CN103103806B - 铜氨、麻和棉混纺面料的生产工艺 - Google Patents
铜氨、麻和棉混纺面料的生产工艺 Download PDFInfo
- Publication number
- CN103103806B CN103103806B CN201210446043.3A CN201210446043A CN103103806B CN 103103806 B CN103103806 B CN 103103806B CN 201210446043 A CN201210446043 A CN 201210446043A CN 103103806 B CN103103806 B CN 103103806B
- Authority
- CN
- China
- Prior art keywords
- copper ammonia
- fiber
- cuprammonium
- cotton
- concise
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明涉及一种铜氨、麻和棉混纺面料的生产工艺,其特征是,包括以下工艺步骤:(1)将铜氨纤维、麻纤维和棉纤维混纺得到铜氨混纺坯布,铜氨纤维、麻纤维和棉纤维的质量比为40~60:15~30:25~30;(2)水洗:将铜氨混纺坯布在水洗机中进行清洗;(3)精练:将水洗后的铜氨混纺坯布浸泡在精练液中,浴比为1:20~25,精练液的组份为:氢氧化钠30~35g/L、精练剂1~1.5g/L,其余为水;精练时间为0.5~1小时,精练温度为75~80℃;(4)染色;(5)漂洗、烘干,得到所述的铜氨、麻和棉混纺面料。本发明采用铜氨纤维、麻纤维和棉纤维混纺得到,不会破坏铜氨纤维的抗菌性能,同时具有较好的穿着舒适性。
Description
技术领域
本发明涉及一种面料,尤其是一种铜氨、麻和棉混纺面料的生产工艺,属于纺织服装技术领域。
背景技术
铜氨纤维是一种再生纤维素纤维,它是将棉短绒等天然纤维素原料溶解在氢氧化铜或碱性铜盐的浓氨溶液内,配成纺丝液,在凝固浴中铜氨纤维素分子化合物分解再生出纤维素,生成的水合纤维素经后加工即得到铜氨纤维。铜氨纤维的截面呈圆形,无皮芯结构,纤维可承受高度提伸,制得的单丝较细,所以面料手感柔软,光泽柔和,有真丝感。
由于铜氨纤维对含氯漂白剂、过氧化氢等氧化剂的抵抗能力差,所以铜氨纤维与其他纤维混纺的面料,在后续的前处理、染色及后整理过程中存在一定的难度。
发明内容
本发明的目的是克服现有技术中存在的不足,提供一种铜氨、麻和棉混纺面料的生产工艺,该铜氨混纺面料由铜氨纤维、麻纤维和棉纤维混纺得到,不会破坏铜氨纤维的抗菌性能,具有良好的服用性能。
按照本发明提供的技术方案,所述铜氨、麻和棉混纺面料的生产工艺,其特征是,包括以下工艺步骤:
(1)将铜氨纤维、麻纤维和棉纤维混纺得到铜氨混纺坯布,铜氨纤维、麻纤维和棉纤维的质量比为40~60:15~30:25~30;
(2)水洗:将铜氨混纺坯布在水洗机中进行清洗,浴比为1:30~50,并加入中性清洁剂,清洁剂的用量为每升水3~5g,水温为60~65℃,水洗时间为0.5~1小时;
(3)精练:将水洗后的铜氨混纺坯布浸泡在精练液中,浴比为1:20~25,精练液的组份为:氢氧化钠30~35g/L、精练剂1~1.5g/L,其余为水;精练时间为0.5~1小时,精练温度为75~80℃;
(4)染色:将精练后的铜氨混纺坯布放入染色机中,染液浴比为1:10~13,每升水加入1~2g柔软剂和1~3g匀染剂,升温至70~90℃,保温10~15分钟;再升温至110~120℃,保温10~15分钟;再升温至120~130℃,保温30~45分钟;降温到室温,排出染液;
(5)漂洗、烘干,得到所述的铜氨、麻和棉混纺面料。
步骤(4)中的升温速度为1~2℃/分钟。
本发明所述的铜氨、麻和棉混纺面料的生产工艺,采用铜氨纤维、麻纤维和棉纤维混纺得到,不会破坏铜氨纤维的抗菌性能,同时具有较好的穿着舒适性。
具体实施方式
下面结合具体实施例对本发明作进一步说明。
