CN102922750A - 一种pps复合材料的制备方法 - Google Patents

一种pps复合材料的制备方法 Download PDF

Info

Publication number
CN102922750A
CN102922750A CN201210471972XA CN201210471972A CN102922750A CN 102922750 A CN102922750 A CN 102922750A CN 201210471972X A CN201210471972X A CN 201210471972XA CN 201210471972 A CN201210471972 A CN 201210471972A CN 102922750 A CN102922750 A CN 102922750A
Authority
CN
China
Prior art keywords
pps
pressure
powder
fiber cloth
temperature
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201210471972XA
Other languages
English (en)
Other versions
CN102922750B (zh
Inventor
邓志东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ZHANGJIAGANG XINDONGPO GLASS COTTON PRODUCTS FACTORY
Original Assignee
ZHANGJIAGANG XINDONGPO GLASS COTTON PRODUCTS FACTORY
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ZHANGJIAGANG XINDONGPO GLASS COTTON PRODUCTS FACTORY filed Critical ZHANGJIAGANG XINDONGPO GLASS COTTON PRODUCTS FACTORY
Priority to CN201210471972.XA priority Critical patent/CN102922750B/zh
Publication of CN102922750A publication Critical patent/CN102922750A/zh
Application granted granted Critical
Publication of CN102922750B publication Critical patent/CN102922750B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种PPS复合材料的制备方法，其步骤为：1）将PPS粉料、纤维布交替铺展均匀；2）将步骤1）铺设好的模具放入热压机，按步骤加压升温，然后降温定型开模，得PPS复合材料。该生产工艺简单，能耗低，生产周期短，所得产品的拉伸强度高、应用范围广。

Description

一种PPS复合材料的制备方法
技术领域
本发明涉及复合材料技术领域，具体涉及一种PPS复合材料的制备方
法。
背景技术
由于工业与技术的日益发达，以及人们对节能和环保的重视，人们对材料也提出了质量轻、强度高、模量高、易于制造、可回收利用等要求。传统的单一材料无法满足这样的要求。而将两种或两种以上物理和化学性质不同的物质组合而成的复合材料不仅能满足这些要求，还具有材料的可设计性，使得最大限度的发挥材料的性能成为可能。因此，复合材料近几十年来一直被大力研究、发展和应用于航天航空工业、汽车制造业、船舶工业、高档运动器材等领域。
目前市场中复合材料的制备过程中，采用用以差异较大，存在的缺点较多，由于受工艺条件的限制，所得产品的抗拉伸性能不佳，使的复合材料在工程上实现较慢。
发明内容
本发明主要解决的技术问题是：提供一种综合性能佳、抗拉伸强度高的PPS复合材料的制备方法。
为了解决上述问题，本发明的技术方案是：一种PPS复合材料的制备方法，其步骤为：
1）将PPS粉料，按15-20Kg/m2注入模具，铺展均匀，加入纤维布，然后在纤维布上方将PPS粉料按25-30Kg/m2注入模具，铺展均匀；
2）将步骤1）铺设好的模具放入热压机，加以1.6~1.8MPa的初始压力，使原料更加密实，以10~12℃／min的速率，从室温加热至285±2℃；然后再以4~5℃／min的速度，温度由285±2℃加热上升至318±2℃；将压力加至3.5~4MPa，保持温度318±2℃，压力3.5~4MPa，时间为30~40min；l~2℃／min的速率降至室温，降温过程中保持压力3.5±0.2MPa，降至室温后开模，取出PPS复合材料。
所述纤维布为玻璃纤维布或碳纤维布。
步骤1）中所述PPS粉料铺展均匀的方法为：采用200~500Hz下震动
15~25s。
本发明的有益效果是：该生产工艺简单，能耗低，生产周期短，所得产品
的拉伸强度高、应用范围广。
具体实施例
为进一步理解本发明，下面结合实施例对本发明做进一步解释。
实施例1
1）将PPS粉料，按15Kg/m2注入模具，200~500Hz下震动15~25s，使其铺展均匀，加入玻璃纤维布，然后在玻璃纤维布上方将PPS粉料按30Kg/m2注入模具，200~500Hz下震动15~25s使其铺展均匀；
2）将步骤1）铺设好的模具放入热压机，加以1.6MPa的初始压力，使原料更加密实，以10℃／min的速率，从室温加热至285℃，这个阶段由于聚苯硫醚粉末的逐步软化，初始压力将降为0；然后再以5℃／min的速度，温度由285℃加热上升至319℃，将压力加至3.8MPa；持温度319℃，压力3.8MPa，时间为35min；2℃／min的速率降至室温，降温过程中保持压力3.5MPa，降至室温后开模，取出PPS复合材料。
25℃测试产品的拉伸强度为187MPa。
实施例2
1）将PPS粉料，按20Kg/m2注入模具，200~500Hz下震动15~25s，使其铺展均匀，加入碳纤维布，然后在碳纤维布上方将PPS粉料按25Kg/m2注入模具，200~500Hz下震动15~25s使其铺展均匀；
2）将步骤1）铺设好的模具放入热压机，加以1.8MPa的初始压力，使原料更加密实，以12℃／min的速率，从室温加热至286℃；然后再以5℃／min的速度，温度由286℃加热上升至320℃；将压力加至4MPa，保持温度320℃，压力4MPa，时间为30min；l.5℃／min的速率降至室温，降温过程中保持压力3.6MPa，降至室温后开模，取出PPS复合材料。
25℃测试产品的拉伸强度为203MPa。

Claims (3)

1.一种PPS复合材料的制备方法，其步骤为：
1）将PPS粉料，按15-20Kg/m2注入模具，铺展均匀，加入纤维布，然后在纤维布上方将PPS粉料按25-30Kg/m2注入模具，铺展均匀；
2）将步骤1）铺设好的模具放入热压机，加以1.6~1.8MPa的初始压力，使原料更加密实，以10~12℃／min的速率，从室温加热至285±2℃；然后再以4~5℃／min的速度，温度由285±2℃加热上升至318±2℃；将压力加至3.5~4MPa，保持温度318±2℃，压力3.5~4MPa，时间为30~40min；l~2℃／min的速率降至室温，降温过程中保持压力3.5±0.2MPa，降至室温后开模，取出PPS复合材料。
2.根据权利要求1所述的一种PPS复合材料的制备方法，其特征在于：所述纤维布为玻璃纤维布或碳纤维布。
3.根据权利要求1所述的一种PPS复合材料的制备方法，其特征在于：
步骤1）中所述PPS粉料铺展均匀的方法为：采用200~500Hz下震动15~25s。
CN201210471972.XA 2012-11-20 2012-11-20 一种pps复合材料的制备方法 Expired - Fee Related CN102922750B (zh)