CN106968043A - Spinning method of high-cotton-content high-elasticity wear-resistant cloth - Google Patents
Spinning method of high-cotton-content high-elasticity wear-resistant cloth Download PDFInfo
- Publication number
- CN106968043A CN106968043A CN201710383857.XA CN201710383857A CN106968043A CN 106968043 A CN106968043 A CN 106968043A CN 201710383857 A CN201710383857 A CN 201710383857A CN 106968043 A CN106968043 A CN 106968043A
- Authority
- CN
- China
- Prior art keywords
- cotton
- proof cloth
- twist
- polyester
- elasticity abrasion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a spinning method of high-cotton-content high-elasticity wear-resistant cloth, which comprises the following steps: respectively immersing cotton yarn and novel polyester PPT fiber monofilament into the slurry, taking out and drying; stranding to obtain a cotton thread A, and stranding the novel polyester PPT fiber monofilament to obtain a polyester thread B; plying the cotton thread A and the polyester thread B to obtain warp threads and weft threads; separating the outgoing thread up and down and forming a shed, and introducing the weft thread into the shed; interweaving the warps and the wefts by using a textile machine to form cloth, and rolling after the cloth is inspected to be qualified. The textile method of the high-cotton-content high-elasticity wear-resistant cloth material provided by the invention has the advantages of simple textile process, high textile efficiency, improvement on wrinkle resistance and wear resistance of the cloth material and reduction of production cost.
Description
Technical field
The present invention relates to cloth textile technology technical field, more particularly to a kind of spinning of high cotton content high elasticity abrasion-proof cloth
Organization method.
Background technology
Purified cotton cloth refers to the fabric produced using cotton as raw material, and hygroscopicity, the heat resistance of pure-cotton fabric are fabulous, and
And it is comfortable and easy to wear, will not occur electrostatic, gas permeability is outstanding, prevent sensitive, easy clean.Purified cotton cloth is widely used in the life of people
Among living, the work clothes of the more especially industry higher to clothes moisture absorption requirement may be selected by pure-cotton fabric and be added
Work.But pure-cotton fabric it is flexible it is poor, easily shrink, the shortcomings of easily go mouldy, based on above mentioned problem, the present invention proposes a kind of height
The Weaving method of cotton content high elasticity abrasion-proof cloth.
The content of the invention
The invention aims to solve shortcoming present in prior art, and a kind of high cotton content high resiliency proposed
The Weaving method of wear-resistant fabric.
A kind of Weaving method of high cotton content high elasticity abrasion-proof cloth, comprises the following steps:
Cotton yarn and new polyester PPT fibre single threads after S1, selection combing, cotton yarn and new polyester PPT fibre single threads are distinguished
Immerse after 4~8min of slurries added with nanometer silver-based inorganic antibacterial agent, take out pressure and go extraction raffinate, 30 are dried at 50~70 DEG C of high temperature
~50min;
S2, by the cotton yarn of 10~15 using the twist as 300~500, twist direction is pooled capital for Z twisted mode, cotton thread A is obtained, by 1
The new polyester PPT fibre single threads of~4, using the twist as 400~600, twist direction is pooled capital for Z twisted mode, obtains polyester
Line B;
S3, by 3~6 cotton thread A and 1 polyester line B using the twist as 350~500, twist direction is pooled capital for S twisted mode, is obtained
Warp, by 5~10 cotton thread A and 1~2 polyester line B using the twist as 350~500, twist direction is pooled capital for S twisted mode,
Obtain parallel;
S4, the warp close wind of gained in step S3 drawn in warp beam, then from warp beam, separate up and down and form shuttle
Mouthful, the parallel of gained in step S3 is introduced into shed open;
S5 is risen and fallen latitude and longitude using weaving loom in length and breadth to be interweaved, and forms high cotton content high elasticity abrasion-proof cloth, passed examination
Produce in rolls afterwards.
It is preferred that, the consumption of the nanometer silver-based inorganic antibacterial agent in the step S1 is the 2%~5% of slurries amount.
It is preferred that, the breadth of the high cotton content high elasticity abrasion-proof cloth in the step S5 is 2~5m, thickness is 0.3~
3mm。
It is preferred that, the cotton content of the high cotton content high elasticity abrasion-proof cloth in the step S5 is 98%~99%.
It is preferred that, the bar number of the warp of the high cotton content high elasticity abrasion-proof cloth in the step S5 for per inch 220~
250.
It is preferred that, the bar number of the parallel of the high cotton content high elasticity abrasion-proof cloth in the step S5 is per inch 25~40
Bar.
