CN103450740B - 用于工业喷头的热升华喷墨墨水及其制备方法 - Google Patents
用于工业喷头的热升华喷墨墨水及其制备方法 Download PDFInfo
- Publication number
- CN103450740B CN103450740B CN201310454753.5A CN201310454753A CN103450740B CN 103450740 B CN103450740 B CN 103450740B CN 201310454753 A CN201310454753 A CN 201310454753A CN 103450740 B CN103450740 B CN 103450740B
- Authority
- CN
- China
- Prior art keywords
- ink
- disperse
- red
- agent
- yellow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种喷墨墨水，尤其涉及一种用于工业喷头的热升华喷墨墨水及其制备方法，所述热升华喷墨墨水按重量百分比包括以下组分：分散染料1～6%，保湿剂10～40%，黏度调节剂5～20%，杀菌剂0.1～2%，pH缓冲剂0.01～1%，树脂液1～10%，分散剂0.1～40%，消泡剂0.01～5%，表面活性剂0.1～5%，金属离子螯合剂0.01～2%，纯净水10～80%。该用于工业喷头的热升华喷墨墨水的制备方法包括色浆的制备和成品的制备。该用于工业喷头的热升华喷墨墨水,其制备方法简单，喷墨流畅，不会堵塞喷头，且粒径分散均匀，分散稳定性好，长时间储存也不会变腐或变性，成本较低。
Description
技术领域
本发明涉及一种喷墨墨水，尤其涉及一种用于工业喷头的热升华喷墨墨水及其制备方法。
背景技术
随着印刷技术的快速发展，纳米研磨技术的广泛应用，个性化服饰的设计和定制及新型数码喷绘机械设备的投入，数码纺织墨水也得到了前所未有的发展，喷墨打印机用热升华墨水由于其色彩鲜艳、分辨率高、操作灵活而被应用于个性化产品的定制，如转印有各种不同图案的杯子、水晶、T恤等。热升华墨水一般需要转印介质与其配合才能实施转印，因此其应用范围一般局限于小型喷墨打印机，对无转印介质配合要求的精工等工业喷头几乎没有适用性，以致在纺织品领域不能实现大批量的工业生产。
喷墨印花技术以其小批量、短工艺流程以及快速交付的特点，可满足于消费者个性化、多样化的需求，广泛地应用于户外广告喷绘、纺织品喷墨印花等各个领域。
近年来，随着国内喷墨打印机生产技术的不断提高，陆续出现了各种品牌的宽幅压电喷墨打印机，以用于热升华墨水的纺织品打印，这些喷墨打印机其喷墨速度快，工作效率高，无需进行转印即可将图案直接升华到记录介质上。然而由于进口墨水耗材价格昂贵，运输期长，成本高昂；国产墨水由于在使用过程中会出现堵头现象，且颜色不正，转移率低，极大地影响了生产效率。
发明内容
本发明的目的之一在于：针对现有技术存在的不足，提供一种成本低，转移率高，不会堵塞打印机喷头的用于工业喷头的热升华喷墨墨水。
为解决上述技术问题，本发明的技术方案是：
用于工业喷头的热升华喷墨墨水，所述喷墨墨水按重量百分比包括以下组分：分散染料1～6%，保湿剂10～40%，黏度调节剂5～20%，杀菌剂0.1～2%，pH缓冲剂0.01～1%，树脂液1～10%，分散剂0.1～40%，流平剂0.01～5%，表面活性剂0.1～5%，消泡剂0.1～1%，金属离子螯合剂0.01～2%，余量为超纯水。
作为一种改进，所述喷墨墨水按重量百分比包括以下组分：所述分散染料1～3%，所述保湿剂15～25%，所述黏度调节剂15～20%，所述杀菌剂0.1～0.8%，所述pH缓冲剂0.01～0.5%，所述树脂液4～8%，所述分散剂10～30%，所述流平剂1～3%，所述表面活性剂0.1～3%，所述消泡剂0.5～1%，所述金属离子螯合剂1.5～2%，余量为超纯水。
