CN103613963B - A kind of Nano inorganic anti-oxidation water-borne coatings - Google Patents
A kind of Nano inorganic anti-oxidation water-borne coatings Download PDFInfo
- Publication number
- CN103613963B CN103613963B CN201310593916.8A CN201310593916A CN103613963B CN 103613963 B CN103613963 B CN 103613963B CN 201310593916 A CN201310593916 A CN 201310593916A CN 103613963 B CN103613963 B CN 103613963B
- Authority
- CN
- China
- Prior art keywords
- auxiliary agent
- raw material
- borne coatings
- inorganic anti
- stirring
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention discloses a kind of Nano inorganic anti-oxidation water-borne coatings, it is made up of the raw material of following weight parts: silica sol 46-50, tragacanth gum 1-2, polyvinyl ether 0.65-1, sal enixum 1-2, polyvinylpyrrolidone 0.1-0.3, Ethylene glycol dimethacrylate 0.7-1, diethanolamine 1-2, diphenyl-imidazole quinoline 2-3, polyisobutene 2-3, silicon carbide 4-5, antioxidant 1010? 0.8-2, sepiolite powder 10-13, auxiliary agent 5-6, deionized water 10-25, the slickness of waterproof paint coating of the present invention and good compactness, the auxiliary agent added improves adhesive property greatly, enhance the protectiveness to base material, coating weathering resistance of the present invention is strong, also there is good heat insulation property.
Description
Technical field
The present invention relates generally to a kind of coating, particularly relates to a kind of Nano inorganic anti-oxidation water-borne coatings.
Background technology
Coating a kind ofly has the product that defencive function has again beautifying articles, and visible everywhere in the middle of people live, it is widely used in all respects such as building, steel product, woodenware, has become the product that society is indispensable.
In the middle of a large amount of coating used with paint; due to the quality of product and the different of cost performance; also many problems are exposed; such as a lot of product use just there is not efflorescence for a long time, come off, the phenomenon of variable color (fading); its due defencive function is reduced greatly, loses the decoration function to object and article.Effect attractive in appearance and work-ing life are not long, waste resource greatly.
Its reason is exactly that people just think that coating, paint just can play the protection of object and increase gorgeous color for a long time, ignores the Nature and destroys them, and also not understanding coating with painting also needs to protect.
The destruction of coating and paint is mainly derived to the cold and hot change of weather, the impact of dust storm, environmental pollution and sunlight are to its infringement.If for causing coating and painting the reason damaged, to its protection, just can make extend its work-ing life.
The annual production of domestic 2010 at present statistics building coatings is at about 5,000,000 tons, and the output of common paint, at-ten thousand tons, if can extend coating and the work-ing life of paint 10%, just means can reduce every year and produces building coating 500,000 tons, paint-ton.By middle-grade building coating 30,000 yuan/ton calculating, 1 year by the use of minimizing 15,000,000,000 yuan of coating.This is a huge amount of money, if can reduce input, economize on resources, makes great efforts the concrete manifestation facilitating conservation-minded society exactly.Just can economize on resources and the energy, cut the waste and pollute, economic benefit that adding users uses and the effect of social benefit.
Our company utilizes a kind of of high-tech approach research and production to have the ultraviolet isolating paint being applied to the existing coating such as building, steel-product, timber and plastics, paint has defencive function.
Summary of the invention
The object of the invention is just to provide a kind of ultraviolet isolating paint having defencive function.
The present invention is achieved by the following technical solutions:
A kind of Nano inorganic anti-oxidation water-borne coatings, it is made up of the raw material of following weight parts:
Silica sol 46-50, tragacanth gum 1-2, polyvinyl ether 0.65-1, sal enixum 1-2, polyvinylpyrrolidone 0.1-0.3, Ethylene glycol dimethacrylate 0.7-1, diethanolamine 1-2, diphenyl-imidazole quinoline 2-3, polyisobutene 2-3, silicon carbide 4-5, antioxidant 1010 0.8-2, sepiolite powder 10-13, auxiliary agent 5-6, deionized water 10-25;
Described auxiliary agent is made up of the raw material of following weight parts:
Polyvinyl acetate emulsion 10-15, propolis 2-3, polyoxyethylene oleic acid ester 0.8-1, sodium silicoaluminate 1-2, polyoxypropyleneglycol 1-2, nano montmorillonite powder 4-5;
By above-mentioned propolis and polyoxypropyleneglycol Hybrid Heating to 60-80 DEG C, nano montmorillonite powder is added after stirring, 100-200 rev/min of dispersed with stirring 4-6 minute, add polyoxyethylene oleic acid ester, 400-600 rev/min of dispersed with stirring 2-4 minute, adds each raw material of residue, at 80-100 DEG C, is incubated 10-15 minute, abundant ball milling, obtains described auxiliary agent.
