CN102925866A - 一种单一相Mg2Si半导体薄膜的制备工艺 - Google Patents
一种单一相Mg2Si半导体薄膜的制备工艺 Download PDFInfo
- Publication number
- CN102925866A CN102925866A CN2012104558817A CN201210455881A CN102925866A CN 102925866 A CN102925866 A CN 102925866A CN 2012104558817 A CN2012104558817 A CN 2012104558817A CN 201210455881 A CN201210455881 A CN 201210455881A CN 102925866 A CN102925866 A CN 102925866A
- Authority
- CN
- China
- Prior art keywords
- annealing
- semiconductor film
- phase
- evaporation
- preparation technology
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种单一相Mg2Si半导体薄膜的制备工艺,它包括以下过程:第一、Si衬底上蒸发沉积Mg膜,首先将Si片清洗干燥,将Si片固定在电阻热蒸发室上方的样品架上,Mg颗粒放置在蒸发坩埚内,进行蒸镀;第二、退火工艺,蒸镀完成后的Si片置于高真空退火炉中进行低真空氛围退火,最后制备出单一相Mg2Si半导体薄膜;解决了现有技术存在的实验条件苛刻,成本较高,难于工业化推广等缺点,以及采用电子束蒸发沉积工艺,在退火炉中退火过程中采用氩气氛围退火,有MgO氧化物等杂质的产生,最终影响Mg2Si的品质等问题。
Description
技术领域
本发明涉及一种单一相Mg2Si半导体薄膜的制备工艺。
背景技术
Mg2Si作为一种拥有良好发展前景的金属硅化物环境友好半导体材料,具有以下特点:元素Mg、Si的原料资源丰富、地壳蕴藏量大、价格低廉;元素无毒无污染,Mg2Si耐腐蚀、抗氧化。环境友好半导体Mg2Si材料之所以具有广阔的应用前景,还因为它具有一系列优良的特性,如其制备方法与现有的Si基微电子工艺相兼容,减少了生产设备升级带来的成本压力;1.2-1.8 μm红外线波段适用于现代通讯器件;与n型Si有着很好的欧姆接触,接触电阻率为2.2×10-7 W·cm,比金属Al还小一个数量级。同时,Mg2Si被认为是一种热电效率高(ZT>1)的热电材料。在光电及热电性质的研究方面,作为一种窄带隙半导体材料,Mg2Si在红外传感器领域有一定的应用前景,通过掺杂不同元素进行分析,证明了Mg2Si具有良好的热电材料应用前景。总之,Mg2Si薄膜材料在光电器件、电子器件、能源器件领域具有重要的应用前景,有望逐步取代以前有毒或容易造成环境污染的半导体材料,具有较大的社会效益及环境效益。目前已经有多种技术被应用于Mg2Si薄膜材料的制备,其中包括:脉冲激光沉积,分子束外延,离子束合成等,这些方法均存在实验条件苛刻,成本较高,难于工业化推广等缺点,采用电子束蒸发沉积工艺,在退火炉中退火过程中采用氩气氛围退火,发现会有MgO氧化物等杂质的产生,最终影响Mg2Si的品质。
发明内容
本发明要解决的技术问题:提供一种单一相Mg2Si半导体薄膜的制备工艺,以克服现有技术存在的实验条件苛刻,成本较高,难于工业化推广等缺点,以及采用电子束蒸发沉积工艺,存在有MgO氧化物等杂质,最终影响Mg2Si的品质等问题。本发明技术方案:
一种单一相Mg2Si半导体薄膜的制备工艺,它包括以下过程:第一、Si衬底上蒸发沉积Mg膜, 首先将Si片清洗干燥,将Si片固定在电阻热蒸发室上方的样品架上,Mg颗粒放置在蒸发坩埚内,进行蒸镀;第二、退火工艺,蒸镀完成后的Si片置于高真空退火炉中进行低真空氛围退火,最后制备出单一相Mg2Si半导体薄膜。
