CN103556557A - Manufacturing method of color concrete granite flamed-surface terrace - Google Patents
Manufacturing method of color concrete granite flamed-surface terrace Download PDFInfo
- Publication number
- CN103556557A CN103556557A CN201310582307.2A CN201310582307A CN103556557A CN 103556557 A CN103556557 A CN 103556557A CN 201310582307 A CN201310582307 A CN 201310582307A CN 103556557 A CN103556557 A CN 103556557A
- Authority
- CN
- China
- Prior art keywords
- granite
- concrete
- fired
- terrace
- colorant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a manufacturing method of a color concrete granite flamed-surface terrace, relates to the technical field of building construction and specifically relates to a manufacturing method of a color concrete terrace. The manufacturing method comprises the following steps: (I), erecting a form; (II), casting concrete; (III), leveling; (IV), throwing a reinforcing agent; (V), finishing; (VI), throwing a granite coloring agent; (VII), throwing a release agent; (VIII), rubbing textures; (IX), cutting an expansion joint, (X), cleaning a surface layer, and (XI), spraying and brushing a sealing agent. The manufacturing method disclosed by the invention solves the problems that existing granite stone is high in manufacturing cost, easy to break, large in loss and short in service life. Moreover, a series of environment-friendly problems that stone energy resources are exploited, a geological environment is affected, energy resources are exhausted, ecological damage is caused can be effectively relieved.
Description
Technical field
The present invention relates to technical field of building construction, be specifically related to the method for production of colour concrete terrace.
Background technology
Because Chinese Urbanization construction progress makes much progress, and city proper hardened ground accounts for city area area significant proportion, and the reconstruction of the old city town in additional each city causes many natural engineerings stone material famines used such as China's marble, granite and exploitation excessively.This certainly will have influence on the environment that we depend on for existence, and stone mining excessively can cause some basic disasters.As soft in soil property, forest water-holding capacity decline, vegetation destruction etc.Situation seriously will cause the serious consequences such as flash flood, dust be boundless.According to the existing various places of investigation China, occurred because of the excessive caused a series of disasters of the stone material exploitation.But urban construction and development is the origin of state, be not modifiable trend.Therefore, reduce lithotome utilization, alleviate the exploitation of natural energy resource, find and replace engineering nature stone material, maintaining ecological balance to be one benefiting the nation and the people and be badly in need of a systems technology for Chinese society and economic development.
This year, Lai, China was for introduction of foreign technology, developed the concrete systems technology of a series of natural-like stone, and the concrete product of various artificial granite marbles is of common occurrence.But effect is all undesirable.Reason is people to the dependence of lithotome and spoils.Artificial imitate natural certain difficulty that originally just had, but through every personage's so for many years continuous renewal and grope research and development.The concrete floor of natural-like stone has begun to take shape.And the present invention extracts experience from the failure through many times, finally develop the systems technology that energy and natural granite compare favourably and even surmount.
Summary of the invention
The invention provides the manufacture method of granite fired terrace of colour concrete, the cost that the invention solves existing granite stone is high, cracky, and loss is large, and application life is not long.More can effectively alleviate stone material energy extraction, affect geological environment, lack of energy destroys a series of environmental issues such as ecological.
For addressing the above problem, the present invention adopts following technical scheme: the manufacture method of granite fired terrace of colour concrete, comprises the steps:
(1) formwork: formwork processing is carried out in the section that construct;
(2) concreting: by concrete evenly build with formwork within the scope of;
(3) be closed flat: the concrete of building is closed flat processing; While being closed flat, as found, concrete surface has excessive moisture, should be scraped;
(4) shed hardening agent: at the concrete being closed flat after processing, in initial set, during the stage, first use the special-purpose hardening agent of 2/3 granite fired autogram ground, evenly shed to concrete surface;
(5) essence is received light: shed the special-purpose hardening agent of granite fired autogram ground, treating that special-purpose hardening agent wet and changes carries out essence receipts light after color and process; To not shedding the very few part of hardening agent or hardening agent, use remaining 1/3 hardening agent to fill up;
(6) shed granite colorant: when essence is received the obvious moisture content of granite hardening agent surface nothing of light, carry out the processing of shedding of granite colorant;
(7) shed release agent: complete after granite colorant sheds, when concrete tentatively condenses, carry out release agent and shed;
(8) inscription rubbing texture: use granite fired face mould tool to be laid in granite fired face colouring agent surface, spelled gap; With skin hammer, evenly beat mould, make its granite fired surface can leave mould lines clearly;
(9) cutting shrinkage joint: treat the completely dry anhydrous timesharing of concrete completing above-mentioned all flow processs, use cutting machine cutting shrinkage joint; Shrinkage joint width is 2-4 millimeter; Then with weather-proof, use glue joint filling;
(10) clean top layer: complete after above-mentioned all flow processs after maintenance 7-10 days; During maintenance, use clear water to rinse out the release agent of concrete surface layer;
(11) spary sealant: when exclusion is dried up on good road surface to be cleaned completely, use flush coater or rotary broom that sealant is evenly sprayed to concrete surface.
