CN103525252B - A kind of attapulgite interior wall powder coating - Google Patents
A kind of attapulgite interior wall powder coating Download PDFInfo
- Publication number
- CN103525252B CN103525252B CN201310396103.XA CN201310396103A CN103525252B CN 103525252 B CN103525252 B CN 103525252B CN 201310396103 A CN201310396103 A CN 201310396103A CN 103525252 B CN103525252 B CN 103525252B
- Authority
- CN
- China
- Prior art keywords
- interior wall
- powder coating
- attapulgite
- wall powder
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of attapulgite interior wall powder coating, it is made up of the raw material of following weight parts: E-12 epoxy resin 10-15, attapulgite 60-70, superfine light calcium carbonate 5-10, polyvinyl alcohol superfines 4-6, titanium dioxide 1-2, BYK-2163 dispersant 0.8-1.2, propane diols phenylate 3-4, dimethicone 0.5-1.0, sodium acid carbonate 2.3-2.8, nano-calcium carbonate 8-9, compounded mix 10-20; Coating of the present invention has good durability, resistance to water, rub resistance and stain resistance, and formaldehyde and volatile organic matter in energy absorbed air, purify air. Attapulgite interior wall powder coating is white standard paint, can directly mix colours and produce the colour-wash of various different colours, and attapulgite interior wall powder coating is applicable to decorating building.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of attapulgite interior wall powder coating.
Background technology
Powdery paints is and the diverse form of general coating that it is to exist with the state of attritive powder. ByIn not using solvent, so be called powdery paints. The main feature of powdery paints has: have harmless, high efficiency,Saving resource and environmental protection feature. Powdery paints be a kind of novel, containing solvent, 100% solid powdery coating.Have without solvent, pollution-free, save the energy and resource, reduce labor intensity and the high spy of film mechanical strengthPoint.
Summary of the invention
The object of the invention is exactly for a kind of attapulgite interior wall powder coating is provided.
The present invention is achieved by the following technical solutions:
A kind of attapulgite interior wall powder coating, is characterized in that what it was made up of the raw material of following weight parts:
E-12 epoxy resin 10-15, attapulgite 60-70, superfine light calcium carbonate 5-10, polyvinyl alcohol surpassFine powder 4-6, titanium dioxide 1-2, BYK-2163 dispersant 0.8-1.2, propane diols phenylate 3-4, dimethylSilicone oil 0.5-1.0, sodium acid carbonate 2.3-2.8, nano-calcium carbonate 8-9, compounded mix 10-20;
Described compounded mix is made up of the raw material of following weight parts:
Suzhou soil 40-50, blanc fixe 40-50, aluminium nitride 6-8, sodium silicoaluminate 2-3, lanolin 2-3,Polyvinyl alcohol 3-4, methylisothiazolinone 1-2;
Above-mentioned methylisothiazolinone is joined in 6-10 times of water, add Suzhou soil and blanc fixe,Insulated and stirred 2-3 hour at 150-200 DEG C, reduction temperature is 100-120 DEG C, adds aluminium nitride, aluminosilicateSodium, lanolin, stir, finally add polyvinyl alcohol, at 60-80 DEG C, stir 1-2 hour, dry,Grind, cross 60-80 mesh sieve, obtain described compounded mix.
A preparation method for attapulgite interior wall powder coating, comprises the following steps:
After above-mentioned each raw material is mixed, in input pulverizer, pulverize, then abrasive dust, the particle after abrasive dust is thinDegree is less than 0.015 millimeter, obtains described attapulgite interior wall powder coating.
Advantage of the present invention is:
Coating of the present invention has good durability, resistance to water, rub resistance and stain resistance, in energy absorbed airFormaldehyde and volatile organic matter, purify air. Attapulgite interior wall powder coating is white standard paint, canDirectly mix colours and produce the colour-wash of various different colours, attapulgite interior wall powder coating is applicable to buildingThing is decorated.
Detailed description of the invention
Embodiment 1,
A kind of attapulgite interior wall powder coating, it by following weight parts (kilogram) raw material form:
E-12 epoxy resin 15, attapulgite 70, superfine light calcium carbonate 10, polyvinyl alcohol superfines 4,Titanium dioxide 1, BYK-2163 dispersant 1.2, propane diols phenylate 4, dimethicone 1.0, sodium acid carbonate 2.8,Nano-calcium carbonate 8, compounded mix 20;
Described compounded mix is made up of the raw material of following weight parts:
Suzhou soil 50, blanc fixe 50, aluminium nitride 8, sodium silicoaluminate 3, lanolin 3, polyvinyl alcohol 3,Methylisothiazolinone 1;
Above-mentioned methylisothiazolinone is joined in 10 times of water, add Suzhou soil and blanc fixe,Insulated and stirred 2 hours at 200 DEG C, reducing temperature is 120 DEG C, add aluminium nitride, sodium silicoaluminate, lanolin,Stir, finally add polyvinyl alcohol, at 80 DEG C, stir 2 hours, dry, grind, cross 80 mesh sieves,Obtain described compounded mix.
A preparation method for attapulgite interior wall powder coating, comprises the following steps:
After above-mentioned each raw material is mixed, in input pulverizer, pulverize, then abrasive dust, the particle after abrasive dust is thinDegree is less than 0.015 millimeter, obtains described attapulgite interior wall powder coating.
Performance test:
Resistance to solvent: 240 hours, unchanged;
Salt spray test (1000h): unchanged.
Claims (2)
1. an attapulgite interior wall powder coating, is characterized in that what it was made up of the raw material of following weight parts:
E-12 epoxy resin 10-15, attapulgite 60-70, superfine light calcium carbonate 5-10, polyvinyl alcohol superfines 4-6, titanium dioxide 1-2, BYK-2163 dispersant 0.8-1.2, propane diols phenylate 3-4, dimethicone 0.5-1.0, sodium acid carbonate 2.3-2.8, nano-calcium carbonate 8-9, compounded mix 10-20;
Described compounded mix is made up of the raw material of following weight parts:
Suzhou soil 40-50, blanc fixe 40-50, aluminium nitride 6-8, sodium silicoaluminate 2-3, lanolin 2-3, polyvinyl alcohol 3-4, methylisothiazolinone 1-2;
Above-mentioned methylisothiazolinone is joined in 6-10 times of water, add Suzhou soil and blanc fixe, insulated and stirred 2-3 hour at 150-200 DEG C, reduction temperature is 100-120 DEG C, adds aluminium nitride, sodium silicoaluminate, lanolin, stirs, and finally adds polyvinyl alcohol, at 60-80 DEG C, stir 1-2 hour, dry, grind, cross 60-80 mesh sieve, obtain described compounded mix.
2. a preparation method for attapulgite interior wall powder coating as claimed in claim 1, is characterized in that comprising the following steps:
After above-mentioned each raw material is mixed, in input pulverizer, pulverize, then abrasive dust, the grain fineness after abrasive dust is less than 0.015 millimeter, obtains described attapulgite interior wall powder coating.