CN102584113A - Preparation method of novel diatom mud environment-friendly interior wall coatings - Google Patents
Preparation method of novel diatom mud environment-friendly interior wall coatings Download PDFInfo
- Publication number
- CN102584113A CN102584113A CN2012100642292A CN201210064229A CN102584113A CN 102584113 A CN102584113 A CN 102584113A CN 2012100642292 A CN2012100642292 A CN 2012100642292A CN 201210064229 A CN201210064229 A CN 201210064229A CN 102584113 A CN102584113 A CN 102584113A
- Authority
- CN
- China
- Prior art keywords
- preparation
- orders
- parts
- interior wall
- diatom ooze
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a preparation method of novel diatom mud environment-friendly interior wall coatings. The preparation method comprises the following steps of: firstly preparing the following materials in parts by weight: 20 of diatomite (325 meshes), 8 of adhesive powder, 0.6 of methyl cellulose, 7 of talc powder (700 to 900 meshes), 15 of calcium carbonate powder (400 to 600 meshes), 10 of quartz sand (20 to 90 meshes), 10 of kaolin (750 to 850 meshes), 2 of attapulgite powder (550 to 750 meshes), 2 of titanium dioxide powder, 10 of ash calcium (550 to 650 meshes), 14.7 of r heavy calcium carbonate (1200 to 1300 meshes), 0.4 of wood fibers and 0.3 of staple fibers; loading the above materials into a horizontal high-speed dispersion machine according to the given ratio; and dispersing uniformly. The preparation method provided by the invention can produce novel interior wall coatings which are free of VOC (volatile organic compounds), temperature-resistant, fire-proof and wear-resistant and have stable performances, and a long useful service life.
Description
Technical field
The present invention relates to coating and make the field, relate in particular to a kind of preparation method of novel diatom ooze environment-friendly interior wall coating.
Background technology
Present decorative material for internal wall on the market is mainly aqueous emulsion paint, is rubber-emulsion paint again, is divided into two big types of polyvinyl acetate emulsion and ACRYLIC EMULSIONs; The interior wall coating advantage is that construction is simple, and multiple color tones is arranged, and should intersperse various ornamentals above that; The decorative effect simplicity generosity is widely used.China has tens kind models so far since the development and production eighties, and its fundamental property is identical, is made up of water, pigment, emulsion, weighting agent and various auxiliary agent basically.But this interior wall coating of being processed by emulsion, auxiliary agent etc. has VOC discharging, the heatproof of not preventing fires, contains shortcomings such as heavy metal.
Summary of the invention
The technical problem that the present invention will solve provide a kind of have zero VOC, heatproof prevent fires, resistance to wear, have respiratory function, can absorbing formaldehyde, the multiple functions such as organism of toluene and so on; Stable performance, the preparation method of the novel interior wall powdered material that acceptable life is long.
For realizing above purpose; The technical scheme that the present invention adopts: a kind of preparation method of novel diatom ooze environment-friendly interior wall coating, its preparation method is following: at first select 20 parts in 325 purpose zeyssatite, 8 parts of rubber powders, 0.6 part of methylcellulose gum, 700 orders ~ 7 parts of 900 purpose talcum powder, 400 orders ~ 15 parts of 600 purpose dry powders, 20 orders ~ 10 parts of 90 purpose silica sands, 750 orders ~ 10 parts of 850 purpose kaolin, 550 orders ~ 2 parts of 750 purpose attapulgites, 2 parts of white titanium pigments, 550 orders ~ 10 parts of 650 purposes ash calcium, 1200 orders ~ 14.7 parts of 1300 purpose coarse whitings, 0.4 part of xylon, 0.3 part on staple fibre; Putting into the horizontal high-speed dispersion machine after adding above-mentioned materials accurately in proportion is uniformly dispersed; Its characteristic also comprises: what described rubber powder was selected vinyl acetate outsourcing Z 150PH can be in dispersed latex powder, and above-described methylcellulose gum is the methylcellulose gum of 20000 viscosity.
Among the present invention, preferred 800 orders of described talcum powder.