In (four) step, described hardening agent raw material weight match ratio is; High strength cement: 600, quartz sand: 400, dimension silica flour: 8, based water reducer how: 3, calcium formate: 3, colorant is appropriate.Colorant adopts iron oxide series colorant to require to allocate according to color.Described quartz sand diameter is 0.5-1mm.
In (six) step: described colorant raw material weight proportioning: high strength cement: 80, quartz sand: 20, resin rubber powder: 0.5, based water reducer how: 0.3, calcium formate: 0.2, colorant 0.5.Described quartz sand diameter is 0.5-1mm.
In (seven) step: described release agent raw material weight proportioning: heavy fat calcium: 50, light fat calcium: 50, French chalk: 100.
In (11) step, sealant raw material used: acrylic resin.
The object of this invention is to provide a kind of texture color and luster of natural-like stone and concrete surface and the job practices thereof of outward appearance, the exhaustive exploitation that solve lithotome possesses the ornamental problem of lithotome simultaneously.Solution is never used lithotome but can be possessed the technical problem of the aesthetic of lithotome.
Overusing of nature stone material not only can be effectively alleviated on this road surface of the present invention, and has hardness and the pressure-proof and snap-resistent intensity of nature stone material.And improved easily the coming off of natural stone material terrace, cracky, the shortcoming such as lifting surface area is single, construction is slow, cost is high, loss waste, application life are short.
The present invention and granite are burnt face outward appearance phase knowledge and magnanimity can reach surprising more than 95%.As everyone knows, natural granite is not pure white but there is the spot of similar Semen sesami nigrum its inside.Its outside pitted skin presents irregularly shaped, all can not effectively accomplish above-mentioned 2 points on the market with the similar imitative stone floor occurring in the past.And this cover system technology of this product has effectively solved its above-mentioned 2 points.
Accompanying drawing explanation
Fig. 1 is the structural representation of granite fired terrace aspect of colour concrete of the present invention.
Symbol description in figure: resin-sealed layer 1, dyed layer 2, hardening agent layer 3, layer of concrete 4, basic unit 5.
The specific embodiment
With best embodiment, the present invention is described in detail below
.
The manufacture method of granite fired terrace of colour concrete, comprises the steps:
(1) formwork: formwork processing is carried out in the section that construct; This mould is divided into side form and internal mold; Mould is all used quarter bend or the consistent batten of specification.Mould requires: straight, length, highly consistent.Height can be got and order according to construction requirement.
(2) concreting: by concrete evenly build with formwork within the scope of;
Described concrete material comprises: hardening agent raw material weight match ratio is; (the one ton of hardening agent of take is example) high strength cement: 600, quartz sand: 400, (quartz sand diameter is 0.5 ~ 1mm) dimension silica flour: 8, based water reducer how: 3, calcium formate: 3, colorant, iron oxide series colorant requires to allocate according to color;
(3) be closed flat: the concrete of building is closed flat processing; While being closed flat, as found, concrete surface has excessive moisture, should be scraped;
(4) shed hardening agent: at the concrete being closed flat after processing, in initial set, during the stage, first use the special-purpose hardening agent of 2/3 granite fired autogram ground, evenly shed to concrete surface; While shedding, shed the grasp of dynamics, can not have and omit or phenomenon in heaps.Note: this flow process need be grasped the concrete initial set time, too early unsuitable, also should not be excessively late.
(5) essence is received light: after waiting and having shed the special-purpose hardening agent of granite fired autogram ground, treating that special-purpose hardening agent wet and changes carries out essence after color and receive light and process, and receives light and processes with nothing receipts light vestige and be advisable.Receive only as find that there is and do not shed hardening agent or the very few part of hardening agent carrying out essence, use remaining 1/3 hardening agent to fill up;
(6) shed granite colorant: when essence is received the obvious moisture content of granite hardening agent surface nothing of light, use special tool to carry out the processing of shedding of granite colorant.While shedding colorant, should note shedding in heaps.
Described colorant raw material and proportioning: (take 100kg as example) high strength cement: 80kg is quartzy: 20kg(quartz sand diameter is 0.5 ~ 1mm) resin rubber powder: SILICA FUME 0.5kg: based water reducer 0.3kg how: calcium formate 0.2kg:0.5kg colorant, iron oxide series colorant requires to allocate according to color.
(7) shed release agent: complete after granite colorant sheds, when concrete tentatively condenses, carry out release agent and shed.Release agent is too much unsuitable, can uniform fold concrete surface layer.Note: this concrete coagulation is judged; Available hand, with defeating concrete surface, can leave slight finger mark.
