CN102731062B - 一种电容器瓷套的配方 - Google Patents
一种电容器瓷套的配方 Download PDFInfo
- Publication number
- CN102731062B CN102731062B CN2012101955947A CN201210195594A CN102731062B CN 102731062 B CN102731062 B CN 102731062B CN 2012101955947 A CN2012101955947 A CN 2012101955947A CN 201210195594 A CN201210195594 A CN 201210195594A CN 102731062 B CN102731062 B CN 102731062B
- Authority
- CN
- China
- Prior art keywords
- raw materials
- parts
- porcelain
- soil
- ninghai
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明涉及一种电容器用瓷套的瓷材料配方。现有电容器瓷套的配方原料含量稀少、取用不便,导致配方成本较高。本发明的电容器瓷套由以下重量份的原料组分制成:后溪瓷土 9.2-10.2 份、广东白6.0-7.5份、叶腊石4.2-4.8 份、左云土3.2-3.7份、铝矾土粉1.5-1.8 份、宁海土1.0-1.3份、长石粉1.0份。本发明所需的各项原料中30%取自江浙一带的本地瓷土,15%取用的是本地的石蜡,还有少部分源自浙江宁海的粘土,剩余原料均是常用的粘土、矾土和长石等。因此,各类原料蕴藏丰富、取用方便、成本较低,制出的瓷套产品性能达到且优于相应指标。
Description
技术领域
本发明涉及一种电容器用瓷套的瓷材料配方。
背景技术
现有电容器瓷套的配方主要由铝矾土、长石粉、绢云母类瓷土、左云土、高性能球土、漳州黑泥等高可塑性的粘土组成,其中绢云母瓷土矿藏类主要集中江西西部、湖南等地,粘土类矿物也绝大多数在北方或华南,由于主要配方的分布地分散,且原料含量稀少、取用不便,导致配方成本较高。
发明内容
本发明针对现有技术存在的缺陷,提供一种电容器瓷套的配方,各原材料取材方便,成本较低,制出的电容器瓷套满足JB/T 11052-2010《电容器用压嵌式绝缘套管技术条件》的各项机械及电性能指标。
为此,本发明采取如下技术方案:所述电容器瓷套由以下重量份的原料组分制成:
所述的后溪瓷土中主要包含有SiO2、Al2O3和K2O,其中SiO2、Al2O3和K2O所占的百分含量分别是76%、14%、4.5%;所述的宁海土中主要包含有SiO2、Al2O3,其中SiO2、Al2O3所占的百分含量分别是57%、24%、4%。
所述后溪瓷土主要矿物成分为:石英、伊利石、高岭土、钾长石。
所述宁海土主要矿物成为:高岭土、石英、少量蒙脱石,具有良好的可塑性及较高的干燥度。
本发明所需的各项原料中30%取自江浙一带的本地瓷土,15%取用的是本地的石蜡,还有少部分源自浙江宁海的粘土,剩余原料均是常用的粘土、矾土和长石等。因此,各类原料蕴藏丰富、取用方便、成本较低,制出的瓷套产品性能达到且优于相应指标。
具体实施方式
下面通过实施例,对本发明的技术方案作进一步具体说明(各组分的含量以千克为单位)
实施例1:
实施例2:
实施例3:
其中后溪瓷土主要矿物成分为:石英、伊利石、高岭土、钾长石、白云母。宁海土主要矿物成为:高岭土、石英、蒙脱石。后溪瓷土和宁海土中均包含SiO2、Al2O3、Fe2O3、TiO2、MgO、CaO、K2O、Na2O,其中后溪瓷土中SiO2、Al2O3、Fe2O3、K2O所占百分比分别为76%、14%、1%、4.7%,宁海土中SiO2、Al2O3和Fe2O3所占百分比分别是57%、24%、4%。
本发明采用湿法成型,工艺流程如下:配料→球磨→榨泥→陈腐→练泥→成型→烘房干燥→窑炉烧成→组装→检测。
采用本配方生产的瓷套产品,主要有6伞、10伞、13伞电容器瓷套,经检测其主要性能指标如下:
经孔隙性试验:压力应不小于20Mpa,压力与时间(h)的乘积不小于180Mpa.h,且无渗透现象。
需要特别指出的是,上述实施例的方式仅限于描述实施例,但本发明不止局限于上述方式,且本领域的技术人员据此可在不脱离本发明的范围内方便的进行修饰,因此本发明的范围应当包括本发明所揭示的原理和新特征的最大范围。
Claims (1)
1.一种电容器瓷套,其特征在于所述电容器瓷套由以下原料组分制成:
后溪瓷土 335kg 广东白泥 260kg
叶腊石 165kg 左云土 130kg
矾土粉 60kg 宁海土 35kg
长石粉 35kg
其中后溪瓷土主要矿物成分为:石英、伊利石、高岭土、钾长石、白云母,宁海土主要矿物成分为:高岭土、石英、蒙脱石,后溪瓷土和宁海土中均包含SiO2、Al2O3、Fe2O3、TiO2、MgO、CaO、K2O、Na2O,其中后溪瓷土中SiO2、Al2O3、Fe2O3、K2O所占百分比分别为76%、14%、1%、4.7%,宁海土中SiO2、Al2O3和Fe2O3所占百分比分别是57%、24%、4%。