CN102642842A - 一种用酸性硅溶胶制备二氧化硅气凝胶的方法 - Google Patents
一种用酸性硅溶胶制备二氧化硅气凝胶的方法 Download PDFInfo
- Publication number
- CN102642842A CN102642842A CN201210123519XA CN201210123519A CN102642842A CN 102642842 A CN102642842 A CN 102642842A CN 201210123519X A CN201210123519X A CN 201210123519XA CN 201210123519 A CN201210123519 A CN 201210123519A CN 102642842 A CN102642842 A CN 102642842A
- Authority
- CN
- China
- Prior art keywords
- gel
- acidic silicasol
- aerosil
- preparation
- sio
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种用酸性硅溶胶制备二氧化硅气凝胶的方法,属于无机绝热材料制备领域,本发明以酸性硅溶胶为原料,在酸、碱催化剂的作用下直接形成凝胶,制备凝胶过程中不涉及有机溶剂提高其生产的安全性,经溶剂置换、表面甲硅烷基化后,通过超临界或常压干燥制得SiO2气凝胶。本发明在凝胶过程中避免了以有机硅为原料制备溶胶的过程以及水玻璃除盐的复杂工艺,以成本低廉、性能稳定的酸性硅溶胶为原料,工艺简单、生产周期短、反应过程可控、设备要求及投入低,可实现SiO2气凝胶的工业化生产。
Description
技术领域:
本发明属于无机绝热材料制备领域,特别涉及一种以酸性硅溶胶为原料制备纳米多孔二氧化硅气凝胶的方法。
背景技术:
二氧化硅(SiO2)气凝胶是一种轻质多孔材料,美国宇航局科学家研制出密度仅为3kg/m3 的气凝胶,作为世界最轻的固体,已入选吉尼斯世界纪录。其独特的三维网络结构、气体分散介质以及纳米量级的固体相和孔隙结构使其具有独特的物理化学性质,如:在固体材料中它的密度最低、热导热最小(室温真空热导率可降低至0.001W/m·K)、声传递速度最低、孔隙率最高(可达99.8%),比表面积较高(可达1000m2/g)、热稳定性好等等。因此作为隔热保温材料可用于建筑墙材、保温窗、太阳能集热器、太阳能房子和航天器上理想的隔热层等;在光学方面的应用可用于制造特殊环境使用的透镜、Cerenkov探测器;在电学方面可作为双层电化学电容器和高效可充电电池的电极材料;另外在声学、催化医学和生命科学等领域都表现出很好的应用价值。因此,制备SiO2气凝胶及其复合材料引起了世界科学家们极大的兴趣。
目前,最常见的SiO2气凝胶一般采用溶胶—凝胶工艺结合超临界干燥或常压干燥方法制备。如专利EP-A-0396076、WO92/03378、WO94/25149、WO92/20623、CN1557778中已公开。这些方法存在原料非常昂贵,且具有毒性,工艺复杂,安全性低等问题严重制约了SiO2气凝胶的规模化生产和应用。
为降低成本,研究人员往往采用成本低廉的水玻璃或硅溶胶为原料制备SiO2气凝胶。专利EP-A-0658513、CN1636871B以水玻璃为起始原料,借助离子交换树脂去除高浓度的钠或钾离子,然后通过加入碱缩聚成凝胶,经有机溶剂置换、表面甲硅烷基化后制得SiO2气凝胶。专利CN1241953B采用水玻璃水解法制备凝胶,然后用热水反复洗涤所得的凝胶,再通过有机溶剂置换和表面甲硅烷基化反应后常压制得SiO2气凝胶。CN101844771AA公开了以硅酸钠水溶液为硅源,用浓盐酸调节pH值到1,在50℃环境中静置凝胶,然后依次用去离子水、乙醇、正己烷和体积比为20%的正己烷和三甲基氯硅烷的混合溶液各处理24h,最后在150℃下干燥,得到SiO2气凝胶。此类方法操作繁琐,生产周期长,且制备工艺中会产生的大量含盐废水。