A kind of Weaving method of high cotton content high elasticity abrasion-proof cloth proposed by the present invention, textile technology is simple, weaving effect
Rate is high, and by plus nano silver-based inorganic antibacterial agent during soaking and dyeing, its spectrum antimicrobial properties and excellent antibacterial ability are greatly carried
The high antibacterial and mouldproof of cloth, cloth cotton content is up to 98%~99%, it is ensured that the sweat-absorbing breathable and pliability of cloth, with
New polyester ptt fiber replaces spandex fibre conventional on the market, while ensureing that cloth is elastic, effectively raises cloth
Wrinkle resistance and wearability, reduce production cost, the high cotton content high elasticity abrasion-proof cloth that the present invention weaves, with good
Moisture absorption, moisture retention, heat-resisting, alkali resistance, good permeability, soft comfortable are specious, and antibacterial, abrasion resistant effect are good, can extensive use
In manufacture clothing articles, bedding, it is worthy to be popularized.
Embodiment
The present invention is made with reference to specific embodiment further to explain.
Embodiment one
A kind of Weaving method of high cotton content high elasticity abrasion-proof cloth proposed by the present invention, comprises the following steps:
Cotton yarn and new polyester PPT fibre single threads after S1, selection combing, cotton yarn and new polyester PPT fibre single threads are distinguished
Immerse after the slurries 5min added with consumption for 4% nanometer silver-based inorganic antibacterial agent of slurries amount, take out pressure and go extraction raffinate, in high temperature
40min is dried at 60 DEG C;
S2, by the cotton yarn of 12 using the twist as 400, twist direction is pooled capital for Z twisted mode, obtains cotton thread A, new by 3
Polyester PPT fibre single threads, using the twist as 500, twist direction is pooled capital for Z twisted mode, obtains polyester line B;
S3, by 5 cotton thread A and 1 polyester line B using the twist as 400, twist direction is pooled capital for S twisted mode, warp is obtained, by 7
Root cotton thread A and 1 polyester line B are using the twist as 400, and twist direction is pooled capital for S twisted mode, obtains parallel;
S4, the warp close wind of gained in step S3 drawn in warp beam, then from warp beam, separate up and down and form shuttle
Mouthful, the parallel of gained in step S3 is introduced into shed open;
S5 is risen and fallen latitude and longitude using weaving loom in length and breadth to be interweaved, and forms breadth for 3m, and thickness is the high cotton content high resiliency of 2mm
Produced in rolls after wear-resistant fabric, passed examination, wherein the bar number of the warp of the high cotton content high elasticity abrasion-proof cloth of gained is per English
Very little 230, the bar number of parallel is per inch 28.
Embodiment two
A kind of Weaving method of high cotton content high elasticity abrasion-proof cloth proposed by the present invention, comprises the following steps:
Cotton yarn and new polyester PPT fibre single threads after S1, selection combing, cotton yarn and new polyester PPT fibre single threads are distinguished
Immerse after the slurries 8min added with consumption for 2% nanometer silver-based inorganic antibacterial agent of slurries amount, take out pressure and go extraction raffinate, in high temperature
45min is dried at 55 DEG C;
S2, by the cotton yarn of 10 using the twist as 350, twist direction is pooled capital for Z twisted mode, obtains cotton thread A, new by 1
Polyester PPT fibre single threads, using the twist as 450, twist direction is pooled capital for Z twisted mode, obtains polyester line B;
S3, by 3 cotton thread A and 1 polyester line B using the twist as 350, twist direction is pooled capital for S twisted mode, warp is obtained, by 5
Root cotton thread A and 1 polyester line B are using the twist as 350, and twist direction is pooled capital for S twisted mode, obtains parallel;
S4, the warp close wind of gained in step S3 drawn in warp beam, then from warp beam, separate up and down and form shuttle
Mouthful, the parallel of gained in step S3 is introduced into shed open;
S5 is risen and fallen latitude and longitude using weaving loom in length and breadth to be interweaved, and forms breadth for 3.5m, and thickness is that the high cotton contents of 0.3mm are high
Produced in rolls after elastic wear-resisting cloth, passed examination, wherein the bar number of the warp of the high cotton content high elasticity abrasion-proof cloth of gained is
Per inch 240, the bar number of parallel is per inch 40.