优选的，所述分散染料是C.I.分散红4、C.I.分散红9、C.I.分散红11、C.I.分散红19、C.I.分散红22、C.I.分散红50、C.I.分散红53、C.I.分散红54、C.I.分散红60、C.I.分散红72、C.I.分散红73、C.I.分散红74、C.I.分散红82、C.I.分散红86、C.I.分散红92、C.I.分散红146、C.I.分散红153、C.I.分散红167、C.I.分散红177、C.I.分散红278、C.I.分散紫41、C.I.分散蓝3、C.I.分散蓝14、C.I.分散蓝20、C.I.分散蓝35、C.I.分散蓝56、C.I.分散蓝60、C.I.分散蓝72、C.I.分散蓝73、C.I.分散蓝87、C.I.分散蓝165、C.I.分散蓝183、C.I.分散蓝301、C.I.分散蓝359、C.I.分散蓝366、C.I.分散黄3、C.I.分散黄5、C.I.分散黄7、C.I.分散黄23、C.I.分散黄42、C.I.分散黄50、C.I.分散黄51、C.I.分散黄54、C.I.分散黄60、C.I.分散黄64、C.I.分散黄65、C.I.分散黄79、C.I.分散黄82、C.I.分散黄98、C.I.分散黄104、C.I.分散黄124、C.I.分散黄160、C.I.分散黄211、C.I.分散黑9中的一种或几种。
优选的，所述保湿剂为醇类或酯类，优选为乙二醇、二乙二醇、三乙二醇、四乙二醇、甘油、聚乙二醇200、聚乙二醇400、聚乙二醇600、N-甲基吡咯烷酮、2-吡咯烷酮乙二醇丁醚、二乙二醇丁醚、三乙二醇丁醚、二乙二醇二***、丙二醇甲醚中的一种或几种。
优选的，所述黏度调节剂为甘油、山梨醇、木糖醇、甘露糖醇、苏糖醇、赤藓糖醇、半乳糖醇、麦芽醇、1,5-戊二醇、1,2-己二醇、丙二醇中的一种或几种；所述杀菌剂为5-氯-2-甲基-4-异噻唑啉-3-酮、20%1,2-苯并异噻唑啉-3-酮的二丙二醇水溶液中的一种或两者的混合物。
优选的，所述pH缓冲剂为三乙醇胺、二乙醇胺、乙醇胺、三羟甲基氨基甲烷、氢氧化钠、碳酸氢钠、碳酸钠中的一种或几种；所述树脂液为水性丙烯酸树脂液、水性聚氨酯树脂液、改性二元氯醋树脂液中的一种或几种。
优选的，所述分散剂为木质素磺酸钠盐、乙撑双硬脂酸酰胺、芳香族磺酸钠盐的***缩合物、BYK分散剂、Tego分散剂中的一种或几种，其中BYK分散剂优选为BYK-190、BYK-191或BYK-2012中的一种或几种，Tego分散剂优选为Tego-775。
优选的，所述流平剂为BYK流平剂、EFKA流平剂中的一种或几种，其中BYK流平剂优选为BYK-380N或BYK-333，EFKA流平剂优选为EFKA-4560。
优选的，所述消泡剂为Surfynol消泡剂、EnviroGem消泡剂中的一种或几种，其中EnviroGem消泡剂优选为EnviroGemAD-01，其中Surfynol消泡剂优选为SurfynolMD-20、SurfynolDF-75中的一种或几种。
BYK的主要成分是有机硅，属于有机硅类表面活性剂;EFKA的主要成分为改性的聚丙烯酸酯;TEGO的主要成分为有机硅丙烯酸酯，是反应性聚硅氧烷丙烯酸酯类;Surfynol是一种液态、含100%活性成分的无硅酮消泡剂。
优选的，所述表面活性剂为ET表面活性剂、Surfynol表面活性剂、BYK表面活性剂中的一种或几种，所述ET表面活性剂优选为ET-115或ET-135，所述Surfynol表面活性剂优选为Surfynol465、Surfynol104e、SurfynolTG、SurfynolCT-221中的一种或几种，所述BYK表面活性剂优选为BYK-345，其中ET表面活性剂属于烷基聚氧乙烯醚类。
优选的，所述金属离子螯合剂为EDTA、EDTA-2Na、EDTA-4Na、柠檬酸铵中的一种或几种。
