Summary of the invention
One of purpose of the present invention is: the deficiency existed for prior art, and provide a kind of cost low, the rate of transform is high, can not stop up the ink for ink-jet print of the heat sublimation for industrial nozzle of printer head.
For solving the problems of the technologies described above, technical scheme of the present invention is:
For the heat sublimation ink for ink-jet print of industrial nozzle, described ink for ink-jet print comprises following component by weight percentage: dispersed dye 1~6%, wetting Agent for Printing Inks 10~40%, viscosity-controlling agent 5~20%, sterilant 0.1~2%, pH buffer reagent 0.01~1%, resin liquid 1~10%, dispersion agent 0.1~40%, flow agent 0.01~5%, tensio-active agent 0.1~5%, defoamer 0.1~1%, metal ion chelation agent 0.01~2%, surplus is ultrapure water.
As a kind of improvement, described ink for ink-jet print comprises following component by weight percentage: described dispersed dye 1~3%, described wetting Agent for Printing Inks 15~25%, described viscosity-controlling agent 15~20%, described sterilant 0.1~0.8%, described pH buffer reagent 0.01~0.5%, described resin liquid 4~8%, described dispersion agent 10~30%, described flow agent 1~3%, described tensio-active agent 0.1~3%, described defoamer 0.5~1%, described metal ion chelation agent 1.5~2%, surplus is ultrapure water.
Preferably, described dispersed dye are C.I. Disperse Red 4, C.I. Disperse Red 9, C.I. dispersion red 11, C.I. Red-1 200 9, C.I. Disperse Red 22, C.I. Disperse Red 50, C.I. Disperse Red 53, C.I. disperse red 54, C.I. disperse red 60, C.I. Disperse Red 72, C.I. disperse red 73, C.I. Disperse Red 74, C.I. Disperse Red 82, C.I. disperse red 86, C.I. Disperse Red 92, C.I. Red-1 200 46, C.I. Red-1 200 53, C.I. Red 167, C.I. Red-1 200 77, C.I. Disperse Red 278, C.I. 63 ,DIS,PER,SE ,Vio,let, 63 41, C.I. EX-SF DISPERSE BLUE EX-SF 300 3, C.I. EX-SF DISPERSE BLUE EX-SF 300 14, C.I. EX-SF DISPERSE BLUE EX-SF 300 20, C.I. EX-SF DISPERSE BLUE EX-SF 300 35, C.I. Disperse Blue-56, C.I. Disperse Blue-60, C.I. EX-SF DISPERSE BLUE EX-SF 300 72, C.I. EX-SF DISPERSE BLUE EX-SF 300 73, C.I. EX-SF DISPERSE BLUE EX-SF 300 87, C.I. EX-SF DISPERSE BLUE EX-SF 300 165, C.I. EX-SF DISPERSE BLUE EX-SF 300 183, C.I. EX-SF DISPERSE BLUE EX-SF 300 301, C.I. EX-SF DISPERSE BLUE EX-SF 300 359, C.I. EX-SF DISPERSE BLUE EX-SF 300 366, C.I. DISPERSE YELLOW 3, C.I. DISPERSE YELLOW 5, C.I. DISPERSE YELLOW 7, C.I. DISPERSE YELLOW 23, C.I. Disperse Yellow 42, C.I. DISPERSE YELLOW 50, C.I. DISPERSE YELLOW 51, C.I. DISPERSE YELLOW 54, C.I. DISPERSE YELLOW 60, C.I. dispersion yellow 64, C.I. DISPERSE YELLOW 65, C.I. DISPERSE YELLOW 79, C.I. DISPERSE YELLOW 82, C.I. DISPERSE YELLOW 98, C.I. DISPERSE YELLOW 104, C.I. DISPERSE YELLOW 124, C.I. disperse Yellow 160 150, C.I. DISPERSE Yellow 211, C.I. disperse one or more in black 9.
Preferably, described wetting Agent for Printing Inks is alcohols or ester class, is preferably one or more in ethylene glycol, Diethylene Glycol, triethylene glycol, TEG, glycerine, Macrogol 200, poly(oxyethylene glycol) 400, Polyethylene Glycol-600, N-Methyl pyrrolidone, 2-Pyrrolidone butyl glycol ether, Diethylene Glycol butyl ether, triethylene glycol butyl ether, diethylene glycol diethyl ether, propylene glycol monomethyl ether.
