CN103525252A - Attapulgite powder coating for inner walls - Google Patents
Attapulgite powder coating for inner walls Download PDFInfo
- Publication number
- CN103525252A CN103525252A CN201310396103.XA CN201310396103A CN103525252A CN 103525252 A CN103525252 A CN 103525252A CN 201310396103 A CN201310396103 A CN 201310396103A CN 103525252 A CN103525252 A CN 103525252A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder coating
- attapulgite
- inner walls
- polyvinyl alcohol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses attapulgite powder coating for inner walls. The attapulgite powder coating for inner walls is prepared from the following raw materials in parts by weight: 10-15 parts of E-12 epoxy resin, 60-70 parts of attapulgite, 5-10 parts of superfine light calcium carbonate, 4-6 parts of polyvinyl alcohol superfine powder, 1-2 parts of titanium dioxide, 0.8-1.2 parts of BYK-2163 dispersing agent, 3-4 parts of propylene glycol phenylate, 0.5-1.0 part of dimethicone, 2.3-2.8 parts of sodium bicarbonate, 8-9 parts of nano calcium carbonate and 10-20 parts of composite filler. The attapulgite powder coating for inner walls has better durability, water resistance, friction resistance and stain resistance and can adsorb formaldehyde and volatile organic matters in the air and purify the air. The attapulgite powder coating for inner walls is a white standard coating, can be directly subjected to color matching to produce colour coatings in different colours and is applicable to building decoration.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of attapulgite interior wall powder coating.
Background technology
Powder coating is and the diverse form of general coating, and it is that state with fines exists.Owing to not using solvent, so be called powder coating.The principal feature of powder coating has: have harmless, high-level efficiency, saving resource and environmental protection feature.Powder coating be a kind of novel, containing solvent, 100% solid powdery coating.Have without solvent, pollution-free, save the energy and resource, physical strength high reduces labor intensity and films.
Summary of the invention
The object of the invention is exactly for a kind of attapulgite interior wall powder coating is provided.
The present invention is achieved by the following technical solutions:
, it is characterized in that what it was comprised of the raw material of following weight parts:
E-12 epoxy resin 10-15, attapulgite 60-70, superfine light calcium carbonate 5-10, polyvinyl alcohol ultrafine powder 4-6, titanium dioxide 1-2, BYK-2163 dispersion agent 0.8-1.2, propylene glycol phenylate 3-4, dimethyl silicone oil 0.5-1.0, sodium bicarbonate 2.3-2.8, nano-calcium carbonate 8-9, compounded mix 10-20;
Described compounded mix is comprised of the raw material of following weight parts:
Suzhou soil 40-50, blaue fixe 40-50, aluminium nitride 6-8, sodium silicoaluminate 2-3, lanolin 2-3, polyvinyl alcohol 3-4, methylisothiazolinone 1-2;
Above-mentioned methylisothiazolinone is joined in 6-10 times of water, add Suzhou soil and blaue fixe, insulated and stirred 2-3 hour at 150-200 ℃, reduction temperature is 100-120 ℃, adds aluminium nitride, sodium silicoaluminate, lanolin, stirs, and finally adds polyvinyl alcohol, at 60-80 ℃, stir 1-2 hour, dry, grind, cross 60-80 mesh sieve, obtain described compounded mix.
A preparation method for attapulgite interior wall powder coating, comprises the following steps:
After above-mentioned each raw material is mixed, in input pulverizer, pulverize, abrasive dust then, the particle fineness after abrasive dust is less than 0.015 millimeter, obtains described attapulgite interior wall powder coating.
Advantage of the present invention is:
Coating of the present invention has good weather resistance, water tolerance, rub resistance and contamination resistance, and formaldehyde and volatile organic matter in energy absorbed air, purify air.Attapulgite interior wall powder coating is white standard paint, can directly mix colours and produce the colo(u)r coating of various different colours, and attapulgite interior wall powder coating is applicable to decorating building.
Embodiment
Embodiment 1,
, it by following weight parts (kilogram) raw material form:
E-12 epoxy resin 15, attapulgite 70, superfine light calcium carbonate 10, polyvinyl alcohol ultrafine powder 4, titanium dioxide 1, BYK-2163 dispersion agent 1.2, propylene glycol phenylate 4, dimethyl silicone oil 1.0, sodium bicarbonate 2.8, nano-calcium carbonate 8, compounded mix 20;
Described compounded mix is comprised of the raw material of following weight parts:
Suzhou soil 50, blaue fixe 50, aluminium nitride 8, sodium silicoaluminate 3, lanolin 3, polyvinyl alcohol 3, methylisothiazolinone 1;
Above-mentioned methylisothiazolinone is joined in 10 times of water, add Suzhou soil and blaue fixe, at 200 ℃, insulated and stirred is 2 hours, reducing temperature is 120 ℃, adds aluminium nitride, sodium silicoaluminate, lanolin, stirs, and finally adds polyvinyl alcohol, at 80 ℃, stir 2 hours, dry, grind, cross 80 mesh sieves, obtain described compounded mix.
A preparation method for attapulgite interior wall powder coating, comprises the following steps:
After above-mentioned each raw material is mixed, in input pulverizer, pulverize, abrasive dust then, the particle fineness after abrasive dust is less than 0.015 millimeter, obtains described attapulgite interior wall powder coating.
Performance test:
Resistance to solvent: 240 hours, unchanged;
Salt-fog test (1000h): unchanged.
Claims (2)
1. an attapulgite interior wall powder coating, is characterized in that what it was comprised of the raw material of following weight parts:
E-12 epoxy resin 10-15, attapulgite 60-70, superfine light calcium carbonate 5-10, polyvinyl alcohol ultrafine powder 4-6, titanium dioxide 1-2, BYK-2163 dispersion agent 0.8-1.2, propylene glycol phenylate 3-4, dimethyl silicone oil 0.5-1.0, sodium bicarbonate 2.3-2.8, nano-calcium carbonate 8-9, compounded mix 10-20;
Described compounded mix is comprised of the raw material of following weight parts:
Suzhou soil 40-50, blaue fixe 40-50, aluminium nitride 6-8, sodium silicoaluminate 2-3, lanolin 2-3, polyvinyl alcohol 3-4, methylisothiazolinone 1-2;
Above-mentioned methylisothiazolinone is joined in 6-10 times of water, add Suzhou soil and blaue fixe, insulated and stirred 2-3 hour at 150-200 ℃, reduction temperature is 100-120 ℃, adds aluminium nitride, sodium silicoaluminate, lanolin, stirs, and finally adds polyvinyl alcohol, at 60-80 ℃, stir 1-2 hour, dry, grind, cross 60-80 mesh sieve, obtain described compounded mix.
2. a preparation method for attapulgite interior wall powder coating as claimed in claim 1, is characterized in that comprising the following steps:
After above-mentioned each raw material is mixed, in input pulverizer, pulverize, abrasive dust then, the particle fineness after abrasive dust is less than 0.015 millimeter, obtains described attapulgite interior wall powder coating.