A kind of periodic amorphous master alloy vacuum induction casting furnace
Technical field
The present invention relates to a kind of periodic amorphous master alloy vacuum induction casting furnace, it is that spray band preparation is steady for amorphous industry
Fixed consistent T-shaped amorphous master alloy ingot blank.
Background technology
As an emerging new material new forms of energy industry, the branch that amorphous grew up beyond doubt in recent years.?
At present amorphous industry field is many prepares foundry alloy using antivacuum stove, the amorphous band oxygen content prepared high impure high and
Internal component inaccurate so that the permeability of finished product band. iron loss and surface quality are unqualified.Smelted using vacuum drying oven and be also
Pour and cast out a big billet, also need to be divided into bar or fritter, so not only efficiency is low but also waste of material is also big before spray band.Week
, equipped with material alloying and T-shaped multiple rows of ingot mould, the ingot blank produced need not for phase formula amorphous master alloy vacuum induction casting furnace
Segmentation and composition accuracy is high, improve quality and efficiency.
Content of the invention
In order to overcome the above-mentioned deficiencies of the prior art, it is an object of the invention to provide a kind of periodic amorphous master alloy vacuum
Induction fusion casting stove, has the characteristics that efficient energy-saving, can increase substantially amorphous band quality.
To achieve these goals, the technical solution used in the present invention is:A kind of periodic amorphous master alloy vacuum induction
Casting furnace, includes fusing casting room, and fusing casting interior is provided with sensing heating crucible device, and the side of fusing casting room is provided with
Coupled logical ingot mould rest area, the front of sensing heating crucible device is provided with water cooled mo(u)ld car, and water cooled mo(u)ld car is provided with T-shaped many
Row's ingot mould, on the top of the T-shaped multiple rows of ingot mould adjacent with sensing heating crucible device, is provided with molten metal splitter box, fusing casting
The top of room is additionally provided with continuous feeding;The opposite side of fusing casting room is also connected with vacuum system.
Described fusing casting room top is additionally provided with material alloying mouth.
Described fusing casting room is square room.
Described sensing heating crucible device is vertical circular shape.
Described ingot mould rest area is square, and ingot mould rest area is provided with openable door.
The mode of heating of described induction heating apparatus can be using intermediate frequency, power frequency or high frequency.
The present invention beneficial effect be:
Using continuous feeding so that sensing heating crucible device open-assembly time is few in atmosphere, improve production effect
Rate reduces the heat loss of body of heater;And the design of water cooled mo(u)ld car, it is achieved that the quick cooling of amorphous ingot blank, reaches to a certain extent
Arrive the purpose of directional solidification, having the ingot blank produced need not split, the feature of efficient material-saving.
Brief description
Fig. 1 is the structural representation of the present invention.
Specific embodiment
Below in conjunction with the accompanying drawings the present invention is described in further detail.
Referring to accompanying drawing 1, a kind of periodic amorphous master alloy vacuum induction casting furnace, include fusing casting room 7, fusing is poured
It is provided with sensing heating crucible device 6, the side of fusing casting room 7 is provided with coupled logical ingot mould rest area 9, sense in casting room 7
The front answering heating crucible device 6 is provided with water cooled mo(u)ld car 5, and water cooled mo(u)ld car 5 is provided with T-shaped multiple rows of ingot mould 4, with sensing heating earthenware
The top of the adjacent T-shaped multiple rows of ingot mould 4 of crucible device 6, is provided with molten metal splitter box 3, and the top of fusing casting room 7 is additionally provided with continuously
Feeding device 1;The opposite side of fusing casting room 7 is also connected with vacuum system 8.
Described fusing casting room 7 top is additionally provided with material alloying mouth 2.
Described fusing casting room 7 is square room.
Described sensing heating crucible device 6 is vertical circular shape.
Described ingot mould rest area 9 is square, and ingot mould rest area 9 is provided with openable door.
The mode of heating of described induction heating apparatus 6 can be using intermediate frequency, power frequency or high frequency.
Sensing heating crucible device 6 in fusing casting room 7, after molten metal is melting down, can select according to molten metal composition situation
Select and alloy interpolation is carried out by material alloying mouth 2 or continuous feeding 1.
The operation principle of the present invention is:
During work, fusing casting room 7 carries out evacuation by pumped vacuum systems 8, by continuous feeding 1, amorphous is female
Alloy adds in sensing heating crucible device 6, and after foundry alloy fusing, sensing heating crucible device 6 fascinates, and molten metal is poured into
Molten metal is uniformly injected into T-shaped multiple rows of ingot mould 4 by shunting by molten metal splitter box 3.