CN102911440B - 一种航空用绝缘电缆料及其制备方法 - Google Patents

一种航空用绝缘电缆料及其制备方法 Download PDF

Info

Publication number
CN102911440B
CN102911440B CN201210346101.5A CN201210346101A CN102911440B CN 102911440 B CN102911440 B CN 102911440B CN 201210346101 A CN201210346101 A CN 201210346101A CN 102911440 B CN102911440 B CN 102911440B
Authority
CN
China
Prior art keywords
parts
compound
insulated cable
cable material
aviation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210346101.5A
Other languages
English (en)
Other versions
CN102911440A (zh
Inventor
赵家玉
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou sunrise Electronics Co., Ltd.
Original Assignee
TONGLING CITY TONGDU SPECIAL CABLE CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING CITY TONGDU SPECIAL CABLE CO Ltd filed Critical TONGLING CITY TONGDU SPECIAL CABLE CO Ltd
Priority to CN201210346101.5A priority Critical patent/CN102911440B/zh
Publication of CN102911440A publication Critical patent/CN102911440A/zh
Application granted granted Critical
Publication of CN102911440B publication Critical patent/CN102911440B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种航空用聚四氟乙烯绝缘电缆料及其制备方法，其组成原料的重量份为：混合料A：高密度聚乙烯树脂30-40、马来酸酐接枝乙烯-醋酸乙酯共聚物20-30、马来酸酐接枝PE 25-35、甲基乙烯基硅橡胶20-30、沉淀法白炭黑1-3、改性海泡石粉40-60、不溶性硫磺1-3、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷1.5-2.5、硬脂酸钙1-3和抗氧剂1035 3-4；混合料B：氯化聚乙烯 50-70、聚苯醚树脂 30-40、乙烯醋酸乙烯酯20-30、聚-4-甲基-1-戊烯0.3-0.5、防老剂RD 1-3、氧化聚乙烯蜡2-4、聚己酸内醋5-10、水溶性酚醛树脂1-3、双巯基乙酸异辛酯二正辛基锡2-4和硼酸锌10-15。本发明制备方法简单，组成原料配方合理，性能大大提高，拉伸强度、断裂延伸率、老化后的拉伸强度保持率及断裂伸出保持率，冲击脆化温度能同时获得优异的性能。

Description

一种航空用绝缘电缆料及其制备方法
技术领域
本发明涉及一种航空用聚四氟乙烯绝缘电缆料及其制备方法，属于电缆料技术领域。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用，随着电气火灾事故的频繁发生，电线电缆的阻燃问题逐渐引起世界各国的重视，电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素，在火灾中妨碍了人们的安全撤离和灭火工作，使生命财产遭到严重损失，同时随着通讯事业、汽车工业和计算机工业的发展，特别是船用导线、汽车用线、高温仪表电缆、石油钻井平台电缆等许多场合，当然航空用聚四氟乙烯绝缘电缆料也是必不可少的。
发明内容
本发明的目的是提供一种航空用聚四氟乙烯绝缘电缆料及其制备方法，本发明制备方法简单，组成原料配方合理，性能大大提高，拉伸强度、断裂延伸率、老化后的拉伸强度保持率及断裂伸出保持率，冲击脆化温度能同时获得优异的性能。
为实现上述目的本发明的采用如下技术方案：
航空用聚四氟乙烯绝缘电缆料，其组成原料的重量份为：
混合料A：高密度聚乙烯树脂30-40、马来酸酐接枝乙烯-醋酸乙酯共聚物20-30、马来酸酐接枝PE  25-35、甲基乙烯基硅橡胶20-30、沉淀法白炭黑1-3、改性海泡石粉40-60、不溶性硫磺1-3、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷1.5-2.5、硬脂酸钙1-3和抗氧剂1035  3-4；
混合料B：氯化聚乙烯  50-70、聚苯醚树脂  30-40、乙烯醋酸乙烯酯20-30、聚-4-甲基-1-戊烯0.3-0.5、防老剂RD  1-3、氧化聚乙烯蜡2-4、聚己酸内醋5-10、水溶性酚醛树脂1-3、双巯基乙酸异辛酯二正辛基锡2-4和硼酸锌10-15。
航空用聚四氟乙烯绝缘电缆料，其组成原料的重量份为：
混合料A：高密度聚乙烯树脂35、马来酸酐接枝乙烯-醋酸乙酯共聚物25、马来酸酐接枝PE  30、甲基乙烯基硅橡胶25、沉淀法白炭黑2、改性海泡石粉50、不溶性硫磺2、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷2、硬脂酸钙2和抗氧剂1035  3.5；
混合料B：氯化聚乙烯  60、聚苯醚树脂  35、乙烯醋酸乙烯酯25、聚-4-甲基-1-戊烯0.4、防老剂RD  2、氧化聚乙烯蜡3、聚己酸内醋8、水溶性酚醛树脂2、双巯基乙酸异辛酯二正辛基锡3和硼酸锌12。
航空用聚四氟乙烯绝缘电缆料的制备方法，包括以下步骤：
（1）首先按组成原料的重量份分别称取混合料A、B的各原料；分别将混合料A、B的原料分别在温度105-115℃在密炼4-6分钟后，密炼后再在温度175-185℃下混炼28-32分钟，分别得到混合料A和混合料B；
（2）混合混合料A和混合料B，再加入混炼机中混炼10-20分钟，控制温度在130-150℃，最后在140-150℃下塑炼3-5分钟，出料。
所述的改性海泡石粉制备方法为先用15-20%盐酸浸泡海泡石1-2小时，静置，澄清，离心，固体用水洗至中性，烘干后，加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀，烘干，粉碎成粉末。
本发明的优点：
本发明制备方法简单，组成原料配方合理，性能大大提高，拉伸强度、断裂延伸率、老化后的拉伸强度保持率及断裂伸出保持率，冲击脆化温度能同时获得优异的性能。
具体实施方式
实施例1：航空用聚四氟乙烯绝缘电缆料，其组成原料的重量份为：
混合料A：高密度聚乙烯树脂35、马来酸酐接枝乙烯-醋酸乙酯共聚物25、马来酸酐接枝PE  30、甲基乙烯基硅橡胶25、沉淀法白炭黑2、改性海泡石粉50、不溶性硫磺2、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷2、硬脂酸钙2和抗氧剂1035  3.5；
混合料B：氯化聚乙烯  60、聚苯醚树脂  35、乙烯醋酸乙烯酯25、聚-4-甲基-1-戊烯0.4、防老剂RD  2、氧化聚乙烯蜡3、聚己酸内醋8、水溶性酚醛树脂2、双巯基乙酸异辛酯二正辛基锡3和硼酸锌12。
航空用聚四氟乙烯绝缘电缆料的制备方法，包括以下步骤：
（1）首先按组成原料的重量份分别称取混合料A、B的各原料；分别将混合料A、B的原料分别在温度105-115℃在密炼4-6分钟后，密炼后再在温度175-185℃下混炼28-32分钟，分别得到混合料A和混合料B；
（2）混合混合料A和混合料B，再加入混炼机中混炼10-20分钟，控制温度在130-150℃，最后在140-150℃下塑炼3-5分钟，出料。
所述的改性海泡石粉制备方法为先用15-20%盐酸浸泡海泡石1-2小时，静置，澄清，离心，固体用水洗至中性，烘干后，加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀，烘干，粉碎成粉末。
本发明制得的航空用聚四氟乙烯绝缘电缆料性能：

