CN102808331A - 一种具有抗起球效果的莫代尔面料生产方法 - Google Patents
一种具有抗起球效果的莫代尔面料生产方法 Download PDFInfo
- Publication number
- CN102808331A CN102808331A CN2012103039377A CN201210303937A CN102808331A CN 102808331 A CN102808331 A CN 102808331A CN 2012103039377 A CN2012103039377 A CN 2012103039377A CN 201210303937 A CN201210303937 A CN 201210303937A CN 102808331 A CN102808331 A CN 102808331A
- Authority
- CN
- China
- Prior art keywords
- enzyme
- pilling
- fluffing
- dressing liquid
- modal fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种具有抗起球效果的莫代尔面料生产方法,它涉及针织面料抗起毛起球制备方法领域。它包括酶预处理工艺和抗起毛起球剂整理工艺,首先用RUCOLASEZER蚀毛酵素制备酶整理液,RUCOLASEZER蚀毛酵素的体积百分比浓度为2-4%和15-20︰1的浴比配成整理液;其次制备抗起毛起球整理液配方:每升水中加入14-18g多元羧酸,14-18g的CONDENSOL康定素-FM催化剂;最后将经过酶预处理的莫代尔面料浸渍在整理溶液中,在40-50℃下整理20-30分钟,烘干后,还需在175℃高温下焙烘45~60秒。从而使面料手感更柔软和蓬松,其抗起毛起球性能更提高。
Description
技术领域
本发明涉及针织面料抗起毛起球制备方法领域,具体涉及一种具有抗起球效果的莫代尔面料生产方法。
背景技术
莫代尔面料在加工、穿着以及洗涤过程中,由于织物间或织物与其他物体之间的摩擦作用,其表面会产生许多绒毛,加之静电作用,使得莫代尔面料表面会产生起毛起球现象,从而造成面料的外观和手感变差,影响了面料的使用性能。
发明内容
本发明的目的是提供一种具有抗起球效果的莫代尔面料生产方法,它采用先酶预处理工艺和后抗起毛起球剂整理工艺,从而使面料手感更柔软和蓬松,其抗起毛起球性能更提高。
为了解决背景技术所存在的问题,本发明是采用以下技术方案:一种具有抗起球效果的莫代尔面料生产方法,包括酶预处理工艺和抗起毛起球剂整理工艺,所述酶预处理工艺包括:
(1)、用RUCOLASE ZER蚀毛酵素制备酶整理液,所述RUCOLASE ZER蚀毛酵素的体积百分比浓度为2-4%和15-20︰1的浴比配成整理液;
(2)、将准备好的所述莫代尔面料浸渍入所述酶整理液中,所述酶整理液的温度为55℃,浸渍时间为60分钟;
(3)、用柠檬酸或冰醋酸或果酸,酸度为1-3%,调节所述酶整理液的pH值至4.5~5.5的弱酸性;
(4)、将所述经酶整理液浸渍的莫代尔面料在50-60℃的水浴中处理30-60分钟,处理完后升温至80℃,再处理10~20分钟时间,使酶失去活性;
所述抗起毛起球剂整理工艺包括:
(5)、抗起毛起球整理液配方:每升水中加入14-18g多元羧酸,14-18g的CONDENSOL 康定素-FM催化剂;
(6)、将所述步骤(5)的整理液按浴比15-20︰1配置成整理溶液;
(7)、将所述经过酶预处理的莫代尔面料浸渍在所述步骤(6)整理溶液中,在40-50℃下整理20-30分钟,烘干后,还需在175℃高温下焙烘45~60秒,从而使整理织物的抗起毛起球性能提高。
本发明具有以下有益效果:由于在酶处理过程中,因纤维素酶分子比水分子要大1千倍以上,不能进入纤维的内部,所以只有接近纤维素纤维表面的β-1,4-葡萄糖苷键受到影响,织物表面的纤细纤维在生物降解和机械力作用的影响下脱落,得到了平滑的纤维表面。首先采用酶预处理工艺,面料经纤维素酶处理后,降低了起毛起球的趋势,纤维素酶在抛光过程中对面料进行了减量,抛光以后构成面料的纱线相对抛光之前变得更细,变细的纱线使纱线之间移动的空间更大,结果面料的手感变得比抛光前更柔软和蓬松;其次选用多元羧酸及催化剂为抗起毛起球整理剂,催化剂在焙烘时能促进多元羧酸的相邻羧基脱水成酸酐,利于酸与纤维素分子上羟基的酯化反应,与纤维交联反应更充分,从而使整理面料的抗起毛起球性能提高。
具体实施方式
实施例一
一种具有抗起球效果的莫代尔面料生产方法,包括酶预处理工艺和抗起毛起球剂整理工艺,所述酶预处理工艺包括:
