CN103360719A - 抗老化pa-abs塑料合金 - Google Patents

抗老化pa-abs塑料合金 Download PDF

Info

Publication number
CN103360719A
CN103360719A CN2013103004669A CN201310300466A CN103360719A CN 103360719 A CN103360719 A CN 103360719A CN 2013103004669 A CN2013103004669 A CN 2013103004669A CN 201310300466 A CN201310300466 A CN 201310300466A CN 103360719 A CN103360719 A CN 103360719A
Authority
CN
China
Prior art keywords
aging
abs
mah
polyblend
plastic alloy
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013103004669A
Other languages
English (en)
Other versions
CN103360719B (zh
Inventor
黄美蓉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Dongguan Yan Tao Plastic Industry Co. Ltd.
Original Assignee
Shanghai Qiucheng New Material Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanghai Qiucheng New Material Technology Co Ltd filed Critical Shanghai Qiucheng New Material Technology Co Ltd
Priority to CN201310300466.9A priority Critical patent/CN103360719B/zh
Publication of CN103360719A publication Critical patent/CN103360719A/zh
Application granted granted Critical
Publication of CN103360719B publication Critical patent/CN103360719B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗老化PA-ABS塑料合金，由下述组分按重量份组成：20-30份PA、70-80份ABS、2-4份相容剂、0.5-1.5份抗老化剂。本发明的抗老化PA-ABS塑料合金，力学性能优良,尤其是冲击强度高，且具有优秀的热老化性能，适合在极端高温环境下使用。