Claims (3)

1.一种航空用绝缘电缆料，其特征在于其组成原料的重量份为：
混合料A：高密度聚乙烯树脂30-40、马来酸酐接枝乙烯-醋酸乙酯共聚物20-30、马来酸酐接枝PE  25-35、甲基乙烯基硅橡胶20-30、沉淀法白炭黑1-3、改性海泡石粉40-60、不溶性硫磺1-3、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷1.5-2.5、硬脂酸钙1-3和抗氧剂1035  3-4；
混合料B：氯化聚乙烯  50-70、聚苯醚树脂  30-40、乙烯醋酸乙烯酯20-30、聚-4-甲基-1-戊烯0.3-0.5、防老剂RD  1-3、氧化聚乙烯蜡2-4、聚己酸内酯5-10、水溶性酚醛树脂1-3、双巯基乙酸异辛酯二正辛基锡2-4和硼酸锌10-15;
所述的改性海泡石粉制备方法为：先用15-20%盐酸浸泡海泡石1-2小时，静置，澄清，离心，固体用水洗至中性，烘干后，加入相当于固体重量3-5%的乙烯基三乙氧基硅烷拌搅均匀，烘干，粉碎成粉末。
2.根据权利要求1所述的航空用绝缘电缆料，其特征在于其组成原料的重量份为：
混合料A：高密度聚乙烯树脂35、马来酸酐接枝乙烯-醋酸乙酯共聚物25、马来酸酐接枝PE  30、甲基乙烯基硅橡胶25、沉淀法白炭黑2、改性海泡石粉50、不溶性硫磺2、N-（β一氨乙基）-γ-氨丙基三甲（乙）氧基硅烷2、硬脂酸钙2和抗氧剂1035  3.5；
混合料B：氯化聚乙烯  60、聚苯醚树脂  35、乙烯醋酸乙烯酯25、聚-4-甲基-1-戊烯0.4、防老剂RD  2、氧化聚乙烯蜡3、聚己酸内酯8、水溶性酚醛树脂2、双巯基乙酸异辛酯二正辛基锡3和硼酸锌12。
3.一种如权利要求1或2所述的航空用绝缘电缆料的制备方法，其特征在于包括以下步骤：
（1）首先按组成原料的重量份分别称取混合料A、B的各原料；分别将混合料A、B的原料分别在温度105-115℃密炼4-6分钟，密炼后再在温度175-185℃下混炼28-32分钟，分别得到混合料A和混合料B；
（2）混合混合料A和混合料B，再加入混炼机中混炼10-20分钟，控制温度在130-150℃，最后在140-150℃下塑炼3-5分钟，出料。
CN201210346101.5A 2012-09-18 2012-09-18 一种航空用绝缘电缆料及其制备方法 Expired - Fee Related CN102911440B (zh)