CN103056183A - 一种厚壁无缝钢管短流程铸挤连续成形的方法 - Google Patents

一种厚壁无缝钢管短流程铸挤连续成形的方法 Download PDF

Info

Publication number
CN103056183A
CN103056183A CN2013100257374A CN201310025737A CN103056183A CN 103056183 A CN103056183 A CN 103056183A CN 2013100257374 A CN2013100257374 A CN 2013100257374A CN 201310025737 A CN201310025737 A CN 201310025737A CN 103056183 A CN103056183 A CN 103056183A
Authority
CN
China
Prior art keywords
steel tube
thick
steel
seamless steel
walled seamless
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013100257374A
Other languages
English (en)
Other versions
CN103056183B (zh
Inventor
李永堂
贾璐
付建华
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taiyuan University of Science and Technology
Original Assignee
Taiyuan University of Science and Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taiyuan University of Science and Technology filed Critical Taiyuan University of Science and Technology
Priority to CN201310025737.4A priority Critical patent/CN103056183B/zh
Publication of CN103056183A publication Critical patent/CN103056183A/zh
Application granted granted Critical
Publication of CN103056183B publication Critical patent/CN103056183B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种厚壁无缝钢管短流程铸挤连续成形的方法，它属于一种生产大口径厚壁无缝钢管短流程铸挤连续成形的方法。本发明主要是解决现有生产大口径厚壁无缝钢管的方法存在的对材料和能源浪费严重的技术问题。本发明的技术方案是：一种厚壁无缝钢管短流程铸挤连续成形的方法，其包括合金熔化-钢液精炼-冒口浇铸环坯-热挤压-热处理-精密整形步骤；所述钢液精炼是采用中频感应电炉精炼，冶炼温度为1650℃~1700℃；所述冒口浇铸环坯是将精炼钢水在1590℃~1610℃进行细颈冒口浇注，浇注结束后在1280℃~1330℃出模；所述热挤压是将铸造空心环坯放在钢管挤压机上，利用铸坯余热在初始挤压温度1200℃~1250℃下直接进行挤压成形，挤压比为10~12。

