CN103360967A - 冰箱专用铝箔胶带及制造工艺 - Google Patents
冰箱专用铝箔胶带及制造工艺 Download PDFInfo
- Publication number
- CN103360967A CN103360967A CN2012101024733A CN201210102473A CN103360967A CN 103360967 A CN103360967 A CN 103360967A CN 2012101024733 A CN2012101024733 A CN 2012101024733A CN 201210102473 A CN201210102473 A CN 201210102473A CN 103360967 A CN103360967 A CN 103360967A
- Authority
- CN
- China
- Prior art keywords
- film
- aluminium foil
- adhesive tape
- conjunction
- foaming
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
冰箱专用铝箔胶带及制造工艺，铝箔胶带是由发泡结合离型层、柔性膜层、胶粘层、铝箔层、压敏胶层所组成；所述的发泡结合离型层厚度为0.3-1μm，主要采用硅橡胶与发泡料相容制成；所述的柔性膜层厚度为6-30μm，选用聚酯PET膜、聚乙烯PE膜、聚丙烯PP、BOPP薄膜、聚氯乙烯PVC膜制成；所述的胶粘层厚度为8-20μm ，选用橡胶、聚氨脂、丙烯酸加胶粘剂制成；所述的铝箔层厚度10-30μm，是由纯度80%-99.99%的压延铝箔制成。本发明与传统的铝箔胶带相比，具有提升冰箱整体质量，贴合平整，柔软，金属感强，很好的发泡结合效果。节省了冰箱厂员工的操作时间，成本低，更环保，减少了资源浪费。
Description
技术领域：
本发明涉及到冰箱专用铝箔胶带及制造工艺
背景技术：
市场上的铝箔胶带品种烦多，有带离型纸的铝箔胶带，不带离型纸的铝箔胶带，还有复塑铝箔胶带在冰箱制冷行业中的使用，都存在着使用不方便，冰箱内毛细管的固定效果不好，与发泡剂结合不牢固，制造成本高，浪费资源等问题。
发明内容：
本发明的目的就是要提供一种冰箱专用铝箔胶带及制造工艺，它能克服现有铝箔胶带所存在的以上问题。本发明的目的是这样实现的，冰箱专用铝箔胶带及制造工艺，其特征在于：铝箔胶带是由发泡结合离型层、柔性膜层、胶粘层、铝箔层、压敏胶层所组成；所述的发泡结合离型层厚度为0.3-1μm，主要采用硅橡胶与发泡料相容制成；所述的柔性膜层厚度为6-30μm，选用聚酯PET膜、聚乙烯PE膜、聚丙烯PP、BOPP薄膜、聚氯乙烯PVC膜制成；所述的胶粘层厚度为8-20μm ，选用橡胶、聚氨脂、丙烯酸加胶粘剂制成；所述的铝箔层厚度10-30μm，纯度80%-99.99%的压延铝箔制成；制造工艺是采用柔性薄膜厚度在6μm-30μm的聚烃类薄膜或聚酯类薄膜，进行处理；在柔性薄膜表面，涂发泡结合离型剂；在柔性薄膜的另一表面与铝箔表面之间采用干式贴合工艺，使柔性薄膜与铝箔间结合紧密牢固，使外力无法分开铝箔；所述的铝箔为压延铝箔，厚度在8μm-75μm；在铝箔的另一表面涂覆厚度15μm-50μm的压敏胶层；所述的压敏胶包括水性压克力胶系、油性压克力胶系、橡胶型胶系、硅胶系；在柔性膜表面涂发泡结合离型剂时，采用凹版涂布法上离型剂，后经12m-32m烘道，烘道温度控制在120℃-180℃，烘干固化，速度60 -160 m /min，收卷即形成发泡结合离型膜，用发泡结合离型膜的另一面采用凹版涂布头涂上胶粘剂后经12m-20m烘道，烘道温度控制在60℃-120℃烘干，经贴合收卷部位与铝箔贴合，贴合温度控制在100℃-160℃,速度60 -160 m /min，即形成复塑铝箔，在复塑铝箔的铝箔面采用胶液直刮式涂布头，涂压敏胶；后经24m-32m烘道烘干，速度120-160m/ min，收卷即形成冰箱专用铝箔胶带。