Preferably, described viscosity-controlling agent is glycerine, sorbyl alcohol, Xylitol, mannitol, threitol, erythritol, melampyrum, maltol, 1,5-PD, 1, one or more in 2-hexylene glycol, propylene glycol; Described sterilant is CMIT, 20%1, a kind of in the dipropylene glycol aqueous solution of 2-benzisothiazole-3-ketone or both mixtures.
Preferably, described pH buffer reagent is one or more in trolamine, diethanolamine, thanomin, Tutofusin tris, sodium hydroxide, sodium bicarbonate, sodium carbonate; Described resin liquid is one or more in water-borne acrylic resin liquid, waterborne polyurethane resin liquid, modification binary vinyl chloride-vinyl acetate resin liquid.
Preferably, one or more in the formalin condenses that described dispersion agent is lignosulfonic acid sodium salt, ethylene bis stearic acid amide, aromatic sulphonic acid sodium salt, BYK dispersion agent, Tego dispersion agent, wherein the BYK dispersion agent is preferably one or more in BYK-190, BYK-191 or BYK-2012, and the Tego dispersion agent is preferably Tego-775.
Preferably, described flow agent is one or more in BYK flow agent, EFKA flow agent, and wherein the BYK flow agent is preferably BYK-380N or BYK-333, and the EFKA flow agent is preferably EFKA-4560.
Preferably, described defoamer is one or more in Surfynol defoamer, EnviroGem defoamer, wherein the EnviroGem defoamer is preferably EnviroGemAD-01, and wherein the Surfynol defoamer is preferably one or more in SurfynolMD-20, SurfynolDF-75.
The main component of BYK is organosilicon, belongs to organosilicone surfactants; The polyacrylic ester that the main component of EFKA is modification; The main component of TEGO is organic silicon acrylic ester, is the reactive polysiloxane esters of acrylic acid; Surfynol be a kind of liquid state, containing 100% activeconstituents without silicone defoamer.
Preferably, described tensio-active agent is one or more in ET tensio-active agent, Surfynol tensio-active agent, BYK tensio-active agent, described ET tensio-active agent is preferably ET-115 or ET-135, described Surfynol tensio-active agent is preferably one or more in Surfynol465, Surfynol104e, SurfynolTG, SurfynolCT-221, described BYK tensio-active agent is preferably BYK-345, and wherein the ET tensio-active agent belongs to the alkyl polyoxyethylene ether class.
Preferably, described metal ion chelation agent is one or more in EDTA, EDTA-2Na, EDTA-4Na, ammonium citrate.
In formula of the present invention:
Dispersed dye, its molecule is less, and its particle diameter is usually below 2 μ m, containing water-soluble group not on structure, disperse and dyeed by means of the homogeneous in dye liquor that acts on of dispersion agent, its can on dye trevira, the dedicated dye of cellulose acetate fibre and polyesteramine fiber, especially terylene.Dispersed dye are broadly divided into DISPERSE ORANGE 30 200, EX-SF DISPERSE BLUE EX-SF 300, DISPERSE YELLOW, Disperse Red, can be arranged in pairs or groups according to a certain percentage by several different dispersed dye, obtain the dispersion dyestuffs such as dispersion is black, Disperse Green, 63 DISPERSE Violet 63.Dispersed dye can enter the intermolecular fabric coloring that makes of trevira by distillation, and its good dispersity can not produce precipitation and the obstruction shower nozzle, and can not affect the feel of fabric.
Wetting Agent for Printing Inks is water-miscible organic solvent, and dispersed dye in water-soluble solubleness organic solvent, can improve the performance of keeping humidity of ink for ink-jet print well, can also improve the rate of transform of dispersed dye simultaneously.
Viscosity-controlling agent is mainly used in regulating the viscosity of ink for ink-jet print, avoids ink feeding-up or excessively rare, increases its mobility, and can not affect the pliability of fabric.
Sterilant, for eliminating the various pathogenic micro-organisms of ink for ink-jet print, improves the stability of ink for ink-jet print, extends its storage time.
The potential of hydrogen of pH buffer reagent for regulating ink for ink-jet print, make ink for ink-jet print have certain basicity, and the one, improve its color, the 2nd, reduce the corrosive nature of ink for ink-jet print to shower nozzle.
Other components in resin liquid and the present invention cooperatively interact, make ink for ink-jet print can be on non-absorbability base material very fast dry, there is tack well, and can make the photostabilization with photostabilization material be unlikely to descend, there is again good physicals simultaneously.
