CN102803539B - 面疲劳强度优异的气体渗碳钢部件、气体渗碳用钢材以及气体渗碳钢部件的制造方法 - Google Patents
面疲劳强度优异的气体渗碳钢部件、气体渗碳用钢材以及气体渗碳钢部件的制造方法 Download PDFInfo
- Publication number
- CN102803539B CN102803539B CN201180014915.2A CN201180014915A CN102803539B CN 102803539 B CN102803539 B CN 102803539B CN 201180014915 A CN201180014915 A CN 201180014915A CN 102803539 B CN102803539 B CN 102803539B
- Authority
- CN
- China
- Prior art keywords
- steel
- gas cementation
- gas
- quality
- carburizing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
Claims (13)