CN103417125A - 五层金属复合材料烹饪器具及其金属复合板材制备方法 - Google Patents
五层金属复合材料烹饪器具及其金属复合板材制备方法 Download PDFInfo
- Publication number
- CN103417125A CN103417125A CN2013102518044A CN201310251804A CN103417125A CN 103417125 A CN103417125 A CN 103417125A CN 2013102518044 A CN2013102518044 A CN 2013102518044A CN 201310251804 A CN201310251804 A CN 201310251804A CN 103417125 A CN103417125 A CN 103417125A
- Authority
- CN
- China
- Prior art keywords
- thickness
- layers
- metallic composite
- cooking apparatus
- layer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及五层金属复合材料烹饪器具,包括烹饪器具本体以及设置于所述烹饪器具本体上的把手,其中,所述烹饪器具本体由五层金属复合板材冲压成型,所述五层金属复合板材自内而外依次由厚度在0.5mm-2mm之间的304不锈钢层、厚度在0.5mm-2mm之间的镁铝合金层、厚度在0.5mm-2mm之间的纯铝层、厚度在0.5mm-2mm之间的铝合金层以及厚度在0.5mm-2mm之间的430不锈钢层冲压而成。有益效果:金属复合板材能适应各种深冲、拉伸、胀形、弯曲、冲孔、曳边等冷加工而不分层,使烹饪器具仍然保持其原始的牢固结合状态;烹饪器具质量轻,具有良好的热传递性,传热迅速,节约能源,适用于各种不同炉灶。
Description
技术领域
本发明涉及烹饪器具技术领域,尤其是涉及一种五层金属复合材料烹饪器具及其金属复合板材制备方法。
背景技术
现在国内生产烹饪器具制品(如炒锅等)材料通常采用单一的材料。由于单一材料受其固有的物理和化学特性等的限制,使该烹饪器具本体材料的强硬度、耐磨性、耐腐性、热传递性以及电磁感性能和表面处理的工艺性等受到很大局限性,从而使得由单一材料制作的烹饪器具内在和外表的综合性能等表现显得不够领人满意。人们也提出了不少改进措施。例如为弥补不锈钢材料热传导性不足,在不锈钢该烹饪器具本体底部复焊一片热传导性能较好的铝板或铜板来加强传热,制成不锈钢复合锅。又如为使烹饪器具能适合电磁灶具使用,在铝或不锈钢烹饪器具底部复合焊上电磁感应性能较好的材料,使烹饪器具适应在电磁烹饪器具上使用。有时为克服铝烹饪器具材料耐腐蚀性差的缺点,在其表面进行氧化处理,形成氧化膜层保护。又如为克服铁锅易生锈不卫生的缺点,在该烹饪器具本体内表面涂敷防锈保护层。凡此种种,不仅使烹饪器具制造工艺复杂,而且在许多场合也不能给出另人满意的结果。
因此,一种能适应各种深冲、拉伸、胀形、弯曲、冲孔、曳边等冷加工而不分层,使烹饪器具仍然保持其原始的牢固结合状态的五层金属复合板材的出现很有必要了。
发明内容
本发明为解决上述技术问题,在于提供一种五层金属复合材料烹饪器具,及其复合层板材的制备方法,该板材能适应各种深冲、拉伸、胀形、弯曲、冲孔、曳边等冷加工而不分层,使烹饪器具仍然保持其原始的牢固结合状态。
本发明所解决的技术问题采用以下技术方案来实现:
五层金属复合材料烹饪器具,包括烹饪器具本体以及设置于所述烹饪器具本体上的把手,其特征在于,所述烹饪器具本体由五层金属复合板材冲压成型,所述五层金属复合板材自内而外依次由厚度在0.5mm-2mm之间的304不锈钢层、厚度在0.5mm-2mm之间的镁铝合金层、厚度在0.5mm-2mm之间的纯铝层、厚度在0.5mm-2mm之间的铝合金层以及厚度在0.5mm-2mm之间的430不锈钢层冲压而成。
