CN107937917A - 一种用于链条钝化处理的新型缓蚀剂 - Google Patents
一种用于链条钝化处理的新型缓蚀剂 Download PDFInfo
- Publication number
- CN107937917A CN107937917A CN201711192121.0A CN201711192121A CN107937917A CN 107937917 A CN107937917 A CN 107937917A CN 201711192121 A CN201711192121 A CN 201711192121A CN 107937917 A CN107937917 A CN 107937917A
- Authority
- CN
- China
- Prior art keywords
- parts
- sodium
- imidazoline
- acid
- corrosion inhibitor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种用于链条钝化处理的新型缓蚀剂，由以下重量份数原料组成：环烷酸咪唑啉季铵盐20‑24份、葡萄糖酸钠6‑8份、亚硝酸钠8‑10份、多元共聚聚丙烯酸钠4‑6份、聚天冬氨酸4‑6份、羟基乙叉二磷酸4‑6份、壬基酚聚氧乙烯醚2‑5份、巯基苯并噻唑1‑5份、苯并三氮唑10‑14份、三聚磷酸钠10‑14份、乙醇16‑18份、六次甲基四胺12‑16份、咪唑啉11‑13份、烷胺基醇8‑11份、糠醛9‑11份、去离子水30‑40份。本发明的有益效果为：(1)该缓蚀剂能在金属表面形成致密吸附性保护膜，有效抑制露点及其延长区的腐蚀，成本低，防腐能力强，同时适应于各种水质；(2)该新型缓蚀剂水溶性强，属于理想的环保型缓蚀剂，可推广使用。
Description
技术领域
本发明涉及链条生产加工领域，具体涉及一种用于链条钝化处理的新型缓蚀剂。
背景技术
钝化是使金属表面转化为不易被氧化的状态，而延缓金属的腐蚀速度的方法。另外，一种活性金属或合金，其中化学活性大大降低，而成为贵金属状态的现象，也叫钝化。
钝化处理是化学清洗中最后一个工艺步骤，是关键一步，其目的是为了材料的防腐蚀。如锅炉经酸洗、水冲洗、漂洗后，金属表面很清洁，非常活化，很容易遭受腐蚀，所以必须立即进行钝化处理，使清洗后的金属表面生成保护膜，减缓腐蚀。操作简单，使用方便、经济实用，同时添加了高效缓蚀剂、抑雾剂，防止金属出现过腐蚀和氢脆现象、抑制酸雾的产生。特别适用于小型复杂工件，不适合涂膏的情况，优于市场同类产品。其中，缓蚀剂的选用会直接影响到最终钝化的效果。
缓蚀剂，以适当的浓度和形式存在于环境(介质)中时，可以防止或减缓材料腐蚀的化学物质或复合物，因此缓蚀剂也可以称为腐蚀抑制剂。它的用量很小(0.1％～1％)，但效果显著。这种保护金属的方法称缓蚀剂保护。缓蚀剂用于中性介质(锅炉用水、循环冷却水)、酸性介质(除锅垢的盐酸，电镀前镀件除锈用的酸浸溶液)和气体介质(气相缓蚀剂)。
现有大部分缓蚀剂都只溶于有机溶剂，环保性差，同时原料成本高，最终的耐腐蚀能力差，持久性低。
发明内容
本发明的目的是为了克服现有技术中的不足，提供一种用于链条钝化处理的新型缓蚀剂。
