CN103243470B - The Weaving method of a kind of high cotton content high elasticity abrasion-proof cloth and goods - Google Patents
The Weaving method of a kind of high cotton content high elasticity abrasion-proof cloth and goods Download PDFInfo
- Publication number
- CN103243470B CN103243470B CN201310155554.4A CN201310155554A CN103243470B CN 103243470 B CN103243470 B CN 103243470B CN 201310155554 A CN201310155554 A CN 201310155554A CN 103243470 B CN103243470 B CN 103243470B
- Authority
- CN
- China
- Prior art keywords
- yarn
- fingers
- twists
- cotton
- cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the Weaving method of a kind of high cotton content high elasticity abrasion-proof cloth, it comprises the following steps: (1), preparation Z twist with the fingers cotton yarn, and this Z twists with the fingers the cotton yarn wrap yarn as textile cloth；(2), preparing S sth. made by twisting spandex, this S twists with the fingers spandex as yarn in textile cloth；(3), by Z twisting with the fingers cotton yarn and carry out the processing of Z twisted stock with S sth. made by twisting spandex, form strand, this strand is as the raw material of textile cloth；(4) Weaving method carries out weaving and forms cloth or goods routinely.The invention also discloses the goods of a kind of Weaving method implementing high cotton content high elasticity abrasion-proof cloth, these goods are to be formed by weaving by yarn, yarn includes wrap yarn and inner yarn, wrap yarn is that Z twists with the fingers cotton yarn, and inner yarn is that S twists with the fingers spandex, and S twists with the fingers spandex and has higher elasticity, and the mass percent shared by cotton fiber is 96%-98%, make these goods have higher cotton content, improve the comfortableness of textile, and make it have antibacterial, moisture sorption effect preferably.
Description
Technical field
The present invention relates to the technical field of weaving, be specifically related to Weaving method and the goods of a kind of high cotton content.
Background technology
In prior art, owing to naked spandex yarn elasticity is relatively big, in socks braiding process, tension force during naked spandex yarn conveying is difficult to control, and therefore, an existing class quilted stockings adopts spandex covered yarn and cotton yarn to weave.Due to spandex covered yarn finite elastic, and the cotton content of the socks that braiding is out is between 60%-85%, and cotton content is relatively low, and therefore, the comfortableness of socks is poor.It addition, often containing chemical fibres such as terylene, chinlon, acrylon in this kind of socks woven by spandex covered yarn, hygroscopic effect is poor, it is easy to produce abnormal flavour.
Summary of the invention
It is an object of the invention to for above-mentioned deficiency, the Weaving method of a kind of high cotton content high elasticity abrasion-proof cloth is provided, and the goods of enforcement the method, the Weaving method of the present invention can increase the content of cotton and the elasticity of goods itself effectively, improves goods comfortableness, hygroscopic effect.
The present invention be the technical scheme is that for achieving the above object
The Weaving method of a kind of high cotton content high elasticity abrasion-proof cloth, it is characterised in that it comprises the following steps:
(1), preparing Z sth. made by twisting cotton yarn, this Z twists with the fingers the cotton yarn wrap yarn as textile cloth；
(2), preparing S sth. made by twisting spandex, this S twists with the fingers spandex as yarn in textile cloth；
(3), by Z twisting with the fingers cotton yarn and carry out the processing of Z twisted stock with S sth. made by twisting spandex, form strand, this strand is as the raw material of textile cloth；
(4) being weaved by above-mentioned strand Weaving method routinely, inner yarn is coated on the network internal that its yarn is made into by described wrap yarn, forms cloth or goods.
It is that pure cotton fiber is made that described Z twists with the fingers cotton yarn, and in described cloth or goods, Z twists with the fingers the mass percent shared by cotton yarn is 96%-98%.
Step (1) specifically also includes herein below: cotton fiber first carries out softening pretreatment, then Z twists with the fingers cotton yarn, and to be woven into specification be the 32-40 cotton yarn propped up, as the wrap yarn of textile cloth.