Embodiment three
A kind of Weaving method of high cotton content high elasticity abrasion-proof cloth proposed by the present invention, comprises the following steps:
Cotton yarn and new polyester PPT fibre single threads after S1, selection combing, cotton yarn and new polyester PPT fibre single threads are distinguished
Immerse after the slurries 4min added with consumption for 5% nanometer silver-based inorganic antibacterial agent of slurries amount, take out pressure and go extraction raffinate, in high temperature
30min is dried at 70 DEG C;
S2, by the cotton yarn of 14 using the twist as 320, twist direction is pooled capital for Z twisted mode, obtains cotton thread A, new by 3
Polyester PPT fibre single threads, using the twist as 600, twist direction is pooled capital for Z twisted mode, obtains polyester line B;
S3, by 5 cotton thread A and 1 polyester line B using the twist as 500, twist direction is pooled capital for S twisted mode, warp is obtained, by 8
Root cotton thread A and 2 polyester line B are using the twist as 500, and twist direction is pooled capital for S twisted mode, obtains parallel;
S4, the warp close wind of gained in step S3 drawn in warp beam, then from warp beam, separate up and down and form shuttle
Mouthful, the parallel of gained in step S3 is introduced into shed open;
S5 is risen and fallen latitude and longitude using weaving loom in length and breadth to be interweaved, and forms breadth for 4m, and thickness is the high cotton content high resiliency of 1mm
Produced in rolls after wear-resistant fabric, passed examination, wherein the bar number of the warp of the high cotton content high elasticity abrasion-proof cloth of gained is per English
Very little 220, the bar number of parallel is per inch 25.
Example IV
A kind of Weaving method of high cotton content high elasticity abrasion-proof cloth proposed by the present invention, comprises the following steps:
Cotton yarn and new polyester PPT fibre single threads after S1, selection combing, cotton yarn and new polyester PPT fibre single threads are distinguished
Immerse after the slurries 6min added with consumption for 3% nanometer silver-based inorganic antibacterial agent of slurries amount, take out pressure and go extraction raffinate, in high temperature
50min is dried at 50 DEG C;
S2, by the cotton yarn of 11 using the twist as 300, twist direction is pooled capital for Z twisted mode, obtains cotton thread A, new by 2
Polyester PPT fibre single threads, using the twist as 550, twist direction is pooled capital for Z twisted mode, obtains polyester line B;
S3, by 4 cotton thread A and 1 polyester line B using the twist as 450, twist direction is pooled capital for S twisted mode, warp is obtained, by 6
Root cotton thread A and 1 polyester line B are using the twist as 450, and twist direction is pooled capital for S twisted mode, obtains parallel;
S4, the warp close wind of gained in step S3 drawn in warp beam, then from warp beam, separate up and down and form shuttle
Mouthful, the parallel of gained in step S3 is introduced into shed open;
S5 is risen and fallen latitude and longitude using weaving loom in length and breadth to be interweaved, and forms breadth for 2m, and thickness is the high cotton content high resiliency of 3mm
Produced in rolls after wear-resistant fabric, passed examination, wherein the bar number of the warp of the high cotton content high elasticity abrasion-proof cloth of gained is per English
Very little 250, the bar number of parallel is per inch 30.
Embodiment five
A kind of Weaving method of high cotton content high elasticity abrasion-proof cloth proposed by the present invention, comprises the following steps:
Cotton yarn and new polyester PPT fibre single threads after S1, selection combing, cotton yarn and new polyester PPT fibre single threads are distinguished
Immerse after the slurries 7min added with consumption for 4% nanometer silver-based inorganic antibacterial agent of slurries amount, take out pressure and go extraction raffinate, in high temperature
35min is dried at 65 DEG C;
S2, by the cotton yarn of 15 using the twist as 380, twist direction is pooled capital for Z twisted mode, obtains cotton thread A, new by 4
Polyester PPT fibre single threads, using the twist as 400, twist direction is pooled capital for Z twisted mode, obtains polyester line B;
S3, by 6 cotton thread A and 1 polyester line B using the twist as 420, twist direction is pooled capital for S twisted mode, obtains warp, will
10 cotton thread A and 2 polyester line B are using the twist as 420, and twist direction is pooled capital for S twisted mode, obtains parallel;
S4, the warp close wind of gained in step S3 drawn in warp beam, then from warp beam, separate up and down and form shuttle
Mouthful, the parallel of gained in step S3 is introduced into shed open;
S5 is risen and fallen latitude and longitude using weaving loom in length and breadth to be interweaved, and forms breadth for 5m, and thickness is that the high cotton contents of 2.2mm are high-elastic
Property wear-resistant fabric, produce in rolls after passed examination, wherein the bar number of the warp of the high cotton content high elasticity abrasion-proof cloth of gained is every
In2 35, the bar number of parallel is per inch 35.