为解决上述技术问题，本发明的技术方案为：
一种用于链条钝化处理的新型缓蚀剂，由以下重量份数原料组成：环烷酸咪唑啉季铵盐20-24份、葡萄糖酸钠6-8份、亚硝酸钠8-10份、多元共聚聚丙烯酸钠4-6份、聚天冬氨酸4-6份、羟基乙叉二磷酸4-6份、壬基酚聚氧乙烯醚2-5份、巯基苯并噻唑1-5份、苯并三氮唑10-14份、三聚磷酸钠10-14份、乙醇16-18份、六次甲基四胺12-16份、咪唑啉11-13份、烷胺基醇8-11份、糠醛9-11份、去离子水30-40份。
进一步的，由以下重量份数原料组成：环烷酸咪唑啉季铵盐20份、葡萄糖酸钠6份、亚硝酸钠8份、多元共聚聚丙烯酸钠4份、聚天冬氨酸4份、羟基乙叉二磷酸4份、壬基酚聚氧乙烯醚2份、巯基苯并噻唑1份、苯并三氮唑10份、三聚磷酸钠10份、乙醇16份、六次甲基四胺12份、咪唑啉11份、烷胺基醇8份、糠醛9份、去离子水30份。
进一步的，由以下重量份数原料组成：环烷酸咪唑啉季铵盐24份、葡萄糖酸钠8份、亚硝酸钠10份、多元共聚聚丙烯酸钠6份、聚天冬氨酸6份、羟基乙叉二磷酸6份、壬基酚聚氧乙烯醚5份、巯基苯并噻唑5份、苯并三氮唑14份、三聚磷酸钠14份、乙醇18份、六次甲基四胺16份、咪唑啉13份、烷胺基醇11份、糠醛11份、去离子水40份。
进一步的，由以下重量份数原料组成：环烷酸咪唑啉季铵盐22份、葡萄糖酸钠7份、亚硝酸钠9份、多元共聚聚丙烯酸钠5份、聚天冬氨酸5份、羟基乙叉二磷酸5份、壬基酚聚氧乙烯醚4份、巯基苯并噻唑3份、苯并三氮唑12份、三聚磷酸钠12份、乙醇17份、六次甲基四胺14份、咪唑啉12份、烷胺基醇9份、糠醛10份、去离子水35份。
本发明的有益效果为：(1)该缓蚀剂能在金属表面形成致密吸附性保护膜，有效抑制露点及其延长区的腐蚀，成本低，防腐能力强，同时适应于各种水质；(2)该新型缓蚀剂水溶性强，属于理想的环保型缓蚀剂，可推广使用。
具体实施方式
为使对本发明的结构特征及所达成的功效有更进一步的了解与认识，用以较佳的实施例配合详细的说明，说明如下：
实施例1
一种用于链条钝化处理的新型缓蚀剂，由以下重量份数原料组成：环烷酸咪唑啉季铵盐20份、葡萄糖酸钠6份、亚硝酸钠8份、多元共聚聚丙烯酸钠4份、聚天冬氨酸4份、羟基乙叉二磷酸4份、壬基酚聚氧乙烯醚2份、巯基苯并噻唑1份、苯并三氮唑10份、三聚磷酸钠10份、乙醇16份、六次甲基四胺12份、咪唑啉11份、烷胺基醇8份、糠醛9份、去离子水30份。
实施例2
一种用于链条钝化处理的新型缓蚀剂，由以下重量份数原料组成：环烷酸咪唑啉季铵盐24份、葡萄糖酸钠8份、亚硝酸钠10份、多元共聚聚丙烯酸钠6份、聚天冬氨酸6份、羟基乙叉二磷酸6份、壬基酚聚氧乙烯醚5份、巯基苯并噻唑5份、苯并三氮唑14份、三聚磷酸钠14份、乙醇18份、六次甲基四胺16份、咪唑啉13份、烷胺基醇11份、糠醛11份、去离子水40份。
实施例3
一种用于链条钝化处理的新型缓蚀剂，由以下重量份数原料组成：环烷酸咪唑啉季铵盐22份、葡萄糖酸钠7份、亚硝酸钠9份、多元共聚聚丙烯酸钠5份、聚天冬氨酸5份、羟基乙叉二磷酸5份、壬基酚聚氧乙烯醚4份、巯基苯并噻唑3份、苯并三氮唑12份、三聚磷酸钠12份、乙醇17份、六次甲基四胺14份、咪唑啉12份、烷胺基醇9份、糠醛10份、去离子水35份。
