviolet isolating paint that has defencive function.
Summary of the invention
The object of the invention is just to provide a kind of ultraviolet isolating paint that has defencive function.
The present invention is achieved by the following technical solutions:
The anti-oxidant water-borne coatings of nano inorganic, it is comprised of the raw material of following weight parts:
Silica sol 46-50, tragacanth gum 1-2, polyvinyl ether 0.65-1, sal enixum 1-2, polyvinylpyrrolidone 0.1-0.3, Ethylene glycol dimethacrylate 0.7-1, diethanolamine 1-2, diphenyl-imidazole quinoline 2-3, polyisobutene 2-3, silicon carbide 4-5, antioxidant 1010 0.8-2, sepiolite powder 10-13, auxiliary agent 5-6, deionized water 10-25;
Described auxiliary agent is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 10-15, propolis 2-3, polyoxyethylene oleic acid ester 0.8-1, sodium silicoaluminate 1-2, polyoxypropyleneglycol 1-2, nano montmorillonite powder 4-5;
Above-mentioned propolis and polyoxypropyleneglycol Hybrid Heating are arrived to 60-80 ℃, after stirring, add nano montmorillonite powder, 100-200 rev/min of dispersed with stirring 4-6 minute, add polyoxyethylene oleic acid ester, 400-600 rev/min of dispersed with stirring 2-4 minute, adds each raw material of residue, at 80-100 ℃, is incubated 10-15 minute, fully ball milling, obtains described auxiliary agent.
A preparation method for the anti-oxidant water-borne coatings of nano inorganic, comprises the following steps:
Above-mentioned each raw material except auxiliary agent is mixed, and 1600-2000 rev/min of dispersed with stirring 20-30 minute, adds auxiliary agent, stirs, and fully mixes, and obtains the anti-oxidant water-borne coatings of described nano inorganic.
Advantage of the present invention is:
The slickness of waterproof paint coating of the present invention and good compactness, the auxiliary agent adding has improved adhesive property greatly, has strengthened the protectiveness to base material, and coating weathering resistance of the present invention is strong, also has good heat insulation property.
Embodiment
Embodiment 1
A nano inorganic anti-oxidant water-borne coatings, it by following weight parts (kilogram) raw material form:
Silica sol 50, tragacanth gum 1, polyvinyl ether 1, sal enixum 1, polyvinylpyrrolidone 0.3, Ethylene glycol dimethacrylate 0.7, diethanolamine 1, diphenyl-imidazole quinoline 3, polyisobutene 3, silicon carbide 4, antioxidant 1010 0.8, sepiolite powder 13, auxiliary agent 6, deionized water 25;
Described auxiliary agent is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 15, propolis 2, polyoxyethylene oleic acid ester 0.8, sodium silicoaluminate 2, polyoxypropyleneglycol 2, nano montmorillonite powder 4;
By above-mentioned propolis and polyoxypropyleneglycol Hybrid Heating to 80 ℃, after stirring, add nano montmorillonite powder, 200 revs/min of dispersed with stirring 4 minutes, add polyoxyethylene oleic acid ester, 600 revs/min of dispersed with stirring 2 minutes, add each raw material of residue, at 100 ℃, are incubated 15 minutes, fully ball milling, obtains described auxiliary agent.
A preparation method for the anti-oxidant water-borne coatings of nano inorganic, comprises the following steps:
Above-mentioned each raw material except auxiliary agent is mixed, and 2000 revs/min of dispersed with stirring 30 minutes, add auxiliary agent, stir, and fully mix, and obtain the anti-oxidant water-borne coatings of described nano inorganic.
Performance test:
Abrasion resistance test: pass through for 10000 times, paint film is without breakage;
Artificial ageing resistance test: 2000 hours non-foaming, do not peel off, flawless.
Claims (2)
1. the anti-oxidant water-borne coatings of nano inorganic, is characterized in that what it was comprised of the raw material of following weight parts:
Silica sol 46-50, tragacanth gum 1-2, polyvinyl ether 0.65-1, sal enixum 1-2, polyvinylpyrrolidone 0.1-0.3, Ethylene glycol dimethacrylate 0.7-1, diethanolamine 1-2, diphenyl-imidazole quinoline 2-3, polyisobutene 2-3, silicon carbide 4-5, antioxidant 1010 0.8-2, sepiolite powder 10-13, auxiliary agent 5-6, deionized water 10-25;
Described auxiliary agent is comprised of the raw material of following weight parts:
Polyvinyl acetate emulsion 10-15, propolis 2-3, polyoxyethylene oleic acid ester 0.8-1, sodium silicoaluminate 1-2, polyoxypropyleneglycol 1-2, nano montmorillonite powder 4-5;
Above-mentioned propolis and polyoxypropyleneglycol Hybrid Heating are arrived to 60-80 ℃, after stirring, add nano montmorillonite powder, 100-200 rev/min of dispersed with stirring 4-6 minute, add polyoxyethylene oleic acid ester, 400-600 rev/min of dispersed with stirring 2-4 minute, adds each raw material of residue, at 80-100 ℃, is incubated 10-15 minute, fully ball milling, obtains described auxiliary agent.
2. a preparation method for the anti-oxidant water-borne coatings of nano inorganic as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned each raw material except auxiliary agent is mixed, and 1600-2000 rev/min of dispersed with stirring 20-30 minute, adds auxiliary agent, stirs, and fully mixes, and obtains the anti-oxidant water-borne coatings of described nano inorganic.