CN102774069A - 双金属复合装饰板及其制造方法 - Google Patents
双金属复合装饰板及其制造方法 Download PDFInfo
- Publication number
- CN102774069A CN102774069A CN2012102742469A CN201210274246A CN102774069A CN 102774069 A CN102774069 A CN 102774069A CN 2012102742469 A CN2012102742469 A CN 2012102742469A CN 201210274246 A CN201210274246 A CN 201210274246A CN 102774069 A CN102774069 A CN 102774069A
- Authority
- CN
- China
- Prior art keywords
- sheet material
- heating
- decorating board
- metal composite
- decorative plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种双金属复合装饰板,所述双金属复合装饰板有至少两层不同的金属板复合而成,包括基层和表面装饰层,所述基层为铝、铜、铁及其它们的合金之一所形成的板材,所述表面装饰层为贵金属所形成的板材,所述表面装饰板材复合在所述基层的上表面或下表面。本发明双金属复合装饰板及其制造方法,可以同时满足装饰和性能的要求,工艺简单,复合强度高,装饰效果好。
Description
技术领域
本发明涉及复合材料领域,特别是涉及一种双金属复合装饰板的制造方法。
背景技术
随着经济的发展以及社会的进步,物质文化水平随之提高,人们也越来越重视生活的质量,尤其对于家具和一些公共设施的装修的要求越来越高,不仅要求较好的装饰效果还需要有良好的性能。
因而亟需一种建筑装修用复合板,可同时满足装饰和性能的要求。
发明内容
本发明主要解决的技术问题是提供一种双金属复合装饰板及其制造方法,可以同时满足装饰和性能的要求,且复合强度高。
为解决上述技术问题,本发明采用的一个技术方案是:提供一种双金属复合装饰板,所述双金属复合装饰板有至少两层不同的金属板复合而成,包括基层和表面装饰层,所述基层为铝、铜、铁及其它们的合金之一所形成的板材,所述表面装饰层为贵金属所形成的板材,所述表面装饰板材复合在所述基层的上表面或下表面。
本发明的另一个目的是提供一种双金属复合装饰板的制造方法,具体步骤包括:
(100)、选材:按照要求选取基材和表面装饰板材;所述基材为铝、铜、铁及其它们的合金之一所形成的板材;所述表面装饰板材为贵金属所形成的板材;
(200)、挤压:将选取的所述表面装饰板材放置到所述基材的至少一个表面进行加压挤压,挤压压力为500-800Mpa,保持10-15S,形成初步复合的板材;
(300)、加热:将所述初步复合的板材进行加热并保温,形成加热复合的板材;
(400)、冷却:将所述加热复合的板材进行冷却,形成复合板;
(500)、雕刻:复合板的表面装饰层进行雕刻。
在本发明一个较佳实施例中,所述步骤(300)中加热温度为500-800℃,保温时间为2-3小时。
本发明的有益效果是:本发明双金属复合装饰板及其制造方法,可以同时满足装饰和性能的要求,工艺简单,复合强度高,装饰效果好。
附图说明
图1是本发明双金属复合装饰板一种优选实施例的结构示意图;
图2是本发明双金属复合装饰板另一种优选实施例的结构示意图;
图3是本发明双金属复合装饰板的制造方法一较佳实施例的流程示意图。
具体实施方式
下面结合附图对本发明的较佳实施例进行详细阐述,以使本发明的优点和特征能更易于被本领域技术人员理解,从而对本发明的保护范围做出更为清楚明确的界定。
如图1所示,本发明公开了一种双金属复合装饰板,所述双金属复合装饰板有至少两层不同的金属板复合而成,包括基层10和表面装饰层20,所述基层10为铝、铜、铁及其它们的合金之一所形成的板材,所述表面装饰层20为贵金属所形成的板材,所述表面装饰板材20复合在所述基层10的上表面。
如图2所示为本发明双金属复合装饰板的另一种实施例,与图1的主要区别在于所述表面装饰板材20复合在所述基层10的上表面和下表面。
如图3所示,本发明公开了一种双金属复合装饰板的制造方法,具体步骤包括:
(100)、选材:按照要求选取基材和表面装饰板材;所述基材为铝、铜、铁及其它们的合金之一所形成的板材;所述表面装饰板材为贵金属所形成的板材;
(200)、挤压:将选取的所述表面装饰板材放置到所述基材的至少一个表面进行加压挤压,挤压压力为500-800Mpa,保持10-15S,形成初步复合的板材;
(300)、加热:将所述初步复合的板材进行加热并保温,形成加热复合的板材;加热温度优选为500-800℃,保温时间优选为2-3小时。
(400)、冷却:将所述加热复合的板材进行冷却,形成复合板;
(500)、雕刻:复合板的表面装饰层进行雕刻。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书及附图内容所作的等效结构或等效流程变换,或直接或间接运用在其他相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (3)
1.一种双金属复合装饰板,其特征在于,所述双金属复合装饰板有至少两层不同的金属板复合而成,包括基层和表面装饰层,所述基层为铝、铜、铁及其它们的合金之一所形成的板材,所述表面装饰层为贵金属所形成的板材,所述表面装饰板材复合在所述基层的上表面或下表面。
2.一种双金属复合装饰板的制造方法,其特征在于,具体步骤包括:
(100)、选材:按照要求选取基材和表面装饰板材;所述基材为铝、铜、铁及其它们的合金之一所形成的板材;所述表面装饰板材为贵金属所形成的板材;
(200)、挤压:将选取的所述表面装饰板材放置到所述基材的至少一个表面进行加压挤压,挤压压力为500-800Mpa,保持10-15S,形成初步复合的板材;
(300)、加热:将所述初步复合的板材进行加热并保温,形成加热复合的板材;
(400)、冷却:将所述加热复合的板材进行冷却,形成复合板;
(500)、雕刻:复合板的表面装饰层进行雕刻。
3.根据权利要求1所述的双金属复合装饰板的制造方法,其特征在于,所述步骤(300)中加热温度为500-800℃,保温时间为2-3小时。