作为优选的技术方案,所述五层金属复合板材的总厚度为3mm;其中各层厚度分别为,
所述304不锈钢层的厚度为0.5mm;
所述镁铝合金层的厚度为0.7mm;
所述纯铝层厚度为0.6mm;
所述铝合金层的厚度为0.7mm;
所述430不锈钢层的厚度为0.5mm。
作为优选的技术方案,所述镁铝合金层和铝合金层均为3003铝合金层。
制备上述五层金属复合板材的制备方法,包括以下步骤:
步骤a、将纯铝板、铝合金板、304不锈钢板和430不锈钢板进行表面打磨处理,使表面光洁、平整;
步骤b、将所述纯铝板和铝合金板,按铝合金板、纯铝板和铝合金板的次序轧压复合,得复合铝板;
步骤c、将步骤b中的所述复合铝板在400-600℃的温度下进行退火处理4-6小时;
步骤d、将所述304不锈钢板和430不锈钢板分别加热轧压复合在所述复合铝板的两侧,即得复合板材,所述加热轧压复合的温度控制在200-300℃,压力控制在2500-3000KN,板材移动速度2.5-5米/分;
步骤e、将步骤d中的所述复合板材在300-400℃的温度下进行退火处理1-30分钟;
步骤f、将步骤e中退火处理后的所述复合板材进行清洗、打磨,即得。
作为优选的技术方案,所述铝合金板为3003铝合金板。
作为优选的技术方案,步骤c中退火温度为550℃,时间为25分钟。
作为优选的技术方案,步骤d中加热轧压复合的温度为280℃,压力为3000KN,板材移动速度为3米/分。
作为优选的技术方案,步骤e中退火温度为300℃,时间为30分钟。
本发明的有益效果是:(1)金属复合板材能适应各种深冲、拉伸、胀形、弯曲、冲孔、曳边等冷加工而不分层,使烹饪器具仍然保持其原始的牢固结合状态;
(2)烹饪器具质量轻,具有良好的热传递性,传热迅速,节约能源,适用于各种不同炉灶。
附图说明
图1为本发明:五层金属复合材料烹饪器具金属复合板材的结构示意图;
图2为本发明金属复合板材的制备流程图。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解,下面结合具体实施例,进一步阐述本发明。
如图1所示,五层金属复合材料烹饪器具,包括烹饪器具本体以及设置于所述烹饪器具本体上的把手,其中,所述烹饪器具本体由五层金属复合板材1冲压成型,所述五层金属复合板材1自内而外依次由厚度在0.5mm-2mm之间的304不锈钢层11、厚度在0.5mm-2mm之间的镁铝合金层12、厚度在0.5mm-2mm之间的纯铝层13、厚度在0.5mm-2mm之间的铝合金层14以及厚度在0.5mm-2mm之间的430不锈钢层15冲压而成。
本发明中所述金属复合板材1的总厚度为3mm;其中各层厚度分别为,
所述304不锈钢层11的厚度为0.5mm;
所述镁铝合金层12的厚度为0.7mm;
所述纯铝层13厚度为0.6mm;
所述铝合金层14的厚度为0.7mm;
所述430不锈钢层15的厚度为0.5mm。
其中,所述镁铝合金层12和铝合金层14均为3003铝合金层。
采用上述规格制造的烹饪器具质量轻,具有良好的热传递性,传热迅速,节约能源,适用于各种不同炉灶。
实施例1
如图2所示,制备上述金属复合板材的制备方法,包括以下步骤:
步骤101、预处理,将纯铝板、3003铝合金板、304不锈钢板和430不锈钢板进行表面打磨处理,使表面光洁、平整;
步骤102、初次复合,将所述纯铝板和3003铝合金板,按3003铝合金板、纯铝板和3003铝合金板的次序轧压复合,得复合铝板;
步骤103、初次退火,将步骤102中的所述复合铝板在550℃的温度下进行退火处理25分钟;
步骤104、二次复合,将所述304不锈钢板和430不锈钢板分别加热轧压复合在所述复合铝板的两侧,即得复合板材,所述加热轧压复合的温度控制在280℃,压力控制在3000KN,板材移动速度3米/分;