Among the present invention, preferred 500 orders of described dry powder.
Among the present invention, preferred 40 ~ 70 orders of described silica sand.
Among the present invention, preferred 800 orders of described kaolin.
Among the present invention, preferred 600 orders of described attapulgite.
Among the present invention, described white titanium pigment is preferably anatase titanium dioxide, and content of titanium dioxide is greater than 95%.
Among the present invention, preferred 600 orders of described grey calcium, calcium hydroxide content is greater than 90%.
Among the present invention, preferred 1250 orders of described coarse whiting.
Among the present invention, it is thick that described staple fibre is preferably long 24 μ of 6mm.
Beneficial effect of the present invention:
1, health environment-friendly: saved to reaching auxiliary agents such as the harmful film forming of various liquid chemicals that coating property adds, dispersion, wetting, levelling, anticorrosion mildew-resistant, VOC free discharging.
2, transportation and storage are convenient: contain 20-50% water in the common coating approximately, and in the diatom ooze new coating, this part water adds just in the time of will arriving on-the-spot the use, that is to say, this part water neither needs transportation, does not also need storage.In addition, aqueous coating when transportation and the temperature of storing are lower than 0 ℃, tends to freezingly, and there is not this problem in the diatom ooze powder coating.
3, do not need sanitas: in the conventional liquid coating, existing water, germy again grain is easily by bacterial contamination.Therefore, in order to prevent to go bad, adding preservative agent, and diatom ooze powder coating no bacteria pollution problem does not need sanitas.
4, fire prevention heatproof: in the common coating, owing to added easy incendiary organism, in the process that fire takes place, burn easily and produce a large amount of obnoxious flavoures.And the diatom ooze powder coating is not because the inside has organism basically, so the only meeting fusion of under 1000 ℃ high temperature, can not burning.
5, because zeyssatite is contained in the powder coating the inside, and diatomaceous vesicular structure has been given the breathing damping performance of powder coating, ability balance indoor humidity, and can interior free formaldehyde of absorption chamber and oil smoke.
Embodiment
Instance 1: at first select 20 parts in 325 purpose zeyssatite, 8 parts of rubber powders, 0.6 part of methylcellulose gum, 7 parts of 700 order purpose talcum powder, 15 parts of 400 purpose dry powders, 10 parts of 20 purpose silica sands, 10 parts of 750 purpose kaolin, 2 parts of 550 purpose attapulgites, 2 parts of white titanium pigments, 10 parts of 550 purposes ash calcium, 14.7 parts of 1200 purpose coarse whitings, 0.4 part of xylon, 0.3 part on staple fibre; Putting into the horizontal high-speed dispersion machine after adding above-mentioned materials accurately in proportion is uniformly dispersed.
Through the novel diatom ooze environment-friendly interior wall coating that instance 1 is made, its characteristic such as table 1.
Table 1
| VOC release rate (%) | Fusing point (℃) | Coefficient (N/cm resistance to wears 2） | Self rate of decomposition (%) | Work-ing life (year) | Contamination rate (%) |
| 0 | 950 | 5 | 0 | 12 | 0 |
Instance 2: at first select 20 parts in 325 purpose zeyssatite, 8 parts of rubber powders, 0.6 part of methylcellulose gum, 7 parts of 900 purpose talcum powder, 15 parts of 600 purpose dry powders, 10 parts of 90 purpose silica sands, 10 parts of 850 purpose kaolin, 2 parts of 750 purpose attapulgites, 2 parts of white titanium pigments, 10 parts of 650 purposes ash calcium, 14.7 parts of 1300 purpose coarse whitings, 0.4 part of xylon, 0.3 part on staple fibre; Putting into the horizontal high-speed dispersion machine after adding above-mentioned materials accurately in proportion is uniformly dispersed.
Through the novel diatom ooze environment-friendly interior wall coating that instance 2 is made, its characteristic such as table 2.
