CN103469597A - 一种鞋革用全氟烷乙醇泼水剂的制备方法 - Google Patents

一种鞋革用全氟烷乙醇泼水剂的制备方法 Download PDF

Info

Publication number
CN103469597A
CN103469597A CN2012101847868A CN201210184786A CN103469597A CN 103469597 A CN103469597 A CN 103469597A CN 2012101847868 A CN2012101847868 A CN 2012101847868A CN 201210184786 A CN201210184786 A CN 201210184786A CN 103469597 A CN103469597 A CN 103469597A
Authority
CN
China
Prior art keywords
water
agent
preparation
sprinkling
shoe leather
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2012101847868A
Other languages
English (en)
Inventor
蔡建军
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHANGHAI RIDUO HIGH POLYMER MATERIAL Co Ltd
Original Assignee
SHANGHAI RIDUO HIGH POLYMER MATERIAL Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHANGHAI RIDUO HIGH POLYMER MATERIAL Co Ltd filed Critical SHANGHAI RIDUO HIGH POLYMER MATERIAL Co Ltd
Priority to CN2012101847868A priority Critical patent/CN103469597A/zh
Publication of CN103469597A publication Critical patent/CN103469597A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种鞋革用全氟烷乙醇泼水剂的制备方法。该方法是在杜邦BAN的基础上加入DMF及架桥剂等，以达到泼水效果，并在此基础上降低对环境的影响。本发明制备的泼水剂用于鞋革制造，主要是运动鞋，使鞋子具有耐汗、耐水解、防污、透气的性能。

Description

一种鞋革用全氟烷乙醇泼水剂的制备方法
本发明涉及的是一种鞋革用全氟烷乙醇泼水剂的制备方法。 
泼水剂因其疏油疏水性而被广泛应用于合成革行业中。其主要原料为全氟辛酸铵，简称PFOA。它代表全氟辛酸及其含铵的主盐，或称“C8”，为一种人工合成的化学品。它能够在皮革表面形成一层致密的氟化表面层，其极低的表面能使水或油难于亲和，从而使其处理后的皮革在具有防水防油性能的同时，皮革的天然质地保持不变，仍具有良好的透气性及柔软的手感等。 
但随着环境污染问题的日益严重，PFOA由于在结构上造成的难降解问题，慢慢引起人们的重视。据有关研究表明，PFOA难以在自然环境中降解，具备持久性有机污染物的的基本特征。科学家发现接触包括PFOA的化学品可能导致初生婴儿缺陷，对免疫***产生不利影响，也会破坏甲状腺功能。美国环境保护局认为可致癌的PFOA以及职业接触的PFOA都与膀胱癌发生率的增加有关系。因此，如何解决泼水剂对环境以及人体的影响，寻找PFOA的替代品，成为该领域技术人员亟待解决的课题。 
本发明的目的是针对现在泼水剂中PFOA难降解及对环境与人体的影响所存在的问题，找到一种代替PFOA的新产品。本发明的原理就是在杜邦BAN的基础上加入DMF及架桥剂，已达到泼水效果，并在此基础上降低对环境的影响。 
杜邦BAN的外观为棕褐色固体，它的成分见下表： 
  成分   极限％   典型％
  总的所有2全氟烷   92.0   95.0
  2-perfluorohexyl乙醇   5.5最大   1.0
  2，全氟乙醇   40.0最大   50.0
  2perfluorohexyl(或以上)ethanols   18.5最大   15.0
  2，全氟乙基碘   4.0最大   3.0
  水   0.05最大   0.02
本发明的一种鞋革用全氟烷乙醇泼水剂的制备工艺如下： 
本发明的环保型泼水剂是在反应釜中按下表所列配比加入BAN、架桥剂、二甲基甲酰胺(DMF)等原料，控制温度在80℃下反应三小时，最后加入甲醇终止反应而得到的。具体配比如下： 
Figure BSA00000729816700011
用途：本发明所得的泼水剂用于鞋革制造，主要是运动鞋，使鞋子耐汗、耐水解、防污、透气。本发明的泼水剂产品质量稳定，并在成本、原料消耗等方面取得了新的突破，对合成革产业低碳、清洁生产做出了贡献。 
举例： 
本实施例在以本发明技术方案为前提下进行实施，给出了详细的实施方式和过程，不能理解为对本发明保护范围的限制。下列实施例中未注明具体的试验方法，通常按照常规条件，或按照制鞋革厂所建议的条件。 
实施例1 
步骤一，含浸料配制，称取湿法树脂100g，DMF 250g，黑色浆10g，搅拌均匀。 
步骤二，刮涂料配制，称取湿法树脂200g，DMF 114g，色料6g，木质粉3g，S-74g，S-230.6g，搅拌均匀。 
步骤三，将含浸料倒入盘中，无纺布含浸30-50s，用压车进行无间隙挤压，在20％DMF溶液中浸泡30s，再次用压车无间隙挤压。 
步骤四，进行刮涂上料，完成之后浸入20％DMF溶液中凝固20分钟。 
步骤五，挤压清洗10次使其中DMF彻底消除。 
步骤六，在120-130℃烘干并裁剪成长20em，宽3cm的布条进行耐水解高剥离测试。 
剥离强度结果如下：                        单位：kgf/mm 
  无纺布含浸+刮涂   无(没加泼水剂)
  水解前   110
  70℃×3h   75
  24h常温   20
注：测定剥离强度用台湾高铁的微电脑拉力试验机，型号：GT-7010-D2ELP。 
实施例2 
步骤同上，在含浸料中加入泼水剂1.0％。 
剥离强度结果如下：                         单位：kgf/mm 
  无纺布含浸+刮涂   加入1.0％泼水剂
  水解前   220
  70℃×3h   175
  24h常温   90
注：测定剥离强度用台湾高铁的微电脑拉力试验机，型号：GT-7010-D2ELP。 
实施例3 
步骤同上，在含浸料中加入泼水剂2.0％。 
剥离强度结果如下：                          单位：kgf/mm 
  无纺布含浸+刮涂   加入2.0％泼水剂
  水解前   230
  70℃×3h   190
  24h常温   110
注：测定剥离强度用台湾高铁的微电脑拉力试验机，型号：GT-7010-D2ELP。 
实施例1-3比较剥离强度结果如下(单位：kgf/mm)： 
  无纺布含浸+刮涂   无(没加泼水剂)   加入1.0％泼水剂   加入2.0％泼水剂
  水解前   110   220   230
  70℃×3h   75   175   190
  24h常温   20   90   110
注：测定剥离强度用台湾高铁的微电脑拉力试验机，型号：GT-7010-D2ELP。 

Claims (1)

1.一种鞋革用全氟烷乙醇泼水剂的制备方法：其特征是在杜邦BAN的基础上加入DMF、架桥剂、硅油、聚醚及甲醇，控制温度在80℃下反应三小时，制得的泼水剂用于鞋革制造，主要是运动鞋，使鞋子具有耐汗、耐水解、防污、透气的性能。
CN2012101847868A 2012-06-06 2012-06-06 一种鞋革用全氟烷乙醇泼水剂的制备方法 Pending CN103469597A (zh)