CN102745685A - 山茱萸果核制备活性炭工艺 - Google Patents
山茱萸果核制备活性炭工艺 Download PDFInfo
- Publication number
- CN102745685A CN102745685A CN201210248095XA CN201210248095A CN102745685A CN 102745685 A CN102745685 A CN 102745685A CN 201210248095X A CN201210248095X A CN 201210248095XA CN 201210248095 A CN201210248095 A CN 201210248095A CN 102745685 A CN102745685 A CN 102745685A
- Authority
- CN
- China
- Prior art keywords
- activated carbon
- skunk bush
- fruit stone
- 1mol
- bush fruit
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种山茱萸果核制备活性炭工艺，将阴干的山茱萸果核粉碎，过40目筛，按照液料质量比1.5～4.0：1称取山茱萸果核与浓度为40～65wt％的氯化锌溶液混合，充分搅拌后，超声波下浸渍2～12h，移至坩埚中，放置马弗炉里450～700℃活化60～120min，冷却，用1mol/L的盐酸溶液煮沸30min，继续用1mol/L的盐酸溶液反复清洗，再用热水洗涤至中性，最后将所得活性炭样品在120℃温度下干燥12h，粉碎过200目筛得产品，山茱萸果核作为山茱萸生产的副产物，用其制备活性炭不但拓宽了制备活性炭的来源途径，而且高质量的活性炭的制作，充分实现了山茱萸的生物质资源循环利用。
Description
技术领域
本发明属于活性炭技术领域，涉及活性炭的制备，具体涉及一种山茱萸果核制备活性炭工艺。
背景技术
山茱萸系山茱萸科山茱萸属小乔木或灌木，其成熟后的果实去核后又名山萸肉、药枣、枣皮等。山茱萸分布于北温带，亚热带的高山地区。主产于中国、日本、韩国、英国、美国等国家。在我国，主产于陕西、河南、浙江、山西、山东、四川、安微、甘肃等1O多个省。其中，陕西的秦巴山区是山茱萸的主要产地之一，年产量已突破100万Kg。目前对山茱萸果肉研究的比较多，而对其果核利用的研究相对较少，山茱萸的干燥果核，其重量约为果肉的1/3，大量坚硬的果核如得不到有效利用，就浪费了宝贵的生物质资源。
活性炭微孔发达、比表面积高、吸附能力强，是一种优良的吸附材料，广泛应用于化工、环保、食品与制药、催化剂载体和电极材料等领域。目前，国内外主要以煤炭、木材、城市固体有机废弃物、橡胶木锯末，椰子壳、咖啡豆壳、果壳、稻壳等材料作为原料生产活性炭的研究较多，其制备方法有高温炭化、水蒸气或烟道气活化法、化学炭化活化法等。采用不同的原料、不同的制备方法，其活性炭的性能有较大的差异。但以山茱萸果核为原料制备活性炭的研究尚未见相关报道。
发明内容
本发明提供了一种山茱萸果核制备活性炭工艺，包括以下步骤：
将阴干的山茱萸果核粉碎，过40目筛，按照液料质量比1.5～4.0：1称取山茱萸果核与浓度为40～65wt％的氯化锌溶液混合，充分搅拌后，在超声波条件下浸渍2～12h，移至坩埚中，放置马弗炉里450～700℃活化60～120min，冷却，用1mol/L的盐酸溶液煮沸30min后，继续用1mol/L的盐酸溶液反复清洗，再用热水洗涤至中性，最后将所得活性炭样品在120℃温度下干燥12h，粉碎过200目筛，即得到山茱萸果核活性炭产品。
优选氯化锌的浓度为50wt％。
优选山茱萸果核与氯化锌溶液的液料质量比为3.0:1。
优选超声波浸渍时间为4h。
优选活化温度600℃，活化时间120min。
山茱萸果核作为山茱萸生产的副产物，用其制备活性炭不但拓宽了制备活性炭的来源途径，而且高质量的活性炭的制作，充分实现了山茱萸的生物质资源循环利用。
具体实施方式
本发明所用的原材料：氯化锌，盐酸均为分析纯。
实施例1