Table 2
| VOC release rate (%) | Fusing point (℃) | Coefficient (N/cm resistance to wears 2） | Self rate of decomposition (%) | Work-ing life (year) | Contamination rate (%) |
| 0 | 930 | 4.8 | 0 | 11 | 0 |
Instance 3: at first select 20 parts in 300 purpose zeyssatite, 8 parts of rubber powders, 0.6 part of methylcellulose gum, 7 parts of 800 purpose talcum powder, 15 parts of 500 purpose dry powders, 10 parts of 50 purpose silica sands, 10 parts of 800 purpose kaolin, 2 parts of 600 purpose attapulgites, content of titanium dioxide to grow 0.3 part on the thick staple fibre of 24 μ greater than 95% 2 parts of white titanium pigments, 10 parts of 600 purposes ash calcium, 14.7 parts of 1250 purpose coarse whitings, 0.4 part of xylon, 6mm; Putting into the horizontal high-speed dispersion machine after adding above-mentioned materials accurately in proportion is uniformly dispersed and obtains required novel diatom ooze environment-friendly interior wall coating.
Through the novel diatom ooze environment-friendly interior wall coating that instance 3 is made, its characteristic such as table 3.
Table 3
| VOC release rate (%) | Fusing point (℃) | Coefficient (N/cm resistance to wears 2） | Self rate of decomposition (%) | Work-ing life (year) | Contamination rate (%) |
| 0 | 1000 | 5.5 | 0 | 15 | 0 |
Claims (10)
1. the preparation method of a novel diatom ooze environment-friendly interior wall coating, its preparation method is following: at first select 20 parts in 325 purpose zeyssatite, 8 parts of rubber powders, 0.6 part of methylcellulose gum, 700 orders ~ 7 parts of 900 purpose talcum powder, 400 orders ~ 15 parts of 600 purpose dry powders, 20 orders ~ 10 parts of 90 purpose silica sands, 750 orders ~ 10 parts of 850 purpose kaolin, 550 orders ~ 2 parts of 750 purpose attapulgites, 2 parts of white titanium pigments, 550 orders ~ 10 parts of 650 purposes ash calcium, 1200 orders ~ 14.7 parts of 1300 purpose coarse whitings, 0.4 part of xylon, 0.3 part on staple fibre; Putting into the horizontal high-speed dispersion machine after adding above-mentioned materials accurately in proportion is uniformly dispersed; Its characteristic also comprises: what described rubber powder was selected vinyl acetate outsourcing Z 150PH can be in dispersed latex powder, and above-described methylcellulose gum is the methylcellulose gum of 20000 viscosity.
2. the preparation method of a kind of novel diatom ooze environment-friendly interior wall coating according to claim 1 is characterized in that preferred 800 orders of described talcum powder.
3. the preparation method of a kind of novel diatom ooze environment-friendly interior wall coating according to claim 1 is characterized in that preferred 500 orders of described dry powder.
4. the preparation method of a kind of novel diatom ooze environment-friendly interior wall coating according to claim 1 is characterized in that preferred 40 ~ 70 orders of described silica sand.
5. the preparation method of a kind of novel diatom ooze environment-friendly interior wall coating according to claim 1 is characterized in that preferred 800 orders of described kaolin.
6. the preparation method of a kind of novel diatom ooze environment-friendly interior wall coating according to claim 1 is characterized in that preferred 600 orders of described attapulgite.
7. the preparation method of a kind of novel diatom ooze environment-friendly interior wall coating according to claim 1 is characterized in that described white titanium pigment is preferably anatase titanium dioxide, and content of titanium dioxide is greater than 95%.
8. the preparation method of a kind of novel diatom ooze environment-friendly interior wall coating according to claim 1 is characterized in that preferred 600 orders of described grey calcium, and calcium hydroxide content is greater than 90%.
9. the preparation method of a kind of novel diatom ooze environment-friendly interior wall coating according to claim 1 is characterized in that preferred 1250 orders of described coarse whiting.
10. the preparation method of a kind of novel diatom ooze environment-friendly interior wall coating according to claim 1, it is thick to it is characterized in that described staple fibre is preferably long 24 μ of 6mm.