CN104163616A - 一种绢云母质日用炻瓷低温坯料配方 - Google Patents

一种绢云母质日用炻瓷低温坯料配方 Download PDF

Info

Publication number
CN104163616A
CN104163616A CN201410391609.6A CN201410391609A CN104163616A CN 104163616 A CN104163616 A CN 104163616A CN 201410391609 A CN201410391609 A CN 201410391609A CN 104163616 A CN104163616 A CN 104163616A
Authority
CN
China
Prior art keywords
stoneware
porcelain
sericite
daily use
low
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201410391609.6A
Other languages
English (en)
Other versions
CN104163616B (zh
Inventor
汪平和
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201410391609.6A priority Critical patent/CN104163616B/zh
Publication of CN104163616A publication Critical patent/CN104163616A/zh
Application granted granted Critical
Publication of CN104163616B publication Critical patent/CN104163616B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种利用绢云母质瓷石代替长石，石英和部分高岭土，生产日用炻瓷的坯料配方。属于日用陶瓷技术领域。技术方案表现为：以质量50-70%的瓷石，配以30-50%的耐火粘土，并加入少量的矿化剂组成的坯料，生产日用炻瓷。解决了传统配方中大量使用高岭土、瓷土和长石造成的资源短缺,成本高等问题。充分利用了储量丰富、质量稳定、成本低廉的瓷石。该配方配料成本低；使用性能好；可低温快速烧成；节约能源。具有明显的经济效益和社会效益,可在炻瓷行业中广泛推广应用。

Description

一种绢云母质日用炻瓷低温坯料配方
技术领域
本发明涉及一种绢云母质日用炻瓷低温坯料配方,属于日用陶瓷技术领域。
背景技术
炻瓷、系介于陶器和瓷器之间的一类陶瓷制品，通常也称炻器。用于日用陶瓷器皿餐茶具和工艺美术陶瓷的生产。
到目前为止，日用炻瓷坯料主要有二大类型：一类是以长石为熔剂的（长石-石英-高岭土）型，第二类是以钠长石为熔剂的（钠长石-石英-高岭土）型。两种坯料各有其优缺点，第一类烧成温度偏高，燃料耗费较多；第二类烧成温度范围不宽，热稳定性较差，产品强度不高。
炻瓷产品在国外十分流行，在国际货易上已超过瓷器，占有很大比重，国内已大量生产出口二十多年。
由于炻瓷产品比较厚重，加上长年生产，原料耗用巨大、矿山日渐枯竭、供应紧张、价格攀升、成本上涨。寻找替代原料是目前炻瓷行业面临的紧迫问题。
绢云母质瓷石(简称瓷石)是一种传统的制瓷原料，化学成分与长石相比。K 2 O, Na 2 O和AI 2 O 3 较低，而SiO 2 含量较高，因而熔融温度较长石高。在现有技术中，一般以瓷石与高岭土配料来生产瓷器。它是以瓷石中的绢云母类矿物作为熔剂的(绢云母-石英-高岭土)***瓷，简称绢云母质瓷。
瓷石作为制瓷原料使用，有着十分悠久的历史。产地很多，储量丰富。成份稳定也是它的一大特色。
但是将瓷石作为制作炻瓷的主要原料，特别是用于低温烧成的坯料，还未见报道和实例。
本发明的目的，就是要研制一种能大量应用瓷石的低温炻瓷配方，拓宽炻瓷原料来源，降低生产成本。
发明内容
 本发明要解决的技术问题，是针对现有技术的弱点，提供一种能适应低温快速烧成，热稳定好、强度高，同时能与现有各种颜色的釉料相匹配的炻瓷坯料配方。
解决上述问题采取以下技术方案，针对瓷石中的AI 2 O 3 较低，加入耐火粘土，针对烧成温度较高加入海泡石，
本发明的技术要点是:
   1、以瓷石代替现有配方中的全部长石，全部石英和部分高岭土，以耐火粘土代替剩余部分的高岭土。以海泡石作为矿化剂所组成的坯料制造日用炻瓷，
2、试验研究配方中各组份的适当比例和允许范围。
海泡石是一种镁质耐火粘土，在历史上用于制作匣钵。坯料中加入少量海泡石，能降低坯料烧成温度，在较低温度下形成液相，加速莫来石的生成，提高制品的机械强度。同时还能形成一部分堇青石，降低坯料的膨胀系数, 促进坯与釉的结合，改善制品的耐急热变性能。提高热稳定性。
矿化剂的种类可以是海泡石型镁质粘土、滑石和白云石。种类的选择可以根据货源和成本等因素来确定。
采用本发明提供的绢云母质炻瓷低温坯料配方生产炻瓷时,生产工艺与现有的生产工艺相同。
本发明的优点是:
1、充分地利用了资源,缓解了炻瓷原料供应紧张、成本很高的矛盾。(
坯料成本降低了50-60%)
2、克服了现有配方的弱点,可快速烧成,节约能源，
3、配方简单、稳定、操作性能好、产品合格率高，
4、产品热稳定性好,强度高，
具体实施方式。
通过多次反复实验得出，下列各组份的范围适合制作低温日用炻瓷，
瓷石50%-70%     耐火粘土30%-50%     海泡石0.5%-6%
   化学组成范围:
 SiO 2  65.00-70.00%      AI 2 O 3  18.00-25.00%    Fe 2 O 3  0.70-1.00%   TiO 2  0.10-0.15%
 CaO 0.50-0.90%  MgO 1.00-1.20%  K 2 O 3.60-3.80%   Na 2 O 0.20-0.30%
   其中最关键组成为:
                  MgO   AI 2 O 3    SiO 2    
本发明的一个实施例:适合烧成温度为1160-1185℃
瓷石 68%  耐火粘土30%  镁质粘土2%
化学成份:
瓷石化学组成:
瓷石的矿物组成:
样品经热分析,X射线衍射和电子显微镜,偏光显微镜观察结论基本一致,证明矿物组成主要是石英和高岭石,次为云母,并含有少量的残余长石。
瓷石的颗粒组成:
瓷石的各项物理性能:
本发明试验的耐火粘土化学成份:
海泡石化学成份:

Claims (3)

1.一种绢云母质日用炻瓷低温坯料配方,其特征是以瓷石为主料(瓷石的质量小于或等于坯料总质量的70%（以50%-70%为宜)、耐火粘土 30%-50%和0.5-6%矿化剂组成。
2. 根据权利要求书1所述的绢云母质炻瓷，其特征在于坯料的化学组成为:
SiO2 65.00-70.00      AI2O3 18.00-25.00     Fe2O3 0.80-1.00    TiO2 0.10-0.30 
CaO 0.50-0.70  MgO 1.00-1.20   K2O 3.60-3.80    Na2O 0.20-0.30
其中最关键组成为：MgO、AI2O3、SiO2 。
3.根据权利要求书1所述的绢云母质炻瓷坯料配方其中的矿化剂为海泡石型镁质粘土，也可以是滑石、白云石。
CN201410391609.6A 2014-08-11 2014-08-11 一种绢云母质日用炻瓷低温坯料配方 Active CN104163616B (zh)