本发明与传统的铝箔胶带相比，具有提升冰箱整体质量，贴合平整，柔软，金属感强，很好的发泡结合效果。节省了冰箱厂员工的操作时间，成本低，更环保，减少了资源浪费。
附图说明：
图1是本发明结构示意图；
1.发泡结合离型层，2.柔性膜层，3.胶粘层， 4.铝箔层，5.压敏胶层。
具体实施方式：下面结合附图对本发明作进一步说明；
冰箱专用铝箔胶带及制造工艺，其特征在于：铝箔胶带是由发泡结合离型层、柔性膜层、胶粘层、铝箔层、压敏胶层所组成；所述的发泡结合离型层厚度为0.3-1μm，主要采用硅橡胶与发泡料相容制成；所述的柔性膜层厚度为6-30μm，选用聚酯PET膜、聚乙烯PE膜、聚丙烯PP、BOPP薄膜、聚氯乙烯PVC膜制成；所述的胶粘层厚度为8-20μm ，选用橡胶、聚氨脂、丙烯酸加胶粘剂制成；所述的铝箔层厚度10-30μm，纯度80%-99.99%的压延铝箔制成；制造工艺是采用柔性薄膜厚度在6μm-30μm的聚烃类薄膜或聚酯类薄膜，进行处理；在柔性薄膜表面，涂发泡结合离型剂；在柔性薄膜的另一表面与铝箔表面之间采用干式贴合工艺，使柔性薄膜与铝箔间结合紧密牢固，使外力无法分开铝箔；所述的铝箔为压延铝箔，厚度在8μm-75μm；在铝箔的另一表面涂覆厚度15μm-50μm的压敏胶层；所述的压敏胶包括水性压克力胶系、油性压克力胶系、橡胶型胶系、硅胶系；在柔性膜表面涂发泡结合离型剂时，采用凹版涂布法上离型剂，后经12m-32m烘道，烘道温度控制在120℃-180℃，烘干固化，速度60 -160 m /min，收卷即形成发泡结合离型膜，用发泡结合离型膜的另一面采用凹版涂布头涂上胶粘剂后经12m-20m烘道，烘道温度控制在60℃-120℃烘干，经贴合收卷部位与铝箔贴合，贴合温度控制在100℃-160℃,速度60 -160 m /min，即形成复塑铝箔，在复塑铝箔的铝箔面采用胶液直刮式涂布头，涂压敏胶；后经24m-32m烘道烘干，速度120-160m/ min，收卷即形成冰箱专用铝箔胶带。
实施例1
如图所示，本发明所述的发泡结合离型层1与柔性膜层2，是在柔性膜表面用80目凹版涂布发泡结合离型剂经24m烘道，烘道温度控制在120℃，速度80 m /min制成发泡结合膜，在发泡结合膜上涂粘合剂与铝箔结合制成复塑铝箔，再在复塑铝箔的铝箔面上涂压敏胶即制成冰箱专用覆膜铝箔胶带。
所述的发泡结合离型剂80目涂布量，是柔性膜层厚6μm、胶粘剂层厚15μm、铝箔层厚15μm、亚敏胶层厚20μm。
实施例2
如图所示，本发明所述的发泡结合离型层1与柔性膜层2，是在柔性膜表面用90目凹版涂布发泡结合离型剂经26m烘道，烘道温度控制在110℃，速度90m /min制成发泡结合膜，在发泡结合膜上涂粘合剂与铝箔结合制成复塑铝箔，再在复塑铝箔的铝箔面上涂压敏胶即制成冰箱专用覆膜铝箔胶带。
所述的发泡结合离型剂90目涂布量，是柔性膜层厚7μm、胶粘剂层厚17μm、铝箔层厚16μm、亚敏胶层厚22μm。
实施例3
如图所示，本发明所述的发泡结合离型层1与柔性膜层2，是在柔性膜表面用100目凹版涂布发泡结合离型剂经28m烘道，烘道温度控制在100℃，速度120m /min制成发泡结合膜，在发泡结合膜上涂粘合剂与铝箔结合制成复塑铝箔，再在复塑铝箔的铝箔面上涂压敏胶即制成冰箱专用覆膜铝箔胶带。
