CN103122100A - 一种环保型阻燃板及其加工方法 - Google Patents
一种环保型阻燃板及其加工方法 Download PDFInfo
- Publication number
- CN103122100A CN103122100A CN2012104928778A CN201210492877A CN103122100A CN 103122100 A CN103122100 A CN 103122100A CN 2012104928778 A CN2012104928778 A CN 2012104928778A CN 201210492877 A CN201210492877 A CN 201210492877A CN 103122100 A CN103122100 A CN 103122100A
- Authority
- CN
- China
- Prior art keywords
- fire retardant
- environmental
- retardant
- protection flame
- polypropylene
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种环保型阻燃板及其加工方法,该阻燃板以聚丙烯为基材,加入阻燃剂混合搅拌加工而成,根据阻燃剂的配比量不同,其阻燃等级可达到UL94 V0-V1,且本发明具有比重轻、柔性强、机械性能好、色性好、焊接性能好、阻燃性能好的特点。
Description
技术领域
本发明涉及一种阻燃板及其加工方法,特别涉及一种环保型阻燃板及其加工方法,属于阻燃材料的技术领域。
背景技术
以前所有的阻燃板一般都是采用碳酸钙类阻燃,此类板材最大的特性是:A、比重重;B、易老化;C、焊接不牢固;D、脆性强、易断裂;E、不环保,有粉尘污染。
发明内容
本发明所要解决的技术问题是提供一种比重轻、柔性强、机械性能好、色性好、焊接性能好、阻燃性能好的环保型阻燃板,并提供了该阻燃板的加工方法,该加工方法操作方便。
本发明的技术问题所采用的技术方案是:
一种环保型阻燃板,由于以下成分组成,按重量百分比计:
聚丙烯 80%—95%;
阻燃剂 5%—20%。
上述的环保型阻燃板,其中,优选组份为聚丙烯重量百分比为92%,.阻燃剂重量百分比为8%。
上述一种环保型阻燃板的加工方法,其生产流程如下:
1.以聚丙烯为基材(均聚或共聚级原料),加入阻燃剂混合;
2.对混合好的原材料进行搅拌,
3.对搅拌均匀的材料除湿烘干;
4.材料烘干后进行挤塑和三辊压光最终切割成型。
上述一种环保型阻燃板的加工方法,其中,挤塑温度为165—240℃。
上述一种环保型阻燃板的加工方法,其中,搅拌时,转速为每分钟50—100转,时间30—45分钟。
上述一种环保型阻燃板的加工方法,其中,除湿烘干时间为1.5h—2h,温度为65—80℃。
本发明的有益效果为:
1.比重轻。与原材料聚丙烯的比重非常接近,几乎无变化。
2.柔性强。与原材料聚丙烯的柔软性基本一致。
3.机械性能好。因与原材料聚丙烯相溶性能好,各方面性能几乎与纯原料保持一致,特别是其耐腐性能一点都没有变化。
4.色性好。本产品可配置成各种颜色的板材。
5.焊接性能好。因阻燃剂内无滑石粉(碳酸钙),无磷、无溴、低卤,所以在焊接过程中任意焊接且不脆化,其中挥发物≤0.3%
6.阻燃性能好。阻燃等级可达到UL94 V0-V1
7.环保。本产品完全符合新欧盟环保标准(ROHS),不含多溴联苯(PBB)和多溴二苯醚(PBDE),并且无毒,容易分解。