向盐水中添加本发明所述的新型缓蚀剂，按照80-100mg/L的添加量添加。采用旋转挂片测定。挂片材料选用不锈钢，试验温度为35℃，挂片旋转速度为60r/min，实验时间为60个小时。
其中，缓蚀率(R)计算：
R＝(△G0-△G1)/△G0×100％；式中：△G0为对照组试片实验前、后质量差，单位g；△G1为加入缓蚀剂试片实验前、后质量差，单位g。
结果如下：
| 实施例1 | 实施例2 | 实施例3 | |
| 盐水添加量mg/L | 缓蚀率％ | 缓蚀率％ | 缓蚀率％ |
| 90 | 91.6 | 94.3 | 92.4 |
表1
由表1可知，实施例2中配方缓蚀率效果在盐水添加量为90mg/L条件中最好，适合用在海水链条的制作和生产中使用。
本发明的有益效果为：(1)该缓蚀剂能在金属表面形成致密吸附性保护膜，有效抑制露点及其延长区的腐蚀，成本低，防腐能力强，同时适应于各种水质；(2)该新型缓蚀剂水溶性强，属于理想的环保型缓蚀剂，可推广使用。
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是本发明的原理，在不脱离本发明精神和范围的前提下本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明的范围内。本发明要求的保护范围由所附的权利要求书及其等同物界定。
Claims (4)
1.一种用于链条钝化处理的新型缓蚀剂，其特征在于：由以下重量份数原料组成：环烷酸咪唑啉季铵盐20-24份、葡萄糖酸钠6-8份、亚硝酸钠8-10份、多元共聚聚丙烯酸钠4-6份、聚天冬氨酸4-6份、羟基乙叉二磷酸4-6份、壬基酚聚氧乙烯醚2-5份、巯基苯并噻唑1-5份、苯并三氮唑10-14份、三聚磷酸钠10-14份、乙醇16-18份、六次甲基四胺12-16份、咪唑啉11-13份、烷胺基醇8-11份、糠醛9-11份、去离子水30-40份。
2.根据权利要求1所述的一种用于链条钝化处理的新型缓蚀剂，其特征在于：由以下重量份数原料组成：环烷酸咪唑啉季铵盐20份、葡萄糖酸钠6份、亚硝酸钠8份、多元共聚聚丙烯酸钠4份、聚天冬氨酸4份、羟基乙叉二磷酸4份、壬基酚聚氧乙烯醚2份、巯基苯并噻唑1份、苯并三氮唑10份、三聚磷酸钠10份、乙醇16份、六次甲基四胺12份、咪唑啉11份、烷胺基醇8份、糠醛9份、去离子水30份。
3.根据权利要求1所述的一种用于链条钝化处理的新型缓蚀剂，其特征在于：由以下重量份数原料组成：环烷酸咪唑啉季铵盐24份、葡萄糖酸钠8份、亚硝酸钠10份、多元共聚聚丙烯酸钠6份、聚天冬氨酸6份、羟基乙叉二磷酸6份、壬基酚聚氧乙烯醚5份、巯基苯并噻唑5份、苯并三氮唑14份、三聚磷酸钠14份、乙醇18份、六次甲基四胺16份、咪唑啉13份、烷胺基醇11份、糠醛11份、去离子水40份。
4.根据权利要求1所述的一种用于链条钝化处理的新型缓蚀剂，其特征在于：由以下重量份数原料组成：环烷酸咪唑啉季铵盐22份、葡萄糖酸钠7份、亚硝酸钠9份、多元共聚聚丙烯酸钠5份、聚天冬氨酸5份、羟基乙叉二磷酸5份、壬基酚聚氧乙烯醚4份、巯基苯并噻唑3份、苯并三氮唑12份、三聚磷酸钠12份、乙醇17份、六次甲基四胺14份、咪唑啉12份、烷胺基醇9份、糠醛10份、去离子水35份。