在Si片清洗干燥过程中,先将Si片裁切至所需形状尺寸,将其用无水乙醇、丙酮超声波清洗,再使用去离子水超声波清洗;将清洗干净的样品置于干燥箱中70 ℃条件下烘干。使用压片将Si片固定在电阻热蒸发室上方的样品架上。
在进行蒸镀前,先对电阻热蒸发室抽真空,当真空度小于等于2.0×10-4 Pa时,开始蒸镀;蒸发电流逐步加到80 A,正式开始蒸镀;蒸镀时的电阻式热蒸发的功率为16~19 KW,蒸发速率保持在18-24 nm/min,蒸发时间为15-18 min。
退火过程中,高真空退火炉中的退火炉背底真空小于等于10-3 Pa,退火前调节角阀,使真空保持在10-1 Pa-10-2 Pa之间。
退火过程中,退火时间3-7 h,退火温度350 ℃-450 ℃。
在Si衬底上制备了单一相Mg2Si半导体薄膜,即在Si衬底上制备的Mg2Si半导体薄膜中不含MgO或Mg晶粒等其它相物质。
本发明有益效果:
采用本发明-低真空条件下退火方式,制备了单一相Mg2Si半导体薄膜,合成的Mg2Si薄膜中不含MgO或Mg晶粒等杂质的,为Mg2Si半导体薄膜的器件开发利用奠定良好的基础。
本发明采用电阻式热蒸发沉积和低真空退火技术,制备单一相Mg2Si半导体薄膜。电阻式热蒸发沉积技术的基本原理是,把蒸发材料放入适当的电阻加热体内,通电使蒸发材料直接加热蒸发,从而使蒸发材料以气态形式沉积到基片上形成薄膜;本发明首先采用电阻式蒸发技术沉积280-480 nm纯金属Mg膜在Si单晶基片上,形成Si/Mg薄膜结构,随后置于真空退火炉中退火。退火炉背底真空小于等于10-3 Pa,退火前调节角阀,使背底真空保持在10-1 Pa-10-2 Pa之间;退火时间3-7小时,退火温度350 ℃-450 ℃,获得单一相Mg2Si半导体薄膜;本发明的制备工艺,在低真空条件下进行退火处理,处理过程中避免了氧气等其他气体进入,制备的单一相Mg2Si半导体薄膜,不含MgO或Mg晶粒等其它相杂质物质,同样,若在高真空条件下退火,由于金属Mg为高蒸汽压元素,造成金属Mg全部或部分挥发,不利于Si、Mg原子扩散以形成Mg2Si薄膜。因此本发明采用低真空条件下进行退火处理,以获得单一相Mg2Si半导体薄膜,与现有技术相比,本发明具有生产成本较低,能够进行工业化生产的优点,解决了现有技术存在的实验条件苛刻,成本较高,难于工业化推广等缺点,以及采用电子束蒸发沉积工艺,在退火炉中退火过程中采用氩气氛围退火,有MgO氧化物等杂质的产生,最终影响Mg2Si的品质等问题,本发明制备了不含MgO或Mg晶粒等杂质的单一相Mg2Si半导体薄膜,为Mg2Si半导体薄膜的器件开发利用奠定良好的基础。
附图说明
图1为本发明的样品X射线衍射图,在400 ℃退火时间分别为3-7 h的X射线衍射图;
图2为本发明的样品扫描电镜图,在400 ℃退火时间分别为3 h的扫描电镜图;
图3为本发明的样品扫描电镜图,在400 ℃退火时间分别为4 h的扫描电镜图;
图4为本发明的样品扫描电镜图,在400 ℃退火时间分别为5 h的扫描电镜图;
图5为本发明的样品扫描电镜图,在400 ℃退火时间分别为6 h的扫描电镜图;
图6为本发明的样品扫描电镜图,在400 ℃退火时间分别为7 h的扫描电镜图;
图7为本发明的样品X射线衍射图,在300-450 ℃温度退火5 h的X射线衍射图。
具体实施方式
实施例1:
(1)将试验用Si片裁切至所需大小;首先,分别用无水乙醇、丙酮超声波震荡20分钟,目的是去除硅片表面有机物,再使用去离子水超声波清洗5次,每次10分钟;最后将清洗干净的样品置于干燥箱中70 ℃条件下烘干为止;
(2)试验用Si片由于面积较小,使用弹片固定在蒸镀室上方的样品架上。高纯Mg颗粒直接放置在蒸发坩埚内;
(3)对蒸镀室抽真空,当真空度小于等于2.0×10-4 Pa时,并保持一段时间;
(4)当真空度再次小于等于2.0×10-4 Pa时,加热电流逐步加到80 A,开始蒸镀;蒸镀时的电阻式热蒸发的功率为18 KW,蒸发速率保持在18-24 nm/min,蒸发时间为16 min;