步骤105、二次退火,将步骤104中的所述复合板材在300℃的温度下进行退火处理30分钟;
步骤106、清洗、打磨,将步骤105中退火处理后的所述复合板材进行清洗、打磨,即得。
采用上述步骤制作的金属复合板材能适应各种深冲、拉伸、胀形、弯曲、冲孔、曳边等冷加工而不分层,使烹饪器具仍然保持其原始的牢固结合状态。
实施例2
制备上述金属复合板材的制备方法,包括以下步骤:
与实施例1不同的是,
步骤103中退火温度为600℃,时间为24分钟。
步骤104中加热轧压复合的温度为200℃,压力为3000KN,板材移动速度为2.5米/分。
步骤105中退火温度为400℃,时间为20分钟。
采用上述步骤制作的金属复合板材能适应各种深冲、拉伸、胀形、弯曲、冲孔、曳边等冷加工而不分层,使烹饪器具仍然保持其原始的牢固结合状态。
实施例3
制备上述金属复合板材的制备方法,包括以下步骤:
与实施例1不同的是,
步骤103中退火温度为500℃,时间为36分钟。
步骤104中加热轧压复合的温度为300℃,压力为2500KN,板材移动速度为4米/分。
步骤105中退火温度为400℃,时间为20分钟。
采用上述步骤制作的金属复合板材能适应各种深冲、拉伸、胀形、弯曲、冲孔、曳边等冷加工而不分层,使烹饪器具仍然保持其原始的牢固结合状态。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (8)
1.五层金属复合材料烹饪器具,包括烹饪器具本体以及设置于所述烹饪器具本体上的把手,其特征在于,所述烹饪器具本体由五层金属复合板材冲压成型,所述五层金属复合板材自内而外依次由厚度在0.5mm-2mm之间的304不锈钢层、厚度在0.5mm-2mm之间的镁铝合金层、厚度在0.5mm-2mm之间的纯铝层、厚度在0.5mm-2mm之间的铝合金层以及厚度在0.5mm-2mm之间的430不锈钢层冲压而成。
2.根据权利要求1所述的五层金属复合材料烹饪器具,其特征在于:所述五层金属复合板材的总厚度为3mm;其中各层厚度分别为,
所述304不锈钢层的厚度为0.5mm;
所述镁铝合金层的厚度为0.7mm;
所述纯铝层厚度为0.6mm;
所述铝合金层的厚度为0.7mm;
所述430不锈钢层的厚度为0.5mm。
3.根据权利要求1所述的五层金属复合材料烹饪器具,其特征在于:所述铝合金层为3003铝合金层。
4.五层金属复合材料烹饪器具金属复合板材的制备方法,其特征在于:包括以下步骤:
步骤a、将纯铝板、铝合金板、304不锈钢板和430不锈钢板进行表面打磨处理,使表面光洁、平整;
步骤b、将所述纯铝板和铝合金板,按铝合金板、纯铝板和铝合金板的次序轧压复合,得复合铝板;
步骤c、将步骤b中的所述复合铝板在400-600℃的温度下进行退火处理4-6小时;
步骤d、将所述304不锈钢板和430不锈钢板分别加热轧压复合在所述复合铝板的两侧,即得复合板材,所述加热轧压复合的温度控制在200-300℃,压力控制在2500-3000KN,板材移动速度2.5-5米/分;
步骤e、将步骤d中的所述复合板材在300-400℃的温度下进行退火处理1-30分钟;
步骤f、将步骤e中退火处理后的所述复合板材进行清洗、打磨,即得。
5.根据权利要求4所述的五层金属复合材料烹饪器具金属复合板材的制备方法,其特征在于,所述铝合金板为3003铝合金板。
6.根据权利要求4所述的五层金属复合材料烹饪器具金属复合板材的制备方法,其特征在于,步骤c中退火温度为550℃,时间为25分钟。
7.根据权利要求4所述的五层金属复合材料烹饪器具金属复合板材的制备方法,其特征在于,步骤d中加热轧压复合的温度为280℃,压力为3000KN,板材移动速度为3米/分。
8.根据权利要求4所述的五层金属复合材料烹饪器具金属复合板材的制备方法,其特征在于,步骤e中退火温度为300℃,时间为30分钟。