Dispersion agent is a kind of interfacial agent that simultaneously has lipophilicity and two kinds of opposite nature of wetting ability in molecule, can disperse equably those difficulties to be dissolved in the solid particulate of inorganic, the pigment dyestuff of liquid, also can prevent sedimentation and the cohesion of solid particulate simultaneously.Dispersion agent can shorten the jitter time of dispersed dye in water-soluble system, the surface properties of modification dispersed dye particle, adjust the mobility of dispersed dye particle, can improve gloss, tinting strength and the opacifying power of ink for ink-jet print, improve its color developing and toning property, prevent floating and flocculation, dispersion agent and resin liquid have consistency well, have improved the thermostability of ink for ink-jet print.
Flow agent, can impel ink in the drying and forming-film process, form one smooth, smooth, film uniformly.
Defoamer, can prevent the generation of ink jet ink underwater bubble.
Tensio-active agent can improve the tension force on ink for ink-jet print surface, makes dispersed dye more stablize in water-soluble system and make ink for ink-jet print more fully moistening in print substrate.
Metal ion chelation agent can accelerate the volatilization of ink moisture after ink-jet, and can improve the luminance brightness of ink for ink-jet print.
Except water molecules, almost there is no any impurity in ultrapure water, can improve the quality of ink for ink-jet print.
Another object of the present invention is to provide the preparation method of this ink for ink-jet print of heat sublimation for industrial nozzle, technical scheme of the present invention is:
Be used for the preparation method of the heat sublimation ink for ink-jet print of industrial nozzle, comprise the following steps:
The preparation of mill base: get in proportion dispersed dye, dispersion agent and defoamer, go bail for again the humectant consumption 30~50%, 50~70% and ultrapure water consumption of dosage of surfactant 40~60%, mix at normal temperatures, stir, grind 20~30 hours, the median size of the mixture after making to grind is less than 150nm, obtains mill base;
(2) preparation of finished product: get in proportion sterilant, PH buffer reagent, viscosity-controlling agent, resin liquid, flow agent and metal ion chelation agent, get again wetting Agent for Printing Inks consumption, dosage of surfactant and the ultrapure water consumption of above-mentioned mill base, surplus, mix at normal temperatures, grinding distribution 1~2h, centrifugal, the strainer coarse filtration that aperture is 1 μ m after filtration, then the filtration of the strainer that aperture is 0.45 μ m and 0.22 μ m after filtration respectively essence, obtain finished product.
As a kind of improvement, in step (1), the median size of the described mixture after grinding is less than 90nm.
Owing to having adopted technique scheme, the invention has the beneficial effects as follows:
Heat sublimation for industrial nozzle ink for ink-jet print provided by the invention, can be fuming in transfer process few by the mode transfer printing of hot transfer printing, and the transfer printing time is short, and the rate of transform is high, and wash durability is strong; Also can realize by the mode of direct spray printing painted, because its viscosity is low, its ink-jet smoothness, can not stop up shower nozzle, and particle size dispersion is even, dispersion stabilization is good, and long-time the storage can not become corruption or sex change yet, the combination of pH buffer reagent, resin liquid and metal ion chelation agent makes pattern color and the degree of fixation of printing high, ink of the present invention rate of transform in transfer process is high, the dyestuff less residue, and after shifting, the color stereoscopic sensation is strong, the pattern interface edge is clear not fuzzy, and its cost is lower.Black ink prepared by the present invention is black especially, not colour cast.
Embodiment
In order to make purpose of the present invention, technical scheme and advantage clearer, below in conjunction with embodiment, the present invention is further elaborated.Should be appreciated that specific embodiment described herein, only in order to explain the present invention, is not intended to limit the present invention.
Embodiment mono-
Heat sublimation ink for ink-jet print (redness) for industrial nozzle
Formula:
The preparation method:
The preparation of mill base: C.I. disperse red 60, the SurfynolMD-20(Shanghai Sang Jing chemical industry company limited of getting aforementioned proportion) and sodium lignosulfonate (1), get again the Diethylene Glycol consumption 50%, the new will in 1%Surfynol-104e(Shenzhen and industrial chemicals company limited) consumption 50% and ultrapure water consumption 40%, mix at normal temperatures, grind 28h after stirring in sand mill, survey the particle diameter of the mixture after grinding, make its median size d50 be less than 90nm, d90 is less than 150nm, obtains red mill base;
(2) preparation of finished product: get 20%1 of aforementioned proportion, the dipropylene glycol aqueous solution of 2-benzisothiazole-3-ketone, trolamine, glycerine, water-borne acrylic resin liquid, BYK-380N(Bi Ke chemistry (Tongling) company limited) and EDTA-4Na, get again above-mentioned mill base, 50% of Diethylene Glycol consumption, the new will in Surfynol-104e(Shenzhen and industrial chemicals company limited) consumption 50% and ultrapure water consumption 60%, mix at normal temperatures, continue grinding distribution 1h, after being 1 μ m strainer coarse filtration with pore size filter, with pore size filter, be that 0.45 μ m and 0.22 μ m strainer essence are filtered respectively again, make red ink.
