CN102942339A - 一种脱硫灰砌块 - Google Patents
一种脱硫灰砌块 Download PDFInfo
- Publication number
- CN102942339A CN102942339A CN2012104417185A CN201210441718A CN102942339A CN 102942339 A CN102942339 A CN 102942339A CN 2012104417185 A CN2012104417185 A CN 2012104417185A CN 201210441718 A CN201210441718 A CN 201210441718A CN 102942339 A CN102942339 A CN 102942339A
- Authority
- CN
- China
- Prior art keywords
- fly ash
- building block
- desulphurize fly
- cement
- iron tailings
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种脱硫灰砌块,由以下原料按重量配比混合后制成砌块,30-65%脱硫灰,0-22%铁尾矿砂,12-32%石屑,12-18%水泥,可做成标准砖砌块、彩色地面砖。用70-80%脱硫灰和20-30%水泥制成脱硫灰陶粒后可制成脱硫灰空心砌块。本发明采用挤压、振动成型为不同规格的系列墙体砌筑材料,变废为宝,环保节能、保温、防火和隔音效果显著,耐磨损腐蚀,无须后期维护,生产和使用成本低。
Description
技术领域
本发明涉及建筑砌块,具体是一种用脱硫灰做为原料的砌块。
背景技术
随着我国控制和削减SO2排放力度的不断加大,烟气脱硫已进入快速发展阶段。伴随着脱硫装置的陆续安装,脱硫产物越来越多,脱硫灰的综合利用成为急需解决的问题。由于半干法脱硫灰的成分极其复杂,由脱硫剂、脱硫产物与飞灰等多种成分组成,并且脱硫灰中的亚硫酸钙在被利用过程中性质十分不稳定,所以大多是以堆放和抛弃处理为主,不仅造成资源浪费,还会对周围环境造成破坏。
发明内容
本发明的目的是使脱硫灰变废为宝,从而提供一种脱硫灰砌块。
为实现上述目的,本发明采用的技术方案是:
一种脱硫灰砌块,由以下原料按重量配比混合后制成砌块,30-65%脱硫灰,0-22%铁尾矿砂,12-32%石屑,12-18%水泥,其中,脱硫灰的主要化学成分是SiO29.42%、Fe2O32.60%、Al2O34.65%、CaO44.35%、SO33.24%;铁尾矿的主要化学成分是73.27%、三氧化二铝4.07%、三氧化铁11.6%、二氧化锑2.06%、氧化钙3%、氧化钠0.41%、氧化钾0.95%、三氧化硫0.25%、氧化锰0.14%。
做为标准砖砌块优选的配比是50%脱硫灰,10%铁尾矿砂,26%石屑,14%水泥。
做为彩色地面砖优选的配比是30%脱硫灰,22%铁尾矿砂,32%石屑,16%水泥;或是40%脱硫灰,12%铁尾矿砂,30%石屑,18%水泥;或是50%脱硫灰,32%石屑,18%水泥。
本发明同时还提供了一种脱硫灰空心砌块,以重量配比计,先由70-80%脱硫灰和20-30%水泥制成脱硫灰陶粒,再将65%脱硫灰陶粒、8%粉煤灰、12%铁尾矿砂和15%水泥混合后制成空心砌块;其中,脱硫灰的主要化学成分是SiO29.42%、Fe2O32.60%、Al2O34.65%、CaO44.35%、SO33.24%;铁尾矿的主要化学成分是73.27%、三氧化二铝4.07%、三氧化铁11.6%、二氧化锑2.06%、氧化钙3%、氧化钠0.41%、氧化钾0.95%、三氧化硫0.25%、氧化锰0.14%。
干法烟气脱硫产物中CaS03含量较高,CaSO3的转化有助于改善以此为原料生产的建材制品的力学性能和耐久性,具有显著的环境效益、经济效益和社会效益。本发明脱硫灰砌块是以脱硫灰、水泥等为主要原料,采用挤压、振动成型为不同规格的系列墙体砌筑材料,变废为宝,环保节能,保温、防火和隔音性能卓越,是框架结构***护填充墙、隔墙、防火墙等的理想墙材;地面砖有彩色平面、槽纹等各种饰面,通过颜色、规格尺寸、排列及组合方式的变化可实现各种装饰效果,一次安装永葆原色,耐磨损和腐蚀,无须后期维护,造价与传统粘土砖建筑基本持平,与框架结构和剪力墙结构相比较,其价格优势更为显著。
具体实施方式
以下实施例的原料中,脱硫灰的主要化学成分是SiO29.42%、Fe2O32.60%、Al2O34.65%、CaO44.35%、SO33.24%;铁尾矿的主要化学成分是73.27%、三氧化二铝4.07%、三氧化铁11.6%、二氧化锑2.06%、氧化钙3%、氧化钠0.41%、氧化钾0.95%、三氧化硫0.25%、氧化锰0.14%。