(1)、用RUCOLASE ZER蚀毛酵素制备酶整理液,所述RUCOLASE ZER蚀毛酵素的体积百分比浓度为2%和15︰1的浴比配成整理液;
(2)、将准备好的所述莫代尔面料浸渍入所述酶整理液中,所述酶整理液的温度为55℃,浸渍时间为60分钟;
(3)、用柠檬酸或冰醋酸或果酸,酸度为1%,调节所述酶整理液的pH值至4.5的弱酸性;
(4)、将所述经酶整理液浸渍的莫代尔面料在50℃的水浴中处理30分钟,处理完后升温至80℃,再处理10分钟时间,使酶失去活性;
所述抗起毛起球剂整理工艺包括:
(5)、抗起毛起球整理液配方:每升水中加入14g多元羧酸,14g的CONDENSOL 康定素-FM催化剂;
(6)、将所述步骤(5)的整理液按浴比15︰1配置成整理溶液;
(7)、将所述经过酶预处理的莫代尔面料浸渍在所述步骤(6)整理溶液中,在40℃下整理20分钟,烘干后,还需在175℃高温下焙烘45秒,从而使整理织物的抗起毛起球性能提高。
实施例二
一种具有抗起球效果的莫代尔面料生产方法,包括酶预处理工艺和抗起毛起球剂整理工艺,所述酶预处理工艺包括:
(1)、用RUCOLASE ZER蚀毛酵素制备酶整理液,所述RUCOLASE ZER蚀毛酵素的体积百分比浓度为3%和18︰1的浴比配成整理液;
(2)、将准备好的所述莫代尔面料浸渍入所述酶整理液中,所述酶整理液的温度为55℃,浸渍时间为60分钟;
(3)、用柠檬酸或冰醋酸或果酸,酸度为2%,调节所述酶整理液的pH值至5的弱酸性;
(4)、将所述经酶整理液浸渍的莫代尔面料在55℃的水浴中处理50分钟,处理完后升温至80℃,再处理15分钟时间,使酶失去活性;
所述抗起毛起球剂整理工艺包括:
(5)、抗起毛起球整理液配方:每升水中加入16g多元羧酸,16g的CONDENSOL 康定素-FM催化剂;
(6)、将所述步骤(5)的整理液按浴比18︰1配置成整理溶液;
(7)、将所述经过酶预处理的莫代尔面料浸渍在所述步骤(6)整理溶液中,在45℃下整理25分钟,烘干后,还需在175℃高温下焙烘50秒,从而使整理织物的抗起毛起球性能提高。
实施例三
一种具有抗起球效果的莫代尔面料生产方法,包括酶预处理工艺和抗起毛起球剂整理工艺,所述酶预处理工艺包括:
(1)、用RUCOLASE ZER蚀毛酵素制备酶整理液,所述RUCOLASE ZER蚀毛酵素的体积百分比浓度为4%和20︰1的浴比配成整理液;
(2)、将准备好的所述莫代尔面料浸渍入所述酶整理液中,所述酶整理液的温度为55℃,浸渍时间为60分钟;
(3)、用柠檬酸或冰醋酸或果酸,酸度为3%,调节所述酶整理液的pH值至5.5的弱酸性;
(4)、将所述经酶整理液浸渍的莫代尔面料在60℃的水浴中处理60分钟,处理完后升温至80℃,再处理20分钟时间,使酶失去活性;
所述抗起毛起球剂整理工艺包括:
(5)、抗起毛起球整理液配方:每升水中加入18g多元羧酸,18g的CONDENSOL 康定素-FM催化剂;
(6)、将所述步骤(5)的整理液按浴比20︰1配置成整理溶液;
(7)、将所述经过酶预处理的莫代尔面料浸渍在所述步骤(6)整理溶液中,在50℃下整理30分钟,烘干后,还需在175℃高温下焙烘60秒,从而使整理织物的抗起毛起球性能提高。
最后说明的是,以上实施例仅用以说明本发明的技术方案而非限制,本领域普通技术人员对本发明的技术方案所做的其他修改或者等同替换,只要不脱离本发明技术方案的精神和范围,均应涵盖在本发明的权利要求范围当中。
Claims (1)
1.一种具有抗起球效果的莫代尔面料生产方法,包括酶预处理工艺和抗起毛起球剂整理工艺,其特征在于,所述酶预处理工艺包括:
(1)、用RUCOLASE ZER蚀毛酵素制备酶整理液,所述RUCOLASE ZER蚀毛酵素的体积百分比浓度为2-4%和15-20︰1的浴比配成整理液;
(2)、将准备好的所述莫代尔面料浸渍入所述酶整理液中,所述酶整理液的温度为55℃,浸渍时间为60分钟;
(3)、用柠檬酸或冰醋酸或果酸,酸度为1-3%,调节所述酶整理液的pH值至4.5~5.5的弱酸性;
(4)、将所述经酶整理液浸渍的莫代尔面料在50-60℃的水浴中处理30-60分钟,处理完后升温至80℃,再处理10~20分钟时间,使酶失去活性;
所述抗起毛起球剂整理工艺包括:
(5)、抗起毛起球整理液配方:每升水中加入14-18g多元羧酸,14-18g的CONDENSOL 康定素-FM催化剂;
(6)、将所述步骤(5)的整理液按浴比15-20︰1配置成整理溶液;
(7)、将所述经过酶预处理的莫代尔面料浸渍在所述步骤(6)整理溶液中,在40-50℃下整理20-30分钟,烘干后,还需在175℃高温下焙烘45~60秒,从而使整理织物的抗起毛起球性能提高。