Embodiment bis-
Heat sublimation ink for ink-jet print (blueness) for industrial nozzle
Formula:
Component |
Content (% by weight) |
C.I. EX-SF DISPERSE BLUE EX-SF 300 72 |
5 |
Triethylene glycol |
20 |
Sorbyl alcohol |
10 |
CMIT |
0.1 |
Tutofusin tris |
0.5 |
Waterborne polyurethane resin liquid |
3 |
BYK-190 |
40 |
EFKA-4560 |
0.6 |
ET-115 |
0.7 |
SurfynolDF-75 |
0.1 |
EDTA-2Na |
1 |
Ultrapure water |
19 |
The preparation method:
(1) preparation of mill base: C.I. EX-SF DISPERSE BLUE EX-SF 300 72, SurfynolDF-75 (the Guangzhou solid fine chemistry of connection company limited) and BYK-190(Bi Ke chemistry (Tongling) company limited of getting aforementioned proportion), get again the triethylene glycol consumption 30%, 60% and ultrapure water consumption of ET-115 consumption 60%, mix at normal temperatures, grind 28h after stirring in sand mill, survey the particle diameter of the mixture after grinding, make its median size d50 be less than 90nm, d90 is less than 120nm, obtains blue mill base;
The preparation of finished product: CMIT, Tutofusin tris, sorbyl alcohol, waterborne polyurethane resin liquid, the EFKA-4560(BASF China of getting aforementioned proportion) and EDTA-2Na (2), get again above-mentioned mill base, get the triethylene glycol consumption 70%, 40% and ultrapure water consumption of ET-115 consumption 40%, mix at normal temperatures, continue grinding distribution 1.5h, after being 1 μ m strainer coarse filtration with pore size filter, be that 0.45 μ m and 0.22 μ m strainer essence are filtered with pore size filter respectively again, make blue ink.
Embodiment tri-
Heat sublimation ink for ink-jet print (yellow) for industrial nozzle
Formula:
Component |
Content (% by weight) |
C.I. DISPERSE YELLOW 54 |
3 |
Polyethylene Glycol-600 |
30 |
Mannitol |
15 |
CMIT |
1 |
Diethanolamine |
0.2 |
Modification binary vinyl chloride-vinyl acetate resin liquid |
5 |
Ethylene bis stearic acid amide |
30 |
BYK-333 |
3 |
SurfynolCT-221 |
2 |
EnviroGemAD-01 |
0.3 |
EDTA |
0.5 |
Ultrapure water |
10 |
The preparation method:
(1) preparation of mill base: the wind of getting C.I. DISPERSE YELLOW 54, the EnviroGemAD-01(east of aforementioned proportion is imported and exported (Shenzhen) company limited) and chemical (Tongling) company limited of BYK-333(Bi Ke), the new will in SurfynolCT-221(Shenzhen and industrial chemicals company limited again 40% of taking polyethylene glycol 600 consumptions) consumption 70% and ultrapure water consumption 40%, mix at normal temperatures, grind 30h after stirring in sand mill, survey the particle diameter of the mixture after grinding, make its median size d50 be less than 80nm, d90 is less than 120nm, obtains yellow mill base;
(2) preparation of finished product: the CMIT of getting aforementioned proportion, mannitol, diethanolamine, modification binary vinyl chloride-vinyl acetate resin liquid, ethylene bis stearic acid amide and EDTA, get again above-mentioned mill base, 60% of Polyethylene Glycol-600 consumption, the new will in SurfynolCT-221(Shenzhen and industrial chemicals company limited) consumption 30% and ultrapure water consumption 60%, mix at normal temperatures, continue grinding distribution 2h, after being 1 μ m strainer coarse filtration with pore size filter, with pore size filter, be that 0.45 μ m and 0.22 μ m strainer essence are filtered respectively again, make yellow ink.