实施例1
产品为标准砖
原料重量配比:50%脱硫灰,10%铁尾矿砂,26%石屑,14%水泥。
按配比将以上原料送入搅拌机进行搅拌,然后通过湿混料皮带送入主机料斗,通过主机的布料振动压缩成型,生产出脱硫灰砌块,将其放入养护窑实施蒸汽养护,最后捆气包装。
实施例2
产品为彩色地面砖
原料重量配比:30%脱硫灰,22%铁尾矿砂,32%石屑,16%水泥。
按配比将以上原料送入搅拌机进行搅拌,然后通过湿混料皮带送入主机料斗,通过主机的布料振动压缩成型,生产出脱硫灰砌块,将其放入养护窑实施蒸汽养护,最后捆气包装。
以上配料和方法制成的产品做为彩色地面砖的基础底料,可再配合实例1制成的产品做为彩色地面砖的面料,制成更美观、更耐用的彩色地面砖。
实施例3
产品为彩色地面砖
原料重量配比:40%脱硫灰,12%铁尾矿砂,30%石屑,18%水泥。
按配比将以上原料送入搅拌机进行搅拌,然后通过湿混料皮带送入主机料斗,通过主机的布料振动压缩成型,生产出脱硫灰砌块,将其放入养护窑实施蒸汽养护,最后捆气包装。
实施例4
产品为彩色地面砖
原料重量配比:50%脱硫灰,32%石屑,18%水泥。
按配比将以上原料送入搅拌机进行搅拌,然后通过湿混料皮带送入主机料斗,通过主机的布料振动压缩成型,生产出脱硫灰砌块,将其放入养护窑实施蒸汽养护,最后捆气包装。
实施例5
产品为空心砌块
制备脱硫灰陶粒,以重量比计,将70%脱硫灰和30%水泥放入轮碾搅拌机里进行搅拌,搅拌后通过皮带运输机送入成球盘,旋转成直径为3-5mm的陶粒,成型的陶粒通过皮带运输机送入蒸汽室进行蒸汽养护,为下道生产工序做准备。
制备空心砌块,原料重量配比:65%脱硫灰陶粒、8%粉煤灰、12%铁尾矿砂和15%水泥,按配比将以上原料送入搅拌机进行搅拌,然后通过湿混料皮带送入主机料斗,通过主机的布料振动压缩成型,生产出脱硫灰砌块,将其放入养护窑实施蒸汽养护,最后捆扎包装。
实施例6
产品为空心砌块
制备脱硫灰陶粒,以重量比计,将80%脱硫灰和20%水泥放入轮碾搅拌机里进行搅拌,搅拌后通过皮带运输机送入成球盘,旋转成直径为3-5mm的陶粒,成型的陶粒通过皮带运输机送入蒸汽室进行蒸汽养护,为下道生产工序做准备。
制备空心砌块,原料重量配比:65%脱硫灰陶粒、8%粉煤灰、12%铁尾矿砂和15%水泥,按配比将以上原料送入搅拌机进行搅拌,然后通过湿混料皮带送入主机料斗,通过主机的布料振动压缩成型,生产出脱硫灰砌块,将其放入养护窑实施蒸汽养护,最后捆扎包装。
实施例6
产品为空心砌块
制备脱硫灰陶粒,以重量比计,将75%脱硫灰和25%水泥放入轮碾搅拌机里进行搅拌,搅拌后通过皮带运输机送入成球盘,旋转成直径为3-5mm的陶粒,成型的陶粒通过皮带运输机送入蒸汽室进行蒸汽养护,为下道生产工序做准备。
制备空心砌块,原料重量配比:65%脱硫灰陶粒、8%粉煤灰、12%铁尾矿砂和15%水泥,按配比将以上原料送入搅拌机进行搅拌,然后通过湿混料皮带送入主机料斗,通过主机的布料振动压缩成型,生产出脱硫灰砌块,将其放入养护窑实施蒸汽养护,最后捆扎包装。
Claims (6)
1..一种脱硫灰砌块,其特征在于由以下原料按重量配比混合后制成砌块,30-65%脱硫灰,0-22%铁尾矿砂,12-32%石屑,12-18%水泥,其中,脱硫灰的主要化学成分是SiO29.42%、Fe2O32.60%、Al2O34.65%、CaO44.35%、SO33.24%;铁尾矿的主要化学成分是73.27%、三氧化二铝4.07%、三氧化铁11.6%、二氧化锑2.06%、氧化钙3%、氧化钠0.41%、氧化钾0.95%、三氧化硫0.25%、氧化锰0.14%。
2.根据权利要求1所述的脱硫灰砌块,其特征在于:原料是50%脱硫灰,10%铁尾矿砂,26%石屑,14%水泥。
3.根据权利要求1所述的脱硫灰砌块,其特征在于:原料是30%脱硫灰,22%铁尾矿砂,32%石屑,16%水泥。
4.根据权利要求1所述的脱硫灰砌块,其特征在于:原料是40%脱硫灰,12%铁尾矿砂,30%石屑,18%水泥。
5.根据权利要求1所述的脱硫灰砌块,其特征在于:原料是50%脱硫灰,32%石屑,18%水泥。
6.一种脱硫灰空心砌块,其特征在于:以重量配比计,先由70-80%脱硫灰和20-30%水泥制成脱硫灰陶粒,再将65%脱硫灰陶粒、8%粉煤灰、12%铁尾矿砂和15%水泥混合后制成空心砌块;其中,脱硫灰的主要化学成分是SiO29.42%、Fe2O32.60%、Al2O34.65%、CaO44.35%、SO33.24%;铁尾矿的主要化学成分是73.27%、三氧化二铝4.07%、三氧化铁11.6%、二氧化锑2.06%、氧化钙3%、氧化钠0.41%、氧化钾0.95%、三氧化硫0.25%、氧化锰0.14%。