由于工业水玻璃中含有较多杂质,为避免干扰,研究人员采用硅溶胶为原料制备SiO2气凝胶。例如专利CN101468798A以胶体粒径在8nm左右或更低的硅溶胶为硅源,与体积比为硅溶胶5-50倍的醇或酮或醇酮混合体中形成预聚体,密封容器于100-200℃条件下脱水凝胶,并老化3-15天形成湿凝胶,敞开密封盖于30-80℃下干燥形成超低密度SiO2气凝胶,将该凝胶于400-500℃维持1-3小时纯化气凝胶。此方法对硅溶胶粒径要求严格,生产周期长,设备要求高,能耗大,不适合工业大规模生产。专利CN1724354A利用硅溶胶、乙醇、硝酸混匀得醇凝胶,在 50℃下恒温12-24h老化后,用无水乙醇浸泡1-2次,然后用浓度为80%的乙醇浸泡24h,再用体积比为1:1的正硅酸乙酯和乙醇的混合液浸泡48h,所得凝胶置于70℃恒温干燥72h制得硅气凝胶,然后用硝酸铁溶液浸泡来提高气凝胶的热稳定性。此方法通过在硅溶胶中加入乙醇制得醇凝胶,但在凝胶后仍需用不同浓度的乙醇溶液浸泡所得凝胶,对工业化生产来说,过程繁琐,且制备凝胶过程中引入有机溶剂,增加了对设备的密闭性、防爆性、防静电等要求,不仅增加了成本也增加了生产的危险性。
发明内容:
本发明的目的在于提供一种制备成本低,工艺简单,反应条件容易且可控,周期短的SiO2气凝胶制备方法。
本发明采取的技术方案如下,一种用酸性硅溶胶制备二氧化硅气凝胶的方法,其特征在于,包括以下步骤:
⑴、凝胶的制备:
将酸性硅溶胶加水稀释成硅溶胶水溶液,加碱调节硅溶胶水溶液pH 为9.0-11.5,然后加酸使溶胶缩聚成为SiO2水凝胶,在温度0-90℃下陈化0-72h。
步骤⑴中:
所述酸性硅溶胶为工业级原料,pH为2.0-4.0,密度为25℃下1.10-1.21g/cm3,SiO2含量15%-31%,NaO的含量为0-0.06%,SiO2胶粒的粒径集中在9-20nm之间;
所述加碱调节硅溶胶水溶液pH为9.0-11.5,优选pH值10.0-11.4;所述的碱为NaOH、NH3·H2O、KOH、CaOH、LiOH、硅酸钠溶液、硅酸钾溶液、硅酸锂溶液的至少一种。
所述加酸使溶胶缩聚成为SiO2水凝胶,直至凝胶pH值为5.0-8.5,优选pH值6.0-8.0,所述的酸为HCl、H2SO4、HNO3、H3PO4、HF、HBr、H2SeO4、HClO4、H2SO3中的至少一种,
所述加酸使溶胶缩聚成为SiO2水凝胶,优选在室温或30-90℃温度下,15s-48h形成凝胶。
所述的陈化,优选室温或30-90℃温度下陈化0-72h,特别优选优选温度60-80℃下陈化0.5-10h。
⑵、溶剂置换:
采用有机溶剂置换步骤⑴中陈化后的水凝胶,直到凝胶中的含水量≤50 wt %。
所述有机溶剂为醇、醚、酯、酮、脂族或芳族烃中的至少一种,优选乙醇、甲醇、丙酮、正己烷或环己烷。
⑶、表面甲硅烷基化处理:
将步骤⑵中所得到的凝胶进行表面甲硅烷基化处理,以获得疏水表面。
所述表面甲硅烷基化处理采用甲硅烷基化试剂R14-nSiCln、R14-nSi(OR2)n或R3Si-N(H)-SiR3,上述R14-nSiCln、R14-nSi(OR2)n、R3Si-N(H)-SiR3式中:n=1~3,R1、R2和R3相互独立、相同或不同,各表示氢原子或非活性有机直链、直链、支链、环状饱和或不饱和芳族或杂芳族基团,甲硅烷基化试剂特别优选三甲基氯硅烷或六甲基二硅氮烷。
⑷、超临界或常压干燥:
将步骤⑵或⑶所得到的凝胶进行超临界干燥或常压干燥直至形成气凝胶。
