CN103450659B - Acid-and-alkali-resistant and impact-resistant floor material - Google Patents
Acid-and-alkali-resistant and impact-resistant floor material Download PDFInfo
- Publication number
- CN103450659B CN103450659B CN201310366754.4A CN201310366754A CN103450659B CN 103450659 B CN103450659 B CN 103450659B CN 201310366754 A CN201310366754 A CN 201310366754A CN 103450659 B CN103450659 B CN 103450659B
- Authority
- CN
- China
- Prior art keywords
- floor material
- parts
- acid
- alkali
- resistant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention relates to an acid-and-alkali-resistant and impact-resistant floor material. The floor material is composed of the following components in parts by weight: 15-19 parts of diallyl phthalate, 17-22 parts of polyurethane, 17-18 parts of bisphenol S-type epoxy resin, 6-10 parts of verdyl acetate, 5-8 parts of triisodecyl phosphate, 3-4 parts of barium stearate, and 1-2 parts of n-butyl alcohol. The prepared floor material has good acid and alkali resistance and impact resistance.
Description
Technical field
The present invention relates to a kind of floor material, particularly relate to the impact-resistant floor material of a kind of acid and alkali-resistance.
Background technology
Floor material kind is very many, comprises concrete dense curing agent floor material, epoxy self-leveling floor material, silicon carbide Wear-resisting terrace material, antistatic floor material, the anti-skidding floor material of epoxy, carbamide resin floor material etc.Floor material connection is the part of bottom room and soil layer, and it, because subject the load in bottom workshop, needs to ensure certain intensity, and need to have protection against the tide, acid and alkali-resistance, shock-resistant, wear-resisting performance.Therefore need to find and a kind of not only there is the floor material that acid and alkali-resistance characteristic also has shock-resistant characteristic.
Summary of the invention
The technical problem solved: the problem of floor material acid and alkali-resistance and impact resistance difference.
Technical scheme: the invention discloses the impact-resistant floor material of a kind of acid and alkali-resistance, floor material is made up of according to weight ratio following composition: Phthalic acid, diallyl ester 15 ~ 19 parts, urethane 17 ~ 22 parts, bisphenol-s epoxy resin are 17 ~ 18 parts, verdy acetate is 6 ~ 10 parts, tricresyl phosphite isodecyl ester 5 ~ 8 parts, barium stearate are 3 ~ 4 parts, propyl carbinol is 1 ~ 2 part.Preparation method is as follows for the acid and alkali-resistance terrace material of resistance to important place: get that Phthalic acid, diallyl ester is 15 ~ 19kg, urethane 17 ~ 22kg, bisphenol-s epoxy resin are 17 ~ 18kg, verdy acetate is 6 ~ 10kg, tricresyl phosphite isodecyl ester 5 ~ 8kg, barium stearate are 3 ~ 4kg, propyl carbinol is 1 ~ 2kg.Inserted by each composition and stir in tank body, stirred pot temperature is set as 65 ~ 85 DEG C, carries out stirring and evenly mixing, and after mixing, tiling in a mold, is cooled to normal temperature and can obtains the shock-resistant floor material of acid and alkali-resistance.
Beneficial effect: the floor material that the present invention prepares has good resistance to acids and bases and shock-resistance, floor material the sodium hydroxide solution of resistance to 20wt% and the acetum of 30wt% can soak and do not change for 15 days.Under GB/T1732-1993 standard, shock-resistance is 1kg in weight, and highly impact floor material in 120cm situation, floor material maintains the original state, and does not change.Possess good acid and alkali-resistance and shock-resistant floor material, can be used in cleaning shop.
Embodiment
Embodiment 1
Get that Phthalic acid, diallyl ester is 15kg, urethane 22kg, bisphenol-s epoxy resin are 18kg, verdy acetate is 6kg, tricresyl phosphite isodecyl ester 8kg, barium stearate are 3kg, propyl carbinol is 1kg.Inserted by each composition and stir in tank body, stirred pot temperature is set as 85 DEG C, carries out stirring and evenly mixing, and after mixing, tiling in a mold, is cooled to normal temperature and can obtains the shock-resistant floor material of acid and alkali-resistance.
Embodiment 2
Preparation method is with embodiment 1, and difference is that pot temperature is set as 65 DEG C.In the present embodiment, each component content is: Phthalic acid, diallyl ester is 17kg, urethane 17kg, bisphenol-s epoxy resin are 17kg, verdy acetate is 8kg, tricresyl phosphite isodecyl ester 5kg, barium stearate are 4kg, propyl carbinol is 2kg.
Embodiment 3
Preparation method is with embodiment 1, and difference is that pot temperature is set as 75 DEG C.In the present embodiment, each component content is Phthalic acid, diallyl ester is 19kg, urethane 20kg, bisphenol-s epoxy resin are 18kg, verdy acetate is 10kg, tricresyl phosphite isodecyl ester 7kg, barium stearate are 3kg, propyl carbinol is 1kg.
The shock-resistant test result of acid and alkali-resistance
After the product of embodiment 1, embodiment 2, embodiment 3 prepares, three products are put into respectively and soaks 15 days to the sodium hydroxide solution of 20wt% and the acetum of 30wt%, within 15 days, observe the situation of terrace afterwards.Another under GB/T1732-1993 standard, shock-resistance is 1kg in weight, highly for impacting floor material in 120cm situation, measures its impact resistance.Experimental result shows, three products of the present invention are after the sodium hydroxide solution of 20% and the acetum of 30% soak 15 days, and floor material maintains primary characteristic and outward appearance.Also maintain the original state at floor material after shock resistance experiment, do not change.
Claims (5)
1. the impact-resistant floor material of acid and alkali-resistance, is characterized in that floor material is made up of according to weight ratio following composition: Phthalic acid, diallyl ester 15 ~ 19 parts, urethane 17 ~ 22 parts, bisphenol-s epoxy resin are 17 ~ 18 parts, verdy acetate is 6 ~ 10 parts, tricresyl phosphite isodecyl ester 5 ~ 8 parts, barium stearate are 3 ~ 4 parts, propyl carbinol is 1 ~ 2 part;
The preparation method of described floor material is as follows: inserted by each composition and stir in tank body, stirred pot temperature is set as 65-85 DEG C, carries out stirring and evenly mixing, and after mixing, tiling in a mold, is cooled to normal temperature and can obtains the shock-resistant floor material of acid and alkali-resistance.
2. the impact-resistant floor material of a kind of acid and alkali-resistance according to claim 1, is characterized in that in floor material composition, Phthalic acid, diallyl ester is 19 parts.
3. the impact-resistant floor material of a kind of acid and alkali-resistance according to claim 1, is characterized in that in floor material composition, urethane is 17 parts.
4. the impact-resistant floor material of a kind of acid and alkali-resistance according to claim 1, is characterized in that in floor material composition, bisphenol-s epoxy resin is 18 parts.
5. the impact-resistant floor material of a kind of acid and alkali-resistance according to claim 1, is characterized in that in floor material composition, verdy acetate is 10 parts.