CN103181710A - Production technology for modified polyester fiber embossing carpet - Google Patents
Production technology for modified polyester fiber embossing carpet Download PDFInfo
- Publication number
- CN103181710A CN103181710A CN2012105910911A CN201210591091A CN103181710A CN 103181710 A CN103181710 A CN 103181710A CN 2012105910911 A CN2012105910911 A CN 2012105910911A CN 201210591091 A CN201210591091 A CN 201210591091A CN 103181710 A CN103181710 A CN 103181710A
- Authority
- CN
- China
- Prior art keywords
- polyester fiber
- carpet
- modified polyester
- fixation
- gluing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a production technology for a modified polyester fiber embossing carpet, which comprises the following technological process: tufting the modified polyester fiber (terylene) into the blank carpet with the breadth of 4.1 m, then gluing, wherein the viscosity of the glue is 200 CPS, printing after gluing, enabling the blank carpet to enter a drying oven for fixation after printing, wherein the temperature of the drying oven is controlled within 90-99 DEG C, and the fixation time is 5-8 min, washing to remove the flotation pulp after fixation of the blank carpet, then enabling the blank carpet to enter the drying oven again for drying with the controlled temperature of the drying oven of 110-125 DEG C, and finally, inspecting and packaging to obtain the finished product. Compared with the prior art, the modified polyester fiber embossing carpet has the advantages of ageing resistance, crease resistance, no lint, no water absorption, softness and comfort, stain resistance and easiness in cleaning, fire resistance and flame retardancy and the like. The technology is environment-friendly and low in production cost, has no pollution, and has a broad market prospect.
Description
Technical field
The present invention relates to a kind of carpet, particularly relate to a kind of production technology of modified polyester fiber digit printing carpet.
Background technology
Carpet is through pavement artificial or that mechanism forms with materials such as hair, cotton, fiber crops or chemical synthetic fibers.It is to have one of traditional industrial art category of long history in the world wide.Be covered in the ground of dwelling house, hotel, gymnasium, exhibition center, vehicle, boats and ships, aircraft etc., the noise of minimizing, heat insulation and decorative effect are arranged.
The production process of digit printing briefly is exactly by various digitlization means: import computers as the various digitlization patterns that scanning photograph, image or computing mechanism deal with, again by computer pattern software handle, drugget process software by special use after the color separation carries out the pattern layout, dyeing is handled etc.By sprayed printed system with the direct spray printing of various dedicated dyes on various fabrics or other media, through obtaining needed various high-precision stamp products at various weaving face fabrics after the processing.
Polyester carpet is to form by spun polyester thread is woven, spun polyester thread is an important kind in the synthetic fibers, be the trade name of China's polyester fiber, it is a resin terephthalic acid (TPA) or terephthalic acid (TPA) and methyl esters and the ethylene glycol fiber-forming polymer that to be raw material make through esterification or ester exchange and polycondensation reaction---PETG, the fiber of making through imitative silk and post processing.Modified polyester fiber is to make a kind of new technology that yarn is used for the carpet printing be spun into BCF bulk filament or short fiber through fusion method, can reduce old, and increase noise reduction, anti-soil easy cleaning, the carpet printing technique of multinomial function such as fire protection flame retarding.
The stamp product just is widely current in many countries before the thirties, and most of material adopts wool.Nylon, acrylic fibers, linen-cotton etc.Stamp product major part is velvet carpet at present.Terylene stamp product on the market is through steam HTHP printing technology mostly, guarantees that its product colour is bright-coloured, stable.The terylene vapour steaming colour fixing time is long, and color fixing condition needs the high temperature decatize, and the most of HTHP that adopts of terylene stamp is finished, and presses the carpet form, carpet can be divided into full shop blanket, piece blanket and piece blanket.And prior art is mainly carried out the HTHP fixation by big vexed jar to carpet, control product single step of releasing blanket quantity according to vexed jar of size, therefore can not produce the piece blanket continuously, more can not produce full shop and talk, in addition, the length of product and width all are subjected to big vexed jar restriction.
Summary of the invention
Purpose of the present invention is exactly for solving defective and the deficiency that above-mentioned prior art exists, and provides the easy fixation of a kind of product and color rich and varied, and length and width are unrestricted, the modified polyester fiber digit printing carpet manufacture technology of production technology environmental protection.
The technical scheme that adopts is:
A kind of production technology of modified polyester fiber drugget is characterized in that comprising technical process:
Earlier modified polyester fiber (terylene) tufting is become 2-4.1 rice fabric width base blanket, gluing then, the viscosity of glue is 12000CPS, print behind the gluing, enter the baking oven fixation after printing finishes, oven temperature is controlled at the 90-99 degree, and the fixation time is 5-8min, the base blanket washes the floating oar of flush away with water after fixation, and then entering oven for drying, oven temperature is controlled at the 110-125 degree, and is last, through check, packing, make finished product.
In the above-mentioned technology base blanket is carried out carrying out after gluing also can be put into the fixation oven dry.
That the present invention compared with prior art has is anti-aging, crease-resistant, phozy, soft comfortable, anti-soil easy cleaning, special advantage such as fire protection flame retarding, technology environmental protection of the present invention, pollution-free, produce old low, market prospects are wide.
The specific embodiment
Implementation column one
A kind of production technology of modified polyester fiber drugget specifically comprises technical process:
Earlier modified polyester fiber (terylene) tufting is become 2-4.1 rice fabric width base blanket, gluing then, the viscosity of glue is 12000CPS, with cation the disperse dyes tinting paste become pasty state viscosity 200CPS, be transported to the China ink bottle with membrane pump, China ink bottle pressure 2-2.5kg begins to print, enter the baking oven fixation after printing finishes, oven temperature control is at 95 degree, and the fixation time is 6min, the base blanket washes the floating oar of flush away with water after fixation, and then entering oven for drying, oven temperature control is at 120 degree, and is last, through check, packing, make finished product.
Implementation column two
Earlier modified polyester fiber (terylene) tufting is become 2-4.1 rice fabric width base blanket, then with cation the disperse dyes tinting paste become pasty state viscosity 200CPS, be transported to the China ink bottle with membrane pump, China ink bottle pressure 2-2.5kg begins to print, after finishing, printing enters the baking oven fixation, oven temperature control is at 98 degree, the fixation time is 5min, and the base blanket washes the floating oar of flush away with water after fixation, enter oven for drying again, oven temperature control is at 120 degree, then the base blanket after the oven dry is carried out gluing, the viscosity of glue is 200CPS, and is last, through check, packing, make finished product.
Claims (2)
1. modified polyester fiber drugget is characterized in that comprising following technical process:
Earlier modified polyester fiber (terylene) tufting is become 4.1 base blankets, gluing then, the viscosity of glue is 12000CPS, behind the gluing with cation the disperse dyes tinting paste become pasty state viscosity 200CPS, be transported to the China ink bottle with membrane pump, China ink bottle pressure 2-2.5kg begins to print, enter the baking oven fixation after printing finishes, oven temperature is controlled at the 90-99 degree, and the fixation time is 5-8min, the base blanket washes the floating oar of flush away with water after fixation, and then entering oven for drying, oven temperature is controlled at the 110-125 degree, and is last, through check, packing, make finished product.
2. according to the production technology of claims 1 described a kind of modified polyester fiber drugget, it is characterized in that in the described technical process base blanket being carried out carrying out after gluing is put into the fixation oven dry.