CN103254698B - 隔声吸振阻尼浆及生产方法 - Google Patents
隔声吸振阻尼浆及生产方法 Download PDFInfo
- Publication number
- CN103254698B CN103254698B CN201310228688.4A CN201310228688A CN103254698B CN 103254698 B CN103254698 B CN 103254698B CN 201310228688 A CN201310228688 A CN 201310228688A CN 103254698 B CN103254698 B CN 103254698B
- Authority
- CN
- China
- Prior art keywords
- parts
- damping slurry
- sound insulation
- absorbing damping
- vibration
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种隔声吸振阻尼浆,它由以下重量份的原料组成:20~30份水、0.1~0.5份纤维素、0.1~0.2份AMP-95、0.5~2份分散剂、0.05~0.2份润湿剂、0.1~0.5份消泡剂、5~10份钛白粉、10~20份重钙、10~20份云母粉、5~10份蛭石粉、1~2份成膜助剂、1~2份乙二醇、30~40份苯丙乳液、0.05~0.2份防腐剂、0.5~1份碱溶胀增稠剂。本发明的生产成本较低,减振降噪效果较好。
Description
技术领域
本发明涉及一种阻尼浆及生产方法,特别是一种隔声吸振阻尼浆及生产方法。
背景技术
近几十年来,随着现代工业的发展,振动工具及高速和自动化的机械设备日益增多,随之引起的振动、噪声和疲劳断裂问题也越来越突出。在日常生活中,这类振动和噪声会危害人体的健康,严重者甚至丧失工作能力;在工程中,振动和噪声激振共振峰响应还会直接影响电子器件、仪器和仪表的正常工作,严重时会造成灾难性后果。
因此,很多采用阻尼浆涂覆在金属板结构表面对此进行减振降噪,阻尼浆涂料与吸声材料不同,其原理是将振动机械能转化为热能散掉。常规的阻尼浆涂料由丙烯酸IPN乳液、阻尼颜填料、阻燃剂和助剂制成,原料成本较高,使得生产成本提高,而且减振降噪性能一般。
发明内容
本发明的目的在于,提供一种隔声吸振阻尼浆及生产方法。本发明的生产成本较低,减振降噪效果较好。
本发明的技术方案:隔声吸振阻尼浆,其特征在于,它由以下重量份的原料组成:20~30份水、0.1~0.5份纤维素、0.1~0.2份AMP-95、0.5~2份分散剂、0.05~0.2份润湿剂、0.1~0.5份消泡剂、5~10份钛白粉、10~20份重钙、10~20份云母粉、5~10份蛭石粉、1~2份成膜助剂、1~2份乙二醇、30~40份苯丙乳液、0.05~0.2份防腐剂、0.5~1份碱溶胀增稠剂。
前述的隔声吸振阻尼浆中,它由以下重量份的原料组成:25份水、0.3份纤维素、0.15份AMP-95、1.25份分散剂、0.125份润湿剂、0.3份消泡剂、7.5份钛白粉、15份重钙、15份云母粉、7.5份蛭石粉、1.5份成膜助剂、1.5份乙二醇、35份苯丙乳液、0.125份防腐剂、0.75份碱溶胀增稠剂。
前述的隔声吸振阻尼浆中,所述的重钙是800目的重钙。
前述的隔声吸振阻尼浆中,所述的云母粉是600目的云母粉。
前述的隔声吸振阻尼浆中,所述的蛭石粉是300目的蛭石粉。
前述的隔声吸振阻尼浆中,所述的成膜助剂是C-12成膜助剂。
前述的隔声吸振阻尼浆的生产方法,其特征在于,将上述各原料配量后按以下步骤进行:
①先将水、纤维素、分散剂、润湿剂和消泡剂混合用800转/分的速度搅拌使其分散均匀;
②加入钛白粉、重钙、云母粉和蛭石粉用1200转/分的速度搅拌;
③加入C-12成膜助剂、乙二醇和苯丙乳液用800转/分的速度搅拌;
④最后加入防腐剂、AMP-95和碱溶胀型增稠剂,混合均匀得成品。