(5)蒸镀完成后自然冷却至室温,再取出并置于高真空退火炉中,退火炉背底真空小于等于10-3 Pa,退火前调节角阀,使背底真空保持在10-1Pa-10-2Pa之间。退火时间3-7 h,退火温度400 ℃,形成单一相Mg2Si半导体薄膜。
图1为400℃不同退火时间制备的样品的X射线衍射图,图中可见,除衬底Si衍射峰外,各衍射峰均为Mg2Si衍射峰,且与PDF标准谱(卡片号:65-9365)衍射峰一一对应,说明本发明所述制备条件下,制备了单一相Mg2Si半导体薄膜薄膜。
图2至图6为400℃不同退火时间制备的样品表面形貌的扫描电镜图,结果显示Mg2Si晶粒对样品表面覆盖度好,晶粒尺寸较大,表面较为平整。在实验所采用的退火条件下,均有结晶状态良好的Mg2Si薄膜出现。
实施例2:
(1)将试验用Si片裁切至所需大小;首先,分别用无水乙醇、丙酮超声波震荡清洗20 min,目的是去除硅片表面有机物,再使用去离子水超声波震荡清洗5次,每次10 min。最后将清洗干净的样品置于干燥箱中80 ℃条件下烘烤,至表面完全干燥为止;
(2)试验用Si片由于面积较小,使用弹片固定在蒸镀室上方的样品架上。Mg颗粒直接放置在蒸发坩埚内;
(3)对蒸镀室抽真空,当真空度小于等于2.0×10-4 Pa时,并保持一段时间;
(4)当真空度再次小于等于2.0×10-4 Pa时,开始蒸镀;蒸发电流逐步加到80 A,正式开始蒸镀;蒸镀时的电阻式热蒸发的功率为16~19KW,蒸发速率保持在18~24 nm/min,蒸发时间为16 min;
(5)蒸镀完成后自然冷却至室温,再取出并置于高真空退火炉中。退火炉背底真空小于等于10-3 Pa,退火前调节角阀,使背底真空保持在10-1 Pa-10-2 Pa之间。退火时间5h,退火温度350-450 ℃,制备出单一相Mg2Si半导体薄膜。
图7为退火时间为5个小时,在不同退火温度时制备的样品的X射线衍射图,图中可见,除衬底Si衍射峰外,各衍射峰均为Mg2Si衍射峰,且与PDF标准谱(卡片号:65-9365)衍射峰一一对应,说明本发明所述制备条件下,制备了单一相Mg2Si半导体薄膜薄膜。
Claims (6)
1.一种单一相Mg2Si半导体薄膜的制备工艺,其特征在于:它包括以下过程:第一、Si衬底上蒸发沉积Mg膜, 首先将Si片清洗干燥,将Si片固定在电阻热蒸发室上方的样品架上,Mg颗粒放置在蒸发坩埚内,进行蒸镀;第二、退火工艺,蒸镀完成后的Si片置于高真空退火炉中进行低真空氛围退火,最后制备出单一相Mg2Si半导体薄膜。
2.根据权利要求1所述的单一相Mg2Si半导体薄膜的制备工艺,其特征在于:在Si片清洗干燥过程中,先将Si片裁切至所需形状尺寸,将其用无水乙醇、丙酮超声波清洗,再使用去离子水超声波清洗;将清洗干净的样品置于干燥箱中70 ℃条件下烘干,使用压片将Si片固定在电阻热蒸发室上方的样品架上。
3.根据权利要求1所述的单一相Mg2Si半导体薄膜的制备工艺,其特征在于:在进行蒸镀前,先对电阻热蒸发室抽真空,当真空度小于等于2.0×10-4 Pa时,开始蒸镀;蒸发电流逐步加到80 A,正式开始蒸镀;蒸镀时的电阻式热蒸发的功率为16~19 KW,蒸发速率保持在18-24 nm/min,蒸发时间为15-18 min。
4.根据权利要求1所述的单一相Mg2Si半导体薄膜的制备工艺,其特征在于:退火过程中,高真空退火炉中的退火炉背底真空小于等于10-3 Pa,退火前调节角阀,使真空保持在10-1 Pa-10-2 Pa之间。
5.根据权利要求1所述的单一相Mg2Si半导体薄膜的制备工艺,其特征在于:退火过程中,退火时间3-7 h,退火温度350 ℃-450 ℃。
6.根据权利要求1所述的单一相Mg2Si半导体薄膜的制备工艺,其特征在于:在Si衬底上制备了单一相Mg2Si半导体薄膜,即在Si衬底上制备的Mg2Si半导体薄膜中不含MgO或Mg晶粒等其它相物质。