步骤⑷中:常压干燥温度为50℃-200℃,超临界干燥溶剂为二氧化碳、乙醇、丙酮、甲醇、正丙醇、苯、丁醇、戊醇、辛烷中的任意一种,优选二氧化碳或乙醇。
本发明与现有技术相比,具有以下优点:
1、本发明的制备成本低,工艺简单。由于本发明选用的原料为酸性硅溶胶,该硅溶胶在6个月内能稳定存在,省去了使用有机硅(如正硅酸甲酯、正硅酸乙酯、多聚硅氧烷)原料制备湿凝胶所必需经历的水解过程,更加有利于湿凝胶结构的控制,从而使本发明的SiO2气凝胶的制取变得更加容易。同时由于酸性硅溶胶来源极为广泛,国内生产技术极为成熟,产品稳定,性能良好,价格低廉,且原料中的二氧化硅的含量可高达31%,所以本发明以酸性硅溶胶为原料制备SiO2气凝胶的工艺与目前采用有机硅(如正硅酸甲酯、正硅酸乙酯、多聚硅氧烷)为原料的工艺相比,操作条件更加简化,制备效率大大提高,产品成本明显降低。
2、本发明使用的酸性硅溶胶为纳米级的二氧化硅颗粒在水中的分散液,无臭、无毒,减少对人体健康及环境污染的影响。
3、本发明在溶胶-凝胶的过程中未使用有机溶剂,不存在有机溶剂挥发问题,工业化生产中设备要求及投入低,既降低成本又提高生产的安全性。
4、本发明与传统的水玻璃制备SiO2气凝胶工艺相比,避免了用离子交换树脂处理水玻璃溶液的过程,或是水玻璃水解法制备凝胶后反复水洗除盐的过程,提高了工作效率,减少了工艺流程。
5、本发明反应条件容易且可控,周期短。通过在酸、碱催化条件下,迅速发生缩聚反应制得湿凝胶,从而大大缩短了凝胶的制取时间。
6、本发明方法制得的SiO2气凝胶,经测试分析表明,SiO2气凝胶的密度在0.04-0.3g/cm3之间可控,比表面积在400-800m2/g,平均孔径10-70nm,室温下,水在气凝胶表面的接触角可达121-145°。
下面通过实施例进一步描述本发明。
具体实施方式:
实施例1:
取二氧化硅含量为30%(wt)的酸性硅溶胶100ml盛于1000ml烧杯中,量取300ml水加入烧杯中对酸性硅溶胶进行稀释,常温充分搅拌后,以2mol/L的NaOH溶液缓慢滴入配置好的硅溶胶水溶液中,边滴加边搅拌,直至硅溶胶水溶液pH值达到11.0,然后以2mol/L的H2SO4溶液滴定硅溶胶水溶液,边滴加边搅拌,直至pH值达到7.0,将滴加好的溶液置于70℃水浴中,3.5h后溶液形成水凝胶,继续在60℃水浴氛围老化2h,将凝胶取出,置于95%(wt)乙醇中置换,乙醇与水凝胶的体积比为5:1,置换温度为60℃,置换时间为3h,总共置换3次,得到醇凝胶,通过二氧化碳超临界干燥,即得亲水性SiO2气凝胶。
实施例2:
取二氧化硅含量为30%(wt)的酸性硅溶胶100ml盛于1000ml烧杯中,量取200ml水加入烧杯中对酸性硅溶胶进行稀释,常温充分搅拌后,以10%(wt)的硅酸钠溶液缓慢滴入配置好的硅溶胶水溶液中,边滴加边搅拌,直至硅溶胶水溶液pH值达到10.8,然后以2mol/L的HCl溶液滴定硅溶胶水溶液,边滴加边搅拌,直至pH值达到7.05,将滴加好的溶液置于60℃水浴中,1min后溶液形成水凝胶,继续在60℃水浴氛围老化2h,将凝胶取出,置于95%(wt)乙醇中置换,乙醇与水凝胶的体积比为5:1,置换温度为60℃,置换时间为3h,置换2次,将凝胶取出放入三甲基氯硅烷溶液进行表面甲基化处理,60℃浸泡3h,通过乙醇超临界干燥,即得疏水性SiO2气凝胶。
实施例3:
