CN102911468B - 一种控制电力组合型电缆料及其制备方法 - Google Patents
一种控制电力组合型电缆料及其制备方法 Download PDFInfo
- Publication number
- CN102911468B CN102911468B CN201210346170.6A CN201210346170A CN102911468B CN 102911468 B CN102911468 B CN 102911468B CN 201210346170 A CN201210346170 A CN 201210346170A CN 102911468 B CN102911468 B CN 102911468B
- Authority
- CN
- China
- Prior art keywords
- compound
- preparation
- ethylene
- cable material
- minute
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种控制电力组合型电缆料及其制备方法，其组成原料的重量份为：混合料A：马来酸酐接枝乙烯-醋酸乙酯共聚物25-35、氯磺化聚乙烯20-30、乙烯-醋酸乙烯共聚物20-30、乙烯醋酸乙烯酯30-40、半补强炭黑1-3、改性纳米粉40-60、异氰酸酯1-3、苯基三乙氧基硅烷 1.5-2.5、硬脂酸锌1-3、抗氧剂168 3-4、二苯胺1-3和氢氧化镁10-20；混合料B：马来酸酐接枝PE 50-70、氯醚橡胶30-40、硅橡胶20-30、聚丙烯酸酯20-30、聚-4-甲基-1-戊烯0.3-0.5、促进剂DM 1-3、防老剂TPPD 2-4、聚己酸内醋5-10、二丁基萘磺酸钠 2-3、羟丙基甲基纤维素钠1-3和硼酸锌5-7。本发明制备方法简单，组成原料配方合理，性能大大提高，耐热耐老化耐磨性能良好，高温下膨胀变形小，有利于二次硫化加工，低烟阻燃，环保安全。
Description
技术领域
本发明涉及一种控制电力组合型电缆料及其制备方法，属于电缆料技术领域。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用，随着电气火灾事故的频繁发生，电线电缆的阻燃问题逐渐引起世界各国的重视，电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素，在火灾中妨碍了人们的安全撤离和灭火工作，使生命财产遭到严重损失，同时随着通讯事业、汽车工业和计算机工业的发展，特别是船用导线、汽车用线、高温仪表电缆、石油钻井平台电缆等许多场合，当然控制电力组合型电缆料也是必不可少的。
发明内容
本发明的目的是提供一种控制电力组合型电缆料及其制备方法，本发明制备方法简单，组成原料配方合理，性能大大提高，耐热耐老化耐磨性能良好，高温下膨胀变形小，有利于二次硫化加工，低烟阻燃，环保安全。
为实现上述目的本发明的采用如下技术方案：
控制电力组合型电缆料，其组成原料的重量份为：
混合料A：马来酸酐接枝乙烯-醋酸乙酯共聚物25-35、氯磺化聚乙烯20-30、乙烯-醋酸乙烯共聚物20-30、乙烯醋酸乙烯酯30-40、半补强炭黑1-3、改性纳米粉40-60、异氰酸酯1-3、苯基三乙氧基硅烷 1.5-2.5、硬脂酸锌1-3、抗氧剂168 3-4、二苯胺1-3和氢氧化镁10-20；
混合料B：马来酸酐接枝PE 50-70、氯醚橡胶30-40、硅橡胶20-30、聚丙烯酸酯20-30、聚-4-甲基-1-戊烯0.3-0.5、促进剂DM 1-3、防老剂TPPD 2-4、聚己酸内醋5-10、二丁基萘磺酸钠 2-3、羟丙基甲基纤维素钠1-3和硼酸锌5-7。
控制电力组合型电缆料，其组成原料的重量份为：
混合料A：马来酸酐接枝乙烯-醋酸乙酯共聚物30、氯磺化聚乙烯25、乙烯-醋酸乙烯共聚物25、乙烯醋酸乙烯酯35、马来酸酐接枝乙烯-醋酸乙酯共聚物35、半补强炭黑2、改性纳米粉50、异氰酸酯2、苯基三乙氧基硅烷2、硬脂酸锌2、抗氧剂168 3.5、二苯胺2和氢氧化镁15；
混合料B：马来酸酐接枝PE 60、氯醚橡胶35、硅橡胶25、聚丙烯酸酯25、聚-4-甲基-1-戊烯0.4、促进剂DM 2、防老剂TPPD 3、聚己酸内醋8、二丁基萘磺酸钠2.5、羟丙基甲基纤维素钠2和硼酸锌6。