将阴干的山茱萸果核粉碎，过40目筛，称取100g准备好的山茱萸果核与浓度40wt％的氯化锌溶液400g混合，充分搅拌后，在超声波条件下浸渍2h，移至坩埚中，放置在马弗炉里450℃烧制活化120min，冷却，活化得到的样品用1mol/L的盐酸溶液煮沸30min后，继续用1mol/L的盐酸溶液反复清洗，再用热水洗涤至中性，最后将所得活性炭样品在120℃温度下干燥12h，将试样粉碎过200目筛，即得到山茱萸果核活性炭产品。
实施例2
将阴干的山茱萸果核粉碎，过40目筛，称取100g准备好的山茱萸果核与浓度45wt％的氯化锌溶液300g混合，充分搅拌后，在超声波条件下浸渍4h，移至坩埚中，放置在马弗炉里500℃烧制活化100min，冷却，活化得到的样品用1mol/L的盐酸溶液煮沸30min后，继续用1mol/L的盐酸溶液反复清洗，再用热水洗涤至中性，最后将所得活性炭样品在120℃温度下干燥12h，将试样粉碎过200目筛，即得到山茱萸果核活性炭产品。
实施例3
将阴干的山茱萸果核粉碎，过40目筛，称取100g准备好的山茱萸果核与浓度50wt％的氯化锌溶液250g混合，充分搅拌后，在超声波条件下浸渍6h，移至坩埚中，放置在马弗炉里600℃烧制活化90min，冷却，活化得到的样品用1mol/L的盐酸溶液煮沸30min后，继续用1mol/L的盐酸溶液反复清洗，再用热水洗涤至中性，最后将所得活性炭样品在120℃温度下干燥12h，将试样粉碎过200目筛，即得到山茱萸果核活性炭产品。
实施例4
将阴干的山茱萸果核粉碎，过40目筛，称取100g准备好的山茱萸果核与浓度60wt％的氯化锌溶液200g混合，充分搅拌后，在超声波条件下浸渍9h，移至坩埚中，放置在马弗炉里650℃烧制活化80min，冷却，活化得到的样品用1mol/L的盐酸溶液煮沸30min后，继续用1mol/L的盐酸溶液反复清洗，再用热水洗涤至中性，最后将所得活性炭样品在120℃温度下干燥12h，将试样粉碎过200目筛，即得到山茱萸果核活性炭产品。
实施例5
将阴干的山茱萸果核粉碎，过40目筛，称取100g准备好的山茱萸果核与浓度65wt％的氯化锌溶液150g混合，充分搅拌后，在超声波条件下浸渍12h，移至坩埚中，放置在马弗炉里700℃烧制活化60min，冷却，活化得到的样品用1mol/L的盐酸溶液煮沸30min后，继续用1mol/L的盐酸溶液反复清洗，再用热水洗涤至中性，最后将所得活性炭样品在120℃温度下干燥12h，将试样粉碎过200目筛，即得到山茱萸果核活性炭产品。
实施例6
将阴干的山茱萸果核粉碎，过40目筛，称取100g准备好的山茱萸果核与浓度50wt％的氯化锌溶液300g混合，充分搅拌后，在超声波条件下浸渍4h，移至坩埚中，放置在马弗炉里600℃烧制活化120min，冷却，活化得到的样品用1mol/L的盐酸溶液煮沸30min后，继续用1mol/L的盐酸溶液反复清洗，再用热水洗涤至中性，最后将所得活性炭样品在120℃温度下干燥12h，将试样粉碎过200目筛，即得到山茱萸果核活性炭产品。
山茱萸果核作为山茱萸生产的副产物，用其制备活性炭不但拓宽了制备活性炭的来源途径，而且高质量的活性炭的制作，充分实现了山茱萸的生物质资源循环利用。
Claims (5)
1.一种山茱萸果核制备活性炭工艺，包括以下步骤：
将阴干的山茱萸果核粉碎，过40目筛，按照液料质量比1.5～4.0：1称取山茱萸果核与浓度为40～65wt％的氯化锌溶液混合，充分搅拌后，在超声波条件下浸渍2～12h，移至坩埚中，放置马弗炉里450～700℃活化60～120min，冷却，用1mol/L的盐酸溶液煮沸30min后，继续用1mol/L的盐酸溶液反复清洗，再用热水洗涤至中性，最后将所得活性炭样品在120℃温度下干燥12h，粉碎过200目筛，即得到山茱萸果核活性炭产品。
2.根据权利要求1所述的山茱萸果核制备活性炭工艺，其特征在于：所述的氯化锌的浓度为50wt％。
3.根据权利要求1所述的山茱萸果核制备活性炭工艺，其特征在于：所述的山茱萸果核与氯化锌溶液的液料质量比为3.0:1。
4.根据权利要求1所述的山茱萸果核制备活性炭工艺，其特征在于：所述的超声波浸渍时间为4h。
5.根据权利要求1所述的山茱萸果核制备活性炭工艺，其特征在于：所述的活化温度为600℃，活化时间为120min。