本发明的配方中：
分散染料，其分子较小，其粒径通常在2μm以下，结构上不含水溶性基团，借助于分散剂的作用在染液中均一分散而进行染色，其能上染聚酯纤维，醋酯纤维及聚酯胺纤维，尤其是涤纶的专用染料。分散染料大致可分为分散橙、分散蓝、分散黄、分散红，可以几种不同分散染料进行按一定的比例进行搭配，得到分散黑、分散绿、分散紫等分散染料。分散染料可通过升华进入聚酯纤维分子间而使织物着色，其分散性好，不会产生沉淀而堵塞喷头，且不会影响织物的手感。
保湿剂为水溶性有机溶剂，分散染料能很好地溶于水溶性有机溶剂中，既能提高喷墨墨水的保湿性能，同时还能提高分散染料的转移率。
黏度调节剂主要用于调节喷墨墨水的黏度，避免墨水过稠或过稀，增加其流动性，且不会影响织物的柔软度。
杀菌剂用于消除喷墨墨水中的各种病原微生物，提高喷墨墨水的稳定性，延长其储存时间。
pH缓冲剂用于调节喷墨墨水的酸碱度，使喷墨墨水具有一定的碱度，一是提高其色泽度，二是减少喷墨墨水对喷头的腐蚀作用。
树脂液与本发明中的其他组分相互配合，使得喷墨墨水能够在非吸收性基材上很快干燥，具有很好地附着性，且能使得具有耐光性材料的耐光性不至于下降，同时又具有良好的物理性能。
分散剂是一种在分子内同时具有亲油性和亲水性两种相反性质的界面活性剂，可均匀地分散那些难溶解于液体的无机、有机颜料的固体颗粒，同时也能防止固体颗粒的沉降和凝聚。分散剂能缩短分散染料在水溶性体系中的分散时间，改性分散染料粒子的表面性质，调整分散染料粒子的运动性，可提高喷墨墨水的光泽、着色力和遮盖力，改善其展色性和调色性，防止浮色发花和絮凝，分散剂与树脂液有良好地相容性，提高了喷墨墨水的热稳定性。
流平剂，能促使墨水在干燥成膜过程中形成一个平整、光滑、均匀的涂膜。
消泡剂，能够防止喷墨墨水中气泡的产生。
表面活性剂能提高喷墨墨水表面的张力，使分散染料在水溶性体系中更加稳定且使喷墨墨水在打印基材中更加充分湿润。
金属离子螯合剂能够加速喷墨后墨水水分的挥发，且能提高喷墨墨水的光亮度。
超纯水中除了水分子外，几乎没有什么杂质，能够提高喷墨墨水的质量。
本发明的另一目的在于提供该用于工业喷头的热升华喷墨墨水的制备方法，本发明的技术方案是：
用于工业喷头的热升华喷墨墨水的制备方法，包括以下步骤：
色浆的制备：按比例取分散染料、分散剂和消泡剂，再取保湿剂用量的30～50%、表面活性剂用量的50～70%和超纯水用量的40～60%，在常温下混合，搅拌均匀，研磨20～30小时，使研磨后的混合物的平均粒径小于150nm，得色浆；
（2）成品的制备：按比例取杀菌剂、PH缓冲剂、黏度调节剂、树脂液、流平剂和金属离子螯合剂，再取上述色浆、余量的保湿剂用量、表面活性剂用量和超纯水用量，在常温下混合，研磨分散1～2h，离心，经过滤孔径为1μm的过滤器粗过滤，再分别经过滤孔径为0.45μm和0.22μm的过滤器精过滤，得成品。
作为一种改进，步骤（1）中，研磨后的所述混合物的平均粒径小于90nm。
由于采用了上述技术方案，本发明的有益效果是：
本发明提供的用于工业喷头的热升华喷墨墨水，可以通过热转印的方式转印，转印过程中发烟少，转印时间短，转移率高，耐水洗性能强；也可以通过直接喷印的方式实现着色，由于其粘度低，其喷墨流畅，不会堵塞喷头，且粒径分散均匀，分散稳定性好，长时间储存也不会变腐或变性，pH缓冲剂、树脂液和金属离子螯合剂的结合使得打印的图案色泽度和固色率高，本发明的墨水在转移过程中转移率高，染料残留量少，转移后色彩立体感强烈，图案界面边沿清晰不模糊，且其成本较低。本发明制备的黑色墨水特别黑，不偏色。
具体实施方式
为了使本发明的目的、技术方案及优点更加清楚明白，以下结合实施例，对本发明进行进一步详细说明。应当理解，此处所描述的具体实施例仅仅用以解释本发明，并不用于限定本发明。
实施例一
用于工业喷头的热升华喷墨墨水（红色）