控制电力组合型电缆料的制备方法，包括以下步骤：
（1）首先按组成原料的重量份分别称取混合料A、B的各原料；分别将混合料A、B的原料分别在温度105-115℃在密炼4-6分钟后，密炼后再在温度175-185℃下混炼28-32分钟，分别得到混合料A和混合料B；
（2）混合混合料A和混合料B，再加入混炼机中混炼10-20分钟，控制温度在130-150℃，最后在140-150℃下塑炼3-5分钟，出料。
所述的改性纳米粉制备方法为将碳酸钙等600-700℃下烧损4-5小时，后研磨成纳米粉末，拌入相当于粉体重量1-2%的用环氧大豆油、1-2%的木质素磺酸钙拌搅均匀，烘干，粉碎成粉末。
本发明的优点：
本发明制备方法简单，组成原料配方合理，性能大大提高，耐热耐老化耐磨性能良好，高温下膨胀变形小，有利于二次硫化加工，低烟阻燃，环保安全。
具体实施方式
实施例1：控制电力组合型电缆料，其组成原料的重量份为：
混合料A：马来酸酐接枝乙烯-醋酸乙酯共聚物30、氯磺化聚乙烯25、乙烯-醋酸乙烯共聚物25、乙烯醋酸乙烯酯35、马来酸酐接枝乙烯-醋酸乙酯共聚物35、半补强炭黑2、改性纳米粉50、异氰酸酯2、苯基三乙氧基硅烷2、硬脂酸锌2、抗氧剂168 3.5、二苯胺2和氢氧化镁15；
混合料B：马来酸酐接枝PE 60、氯醚橡胶35、硅橡胶25、聚丙烯酸酯25、聚-4-甲基-1-戊烯0.4、促进剂DM 2、防老剂TPPD 3、聚己酸内醋8、二丁基萘磺酸钠2.5、羟丙基甲基纤维素钠2和硼酸锌6。
控制电力组合型电缆料的制备方法，包括以下步骤：
（1）首先按组成原料的重量份分别称取混合料A、B的各原料；分别将混合料A、B的原料分别在温度105-115℃在密炼4-6分钟后，密炼后再在温度175-185℃下混炼28-32分钟，分别得到混合料A和混合料B；
（2）混合混合料A和混合料B，再加入混炼机中混炼10-20分钟，控制温度在130-150℃，最后在140-150℃下塑炼3-5分钟，出料。
所述的改性纳米粉制备方法为将碳酸钙等600-700℃下烧损4-5小时，后研磨成纳米粉末，拌入相当于粉体重量1-2%的用环氧大豆油、1-2%的木质素磺酸钙拌搅均匀，烘干，粉碎成粉末。
本发明制得的控制电力组合型电缆料性能：
| 序号 | 项目名称 | 单位 | 测试值 |
| 1 | 抗张强度 | Mpa | 8.1 |
| 2 | 断裂伸长率 | % | 575 |
| 3 | 200℃，240h老化后抗张强度 | Mpa | 7.5 |
| 4 | 200℃，240h老化后断裂伸长率 | % | 535 |
| 5 | 20℃体积电阻率 | Ω·m | 9.5×1012 |
| 6 | 相对介电常数 | / | 3.3 |
| 7 | 1000℃×90min高温下绝缘电阻 | MΩ | 1.2 |
Claims (2)
1.一种控制电力组合型电缆料，其特征在于其组成原料的重量份为：
混合料A：马来酸酐接枝乙烯-醋酸乙酯共聚物25-35、氯磺化聚乙烯20-30、乙烯-醋酸乙烯共聚物20-30、乙烯-醋酸乙烯酯树脂30-40、半补强炭黑1-3、改性纳米粉40-60、异氰酸酯1-3、苯基三乙氧基硅烷 1.5-2.5、硬脂酸锌1-3、抗氧剂168 3-4、二苯胺1-3和氢氧化镁10-20；
混合料B：马来酸酐接枝PE 50-70、氯醚橡胶30-40、硅橡胶20-30、聚丙烯酸酯20-30、聚-4-甲基-1-戊烯0.3-0.5、促进剂DM 1-3、防老剂TPPD 2-4、聚己酸内酯5-10、二丁基萘磺酸钠 2-3、羟丙基甲基纤维素钠1-3和硼酸锌5-7；
所述的改性纳米粉制备方法为：将碳酸钙600-700℃下烧损4-5小时，后研磨成纳米粉末，拌入相当于粉体重量1-2%的环氧大豆油、1-2%的木质素磺酸钙拌搅均匀，烘干，粉碎成粉末。
2.一种如权利要求1所述的控制电力组合型电缆料的制备方法，其特征在于包括以下步骤：
（1）首先按组成原料的重量份分别称取混合料A、B的各原料；分别将混合料A、B的原料分别在温度105-115℃密炼4-6分钟，密炼后再在温度175-185℃下混炼28-32分钟，分别得到混合料A和混合料B；
（2）混合混合料A和混合料B，再加入混炼机中混炼10-20分钟，控制温度在130-150℃，最后在140-150℃下塑炼3-5分钟，出料。