CN103382259B - 浇注酚醛泡沫体及制造方法 - Google Patents
浇注酚醛泡沫体及制造方法 Download PDFInfo
- Publication number
- CN103382259B CN103382259B CN201210134955.7A CN201210134955A CN103382259B CN 103382259 B CN103382259 B CN 103382259B CN 201210134955 A CN201210134955 A CN 201210134955A CN 103382259 B CN103382259 B CN 103382259B
- Authority
- CN
- China
- Prior art keywords
- manufacture method
- phenolic
- phenolic resin
- foam
- mould
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了浇注酚醛泡沫体及制造方法，所述浇注酚醛泡沫体及制造方法，由下述步骤组成：以含有尿素和水的酚醛树脂，生产中活性的异氰酸酯与水反应，生成二氧化碳，最后形成固化的酚醛泡沫。本发明的制备方法具有合成泡沫时间短，制备成本低的特点。本发明的新工艺很大程度上缩短了合成目标产物的时间，成功解决了合成目标产物原料昂贵、难得等问题，同时又避免了泡沫的烟密度高的问题。
Description
技术领域
本发明涉及一种酚醛泡沫体，用二氧化碳做发泡剂制造泡沫方法，尤其涉及浇注酚醛泡沫体及制造方法。
背景技术
由于近几年酚醛泡沫在中国快速发展，主要都是用二组份浇注机生产酚醛板，主要用低沸点烷烃做发泡剂，用酸做固化剂制得防火的酚醛泡沫，酚醛树脂通常由苯酚和甲醛在碱性物质下通过中温反应、通过中和、脱水制得，因为酚醛泡沫通常是硬和脆的，为了增加韧性，通常要加入塑性有机物，增加了最后泡沫的烟密度。
发明内容
本发明所要解决的技术问题之一就是提供浇注酚醛泡沫体及制造方法，合成泡沫时间短，制备成本低。
本发明的所要解决的技术问题之二的是提供浇注酚醛泡沫体及制造方法。
本发明目的是通过以下实现：
提供浇注酚醛泡沫体及制造方法，由下述步骤组成：
步骤1：以含有尿素和水的酚醛树脂，生产中活性的异氰酸酯与水反应，生成二氧化碳，最后形成固化的酚醛泡沫；
所述酚醛树脂为苯酚和甲醛在碱性下反应生成，苯酚和甲醛摩尔比为1.5---2.5，所述酚醛树脂粘度通常为3000-20000cps/25度，分子量400-3000，酚醛树脂占泡沫总量的60-92％，通常为70-85％；
所述异氰酸酯为一种PAPI，NCO含量为30.8％，平均分子量为375，官能度为3；
所述苯酚和甲醛在一个反应釜中，加入碱性催化剂，如氢氧化钠，氢氧化钡等，在60-100度反应，到目标分子量时，降温中和，脱水，制得固含量约78-82％的酚醛树脂，冷却到45度时，加入尿素；
步骤2：在一个三组份浇注机实现，通常一个组份为酚醛树脂，表面活性剂，一个组份为异氰酸酯和表面活性剂，另一个组份为固化剂。当各组份混合在一起，搅拌均匀后，就形成了泡沫，
所述表面活性剂通常用T-80，DC-193，H203(中山东峻)；
本发明的制备方法具有合成泡沫时间短，制备成本低的特点。本发明的新工艺很大程度上缩短了合成目标产物的时间，成功解决了合成目标产物原料昂贵、难得等问题，同时又避免了泡沫的烟密度高的问题。
具体实施方式
实施例1
聚合和发泡反应，要在酸性物质下进行。通常的酚磺酸，对甲苯磺酸，磷酸的一种或几种，都可用。酸性物质为酚醛树脂的620％，通常为10％。
下面的配方，适合做闭孔泡沫。
A.酚醛树脂：100份
B.阴离子表面活性剂：1-5份
C.非离子表面活性剂：1-5份
D.PAPI：2---15份
E.酸性催化剂：5-15份
F.氢氧化铝：3-10份
在批量生产中，在一个混合容器中A，B，C，F搅拌均匀后，加入D均匀搅拌后再加入E，2-10分钟后，就发泡固化为泡沫了。在连续生产中，可用二或三组份浇注机，物料从浇注头出来后，分布到连续传动带，速度每分钟26米。
实施例2
A.酚醛树脂：100份
B.PAPI： 3份
C.T-80： 2份
D.H-203： 3份
E.70％对甲苯磺酸溶液： 10份
先将A，C，D在一起搅拌3分钟，再加入B搅拌1分钟，再加入E搅拌1分钟，倒入一模具，10分钟后，得到密度70公斤每立方米的泡沫。
本发明的制备方法具有合成泡沫时间短，制备成本低的特点。本发明的新工艺很大程度上缩短了合成目标产物的时间，成功解决了合成目标产物原料昂贵、难得等问题，同时又避免了泡沫的烟密度高的问题。
Claims (4)
1.一种浇注酚醛泡沫体的制造方法，其特征在于，由下述步骤组成：
步骤1：在一个反应釜中，取苯酚与甲醛摩尔比为1.5～2.5，并加入碱性催化剂，在60～100℃下反应，到目标重均分子量时降温中和，脱水制得固含量为78～82％的酚醛树脂，冷却至45℃时，加入尿素；所述酚醛树脂的粘度3000-20000cps/25℃，重均分子量为400-3000；
步骤2：在三组分浇注机中，第一组分为步骤1制得的含有尿素和水分的酚醛树脂和表面活性剂，第二组分为异氰酸酯，第三组分为固化剂，将三组分混合在一起，反应中活性的异氰酸酯与酚醛树脂中的水分反应，生成二氧化碳，经搅拌均匀后，最后形成固化的酚醛泡沫；
所述酚醛树脂占酚醛泡沫总量的60～92％。
2.根据权利要求1所述的一种浇注酚醛泡沫体的制造方法，其特征在于，所述步骤1中所述的碱性催化剂为氢氧化钠或氢氧化钡。
3.根据权利要求1所述的一种浇注酚醛泡沫体的制造方法，其特征在于，所述步骤2中所述的异氰酸酯为一种PAPI，NCO含量为30.8％，平均分子量为375，官能度为3。
4.根据权利要求1所述的一种浇注酚醛泡沫体的制造方法，其特征在于，所述步骤2中所述表面活性剂为T-80，DC-193或H203中的一种或几种。