配方：
制备方法：
（1）色浆的制备：取上述比例的C.I.分散红60、SurfynolMD-20（上海桑井化工有限公司）和木质素磺酸钠，再取二乙二醇用量的50%、1%Surfynol-104e（深圳市新志和化工原料有限公司）用量的50%和超纯水用量的40%，在常温下混合，搅拌均匀后于砂磨机里研磨28h，测研磨后的混合物的粒径，使其平均粒径d50小于90nm，d90小于150nm，得红色色浆；
（2）成品的制备：取上述比例的20%1,2-苯并异噻唑啉-3-酮的二丙二醇水溶液、三乙醇胺、甘油、水性丙烯酸树脂液、BYK-380N（毕克化学（铜陵）有限公司）和EDTA-4Na，再取上述色浆、二乙二醇用量的50%、Surfynol-104e（深圳市新志和化工原料有限公司）用量的50%和超纯水用量的60%，在常温下混合，继续研磨分散1h，用过滤孔径为1μm过滤器粗过滤后，再分别用过滤孔径为0.45μm和0.22μm过滤器精过滤，制成红色墨水。
实施例二
用于工业喷头的热升华喷墨墨水（蓝色）
配方：
| 组分 | 含量（重量%） |
| C.I.分散蓝72 | 5 |
| 三乙二醇 | 20 |
| 山梨醇 | 10 |
| 5-氯-2-甲基-4-异噻唑啉-3-酮 | 0.1 |
| 三羟甲基氨基甲烷 | 0.5 |
| 水性聚氨酯树脂液 | 3 |
| BYK-190 | 40 |
| EFKA-4560 | 0.6 |
| ET-115 | 0.7 |
| SurfynolDF-75 | 0.1 |
| EDTA-2Na | 1 |
| 超纯水 | 19 |
制备方法：
（1）色浆的制备：取上述比例的C.I.分散蓝72、SurfynolDF-75(广州联固精细化学有限公司)和BYK-190（毕克化学（铜陵）有限公司），再取三乙二醇用量的30%、ET-115用量的60%和超纯水用量的60%，在常温下混合，搅拌均匀后于砂磨机里研磨28h，测研磨后的混合物的粒径，使其平均粒径d50小于90nm，d90小于120nm，即得蓝色色浆；
（2）成品的制备：取上述比例的5-氯-2-甲基-4-异噻唑啉-3-酮、三羟甲基氨基甲烷、山梨醇、水性聚氨酯树脂液、EFKA-4560（巴斯夫（中国）有限公司）和EDTA-2Na，再取上述色浆、取三乙二醇用量的70%、ET-115用量的40%和超纯水用量的40%，在常温下混合，继续研磨分散1.5h，用过滤孔径为1μm过滤器粗过滤后，再分别用过滤孔径为0.45μm和0.22μm过滤器精过滤，制成蓝色墨水。
实施例三
用于工业喷头的热升华喷墨墨水（黄色）
配方：
| 组分 | 含量（重量%） |
| C.I.分散黄54 | 3 |
| 聚乙二醇600 | 30 |
| 甘露糖醇 | 15 |
| 5-氯-2-甲基-4-异噻唑啉-3-酮 | 1 |
| 二乙醇胺 | 0.2 |
| 改性二元氯醋树脂液 | 5 |
| 乙撑双硬脂酸酰胺 | 30 |
| BYK-333 | 3 |
| SurfynolCT-221 | 2 |
| EnviroGemAD-01 | 0.3 |
| EDTA | 0.5 |
| 超纯水 | 10 |
制备方法：
（1）色浆的制备：取上述比例的C.I.分散黄54、EnviroGemAD-01（东之风进出口（深圳）有限公司）和BYK-333（毕克化学（铜陵）有限公司），再取聚乙二醇600用量的40%、SurfynolCT-221（深圳市新志和化工原料有限公司）用量的70%和超纯水用量的40%，在常温下混合，搅拌均匀后于砂磨机里研磨30h，测研磨后的混合物的粒径，使其平均粒径d50小于80nm，d90小于120nm，即得黄色色浆；