取二氧化硅含量为30%(wt)的酸性硅溶胶50ml盛于1000ml烧杯中,量取200ml水加入烧杯中对酸性硅溶胶进行稀释,常温充分搅拌后,以10%(wt)的硅酸钠溶液缓慢滴入配置好的硅溶胶水溶液中,边滴加边搅拌,直至硅溶胶水溶液pH值达到9.7,然后以3mol/L的H2SO4溶液滴定硅溶胶水溶液,边滴加边搅拌,直至pH值达到6.15,将滴加好的溶液置于60℃水浴中,12min后溶液形成水凝胶,继续在60℃水浴氛围老化2.5h,将凝胶取出,置于95%(wt)乙醇中置换,乙醇与水凝胶的体积比为5:1,置换温度为60℃,置换时间为3h,置换1次,将凝胶取出放入三甲基氯硅烷溶液进行表面甲基化处理,60℃浸泡3h后,置于100℃下常压干燥2h,即得疏水性SiO2气凝胶。
实施例4:
将实施例1-3制得的SiO2气凝胶进行测试分析如下表所示。
表1、本发明制备的SiO2气凝胶性能表。
Claims (10)
1.一种用酸性硅溶胶制备二氧化硅气凝胶的方法,其特征在于,包括以下步骤:
⑴、凝胶的制备:
将酸性硅溶胶加水稀释成硅溶胶水溶液,加碱调节硅溶胶水溶液pH 为9.0-11.5,然后加酸使溶胶缩聚成为SiO2水凝胶,在温度0-90℃下陈化0-72h;
⑵、溶剂置换:
采用有机溶剂置换步骤⑴中陈化后的水凝胶,直到凝胶中的含水量≤50 wt %;所述有机溶剂为醇、醚、酯、酮、脂族或芳族烃中的至少一种;
⑶、表面甲硅烷基化处理:
将步骤⑵中所得到的凝胶进行表面甲硅烷基化处理,以获得疏水表面;
⑷、超临界或常压干燥:
将步骤⑶得到的凝胶进行超临界干燥或常压干燥直至形成气凝胶。
2.一种用酸性硅溶胶制备二氧化硅气凝胶的方法,其特征在于,包括以下步骤:
⑴、凝胶的制备:
将酸性硅溶胶加水稀释成硅溶胶水溶液,加碱调节硅溶胶水溶液pH 为9.0-11.5,然后加酸使溶胶缩聚成为SiO2水凝胶,在温度0-90℃下陈化0-72h;
⑵、溶剂置换:
采用有机溶剂置换步骤⑴中陈化后的水凝胶,直到凝胶中的含水量≤50 wt %;所述有机溶剂为醇、醚、酯、酮、脂族或芳族烃中的至少一种;
⑶、超临界或常压干燥:
将步骤⑵得到的凝胶进行超临界干燥或常压干燥直至形成气凝胶。
3.根据权利要求1或2所述的一种用酸性硅溶胶制备二氧化硅气凝胶的方法,其特征在于,所述凝胶的制备:酸性硅溶胶为工业级原料,pH为2.0-4.0,密度为25℃下1.10-1.21g/cm3,SiO2含量15%-31%,NaO的含量为0-0.06%,SiO2胶粒的粒径集中在9-20nm之间。
4.根据权利要求1或2所述的一种用酸性硅溶胶制备二氧化硅气凝胶的方法,其特征在于,所述凝胶的制备:加碱调节硅溶胶水溶液pH为9.0-11.5,所述的碱为NaOH、NH3·H2O、KOH、CaOH、LiOH、硅酸钠溶液、硅酸钾溶液、硅酸锂溶液的至少一种。
5.根据权利要求1或2所述的一种用酸性硅溶胶制备二氧化硅气凝胶的方法,其特征在于,所述凝胶的制备:加酸使溶胶缩聚成为SiO2水凝胶,直至凝胶pH值为5.0-8.5,所述的酸为HCl、H2SO4、HNO3、H3PO4、HF、HBr、H2SeO4、HClO4、H2SO3中的至少一种。
6.根据权利要求1或2所述的一种用酸性硅溶胶制备二氧化硅气凝胶的方法,其特征在于,所述凝胶的制备:加酸使溶胶缩聚成为SiO2水凝胶,在室温或30-90℃温度下,15s-48h形成凝胶。
7.根据权利要求1或2所述的一种用酸性硅溶胶制备二氧化硅气凝胶的方法,其特征在于,所述凝胶的制备:在温度60-80℃下陈化0.5-10h。
8.根据权利要求1或2所述的一种用酸性硅溶胶制备二氧化硅气凝胶的方法,其特征在于,所述溶剂置换:有机溶剂为乙醇、甲醇、丙酮、正己烷或环己烷。
9.根据权利要求1所述的一种用酸性硅溶胶制备二氧化硅气凝胶的方法,其特征在于:所述表面甲硅烷基化处理中,甲硅烷基化试剂为三甲基氯硅烷或六甲基二硅氮烷。
10.根据权利要求1或2所述的一种用酸性硅溶胶制备二氧化硅气凝胶的方法,其特征在于:所述超临界或常压干燥:常压干燥温度为50℃-200℃,超临界干燥溶剂为二氧化碳、乙醇、丙酮、甲醇、正丙醇、苯、丁醇、戊醇、辛烷中的任意一种。