实施例一:一种铜氨、麻和棉混纺面料的生产工艺,包括以下工艺步骤:
(1)将铜氨纤维、麻纤维和棉纤维混纺得到铜氨混纺坯布,铜氨纤维、麻纤维和棉纤维的质量比为40:15:30;
(2)水洗:将铜氨混纺坯布在水洗机中进行清洗,浴比为1:30,并加入中性清洁剂,清洁剂的用量为每升水3g,水温为60℃,水洗时间为1小时;
(3)精练:将水洗后的铜氨混纺坯布浸泡在精练液中,浴比为1:20,精练液的组份为:氢氧化钠30g/L、精练剂1g/L,其余为水;精练时间为0.5小时,精练温度为80℃;
(4)染色:将精练后的铜氨混纺坯布放入染色机中,染液浴比为1:10,每升水加入1g柔软剂和1g匀染剂,升温至70℃,保温10分钟;再升温至110℃,保温15分钟;再升温至120℃,保温45分钟;降温到室温,排出染液;所述升温速度为1℃/分钟;
(5)漂洗、烘干,得到所述的铜氨、麻和棉混纺面料。
实施例二:一种铜氨、麻和棉混纺面料的生产工艺,包括以下工艺步骤:
(1)将铜氨纤维、麻纤维和棉纤维混纺得到铜氨混纺坯布,铜氨纤维、麻纤维和棉纤维的质量比为60:15:25;
(2)水洗:将铜氨混纺坯布在水洗机中进行清洗,浴比为1:50,并加入中性清洁剂,清洁剂的用量为每升水5g,水温为65℃,水洗时间为1小时;
(3)精练:将水洗后的铜氨混纺坯布浸泡在精练液中,浴比为1:25,精练液的组份为:氢氧化钠35g/L、精练剂1.5g/L,其余为水;精练时间为1小时,精练温度为80℃;
(4)染色:将精练后的铜氨混纺坯布放入染色机中,染液浴比为1:13,每升水加入2g柔软剂和3g匀染剂,升温至90℃,保温15分钟;再升温至120℃,保温15分钟;再升温至130℃,保温45分钟;降温到室温,排出染液;所述升温速度为2℃/分钟;
(5)漂洗、烘干,得到所述的铜氨、麻和棉混纺面料。
实施例三:一种铜氨、麻和棉混纺面料的生产工艺,包括以下工艺步骤:
(1)将铜氨纤维、麻纤维和棉纤维混纺得到铜氨混纺坯布,铜氨纤维、麻纤维和棉纤维的质量比为50:20: 30;
(2)水洗:将铜氨混纺坯布在水洗机中进行清洗,浴比为1:40,并加入中性清洁剂,清洁剂的用量为每升水4g,水温为62℃,水洗时间为0.6小时;
(3)精练:将水洗后的铜氨混纺坯布浸泡在精练液中,浴比为1:22,精练液的组份为:氢氧化钠32g/L、精练剂1.2g/L,其余为水;精练时间为0.6小时,精练温度为76℃;
(4)染色:将精练后的铜氨混纺坯布放入染色机中,染液浴比为1:12,每升水加入1.5g柔软剂和2g匀染剂,升温至80℃,保温12分钟;再升温至115℃,保温12分钟;再升温至125℃,保温35分钟;降温到室温,排出染液;所述升温速度为1.5℃/分钟;
(5)漂洗、烘干,得到所述的铜氨、麻和棉混纺面料。
本发明所述的铜氨、麻和棉混纺面料中的铜氨纤维接触到真菌、细菌及病毒时能立即发挥保护作用,而且它的抗菌作用不会因为生产工艺中的洗涤或染色等而消失。
Claims (2)
1.一种铜氨、麻和棉混纺面料的生产工艺,其特征是,包括以下工艺步骤:
(1)将铜氨纤维、麻纤维和棉纤维混纺得到铜氨混纺坯布,铜氨纤维、麻纤维和棉纤维的质量比为40~60:15~30:25~30;
(2)水洗:将铜氨混纺坯布在水洗机中进行清洗,浴比为1:30~50,并加入中性清洁剂,清洁剂的用量为每升水3~5g,水温为60~65℃,水洗时间为0.5~1小时;
(3)精练:将水洗后的铜氨混纺坯布浸泡在精练液中,浴比为1:20~25,精练液的组份为:氢氧化钠30~35g/L、精练剂1~1.5g/L,其余为水;精练时间为0.5~1小时,精练温度为75~80℃;
(4)染色:将精练后的铜氨混纺坯布放入染色机中,染液浴比为1:10~13,每升水加入1~2g柔软剂和1~3g匀染剂,升温至70~90℃,保温10~15分钟;再升温至110~120℃,保温10~15分钟;再升温至120~130℃,保温30~45分钟;降温到室温,排出染液;
(5)漂洗、烘干,得到所述的铜氨、麻和棉混纺面料。
2.如权利要求1所述的铜氨、麻和棉混纺面料的生产工艺,其特征是:步骤(4)中的升温速度为1~2℃/分钟。