（2）成品的制备：取上述比例的5-氯-2-甲基-4-异噻唑啉-3-酮、甘露糖醇、二乙醇胺、改性二元氯醋树脂液、乙撑双硬脂酸酰胺和EDTA，再取上述色浆、聚乙二醇600用量的60%、SurfynolCT-221（深圳市新志和化工原料有限公司）用量的30%和超纯水用量的60%，在常温下混合，继续研磨分散2h，用过滤孔径为1μm过滤器粗过滤后，再分别用过滤孔径为0.45μm和0.22μm过滤器精过滤，制成黄色墨水。
实施例四
用于工业喷头的热升华喷墨墨水（红色）
配方：
| 组分 | 含量（重量%） |
| C.I.分散红153 | 1 |
| 二乙二醇丁醚 | 15 |
| 1,5-戊二醇 | 5 |
| 5-氯-2-甲基-4-异噻唑啉-3-酮 | 0.5 |
| 碳酸氢钠 | 0.03 |
| 水性聚氨酯树脂液 | 1 |
| Tego-775 | 0.1 |
| BYK-380 | 0.01 |
| ET-135 | 0.1 |
| SurfynolDF-75 | 0.25 |
| EDTA-2Na | 0.01 |
| 超纯水 | 77 |
制备方法：
（1）色浆的制备：取上述比例的C.I.分散红153、SurfynolDF-75(广州联固精细化学有限公司)和BYK-380（毕克化学（铜陵）有限公司），再取二乙二醇丁醚用量的50%、ET-135用量的55%和超纯水用量的45%，在常温下混合，搅拌均匀后于砂磨机里研磨30h，测研磨后的混合物的粒径，使其平均粒径d50小于80nm，d90小于130nm，即得红色色浆；
（2）成品的制备：取上述比例的5-氯-2-甲基-4-异噻唑啉-3-酮、1,5-戊二醇、碳酸氢钠、水性聚氨酯树脂液、Tego-775（赢创德固赛特种化学（上海）有限公司）和EDTA-2Na，再取上述色浆、二乙二醇丁醚用量的50%、ET-135用量的45%和超纯水用量的55%，在常温下混合，继续研磨分散1.5h，用过滤孔径为1μm过滤器粗过滤后，再分别用过滤孔径为0.45μm和0.22μm过滤器精过滤，制成红色墨水。
实施例五
用于工业喷头的热升华喷墨墨水（蓝色）
配方：
| 组分 | 含量（重量%） |
| C.I.分散蓝359 | 2 |
| N-甲基吡咯烷酮 | 25 |
| 麦芽醇 | 8 |
| 20%1,2-苯并异噻唑啉-3-酮的二 | 0.8 |
| 丙二醇水溶液 | |
| 氢氧化钠 | 0.1 |
| 水性丙烯酸树脂液 | 4 |
| BYK-2012 | 10 |
| EFKA-4560 | 1 |
| SurfynolTG | 3 |
| SurfynolMD-20 | 0.6 |
| EDTA-4Na | 1.5 |
| 超纯水 | 44 |
制备方法：
（1）色浆的制备：取上述比例的C.I.分散蓝359、SurfynolMD-20（上海桑井化工有限公司）和BYK-2012（毕克化学（铜陵）有限公司），再取N-甲基吡咯烷酮用量的38%、SurfynolTG（深圳市新志和化工原料有限公司）用量的57%和超纯水用量的54%，在常温下混合，搅拌均匀后于砂磨机里研磨28h，测研磨后的混合物的粒径，使其平均粒径d50小于60nm，d90小于90nm，即得蓝色色浆；
（2）成品的制备：取上述比例的20%1,2-苯并异噻唑啉-3-酮的二丙二醇水溶液、麦芽醇、氢氧化钠、水性丙烯酸树脂液、BYK-2012（毕克化学（铜陵）有限公司）和EDTA-4Na，再取上述色浆、N-甲基吡咯烷酮用量的62%、SurfynolTG（深圳市新志和化工原料有限公司）用量的43%和超纯水用量的46%，在常温下混合，继续研磨分散2h，用过滤孔径为1μm过滤器粗过滤后，再分别用过滤孔径为0.45μm和0.22μm过滤器精过滤，制成蓝色墨水。
实施例六
用于工业喷头的热升华喷墨墨水（黄色）
配方：
制备方法：