Description

一种厚壁无缝钢管短流程铸挤连续成形的方法
技术领域
本发明涉及一种厚壁无缝钢管短流程铸挤连续成形的方法，它属于一种生产碳素钢、合金钢及不锈钢大口径厚壁无缝钢管短流程铸挤连续成形的方法。
背景技术
随着我国在核电、风电、石油、航空航天、军工、高铁等行业的迅猛发展，对建设用大口径厚壁无缝钢管、巨型铸管模及大型复杂件的要求越来越广泛。传统的无缝钢管生产工艺流程为：合金熔化→钢液精炼→浇注钢锭→镦粗→冲孔→加热→热挤压→热处理→精密整形，这种方法不仅冗长而且对材料和能源的浪费也比较严重，多次加热造成环件氧化皮增多也影响成形件的质量，不利于工业减排、低碳目标的实施。
发明内容
本发明的目的是解决现有生产大口径厚壁无缝钢管的方法存在的对材料和能源浪费严重的技术问题，提供一种厚壁无缝钢管短流程铸挤连续成形的方法，可有效地节省材料、能源和提高生产效率。
本发明为解决上述技术问题而采用的技术方案是：
一种厚壁无缝钢管短流程铸挤连续成形的方法，其包括合金熔化-钢液精炼-冒口浇铸环坯-热挤压-热处理-精密整形步骤；所述钢液精炼是采用中频感应电炉精炼，冶炼温度为1650℃~1700℃；所述冒口浇铸环坯是将精炼钢水在1590℃~1610℃进行细颈冒口浇注，浇注结束后在1280℃~1330℃出模；所述热挤压是将铸造空心环坯放在钢管挤压机上，利用铸坯余热在初始挤压温度1200℃~1250℃下直接进行挤压成形，挤压比为10~12。
所述钢管挤压机为立式钢管挤压机或卧式钢管挤压机中的任意一种。
本发明优点及积极效果是：
1、精简加工流程，提高材料利用率。该工艺省去镦粗冲孔的工艺，材料利用率提高10%~15%。工艺过程中切下的废料及压余料头可以重新投入炉中精炼，极大的节省了材料。
2、利用铸坯余热直接挤压成形。由于本发明直接采用热挤压加工，省去了热处理等及多次加热的过程，极大的节约了能源、设备和人力成本。
3、提高了无缝钢管的质量和精度。经铸造得到性能良好的环坯，直接进行热挤压后，破坏钢锭的铸造组织，细化钢材的晶粒，消除显微组织的缺陷，从而使钢材组织密实，力学性能得到改善。
4、降低生产成本，提高生产效率。通过减少工艺流程，节省了材料、能源和人力成本，从而降低了无缝钢管的生产成本。极大的缩短了背景技术中的工艺流程，提高了生产效率。
具体实施方式
下面结合实施例对本发明作进一步详细描述。
实施例1
本实施例中的一种厚壁无缝钢管短流程铸挤连续成形的方法，其包括合金熔化-钢液精炼-冒口浇铸环坯-热挤压-热处理-精密整形步骤；所述钢液精炼是采用中频感应电炉精炼，加入1%球化剂，球化处理温度为1500℃，冶炼温度为1650℃；所述冒口浇铸环坯是将精炼钢水在1590℃~1610℃进行细颈冒口浇注，浇注结束后在1300℃出模；所述热挤压是将铸造空心环坯放在立式钢管挤压机上，铸造空心环坯内表面涂上润滑剂，利用铸坯余热在初始挤压温度1250℃下直接进行挤压成形，控制钢管挤压机的挤压速度在300~400mm/s范围内，挤压比为10。本实施例选用Q345钢，挤压成形的无缝钢管尺寸要求为：外径
Figure BDA00002767771800021
500~
Figure BDA00002767771800022
800mm，壁厚40~60mm，长度8000~12000mm。
实施例2
本实施例中的一种厚壁无缝钢管短流程铸挤连续成形的方法，其包括合金熔化-钢液精炼-冒口浇铸环坯-热挤压-热处理-精密整形步骤；所述钢液精炼是采用中频感应电炉精炼，加入1%球化剂，球化处理温度为1500℃，冶炼温度为1700℃；所述冒口浇铸环坯是将精炼钢水在1590℃~1610℃进行细颈冒口浇注，浇注结束后在1280℃出模；所述热挤压是将铸造空心环坯放在立式钢管挤压机上，铸造空心环坯内表面涂上润滑剂，利用铸坯余热在初始挤压温度1200℃下直接进行挤压成形，控制钢管挤压机的挤压速度在300~400mm/s范围内，挤压比为11。本实施例选用Q345钢，挤压成形的无缝钢管尺寸要求为：外径
Figure BDA00002767771800031
500~
Figure BDA00002767771800032
800mm，壁厚40~60mm，长度8000~12000mm。
实施例3
本实施例中的一种厚壁无缝钢管短流程铸挤连续成形的方法，其包括合金熔化-钢液精炼-冒口浇铸环坯-热挤压-热处理-精密整形步骤；所述钢液精炼是采用中频感应电炉精炼，加入1%球化剂，球化处理温度为1500℃，冶炼温度为1680℃；所述冒口浇铸环坯是将精炼钢水在1590℃~1610℃进行细颈冒口浇注，浇注结束后在1330℃出模；所述热挤压是将铸造空心环坯放在立式钢管挤压机上，铸造空心环坯内表面涂上润滑剂，利用铸坯余热在初始挤压温度1230℃下直接进行挤压成形，控制钢管挤压机的挤压速度在300~400mm/s范围内，挤压比为12。本实施例选用Q345钢，挤压成形的无缝钢管尺寸要求为：外径
Figure BDA00002767771800033
500~
Figure BDA00002767771800034
800mm，壁厚40~60mm，长度8000~12000mm。
上述实施例中的立式钢管挤压机还可以用卧式钢管挤压机代替。
上述实施例中的冶炼温度还可以在1650℃~1700℃之间任意选择。
上述实施例中的出模温度还可以在1280℃~1330℃之间任意选择。
上述实施例中的初始挤压温度还可以在1200℃~1250℃之间任意选择。

Claims (2)

1.一种厚壁无缝钢管短流程铸挤连续成形的方法，其特征是：它包括合金熔化-钢液精炼-冒口浇铸环坯-热挤压-热处理-精密整形步骤；所述钢液精炼是采用中频感应电炉精炼，冶炼温度为1650℃~1700℃；所述冒口浇铸环坯是将精炼钢水在1590℃~1610℃进行细颈冒口浇注，浇注结束后在1280℃~1330℃出模；所述热挤压是将铸造空心环坯放在钢管挤压机上，利用铸坯余热在初始挤压温度1200℃~1250℃下直接进行挤压成形，挤压比为10~12。
2.根据权利要求1所述的一种厚壁无缝钢管短流程铸挤连续成形的方法，其特征是：所述钢管挤压机为立式钢管挤压机或卧式钢管挤压机中的任意一种。
CN201310025737.4A 2013-01-24 2013-01-24 一种厚壁无缝钢管短流程铸挤连续成形的方法 Expired - Fee Related CN103056183B (zh)