与现有技术相比,本发明通过合理配比组分,使各组分能相互匹配,使得具有以下优点:生产成本较低;粘度低,施工方便,可直接喷涂在彩钢板等板材结构表面进行减振降噪,使施工人员不易接触,卫生环保;附着力强,不易脱落;施工性好,能提高施工效率。本发明的生产方法简单,使用设备少,生产成本低,质量好。本发明采用环保原料,并进行充分的混合,使得各组分均匀分散混合,完全没有有害健康的气味存在,确保使用安全。本发明不仅粘度低、附着力强,可进行喷涂,方便施工,提高施工效率;而且流平性好,使用效果较好。
本发明通过实验得出:实验采用的金属材料长180mm,宽9.1mm,金属板厚度0.86mm,金属材料密度7800kg/m3,材料损耗因数在0.18,在金属材料表面涂覆厚度为1.94mm的阻尼层(本发明的阻尼浆),阻尼材料损耗因数可达0.479。涂覆的阻尼层不仅较薄,而且减振降噪效果较理想,还降低了使用成本。
具体实施方式
下面结合实施例对本发明作进一步的说明,但并不作为对本发明限制的依据。
实施例1。隔声吸振阻尼浆,其特征在于,它由以下重量份的原料组成:20~30份水、0.1~0.5份纤维素、0.1~0.2份AMP-95、0.5~2份分散剂、0.05~0.2份润湿剂、0.1~0.5份消泡剂、5~10份钛白粉、10~20份重钙、10~20份云母粉、5~10份蛭石粉、1~2份成膜助剂、1~2份乙二醇、30~40份苯丙乳液、0.05~0.2份防腐剂、0.5~1份碱溶胀增稠剂。
比较好的是,它由以下重量份的原料组成:25份水、0.3份纤维素、0.15份AMP-95、1.25份分散剂、0.125份润湿剂、0.3份消泡剂、7.5份钛白粉、15份重钙、15份云母粉、7.5份蛭石粉、1.5份成膜助剂、1.5份乙二醇、35份苯丙乳液、0.125份防腐剂、0.75份碱溶胀增稠剂。
更好的是,所述的重钙是800目的重钙。所述的云母粉是600目的云母粉。所述的蛭石粉是300目的蛭石粉。所述的成膜助剂是C-12成膜助剂。
上述的隔声吸振阻尼浆的生产方法,将上述各原料配量后按以下步骤进行:
①先将水、纤维素、分散剂、润湿剂和消泡剂混合用800转/分的速度搅拌使其分散均匀;
②加入钛白粉、重钙、云母粉和蛭石粉用1200转/分的速度搅拌;
③加入C-12成膜助剂、乙二醇和苯丙乳液用800转/分的速度搅拌;
④最后加入防腐剂、AMP-95和碱溶胀型增稠剂,混合均匀得成品。
实施例2。隔声吸振阻尼浆,它也可以由以下重量份的原料组成:20份水、0.5份纤维素、0.1份AMP-95、2份分散剂、0.05份润湿剂、0.5份消泡剂、5份钛白粉、20份重钙、10份云母粉、10份蛭石粉、1份成膜助剂、2份乙二醇、30份苯丙乳液、0.2份防腐剂、0.5份碱溶胀增稠剂。通过实施例1中的生产方法进行制备。
实施例3。隔声吸振阻尼浆,它还可以由以下重量份的原料组成: 30份水、0.1份纤维素、0.2份AMP-95、0.5份分散剂、0.2份润湿剂、0.1份消泡剂、10份钛白粉、10份重钙、20份云母粉、5份蛭石粉、2份成膜助剂、1份乙二醇、40份苯丙乳液、0.05份防腐剂、1份碱溶胀增稠剂。通过实施例1中的生产方法进行制备。
Claims (6)
1.隔声吸振阻尼浆,其特征在于,它由以下重量份的原料组成:25份水、0.3份纤维素、0.15份AMP-95、1.25份分散剂、0.125份润湿剂、0.3份消泡剂、7.5份钛白粉、15份重钙、15份云母粉、7.5份蛭石粉、1.5份成膜助剂、1.5份乙二醇、35份苯丙乳液、0.125份防腐剂、0.75份碱溶胀增稠剂。
2.根据权利要求1所述的隔声吸振阻尼浆,其特征在于:所述的重钙是800目的重钙。
3.根据权利要求1所述的隔声吸振阻尼浆,其特征在于:所述的云母粉是600目的云母粉。
4.根据权利要求1所述的隔声吸振阻尼浆,其特征在于:所述的蛭石粉是300目的蛭石粉。
5.根据权利要求1所述的隔声吸振阻尼浆,其特征在于:所述的成膜助剂是C-12成膜助剂。
6.根据权利要求1-5任一权利要求所述的隔声吸振阻尼浆的生产方法,其特征在于,将上述各原料配量后按以下步骤进行:
①先将水、纤维素、分散剂、润湿剂和消泡剂混合用800转/分的速度搅拌使其分散均匀;
②加入钛白粉、重钙、云母粉和蛭石粉用1200转/分的速度搅拌;
③加入C-12成膜助剂、乙二醇和苯丙乳液用800转/分的速度搅拌;
④最后加入防腐剂、AMP-95和碱溶胀型增稠剂,混合均匀得成品。