Description

抗老化PA-ABS塑料合金
技术领域
本发明涉及一种塑料合金，尤其涉及一种抗老化PA-ABS塑料合金。
背景技术
ABS树脂（丙烯腈-苯乙烯-丁二烯共聚物，ABS是Acrylonitrile ButadieneStyrene的首字母缩写）是一种强度高、韧性好、易于加工成型的热塑型高分子材料结构。
ABS是本世纪40年代发展起来的通用热塑性工程塑料，是一个综合力学性能十分优秀的塑料品种，不仅具有良好的刚性、硬度和加工流动性，而且具有高韧性特点，可以注塑、挤出或热成型。
聚酰胺(PA，俗称尼龙)是美国DuPont公司最先开发用于纤维的树脂，于1939年实现工业化。20世纪50年代开始开发和生产注塑制品，以取代金属满足下游工业制品轻量化、降低成本的要求。PA具有良好的综合性能，包括力学性能、耐热性、耐磨损性、耐化学药品性和自润滑性，且摩擦系数低，有一定的阻燃性，易于加工，适于用玻璃纤维和其它填料填充增强改性，提高性能和扩大应用范围。
PA-ABS塑料合金，作为结构性组分在汽车内饰中使用，是现有材料的实用替代品，同时，从成本角度而言也十分诱人。该材料不仅能够满足设计变化方面的苛刻技术规格要求，同时也能够显著节省***成本。
然而，目前的PA-ABS塑料合金抗老化性能并不佳。
发明内容
针对现有技术中存在的上述不足，本发明所要解决的技术问题是提供一种抗老化PA-ABS塑料合金，具有良好的抗老化性能。
本发明所要解决的技术问题是通过如下技术方案实现的：
一种抗老化PA-ABS塑料合金，由下述组分按重量份组成：20-30份PA、70-80份ABS、2-4份相容剂、0.5-1.5份抗老化剂。
所述抗老化剂，由下述组分按重量份组成：30-50份4,4’-硫代双(6-叔丁基-3-甲基苯酚)、30-50份1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷、10-30份硫代二丙酸双十八醇酯。
4,4’-硫代双(6-叔丁基-3-甲基苯酚)，CAS号：96-69-5，英文名：4,4'-Thio-bis(6-tert-butyl-m-methyl phenol)。
1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷，CAS号:1843-03-4，4,4',4''-(1-methyl-1-propanyl-3-ylidene)tris[2-(1,1-dimethylethyl)-5-methyl-Phenol。
硫代二丙酸双十八醇酯，英文名：Distearyl thiodipropionate，CAS号：693-36-7。
将4,4’-硫代双(6-叔丁基-3-甲基苯酚)、1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷和硫代二丙酸双十八醇酯搅拌混合均匀，即可制得该抗老化剂。
所述相容剂为POE-g-MAH、PP-g-MA、PP-g-AA、EAA、PS-g-PMMA、PS-g-MAH、PP-g-Pa6、PS-b-PMMA、PS-b-PBA、PE-g-ST、PP-g-ST、ABS-g-MAH、PP-g-MAH、EVA、SEBS、SEBS-g-MAH或PE-g-MAH。
可以采用本行业通用方法进行制备本发明的抗老化PA-ABS塑料合金，例如：按配比称取各组分，混合均匀后，熔融混炼、挤出造粒，即获得所述抗老化PA-ABS塑料合金。
具体的，可以为按配比称取各组分，在混合机中，室温下控制转速在300-400转/分钟，混合5-10分钟，取出后转入螺杆挤出机中，在160-220℃温度下挤出造粒，即获得所述抗老化PA-ABS塑料合金。
显然，在本发明中为提高产品的其他性能，还可以适应性地添加其他助剂，如阻燃剂、着色剂和抗静电剂等。
发明人通过大量实验得出，将4,4’-硫代双(6-叔丁基-3-甲基苯酚)、1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷和硫代二丙酸双十八醇酯三种抗老化剂进行合理复配使用，协同增效，抗老化效果明显。
本发明的抗老化PA-ABS塑料合金，力学性能优良,尤其是冲击强度高，且具有优秀的热老化性能，适合在极端高温环境下使用。
具体实施方式
实施例1
按照表1中对应实施例1数据称取各原料。将各组分加入到高速混合机中，室温下控制转速在350转/分钟，混合8分钟，取出后转入螺杆挤出机中，在200℃温度下挤出造粒，获得抗老化PA-ABS塑料合金。
表1：抗老化PA-ABS塑料合金配方表单位：公斤
实施例1 实施例2 实施例3 实施例4
PA树脂 25 25 25 25
ABS树脂 75 75 75 75
相容剂POE-g-MAH 3 3 3 3
4,4’-硫代双(6-叔丁基-3-甲基苯酚) 0.4 0.8 / 0.5
1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷 0.4 / 0.8 0.5
硫代二丙酸双十八醇酯 0.2 0.2 0.2 /
PA树脂选用美国杜邦公司牌号101L的PA66树脂；
ABS树脂选用吉林石化公司牌号0215A的ABS树脂。
实施例2-4
分别按照表1中对应实施例2-4数据称取各原料。采用实施例1所述的方法制备所述抗老化PA-ABS塑料合金。
测试例1
根据热氧老化实验标准GB/T7141-2008，对制得的塑料进行人工加速老化实验（90℃，500h），并分别测定该塑料人工加速老化前后的拉伸强度、悬臂梁缺口冲击强度。
拉伸强度保持率=（人工加速老化后的拉伸强度-人工加速老化前的拉伸强度）÷人工加速老化前的拉伸强度×100%。
冲击强度保持率=（人工加速老化后的悬臂梁缺口冲击强度-人工加速老化前的悬臂梁缺口冲击强度）÷人工加速老化前的悬臂梁缺口冲击强度×100%。
表2：塑料抗老化性能测试表（90℃，500h）
拉伸强度保持率，% 悬臂梁缺口冲击强度保持率，%
实施例1 80.4 80.6
实施例2 79.2 79.6
实施例3 79.5 79.1
实施例4 79.3 79.2

Claims (4)

1.一种抗老化PA-ABS塑料合金，其特征在于，由下述组分按重量份组成：20-30份PA、70-80份ABS、2-4份相容剂、0.5-1.5份抗老化剂。
2.如权利要求1所述的抗老化PA-ABS塑料合金，其特征在于，所述抗老化剂，由下述组分按重量份组成：30-50份4,4’-硫代双(6-叔丁基-3-甲基苯酚)、30-50份1,1,3-三(2-甲基-4-羟基-5-叔丁苯基)丁烷、10-30份硫代二丙酸双十八醇酯。
3.如权利要求1所述的抗老化PA-ABS塑料合金，其特征在于：所述相容剂为POE-g-MAH、PP-g-MA、PP-g-AA、EAA、PS-g-PMMA、PS-g-MAH、PP-g-Pa6、PS-b-PMMA、PS-b-PBA、PE-g-ST、PP-g-ST、ABS-g-MAH、PP-g-MAH、EVA、SEBS、SEBS-g-MAH或PE-g-MAH。
4.如权利要求3所述的抗老化PA-ABS塑料合金，其特征在于：所述相容剂为POE-g-MAH。
CN201310300466.9A 2013-07-15 2013-07-15 抗老化pa-abs塑料合金 Active CN103360719B (zh)