It is 70-85 stringer/5cm that described Z twists with the fingers the horizontal density of cotton yarn or S sth. made by twisting spandex, and vertical density is 50-65 line/5cm.
Described step (4) specifically also includes herein below: described cloth is carried out following PROCESS FOR TREATMENT: grey cloth is checked, and turns over cloth and prints, margin to seam, singe, desizing, kiering, oxygen bleaching, pickling, washing, open rolling is dried, mercerising, multiple drift, dry, calendering, tentering, carry out bleaching and antimicrobial treatment, finally carry out finishing process；Wherein finishing process includes brightening, soft, wrinkle resistant process.
Described cloth is carried out antimicrobial treatment, cloth is sent in the tank body closed, double-face spray painting nano antibacterial coating, powder or aerosol.
It is 600 twists/m that described Z twists with the fingers the twist of cotton yarn.
The horizontal density of described yarn is 73 stringers/5cm, and vertical density is 53 lines/5cm.
The goods of a kind of Weaving method implementing above-mentioned high cotton content high elasticity abrasion-proof cloth, it is characterised in that it adopts described Z to twist with the fingers cotton yarn and twists with the fingers the strand formed after spandex carries out the processing of Z twisted stock as material with S, the weaving of this strand form cloth or goods；Wherein said Z twists with the fingers the cotton yarn wrap yarn as textile cloth, and it is made for pure cotton fiber, and described S twists with the fingers spandex as yarn in textile cloth, and inner yarn is coated on inside its network of yarns being made into by described wrap yarn；In described cloth or goods, Z twists with the fingers the mass percent shared by cotton yarn is 96%-98%.
It is the 32-40 cotton yarn propped up that described Z twists with the fingers cotton yarn；It is 70-85 stringer/5cm that described Z twists with the fingers the horizontal density of cotton yarn or S sth. made by twisting spandex, and vertical density is 50-65 line/5cm.
Described goods, it is possible to be socks or other textiles.
The invention has the beneficial effects as follows: method provided by the invention and goods, it is be formed by weaving by the strand of high lint content, yarn includes wrap yarn and inner yarn, the Z that wrap yarn is textile twists with the fingers cotton yarn, in yarn be S twist with the fingers spandex, S twists with the fingers spandex and has higher elasticity, and the percentage ratio that wrap yarn accounts for whole cloth or goods oeverall quality is 96%-98%wt, cloth or goods are made to have higher cotton content, improve the comfortableness of cloth or goods, and it is absent from other chemical fibres except cotton and spandex, cloth or goods are made to have good moisture absorption, antibacterial, warming, the effect such as wear-resisting；2, Z twists with the fingers cotton yarn is the 32-40 cotton yarn propped up, and makes wrap yarn have higher intensity；3, the horizontal density of yarn is 70-85 stringer/5cm, and vertical density is 50-65 line/5cm, makes cloth or goods have higher degree of tightness comfort level.
The cloth of the present invention or goods are particularly suited for the product such as socks production, physical culture sheath, and other high-end textiles, the excellent product performance such as obtained socks or sheath, comfortable, warming, wear-resisting, antibacterial, moisture absorption, softness, be particularly suitable for autumn and winter, athlete or other consumer that textile requirement is higher is used.
Below in conjunction with accompanying drawing and detailed description of the invention, the present invention is further described.
Accompanying drawing explanation
Fig. 1 is ply yarn structure schematic diagram of the present invention；
Fig. 2 is the Sock structure schematic diagram that the inventive method prepares；
In figure:
1.Z twists with the fingers cotton yarn 2.S and twists with the fingers spandex 3. socks.