A preparation method for Nano inorganic anti-oxidation water-borne coatings, comprises the following steps:
By above-mentioned each raw material mixing except auxiliary agent, 1600-2000 rev/min of dispersed with stirring 20-30 minute, adds auxiliary agent, stirs, fully mixes, obtain described Nano inorganic anti-oxidation water-borne coatings.
Advantage of the present invention is:
The slickness of waterproof paint coating of the present invention and good compactness, the auxiliary agent added improves adhesive property greatly, enhances the protectiveness to base material, and coating weathering resistance of the present invention is strong, also has good heat insulation property.
Embodiment
Embodiment 1
A kind of Nano inorganic anti-oxidation water-borne coatings, it is made up of the raw material of following weight parts (kilogram):
Silica sol 50, tragacanth gum 1, polyvinyl ether 1, sal enixum 1, polyvinylpyrrolidone 0.3, Ethylene glycol dimethacrylate 0.7, diethanolamine 1, diphenyl-imidazole quinoline 3, polyisobutene 3, silicon carbide 4, antioxidant 1010 0.8, sepiolite powder 13, auxiliary agent 6, deionized water 25;
Described auxiliary agent is made up of the raw material of following weight parts:
Polyvinyl acetate emulsion 15, propolis 2, polyoxyethylene oleic acid ester 0.8, sodium silicoaluminate 2, polyoxypropyleneglycol 2, nano montmorillonite powder 4;
By above-mentioned propolis and polyoxypropyleneglycol Hybrid Heating to 80 DEG C, nano montmorillonite powder is added after stirring, 200 revs/min of dispersed with stirring 4 minutes, add polyoxyethylene oleic acid ester, 600 revs/min of dispersed with stirring 2 minutes, add each raw material of residue, at 100 DEG C, are incubated 15 minutes, abundant ball milling, obtains described auxiliary agent.
A preparation method for Nano inorganic anti-oxidation water-borne coatings, comprises the following steps:
By above-mentioned each raw material mixing except auxiliary agent, 2000 revs/min of dispersed with stirring 30 minutes, add auxiliary agent, stir, fully mix, obtain described Nano inorganic anti-oxidation water-borne coatings.
Performance test:
Abrasion resistance is tested: pass through for 10000 times, paint film is without breakage;
Artificial ageing resistance test: 2000 hours non-foaming, do not peel off, flawless.
Claims (2)
1. a Nano inorganic anti-oxidation water-borne coatings, is characterized in that what it was made up of the raw material of following weight parts: silica sol 46-50, tragacanth gum 1-2, polyvinyl ether 0.65-1, sal enixum 1-2, polyvinylpyrrolidone 0.1-0.3, Ethylene glycol dimethacrylate 0.7-1, diethanolamine 1-2,2-benzylimidazoline 2-3, polyisobutene 2-3, silicon carbide 4-5, antioxidant 1010 0.8-2, sepiolite powder 10-13, auxiliary agent 5-6, deionized water 10-25; Described auxiliary agent is made up of the raw material of following weight parts: polyvinyl acetate emulsion 10-15, propolis 2-3, polyoxyethylene oleic acid ester 0.8-1, sodium silicoaluminate 1-2, polyoxypropyleneglycol 1-2, nano montmorillonite powder 4-5; By above-mentioned propolis and polyoxypropyleneglycol Hybrid Heating to 60-80 DEG C, nano montmorillonite powder is added after stirring, 100-200 rev/min of dispersed with stirring 4-6 minute, add polyoxyethylene oleic acid ester, 400-600 rev/min of dispersed with stirring 2-4 minute, adds each raw material of residue, at 80-100 DEG C, is incubated 10-15 minute, abundant ball milling, obtains described auxiliary agent.
2. the preparation method of a Nano inorganic anti-oxidation water-borne coatings as claimed in claim 1, it is characterized in that comprising the following steps: by above-mentioned each raw material mixing except auxiliary agent, 1600-2000 rev/min of dispersed with stirring 20-30 minute, add auxiliary agent, stir, fully mix, obtain described Nano inorganic anti-oxidation water-borne coatings.