（1）色浆的制备：取上述比例的C.I.分散黄160、EnviroGemAD-01（东之风进出口（深圳）有限公司）和木质素磺酸钠盐，再取丙二醇甲醚用量的44%、SurfynolCT-221（深圳市新志和化工原料有限公司）用量的62%和超纯水用量的58%，在常温下混合，搅拌均匀后于砂磨机里研磨28h，测研磨后的混合物的粒径，使其平均粒径d50小于60nm，d90小于90nm，即得黄色色浆；
（2）成品的制备：取上述比例的20%1,2-苯并异噻唑啉-3-酮的二丙二醇水溶液、木糖醇、乙醇胺、水性丙烯酸树脂液、BYK-380N（毕克化学（铜陵）有限公司）和EDTA-4Na，再取上述色浆、丙二醇甲醚用量的56%、SurfynolCT-221（深圳市新志和化工原料有限公司）用量的38%和超纯水用量的42%，在常温下混合，继续研磨分散2h，用过滤孔径为1μm过滤器粗过滤后，再分别用过滤孔径为0.45μm和0.22μm过滤器精过滤，制成黄色墨水。
实施例七
用于工业喷头的热升华喷墨墨水（黑色）
配方：
制备方法：
（1）色浆的制备：取上述比例的C.I.分散黑9、EnviroGemAD-01（东之风进出口（深圳）有限公司）和木质素磺酸钠盐，再取乙二醇用量的50%、ET-115用量的60%和超纯水用量的45%，在常温下混合，搅拌均匀后于砂磨机里研磨30h，测研磨后的混合物的粒径，使其平均粒径d50小于80nm，d90小于110nm，即得黑色色浆；
（2）成品的制备：取上述比例的20%1,2-苯并异噻唑啉-3-酮的二丙二醇水溶液、1,5-戊二醇、三乙醇胺、水性聚氨酯树脂液、EFKA-4560和EDTA，再取上述色浆、乙二醇用量的50%、ET-115用量的40%和超纯水用量的55%，在常温下混合，继续研磨分散2h，用过滤孔径为1μm过滤器粗过滤后，再分别用过滤孔径为0.45μm和0.22μm过滤器精过滤，制成黑色墨水。
| 国外样品1 | 国内样品2 | 国内样品3 | 实施例七 | |
| 转移率 | 90.5% | 85.7% | 81.4% | 92.1% |
| 黑色色相 | 纯黑 | 偏红偏浅 | 偏红偏浅 | 纯黑 |
| 流畅性 | 3 | 5 | 11 | 2 |
| 界面清晰度 | 一般 | 一般 | 模糊 | 清晰 |
| 日晒牢度 | 5 | 4 | 4 | 6 |
| 水洗牢度 | 4 | 4 | 3 | 5 |
转移率、日晒牢度、水洗牢度，均按照行业规定方法检测。
流畅性为四色纯色块连续性打印20m后堵喷孔的个数。
黑色色相为行业内默认观测方法。
实施例八
用于工业喷头的热升华喷墨墨水（黑色）
按重量百分比，取实施例三中的黄色墨水40%、实施例一中的红色墨水30%、实施例二中的蓝色墨水30%，混合后分散1h，用过滤孔径为1μm过滤器粗过滤后，再分别用过滤孔径为0.45μm和0.22μm过滤器精过滤，制成黑色墨水。
实施例九
用于工业喷头的热升华喷墨墨水（黑色）
按重量百分比，取实施例六中的黄色墨水35%、实施例四中的红色墨水35%、实施例五中的蓝色墨水30%，混合后分散1h，用1μm过滤器粗过滤后，再分别用0.45μm和0.22μm过滤器精过滤，制成黑色墨水。
墨水的各项参数测定：
将上述实施例1-9所制的墨水在25℃下进行理化参数测定，其测定的事项和所得数据如下表所示：
从上表中可以看出，本发明提供的用于工业喷头的热升华喷墨墨水粘度小，表面张力大，打印流畅，不会堵塞打印机喷头。
以上所述仅为本发明的较佳实施例而已，并不用以限制本发明，凡在本发明的精神和原则之内所作的任何修改、等同替换和改进等，均应包含在本发明的保护范围之内。
Claims (8)
1.用于工业喷头的热升华喷墨墨水，其特征在于：所述喷墨墨水按重量百分比包括以下组分：分散染料1～3％，保湿剂15～25％，黏度调节剂15～20％，杀菌剂0.1～0.8％，pH缓冲剂0.01～0.5％，树脂液4～8％，分散剂10～30％，流平剂1～3％，表面活性剂0.1～3％，消泡剂0.5～1％，金属离子螯合剂1.5～2％，余量为超纯水；