Detailed description of the invention
Embodiment: referring to Fig. 1 to Fig. 2, the Weaving method of the high cotton content high elasticity abrasion-proof cloth that the present embodiment provides, it comprises the following steps:
(1), preparation Z twist with the fingers cotton yarn 1, it is made for pure cotton fiber, and cotton fiber first carries out softening pretreatment, then Z twists with the fingers cotton yarn 1, and to be woven into specification be the 32-40 cotton yarn propped up, using this cotton yarn wrap yarn as textile cloth；Softening processing procedure is: insert appropriate softening liquid or softening powder in cotton fiber, and applies the ultrasound wave of 500W/80-100KHz, continues to carry out softening in 10-30 minute；
(2), preparing S sth. made by twisting spandex 2, this S twists with the fingers spandex 2 as yarn in textile cloth；
(3), by Z twisting with the fingers cotton yarn 1 and carry out the processing of Z twisted stock with S sth. made by twisting spandex 2, form strand, this strand is as the raw material of textile cloth；
(4), above-mentioned strand Weaving method routinely is weaved, form cloth or goods；Method provided by the invention, it is possible to then high cotton content high elasticity abrasion-proof cloth of weaving out makes textile again, it is also possible to disposable weaving out has the goods of high cotton content high elasticity abrasion-proof cloth, protects articles for use etc. including the physical culture such as socks, sheath.
(5) more described cloth or goods are carried out following PROCESS FOR TREATMENT: grey cloth is checked, turn over cloth and print, margin to seam, singe, desizing, kiering, oxygen bleaching, pickling, washing, open rolling is dried, mercerising, multiple drift, dry, calendering, tentering, carry out bleaching and antimicrobial treatment, finally carry out finishing process；Wherein finishing process includes brightening, soft, wrinkle resistant process.
It is that pure cotton fiber is made that described Z twists with the fingers cotton yarn, and in described cloth or goods, Z twists with the fingers the mass percent of cotton yarn is 96%-98%, and namely in the overall composition of cloth or goods, cotton fiber accounts for 96%-98%wt.
It is 70-85 stringer/5cm that described Z twists with the fingers the horizontal density of cotton yarn 1 or S sth. made by twisting spandex 2, and vertical density is 50-65 line/5cm.
Described cloth or goods are carried out antimicrobial treatment, cloth or goods is sent in the tank body closed, double-face spray painting nano antibacterial coating, powder or aerosol；This nano antibacterial coating, powder or aerosol can have antibacterial, the metal oxide materials of bacteria resistance function, macromolecular material or photocatalyst material etc. for commercially available, it is possible to process with reference to prior art.
It is 600 twists/m that described Z twists with the fingers the twist of cotton yarn.
The horizontal density of described yarn is 73 stringers/5cm, and vertical density is 53 lines/5cm.
Referring to Fig. 2, the Weaving method of the high cotton content high elasticity abrasion-proof cloth of the present invention and goods, being particularly suited for the industry such as socks production, physical culture protection articles for use, obtained socks 3 cotton content may be up to 97%-98%, comfortable and easy to wear, endurable and antibacterial；Twisting with the fingers cotton yarn 1 by Z to twist with the fingers spandex 2 with S and carry out the processing of Z twisted stock, namely spin processing, prepared strand is used for socks 3 of weaving, and the flatness of socks 3 is good, good springiness and wear-resisting.
The goods of a kind of Weaving method implementing above-mentioned high cotton content high elasticity abrasion-proof cloth, it adopts described Z to twist with the fingers cotton yarn 1 and twists with the fingers the strand formed after spandex 2 carries out the processing of Z twisted stock as material with S, the weaving of this strand form cloth or goods；Wherein said Z twists with the fingers cotton yarn 1 and makes for pure cotton fiber, and as the wrap yarn of textile cloth, described S twists with the fingers spandex 2 as yarn in textile cloth；In described cloth, Z twists with the fingers the mass percent of cotton yarn 1 is 96%-98%.
Described Z twists with the fingers cotton yarn 1 and props up the cotton yarn of specification for 32-40；It is 70-85 stringer/5cm that described Z twists with the fingers the horizontal density of cotton yarn 1 or S sth. made by twisting spandex 2, and vertical density is 50-65 line/5cm.