具体实施方式
实例一:
一种环保型阻燃板,由聚丙烯重量百分比为92%和阻燃剂重量百分比为8%组成,阻燃剂由深圳市嘉盛威化工科技有限公司提供,型号为MPC-01,加工时:
1、以重量百分比为92%的聚丙烯为基材(均聚或共聚级原料),加入重量百分比为8%的阻燃剂混合;
2.对混合好的原材料进行搅拌,转速每分钟100转,时间45分钟;
3.对搅拌均匀的材料除湿烘干2h,温度80℃;
4.材料烘干后进行挤塑和三辊压光最终切割成型,挤塑温度为195℃。
增加阻燃剂的聚丙烯材料在比重、拉伸强度、悬臂梁缺口冲击强度、断裂伸长率、弯曲强度、热变型温度等性能中与未增加阻燃剂的聚丙烯材料基本无差异,但是不同于未增加阻燃剂的聚丙烯材料的是增加阻燃剂的聚丙烯材料增加了阻燃性,阻燃等级可达到UL94 V0。
实例二:
一种环保型阻燃板,由于以下成分组成:
1.聚丙烯,重量百分比为95%;2.阻燃剂,重量百分比为5%。
一种环保型阻燃板,其生产流程如下:
1.以重量百分比为95%的聚丙烯为基材(均聚或共聚级原料),加入重量百分比为5%的阻燃剂混合;
2.对混合好的原材料进行搅拌,转速每分钟80转,时间45分钟;
3.对搅拌均匀的材料除湿烘干2h,温度80℃;
4.材料烘干后进行挤塑和三辊压光最终切割成型,挤塑温度为165℃。
增加阻燃剂的聚丙烯材料在比重、拉伸强度、悬臂梁缺口冲击强度、断裂伸长率、弯曲强度、热变型温度等性能中与未增加阻燃剂的聚丙烯材料基本无差异,但是不同于未增加阻燃剂的聚丙烯材料的是增加阻燃剂的聚丙烯材料增加了阻燃性,阻燃等级可达到UL94 V1。
实例三:
一种环保型阻燃板,由于以下成分组成:
1.聚丙烯,重量百分比为85%;2.阻燃剂,重量百分比为15%。
一种环保型阻燃板,其生产流程如下:
1.以重量百分比为85%的聚丙烯为基材(均聚或共聚级原料),加入重量百分比为15%的阻燃剂混合;
2.对混合好的原材料进行搅拌,转速每分钟80转,时间45分钟;
3.对搅拌均匀的材料除湿烘干2h,温度80℃;
4.材料烘干后进行挤塑和三辊压光最终切割成型,挤塑温度为240℃
增加阻燃剂的聚丙烯材料在比重、拉伸强度、悬臂梁缺口冲击强度、断裂伸长率、弯曲强度、热变型温度等性能中与未增加阻燃剂的聚丙烯材料基本无差异,但是不同于未增加阻燃剂的聚丙烯材料的是增加阻燃剂的聚丙烯材料增加了阻燃性,阻燃等级可达到UL94 V1。
综上所述,该环保型阻燃板阻燃剂在高温下与碳酸钙会起化学反应,成分无碳、无磷、无溴、低卤;燃烧时产生的烟雾浓度较低,不同于普通PP材料燃烧时产生的黑色浓烟,含烟量少,无毒性;离开火焰自动熄灭。
Claims (6)
1.一种环保型阻燃板,其特征在于,由以下成分组成,按重量百分比计:
聚丙烯 80%—95%;
阻燃剂 5%—20%。
2.如权利要求1所述的环保型阻燃板,其特征在于,优选组份为聚丙烯重量百分比为92%,.阻燃剂重量百分比为8%。
3.如权利要求1或2所述的环保型阻燃板的加工方法,其特征在于,生产流程如下:
A.以聚丙烯为基材(均聚或共聚级原料),加入阻燃剂混合;
B、对混合好的原材料进行搅拌,
C、对搅拌均匀的材料除湿烘干;
D、材料烘干后进行挤塑和三辊压光最终切割成型。
4.如权利要求3所述的环保型阻燃板的加工方法,其特征在于,挤塑温度为165—240℃。
5.如权利要求3所述的环保型阻燃板的加工方法,其特征在于,搅拌时,转速为每分钟50—100转,时间30—45分钟。
6.如权利要求3所述的环保型阻燃板的加工方法,其特征在于,除湿烘干时间为1.5h—2h,温度为65—80℃。