所述树脂液为水性丙烯酸树脂液、水性聚氨酯树脂液、改性二元氯醋树脂液中的一种或几种；
所述流平剂为BYK流平剂、EFKA流平剂中的一种或几种；
所述消泡剂为Surfynol消泡剂、EnviroGem消泡剂中的一种或几种；
所述表面活性剂为ET表面活性剂、Surfynol表面活性剂、BYK表面活性剂中的一种或几种；
所述金属离子螯合剂为EDTA、EDTA-2Na、EDTA-4Na、柠檬酸铵中的一种或几种。
2.如权利要求1所述的用于工业喷头的热升华喷墨墨水，其特征在于:所述分散染料是C.I.分散红4、C.I.分散红9、C.I.分散红11、C.I.分散红19、C.I.分散红22、C.I.分散红50、C.I.分散红53、C.I.分散红54、C.I.分散红60、C.I.分散红72、C.I.分散红73、C.I.分散红74、C.I.分散红82、C.I.分散红86、C.I.分散红92、C.I.分散红146、C.I.分散红153、C.I.分散红167、C.I.分散红177、C.I.分散红278、C.I.分散紫41、C.I.分散蓝3、C.I.分散蓝14、C.I.分散蓝20、C.I.分散蓝35、C.I.分散蓝56、C.I.分散蓝60、C.I.分散蓝72、C.I.分散蓝73、C.I.分散蓝87、C.I.分散蓝165、C.I.分散蓝183、C.I.分散蓝301、C.I.分散蓝359、C.I.分散蓝366、C.I.分散黄3、C.I.分散黄5、C.I.分散黄7、C.I.分散黄23、C.I.分散黄42、C.I.分散黄50、C.I.分散黄51、C.I.分散黄54、C.I.分散黄60、C.I.分散黄64、C.I.分散黄65、C.I.分散黄79、C.I.分散黄82、C.I.分散黄98、C.I.分散黄104、C.I.分散黄124、C.I.分散黄160、C.I.分散黄211、C.I.分散黑9中的一种或几种。
3.如权利要求1所述的用于工业喷头的热升华喷墨墨水，其特征在于:所述保湿剂为乙二醇、二乙二醇、三乙二醇、四乙二醇、甘油、聚乙二醇200、聚乙二醇400、聚乙二醇600、N-甲基吡咯烷酮、2-吡咯烷酮、乙二醇丁醚、二乙二醇丁醚、三乙二醇丁醚、二乙二醇二***、丙二醇甲醚中的一种或几种。
4.如权利要求1所述的用于工业喷头的热升华喷墨墨水，其特征在于:所述黏度调节剂为甘油、山梨醇、木糖醇、甘露糖醇、苏糖醇、赤藓糖醇、半乳糖醇、麦芽醇、1,5-戊二醇、1,2-己二醇、丙二醇中的一种或几种；所述杀菌剂为5-氯-2-甲基-4-异噻唑啉-3-酮、20％1,2-苯并异噻唑啉-3-酮的二丙二醇水溶液中的一种或两者的混合物。
5.如权利要求1所述的用于工业喷头的热升华喷墨墨水，其特征在于:所述pH缓冲剂为三乙醇胺、二乙醇胺、乙醇胺、三羟甲基氨基甲烷、氢氧化钠、碳酸氢钠、碳酸钠中的一种或几种。
6.如权利要求1所述的用于工业喷头的热升华喷墨墨水，其特征在于:所述分散剂为木质素磺酸钠盐、乙撑双硬脂酸酰胺、芳香族磺酸钠盐的***缩合物、BYK分散剂、Tego分散剂中的一种或几种。
7.一种权利要求1所述的用于工业喷头的热升华喷墨墨水的制备方法，其特征在于包括以下步骤：
(1)色浆的制备：按比例取分散染料、分散剂和消泡剂，再取保湿剂用量的30～50％、表面活性剂用量的50～70％和超纯水用量的40～60％，在常温下混合，搅拌均匀，研磨20～30小时，使研磨后的混合物的平均粒径小于150nm，得色浆；
(2)成品的制备：按比例取杀菌剂、pH缓冲剂、黏度调节剂、树脂液、流平剂和金属离子螯合剂，再取上述色浆，余量的保湿剂、表面活性剂和超纯水，在常温下混合，研磨分散1～2h，离心，经过滤孔径为1μm的过滤器粗过滤，再分别经过滤孔径为0.45μm和0.22μm的过滤器精过滤，得成品。
8.如权利要求7所述的用于工业喷头的热升华喷墨墨水的制备方法，其特征在于：步骤(1)中，使研磨后的所述混合物的平均粒径小于90nm。