Embodiment tetra-
Heat sublimation ink for ink-jet print (redness) for industrial nozzle
Formula:
Component |
Content (% by weight) |
C.I. Red-1 200 53 |
1 |
The Diethylene Glycol butyl ether |
15 |
1,5-PD |
5 |
CMIT |
0.5 |
Sodium bicarbonate |
0.03 |
Waterborne polyurethane resin liquid |
1 |
Tego-775 |
0.1 |
BYK-380 |
0.01 |
ET-135 |
0.1 |
SurfynolDF-75 |
0.25 |
EDTA-2Na |
0.01 |
Ultrapure water |
77 |
The preparation method:
(1) preparation of mill base: C.I. Red-1 200 53, SurfynolDF-75 (the Guangzhou solid fine chemistry of connection company limited) and BYK-380(Bi Ke chemistry (Tongling) company limited of getting aforementioned proportion), get again Diethylene Glycol butyl ether consumption 50%, 55% and ultrapure water consumption of ET-135 consumption 45%, mix at normal temperatures, grind 30h after stirring in sand mill, survey the particle diameter of the mixture after grinding, make its median size d50 be less than 80nm, d90 is less than 130nm, obtains red mill base;
(2) preparation of finished product: the CMIT of getting aforementioned proportion, 1, the 5-pentanediol, sodium bicarbonate, waterborne polyurethane resin liquid, Tego-775(wins the extraordinary chemical (Shanghai) Co., Ltd. of wound Degussa) and EDTA-2Na, get again above-mentioned mill base, 50% of Diethylene Glycol butyl ether consumption, 55% of 45% and ultrapure water consumption of ET-135 consumption, mix at normal temperatures, continue grinding distribution 1.5h, after being 1 μ m strainer coarse filtration with pore size filter, with pore size filter, be that 0.45 μ m and 0.22 μ m strainer essence are filtered respectively again, make red ink.
Embodiment five
Heat sublimation ink for ink-jet print (blueness) for industrial nozzle
Formula:
Component |
Content (% by weight) |
C.I. EX-SF DISPERSE BLUE EX-SF 300 359 |
2 |
N-Methyl pyrrolidone |
25 |
Maltol |
8 |
Two of 20%1,2-benzisothiazole-3-ketone |
0.8 |
Aqueous solution of propylene glycol |
? |
Sodium hydroxide |
0.1 |
Water-borne acrylic resin liquid |
4 |
BYK-2012 |
10 |
EFKA-4560 |
1 |
SurfynolTG |
3 |
SurfynolMD-20 |
0.6 |
EDTA-4Na |
1.5 |
Ultrapure water |
44 |
The preparation method:
(1) preparation of mill base: C.I. EX-SF DISPERSE BLUE EX-SF 300 359, the SurfynolMD-20(Shanghai Sang Jing chemical industry company limited of getting aforementioned proportion) and BYK-2012(Bi Ke chemistry (Tongling) company limited), get again the N-Methyl pyrrolidone consumption 38%, the new will in SurfynolTG(Shenzhen and industrial chemicals company limited) consumption 57% and ultrapure water consumption 54%, mix at normal temperatures, grind 28h after stirring in sand mill, survey the particle diameter of the mixture after grinding, make its median size d50 be less than 60nm, d90 is less than 90nm, obtains blue mill base;
(2) preparation of finished product: get 20%1 of aforementioned proportion, the dipropylene glycol aqueous solution of 2-benzisothiazole-3-ketone, maltol, sodium hydroxide, water-borne acrylic resin liquid, BYK-2012(Bi Ke chemistry (Tongling) company limited) and EDTA-4Na, get again above-mentioned mill base, 62% of N-Methyl pyrrolidone consumption, the new will in Surfynol TG(Shenzhen and industrial chemicals company limited) consumption 43% and ultrapure water consumption 46%, mix at normal temperatures, continue grinding distribution 2h, after being 1 μ m strainer coarse filtration with pore size filter, with pore size filter, be that 0.45 μ m and 0.22 μ m strainer essence are filtered respectively again, make blue ink.
