CN102773484A - 一种粉末冶金制球形止回阀阀体的方法 - Google Patents
一种粉末冶金制球形止回阀阀体的方法 Download PDFInfo
- Publication number
- CN102773484A CN102773484A CN2012102216410A CN201210221641A CN102773484A CN 102773484 A CN102773484 A CN 102773484A CN 2012102216410 A CN2012102216410 A CN 2012102216410A CN 201210221641 A CN201210221641 A CN 201210221641A CN 102773484 A CN102773484 A CN 102773484A
- Authority
- CN
- China
- Prior art keywords
- powder
- sintering
- valve body
- check valve
- powder metallurgy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种粉末冶金制球形止回阀阀体的方法,其特征在于包括有以下步骤:a、配混料,以电解铁粉为基质,其余组份的重量百分含量为:废回炉铁粉末30-40、铜粉1.2-1.8、硫化锰粉1.2-1.5、废铝粉4-5、二硫化钼0.2-0.6、铬粉1.2-1.5、石墨0.8-1.2、小于45微米阿克蜡2.2-2.6;b、压制成形:将配混均匀的粉末冶金材料送到压力机上用模具一次压制成形,就成形为止回阀阀体;本发明粉末冶金材料及制造工艺具有较高的生产连续性,且材料利用率高,适合于大批量生产,降低成本。
Description
技术领域
本发明涉及一种蝶阀阀杆的制备方法,具体属于一种粉末冶金制球形止回阀阀体的方法。
背景技术
目前,制备止回阀行业,国内的球形止回阀阀体均采用普通高速钢素材,或不锈钢素材通过机加工球形止回阀阀体。工速度较慢,材料利用率不高,而粉末冶金工艺制造,不仅材料利用率高,且适于大批量生产,在装配使用前需要对粉末冶金阀体进行少量精磨加工。
发明内容
本发明所要解决的技术问题是针对蝶阀阀杆工艺技术现状,而提供的一种生产效率高、制造成本较低的一种粉末冶金制球形止回阀阀体的方法。
本发明采用的技术方案如下:
一种粉末冶金制球形止回阀阀体的方法,其特征在于包括有以下步骤:
a、配混料:以电解铁粉为基质,其余组份的重量百分含量为:废回炉铁粉末30-40、铜粉1.2-1.8、硫化锰粉1.2-1.5、废铝粉4-5、二硫化钼0.2-0.6、铬粉1.2-1.5、石墨0.8-1.2、小于45微米阿克蜡2.2-2.6;
b、压制成形:将配混均匀的粉末冶金材料送到压力机上用模具一次压制成形,就成形为止回阀阀体;
c、烧结:将压制成形的零件送入粉末冶金烧结炉进行渗铜烧结,烧结温度为1100-1160℃,烧结时间为1-1.5小时;
d、淬火处理:将零件送入热处理炉中加热到850-870℃,并保温2-3小时;然后,用淬火油冷却;
e、回火处理:将淬火后的零件送入回火炉中加热到300-400℃,保温50-70min;
f、深冷处理:将回火后零件装入容器,加入液氮进行深冷处理,时间为10-12小时。
在步骤c中,将压制成形的零件送入粉末冶金烧结炉进行渗铜烧结,烧结温度为1140℃,烧结时间为1.3小时。
与现有技术相比,本发明的优点在于:
与现有高速钢素材或不锈钢素材机加工制造止回阀阀体相比,该粉末冶金材料及制造工艺具有较高的生产连续性,且材料利用率高,适合于大批量生产,降低成本,性能能满足正常使用需要。
具体实施方式
一种粉末冶金制球形止回阀阀体的方法,包括有以下步骤:
a、配混料:配混料:以电解铁粉为基质,其余组份的重量百分含量为:废回炉铁粉末40、铜粉1.8、硫化锰粉1.2、废铝粉4、二硫化钼0.5、铬粉1.2、石墨0.8、小于45微米阿克蜡2.25;
b、压制成形:将配混均匀的粉末冶金材料送到压力机上用模具一次压制成形,就成形为止回阀阀体;
c、烧结:将压制成形的零件送入粉末冶金烧结炉进行渗铜烧结,烧结温度为1140℃,烧结时间为1.3小时;
d、淬火处理:将零件送入热处理炉中加热到850-870℃,并保温2-3小时;然后,用淬火油冷却;
e、回火处理:将淬火后的零件送入回火炉中加热到300-400℃,保温50-70min;
f、深冷处理:将回火后零件装入容器,加入液氮进行深冷处理,时间为10-12小时。
最后经过车削加工得到成品。
Claims (2)
1.一种粉末冶金制球形止回阀阀体的方法,其特征在于包括有以下步骤:
a、配混料:以电解铁粉为基质,其余组份的重量百分含量为:废回炉铁粉末30-40、铜粉1.2-1.8、硫化锰粉1.2-1.5、废铝粉4-5、二硫化钼0.2-0.6、铬粉1.2-1.5、石墨0.8-1.2、小于45微米阿克蜡2.2-2.6;
b、压制成形:将配混均匀的粉末冶金材料送到压力机上用模具一次压制成形,就成形为止回阀阀体;
c、烧结:将压制成形的零件送入粉末冶金烧结炉进行渗铜烧结,烧结温度为1100-1160℃,烧结时间为1-1.5小时;
d、淬火处理:将零件送入热处理炉中加热到850-870℃,并保温2-3小时;然后,用淬火油冷却;
e、回火处理:将淬火后的零件送入回火炉中加热到300-400℃,保温50-70min;
f、深冷处理:将回火后零件装入容器,加入液氮进行深冷处理,时间为10-12小时。
2.根据权利要求1所述的粉末冶金制球形止回阀阀体的方法,其特征在于:
在步骤c中,将压制成形的零件送入粉末冶金烧结炉进行渗铜烧结,烧结温度为1140℃,烧结时间为1.3小时。