所述的发泡结合离型剂100目涂布量，是柔性膜层厚8μm、胶粘剂层厚18μm、铝箔层厚18μm、亚敏胶层厚23μm。
实施例4
如图所示，本发明所述的发泡结合离型层1与柔性膜2，是在柔性膜表面用110目凹版涂布发泡结合离型剂经29m烘道，烘道控制温度90℃，速度110m /min制成发泡结合膜，在发泡结合膜上涂粘合剂与铝箔结合制成复塑铝箔，再在复塑铝箔的铝箔面上涂压敏胶即制成冰箱专用覆膜铝箔胶带。
所述的发泡结合离型剂110目涂布量，是柔性膜层厚9μm、胶粘剂层厚19μm、铝箔层厚19μm、亚敏胶层厚24μm。
实施例5
如图所示，本发明所述的发泡结合离型层1与柔性膜层2，是在柔性膜表面用120目凹版涂布发泡结合离型剂经30m烘道，烘道温度控制在90℃，速度120m /min制成发泡结合膜，在发泡结合膜上涂粘合剂与铝箔结合制成复塑铝箔，再用复塑铝箔的铝箔面涂上压敏胶即制成冰箱专用覆膜铝箔胶带。
所述的发泡结合离型剂120目涂布量，是柔性膜层厚10μm、胶粘剂层厚20μm、铝箔层厚20μm、亚敏胶层厚25μm。
实施例6
如图所示，本发明所述的发泡结合离型层1与柔性膜层2，是在柔性膜表面用130目凹版涂布发泡结合离型剂经31m烘道，烘道温度控制在80℃，速度130m /min制成发泡结合膜，在发泡结合膜上涂粘合剂与铝箔结合制成复塑铝箔，再在复塑铝箔的铝箔面上涂压敏胶即制成冰箱专用覆膜铝箔胶带。
所述的发泡结合离型剂130目涂布量，是柔性膜层厚11μm、胶粘剂层厚21μm、铝箔层厚21μm、亚敏胶层厚26μm。
实施例7
如图所示，本发明所述的发泡结合离型层1与柔性膜层2，是在柔性膜表面用140目凹版涂布发泡结合离型剂经32m烘道，烘道温度控制在120℃，速度80m /min制成发泡结合膜，在发泡结合膜上涂粘合剂与铝箔结合制成复塑铝箔，再在复塑铝箔的铝箔面上涂压敏胶即制成冰箱专用覆膜铝箔胶带。
所述的发泡结合离型剂140目涂布量，是柔性膜层厚9μm、胶粘剂层厚16μm、铝箔层厚16μm、亚敏胶层厚23μm。
Claims (2)
1.冰箱专用铝箔胶带及制造工艺，其特征在于：铝箔胶带是由发泡结合离型层、柔性膜层、胶粘层、铝箔层、压敏胶层所组成；其制造工艺是采用柔性薄膜厚度在6μm-30μm的聚烃类薄膜或聚酯类薄膜，进行处理；在柔性薄膜表面，涂发泡结合离型剂；在柔性薄膜的另一表面与铝箔表面之间采用干式贴合工艺，使柔性薄膜与铝箔间结合紧密牢固；在铝箔的另一表面涂覆压敏胶层；在柔性膜表面涂发泡结合离型剂时，采用凹版涂布法上离型剂，后经12m-32m烘道，烘道温度控制在120℃-180℃，烘干固化，速度60 -160 m /min，收卷即形成发泡结合离型膜，用发泡结合离型膜的另一面采用凹版涂布头涂上胶粘剂后经12m-20m烘道，烘道温度控制在60℃-120℃烘干，经贴合收卷部位与铝箔贴合，贴合温度控制在100℃-160℃,速度60 -160 m /min，即形成复塑铝箔，在复塑铝箔的铝箔面采用胶液直刮式涂布头，涂压敏胶；后经24m-32m烘道烘干，速度120-160m/ min，收卷即形成冰箱专用铝箔胶带。
2.根据权利要求1所述的冰箱专用铝箔胶带及制造工艺，其特征在于：所述的发泡结合离型层厚度为0.3-1μm，主要采用硅橡胶与发泡料相容制成；所述的柔性膜层厚度为6-30μm，选用聚酯PET膜、聚乙烯PE膜、聚丙烯PP、BOPP薄膜、聚氯乙烯PVC膜制成；所述的胶粘层厚度为8-20μm ，选用橡胶、聚氨脂、丙烯酸加胶粘剂制成；所述的铝箔层厚度10-30μm，由纯度80%-99.99%的压延铝箔制成；所述的压敏胶层厚度为15μm-50μm，选用水性压克力胶系、油性压克力胶系、橡胶型胶系、硅胶系制成。