Embodiment six
Heat sublimation ink for ink-jet print (yellow) for industrial nozzle
Formula:
The preparation method:
(1) preparation of mill base: the wind of getting C.I. disperse Yellow 160 150, the EnviroGemAD-01(east of aforementioned proportion is imported and exported (Shenzhen) company limited) and the lignosulfonic acid sodium salt, get again the propylene glycol monomethyl ether consumption 44%, the new will in SurfynolCT-221(Shenzhen and industrial chemicals company limited) consumption 62% and ultrapure water consumption 58%, mix at normal temperatures, grind 28h after stirring in sand mill, survey the particle diameter of the mixture after grinding, make its median size d50 be less than 60nm, d90 is less than 90nm, obtains yellow mill base;
(2) preparation of finished product: get 20%1 of aforementioned proportion, the dipropylene glycol aqueous solution of 2-benzisothiazole-3-ketone, Xylitol, thanomin, water-borne acrylic resin liquid, BYK-380N(Bi Ke chemistry (Tongling) company limited) and EDTA-4Na, get again above-mentioned mill base, 56% of propylene glycol monomethyl ether consumption, the new will in SurfynolCT-221(Shenzhen and industrial chemicals company limited) consumption 38% and ultrapure water consumption 42%, mix at normal temperatures, continue grinding distribution 2h, after being 1 μ m strainer coarse filtration with pore size filter, with pore size filter, be that 0.45 μ m and 0.22 μ m strainer essence are filtered respectively again, make yellow ink.
Embodiment seven
Heat sublimation ink for ink-jet print (black) for industrial nozzle
Formula:
The preparation method:
(1) preparation of mill base: the C.I. that gets aforementioned proportion disperses wind black 9, EnviroGemAD-01(east to import and export (Shenzhen) company limited) and the lignosulfonic acid sodium salt, get again the ethylene glycol consumption 50%, 60% and ultrapure water consumption of ET-115 consumption 45%, mix at normal temperatures, grind 30h after stirring in sand mill, survey the particle diameter of the mixture after grinding, make its median size d50 be less than 80nm, d90 is less than 110nm, obtains black color paste;
(2) preparation of finished product: get 20%1 of aforementioned proportion, the dipropylene glycol aqueous solution, 1 of 2-benzisothiazole-3-ketone, 5-pentanediol, trolamine, waterborne polyurethane resin liquid, EFKA-4560 and EDTA, get again above-mentioned mill base, ethylene glycol consumption 50%, 40% and ultrapure water consumption of ET-115 consumption 55%, mix at normal temperatures, continue grinding distribution 2h, after being 1 μ m strainer coarse filtration with pore size filter, be that 0.45 μ m and 0.22 μ m strainer essence are filtered with pore size filter respectively again, make black ink.
? |
Abroad 1 |
Domestic sample 2 |
Domestic sample 3 |
Embodiment seven |
The rate of transform |
90.5% |
85.7% |
81.4% |
92.1% |
The black form and aspect |
Black |
Partially red partially shallow |
Partially red partially shallow |
Black |
Fluency |
3 |
5 |
11 |
2 |
The interface sharpness |
Generally |
Generally |
Fuzzy |
Clear |
Light fastness |
5 |
4 |
4 |
6 |
Washing fastness |
4 |
4 |
3 |
5 |
The rate of transform, light fastness, washing fastness, all detect according to the industry prescriptive procedure.
Fluency is that four colour purity color lump continuitys are printed the number of after 20m, blocking up spray orifice.
The black form and aspect are acquiescence observation procedure in industry.
Embodiment eight
Heat sublimation ink for ink-jet print (black) for industrial nozzle
By weight percentage, get yellow ink 40% in embodiment tri-, the red ink 30% in embodiment mono-, the blue ink 30% in embodiment bis-, disperse 1h after mixing, after being 1 μ m strainer coarse filtration with pore size filter, be that 0.45 μ m and 0.22 μ m strainer essence are filtered with pore size filter respectively again, make black ink.
Embodiment nine
Heat sublimation ink for ink-jet print (black) for industrial nozzle
By weight percentage, get yellow ink 35% in embodiment six, the red ink 35% in embodiment tetra-, the blue ink 30% in embodiment five, disperse 1h after mixing, with after 1 μ m strainer coarse filtration, filter by 0.45 μ m and 0.22 μ m strainer essence respectively again, make black ink.
The parameters of ink is measured:
The ink that above-described embodiment 1-9 is made carries out physical and chemical parameter mensuration under 25 ℃, and item and the data obtained of its mensuration are as shown in the table:
As can be seen from the above table, the ink for ink-jet print of the heat sublimation for industrial nozzle viscosity provided by the invention is little, and surface tension is large, prints smoothness, can not stop up printer head.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, all any modifications of doing within the spirit and principles in the present invention, be equal to and replace and improvement etc., within all should being included in protection scope of the present invention.