CN103553218B - 一种复合缓蚀剂 - Google Patents

一种复合缓蚀剂 Download PDF

Info

Publication number
CN103553218B
CN103553218B CN201310440704.6A CN201310440704A CN103553218B CN 103553218 B CN103553218 B CN 103553218B CN 201310440704 A CN201310440704 A CN 201310440704A CN 103553218 B CN103553218 B CN 103553218B
Authority
CN
China
Prior art keywords
corrosion inhibitor
water
composite corrosion
gelatin
hydrolysis liquid
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310440704.6A
Other languages
English (en)
Other versions
CN103553218A (zh
Inventor
马健岩
许峰
王丽娟
宛美
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Yingkou Kelin Membrane Technology Engineering Service Co.,Ltd.
Original Assignee
Shenyang Jianzhu University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shenyang Jianzhu University filed Critical Shenyang Jianzhu University
Priority to CN201310440704.6A priority Critical patent/CN103553218B/zh
Publication of CN103553218A publication Critical patent/CN103553218A/zh
Application granted granted Critical
Publication of CN103553218B publication Critical patent/CN103553218B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种复合缓蚀剂，可用循环冷却水处理，明胶水解液作为缓蚀组份，加入葡萄糖酸钠、亚硝酸钠和水混合均匀制备而成，其特征在于：该复合缓蚀剂的组份和重量份数为：明胶水解液5~20；葡萄糖酸钠0.3~8；亚硝酸钠1~4；水余量。明胶水解液的主要成份为氨基酸和多肽化合物，用它作为主要原料制备的复合缓蚀剂具有可生物降解，安全环保等优点，并且可以大大降低复合缓蚀剂成本。

Description

一种复合缓蚀剂
技术领域
本发明涉及一种复合缓蚀剂，属于化学工程水处理药剂生产技术领域。
背景技术
水是人类赖以生存的基础，是工业生产运行的命脉，也是我国经济安全和社会发展的“三大战略资源”之一。随着我国工业、经济的迅速发展，工业用水需求快速增长，现有水资源供需矛盾愈显紧张。 水处理化学品，也称水处理剂，它包括工业、城建、环保等方面用于水处理过程的各种药剂，在工业用水中应用广泛，是一类重要的精细化学品。
在城市用水中，工业用水约占80%，冷却用水在我国工业用水中占了相当大的比重（三分之一以上），因此，节约冷却水的用量是节水的关键，是我国目前和今后工业节水工作的重点，已引起了国家政府部门的高度重视。围绕着提高工业循环冷却水的循环再利用率，实现废水深度处理后的回用，降低对水资源的污染，实现低排放和零排放，工业循环冷却水处理化学品也将面临着新的市场机遇和挑战。
工业用水中循环冷却水的耗水量占了相当大的比重，而我国冶金、发电、石油、化工等行业工业循环水年耗水量占到工业用水总量的 50~80%。由此可见，减少直流冷却水***，应用循环冷却水***，提高工业用水的循环利用效率和冷却水***运行浓缩倍数是节水的重要途径之一，也是目前解决我国工业用水紧缺、减少水污染物排放的关键环节。但是，随着浓缩倍数的提高，运行水中Ca2+、Mg2+、CO3 2-、HCO3 -等物质的浓度也相应提高，循环水水质进一步恶化，容易导致循环水***腐蚀、结垢和粘泥滋生。防止循环水***腐蚀与结垢的常用方法是使用水处理剂。
目前新型绿色缓蚀剂开发中，较成功的是聚天冬氨酸。聚天冬氨酸为水溶性聚合物，是一种新型绿色水处理剂，具有无磷、无毒、无公害和可完全生物降解的特性。对离子有极强的螯合能力，具有缓蚀与阻垢双重功效，对碳酸钙等成垢盐类具有良好的阻垢效果，对碳酸钙的阻垢率可达100%，同时具有分散作用并可有效防止金属设备的腐蚀。但其合成制备成本较高。
发明内容
本发明的目的是研制一种成本较低廉，使用方便的复合缓蚀剂。本复合缓蚀剂的特征是以明胶水解液作为主要缓蚀组份，加入葡萄糖酸钠、亚硝酸钠和水混合均匀制备而成，明胶水解液中，主要含有氨基酸和多肽化合物，是缓蚀剂的主要成份，因此，只需要在明胶水解液的基础上复合一定量的其它组份，就可以得到质优价廉的复合缓蚀剂。本发明涉及的复合缓蚀剂，其特征在于该复合缓蚀剂的组份和重量份数为：
明胶水解液 5~20
葡萄糖酸钠 0.3~8
亚硝酸钠 1~4
余量 水 加入30为佳。
优选组份和重量份数为：
明胶水解液 12~18
葡萄糖酸钠 0.6~4
亚硝酸钠 1.2~2
余量 水 加入30为佳。
本发明所说的明胶水解液采用明胶为原料制得，制备方法如下：
配方（重量份数）：
明胶20
硝酸水溶液30~60。
明胶水解液的制备工艺：首先将明胶烘干，然后按配方将计量好的硝酸水溶液和明胶投入到反应釜中，升温至45℃以上，优选为50~65℃，反应2~8小，优选为3~5小时，反应结束后，降温至35℃以下，产物用氢氧化钠中和至pH值7~8，得明胶水解液。
本发明所说的明胶水解用的硝酸水溶液的质量浓度是10%~25%，优选12~15%。
本发明说的水无需特殊处理，普通自来水即可。
上述技术方案所提及的各种原料均可从国内市场上购得。
与现有技术相比，本发明的有益效果是：
1、产品不含磷，对水体无不良影响。
2、使用明胶水解液作为复合缓蚀剂主要组份，可以生物降解，对环境影响较小。
具体实施方式
实施例 将30份水放入混料槽中，依次加入15份明胶水解液，1份葡萄糖酸钠，1.5份亚硝酸钠室温搅拌30分钟，出料得混合均匀复合缓蚀剂。
明胶水解液的制备工艺：首先将明胶烘干，然后按配方将计量好的45份15%硝酸水溶液和20份明胶投入到反应釜中，升温至55℃，反应4小时，反应结束后，降温至35℃以下，用氢氧化钠中和至pH值7~8，得明胶水解液。
在循环冷却时中加入本复合缓蚀剂，保持循环水中复合缓蚀剂的浓度为45mg/L。其结果为：
测定项目 不锈钢腐蚀率 碳钢腐蚀率 污垢热阻 浓缩倍数
单位 mm/a mm/a m2·K/W 以K+计
GB50050-2007 <0.0 <0.075 <3.44╳10-4 5
实施例 0.00004 0.003372 6.22╳10-5 7.121
实例运用得到的四项指标均优于GB50050-2007的规定。

Claims (2)

1.一种复合缓蚀剂，其特征在于：将30份水放入混料槽中，依次加入15份明胶水解液，1份葡萄糖酸钠，1.5份亚硝酸钠室温搅拌30分钟，出料得混合均匀复合缓蚀剂。
2.一种如权利要求1所述的复合缓蚀剂的制备方法，其特征在于：明胶水解液的制备工艺：首先将明胶烘干，然后按配方将计量好的45份15%硝酸水溶液和20份明胶投入到反应釜中，升温至55℃，反应4小时，反应结束后，降温至35℃以下，用氢氧化钠中和至pH值7~8，得明胶水解液。
CN201310440704.6A 2013-09-25 2013-09-25 一种复合缓蚀剂 Active CN103553218B (zh)