Described goods, it is possible to be cloth, or socks, physical culture sheath, knee cap, wrister or other concrete textiles.
Described goods are bleached and antimicrobial treatment；Described bleaching process processes to be checked for grey cloth, turns over cloth and prints, and margin to seam is singed, desizing, kiering, oxygen bleaching, pickling, washing, and open rolling is dried, mercerising, and multiple drift is dried, calendering, tentering, Final finishing, and wherein finishing process includes brightening, soft, wrinkle resistant process.
The present invention is not limited to above-mentioned embodiment, adopts or approximation method identical with the above embodiment of the present invention, and other obtaining are for the Weaving method of high cotton content high elasticity abrasion-proof cloth and goods, all within protection scope of the present invention.
Claims (4)
1. the Weaving method of one kind high cotton content high elasticity abrasion-proof cloth, it is characterised in that it comprises the following steps:
(1), preparing Z sth. made by twisting cotton yarn, this Z twists with the fingers the cotton yarn wrap yarn as textile cloth；It is that pure cotton fiber is made that described Z twists with the fingers cotton yarn, and in the goods of described cloth or its formation, Z twists with the fingers the mass percent shared by cotton yarn is 96%-98%；First cotton fiber is carried out softening pretreatment, then Z twists with the fingers cotton yarn, and to be woven into specification be the 32-40 cotton yarn propped up, as the wrap yarn of textile cloth；
(2), preparing S sth. made by twisting spandex, this S twists with the fingers spandex as yarn in textile cloth；It is 600 twists/m that described Z twists with the fingers the twist of cotton yarn；
(3), by Z twisting with the fingers cotton yarn and carry out the processing of Z twisted stock with S sth. made by twisting spandex, form strand, this strand is as the raw material of textile cloth；It is 70-85 stringer/5cm that described Z twists with the fingers the horizontal density of cotton yarn or S sth. made by twisting spandex, and vertical density is 50-65 line/5cm；
(4) being weaved by above-mentioned strand Weaving method routinely, inner yarn is coated on the network internal that its yarn is made into by described wrap yarn, forms cloth or goods；Described step (4) specifically also includes herein below:
Described cloth is carried out following PROCESS FOR TREATMENT: grey cloth is checked, turn over cloth and print, margin to seam, to singe, desizing, kiering, oxygen bleaching, pickling, washing, open rolling is dried, mercerising, multiple drift, dries, calendering, tentering, carries out bleaching and antimicrobial treatment, finally carry out finishing process；Wherein finishing process includes brightening, soft, wrinkle resistant process.
2. the Weaving method of high cotton content high elasticity abrasion-proof cloth according to claim 1, it is characterised in that described cloth or goods are carried out antimicrobial treatment, sends into cloth in the tank body closed, double-face spray painting nano antibacterial coating, powder or aerosol.
3. the Weaving method of high cotton content high elasticity abrasion-proof cloth according to claim 1, it is characterised in that described Z twists with the fingers cotton yarn or the S sth. made by twisting horizontal density of spandex is 73 stringers/5cm, and vertical density is 53 lines/5cm.
4. the goods of the Weaving method implementing the described high cotton content high elasticity abrasion-proof cloth of one of claim 1-2, it is characterized in that, it adopts described Z to twist with the fingers cotton yarn and twists with the fingers the strand formed after spandex carries out the processing of Z twisted stock as material with S, the weaving of this strand form goods；Wherein said Z twists with the fingers the cotton yarn wrap yarn as textile fabrics, and it is made for pure cotton fiber, and described S twists with the fingers spandex as yarn in textile fabrics；Inner yarn is coated on the network internal that its yarn is made into by described wrap yarn；In described goods, Z twists with the fingers the mass percent of cotton yarn is 96%-98%；It is the 32-40 cotton yarn propping up specification that described Z twists with the fingers cotton yarn；It is 70-85 stringer/5cm that described Z twists with the fingers the horizontal density of cotton yarn or S sth. made by twisting spandex, and vertical density is 50-65 line/5cm.