The high cotton content high elasticity abrasion-proof cloth prepared in above-mentioned five groups of embodiments is subjected to wearability comparison, polyester is fine
The wearability of dimension preferably, and in the case of material identical, organizes close, thickness is more big more wear-resisting, it can thus be appreciated that:Implement
The wearability for the high cotton content high elasticity abrasion-proof cloth prepared in example five is optimal, and the high cotton content prepared in embodiment two
The wearability of high elasticity abrasion-proof cloth is worst.A kind of Weaving method of high cotton content high elasticity abrasion-proof cloth proposed by the present invention,
Textile technology is simple, weaving efficiency high, by plus nano silver-based inorganic antibacterial agent during soaking and dyeing, its spectrum antimicrobial properties and excellent
Antibacterial ability, greatly improve the antibacterial and mouldproof of cloth, cloth cotton content is up to 98%~99%, it is ensured that the suction of cloth
Sweat gas permeability and pliability, spandex fibre conventional on the market is replaced with new polyester ptt fiber, is ensureing the same of cloth elasticity
When, the wrinkle resistance and wearability of cloth are effectively raised, production cost, the high cotton content high resiliency that the present invention weaves is reduced
Wear-resistant fabric, with good moisture absorption, moisture retention, heat-resisting, alkali resistance, good permeability, soft comfortable is specious, antibacterial, resistance to
Grind effect good, can be widely applied to manufacture clothing articles, bedding, be worthy to be popularized.
The foregoing is only a preferred embodiment of the present invention, but protection scope of the present invention be not limited thereto,
Any one skilled in the art the invention discloses technical scope in, technique according to the invention scheme and its
Inventive concept is subject to equivalent substitution or change, should all be included within the scope of the present invention.
Claims (6)
1. a kind of Weaving method of high cotton content high elasticity abrasion-proof cloth, it is characterised in that comprise the following steps:
Cotton yarn and new polyester PPT fibre single threads after S1, selection combing, cotton yarn and new polyester PPT fibre single threads are distinguished
Immerse after 4~8min of slurries added with nanometer silver-based inorganic antibacterial agent, take out pressure and go extraction raffinate, 30 are dried at 50~70 DEG C of high temperature
~50min;
S2, by the cotton yarn of 10~15 using the twist as 300~500, twist direction is pooled capital for Z twisted mode, cotton thread A is obtained, by 1
The new polyester PPT fibre single threads of~4, using the twist as 400~600, twist direction is pooled capital for Z twisted mode, obtains polyester
Line B;
S3, by 3~6 cotton thread A and 1 polyester line B using the twist as 350~500, twist direction is pooled capital for S twisted mode, is obtained
Warp, by 5~10 cotton thread A and 1~2 polyester line B using the twist as 350~500, twist direction is pooled capital for S twisted mode,
Obtain parallel;
S4, the warp close wind of gained in step S3 drawn in warp beam, then from warp beam, separate up and down and form shuttle
Mouthful, the parallel of gained in step S3 is introduced into shed open;
S5 is risen and fallen latitude and longitude using weaving loom in length and breadth to be interweaved, and forms high cotton content high elasticity abrasion-proof cloth, passed examination
Produce in rolls afterwards.
2. the Weaving method of a kind of high cotton content high elasticity abrasion-proof cloth according to claim 1, it is characterised in that described
The consumption of nanometer silver-based inorganic antibacterial agent in step S1 is the 2%~5% of slurries amount.
3. the Weaving method of a kind of high cotton content high elasticity abrasion-proof cloth according to claim 1, it is characterised in that described
The breadth of high cotton content high elasticity abrasion-proof cloth in step S5 is 2~5m, and thickness is 0.3~3mm.
4. the Weaving method of a kind of high cotton content high elasticity abrasion-proof cloth according to claim 1, it is characterised in that described
The cotton content of high cotton content high elasticity abrasion-proof cloth in step S5 is 98%~99%.
5. the Weaving method of a kind of high cotton content high elasticity abrasion-proof cloth according to claim 1, it is characterised in that described
The bar number of the warp of high cotton content high elasticity abrasion-proof cloth in step S5 is per inch 220~250.
6. the Weaving method of a kind of high cotton content high elasticity abrasion-proof cloth according to claim 1, it is characterised in that described
The bar number of the parallel of high cotton content high elasticity abrasion-proof cloth in step S5 is per inch 25~40.