Described release agent raw material and proportioning: (take 200kg as example) heavy fat calcium: the light fat calcium of 50kg: 50kg French chalk: 100kg
(8) inscription rubbing texture: use granite fired face mould tool to be laid in granite fired face colouring agent surface, spelled gap.With skin hammer, evenly beat mould, make its granite fired surface can leave mould lines clearly.While beaing mould, should be noted firmly equilibrium, according to the concrete hardness of condensing, suitably adjust and beat dynamics, and need evenly beat mould, can not omit or repeatedly repeat, cause concrete surface texture depth inconsistent.
(9) cutting shrinkage joint: treat the completely dry anhydrous timesharing of concrete completing above-mentioned all flow processs, use cutting machine cutting shrinkage joint.Shrinkage joint width is 2-4 millimeter.Then with weather-proof, use glue joint filling;
(10) clean top layer: complete after above-mentioned all flow processs after maintenance 7-10 days.Use clear water to rinse out the release agent of concrete surface layer.
(11) spary sealant: when exclusion is dried up on good road surface to be cleaned completely, use flush coater or rotary broom that sealant is evenly sprayed to concrete surface;
Sealant raw material used: acrylic resin.
As shown in Figure 1, granite fired terrace of colour concrete of the present invention, is followed successively by from bottom to top: basic unit 5, layer of concrete 4, hardening agent layer 3, dyed layer 2, resin-sealed layer 1.
Finally it should be noted that: obviously, above-described embodiment is only for example of the present invention is clearly described, and the not restriction to embodiment.For those of ordinary skill in the field, can also make other changes in different forms on the basis of the above description.Here exhaustive without also giving all embodiments.And the apparent variation of being amplified out thus or change are still among protection scope of the present invention.
Claims (8)
1. the manufacture method of granite fired terrace of colour concrete, is characterized in that, comprises the steps:
(1) formwork: formwork processing is carried out in the section that construct;
(2) concreting: by concrete evenly build with formwork within the scope of;
(3) be closed flat: the concrete of building is closed flat processing; While being closed flat, as found, concrete surface has excessive moisture, should be scraped;
(4) shed hardening agent: at the concrete being closed flat after processing, in initial set, during the stage, first use the special-purpose hardening agent of 2/3 granite fired autogram ground, evenly shed to concrete surface;
(5) essence is received light: shed the special-purpose hardening agent of granite fired autogram ground, treating that special-purpose hardening agent wet and changes carries out essence receipts light after color and process; To not shedding the very few part of hardening agent or hardening agent, use remaining 1/3 hardening agent to fill up;
(6) shed granite colorant: when essence is received the obvious moisture content of granite hardening agent surface nothing of light, carry out the processing of shedding of granite colorant;
(7) shed release agent: complete after granite colorant sheds, when concrete tentatively condenses, carry out release agent and shed;
(8) inscription rubbing texture: use granite fired face mould tool to be laid in granite fired face colouring agent surface, spelled gap; With skin hammer, evenly beat mould, make its granite fired surface can leave mould lines clearly;
(9) cutting shrinkage joint: treat the completely dry anhydrous timesharing of concrete completing above-mentioned all flow processs, use cutting machine cutting shrinkage joint; Shrinkage joint width is 2-4 millimeter; Then with weather-proof, use glue joint filling;
(10) clean top layer: complete after above-mentioned all flow processs after maintenance 7-10 days; During maintenance, use clear water to rinse out the release agent of concrete surface layer;
(11) spary sealant: when exclusion is dried up on good road surface to be cleaned completely, use flush coater or rotary broom that sealant is evenly sprayed to concrete surface.
2. the manufacture method of granite fired terrace of colour concrete as claimed in claim 1, is characterized in that, in (four) step, described hardening agent raw material weight match ratio is; High strength cement: 600, quartz sand: 400, dimension silica flour: 8, based water reducer how: 3, calcium formate: 3, colorant is appropriate.
3. the manufacture method of granite fired terrace of colour concrete as claimed in claim 2, is characterized in that, colorant adopts iron oxide series colorant to require to allocate according to color.
4. the manufacture method of granite fired terrace of colour concrete as claimed in claim 2, is characterized in that, described quartz sand diameter is 0.5-1mm.
5. the manufacture method of granite fired terrace of colour concrete as claimed in claim 1, it is characterized in that, in (six) step: described colorant raw material weight proportioning: high strength cement: 80, quartz sand: 20, resin rubber powder: 0.5, how based water reducer: 0.3, calcium formate: 0.2, colorant 0.5.
6. the manufacture method of granite fired terrace of colour concrete as claimed in claim 5, is characterized in that, described quartz sand diameter is 0.5-1mm.
7. the manufacture method of granite fired terrace of colour concrete as claimed in claim 1, is characterized in that, in (seven) step: described release agent raw material weight proportioning: heavy fat calcium: 50, light fat calcium: 50, French chalk: 100.
8. the manufacture method of granite fired terrace of colour concrete as claimed in claim 1, is characterized in that, in (11) step, and sealant raw material used: acrylic resin.