CN1392209A - Environmental protection building inner wall paint and its producing method - Google Patents
Environmental protection building inner wall paint and its producing method Download PDFInfo
- Publication number
- CN1392209A CN1392209A CN 02111493 CN02111493A CN1392209A CN 1392209 A CN1392209 A CN 1392209A CN 02111493 CN02111493 CN 02111493 CN 02111493 A CN02111493 A CN 02111493A CN 1392209 A CN1392209 A CN 1392209A
- Authority
- CN
- China
- Prior art keywords
- environment
- friendly type
- building body
- type building
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The environment protecting building inner wall paint has no volatile poisonous matter and environment pollution. It is prepared with deionized water, titanium white powder, emulsion, superfine calcium carbonate, superfine medical talcum powder, dispersant, leveling agent, thickening agent, anti-mildew agent, filming agent and defoaming agent and through mixing and other steps. It has low content of volatile organic matter, soluble heavy metal and ecological poisonous matter, certain antibacterial effect and no environmental pollution and no harm to human body.
Description
Technical field:
What the present invention relates to is the building wall paint technical field, and particularly environment-friendly type building body of wall interior wall coating and production method thereof are applied to the interior walls brushing.
Background technology:
At present, known dope for inner wall of architecture is formulated by water, titanium dioxide, emulsion, stopping composition and various auxiliary agent, require not tight owing to select materials, contain halohydrocarbon, benzene series material, heavy metal compound, yuban, the organic top grade toxic substance of volatility in the coating, the environment human body has been brought in various degree and endangers.
Summary of the invention:
The technical issues that need to address of the present invention are: a kind of environmental protection building inner wall paint and dope for inner wall of architecture and production method thereof that environment is not had pollution is provided, its technology is achieved in that environment-friendly type building body of wall interior wall coating and production method thereof, it is characterized in that: in 100 parts, the weight proportion of its each component is:
15 parts of deionized waters;
20 parts of titanium dioxides;
25 parts of emulsions;
20 parts of calcium carbonate superfine powders;
15 parts of ultra-fine medical talc powders;
1.5 parts of dispersion agents;
0.3 part of flow agent;
0.5 part of thickening material;
0.2 part of mould inhibitor;
1.7 parts of membrane-forming agents;
0.8 part of defoamer;
Component in the above-mentioned prescription is the commercial goods, and emulsion is preferably vinyl acetate between to for plastic-acrylate copolymer emulsion, and dispersion agent is preferably T-19, flow agent is preferably T-2020, and thickening material is preferably T-17, and mould inhibitor is preferably T-75, membrane-forming agent is preferably TX-12, and defoamer is preferably T-202.Volatile organic matter of the present invention (VOC) content is less than 250mg/kg, and heavy metal compound is less than 500mg/kg, and the polymer content of formaldehyde and formaldehyde is less than 500mg/kg.
Its production method is: component is made slurry and base-material respectively, and slurry and base-material mix, and adding flow agent, thickening material, mould inhibitor, membrane-forming agent, defoamer stir, toning, check finished product warehouse-in.Wherein: 1. slurry: deionized water+titanium dioxide+calcium carbonate superfine powder+ultra-fine medical talc powder stirs 2. base-materials: deionized water+emulsion+dispersion agent stirs 3. coating: slurry+base-material mixes, add flow agent, thickening material, mould inhibitor, membrane-forming agent, defoamer,
Toning stirring → test → warehouse-in.
The invention has the beneficial effects as follows: because this coating adopts clearer production technology, in production and construction process, has low content of volatile organic compounds, soluble heavy metal and eco-toxicity index are lower than national standard, volatile organic matter (VOC) content is less than 250mg/kg, heavy metal compound is less than 500mg/kg, the polymer content of formaldehyde and formaldehyde is less than 500mg/kg, and the positive effect of environment-friendly antibacterial has been played in the harm of non-environmental-pollution and human body.The present invention has a good jar property, the levelling property of filming opened, and hiding rare is strong, washability, anti-ly fade, alkali resistant, antifungal, nontoxic, tasteless.
Description of drawings:
Fig. 1 is a process flow sheet of the present invention,
Embodiment:
Below the present invention is further described with producing 1 ton of dope for inner wall of architecture:
According to accompanying drawing 1, whole technology is undertaken by following three steps after batching, 1. slurry: the ultra-fine medical talc powder 150Kg of deionized water 150Kg+ titanium dioxide 200Kg+ calcium carbonate superfine powder 200Kg+ mixes stirring 2. base-materials: deionized water
5Kg+ emulsion 250Kg+ dispersion agent 15Kg mixes 3. coating: slurry 700Kg+ base-material 265Kg mixes, and adding flow agent 3Kg, thickening material 5Kg, mould inhibitor 2Kg, membrane-forming agent 17Kg, defoamer 8Kg stir toning → test → warehouse-in.
Claims (10)
1, environment-friendly type building body of wall interior wall coating is characterized in that: in 100 parts, the weight proportion of its each component is:
15 parts of deionized waters;
20 parts of titanium dioxides;
25 parts of emulsions;
20 parts of calcium carbonate superfine powders;
15 parts of ultra-fine medical talc powders;
1.5 parts of dispersion agents;
0.3 part of flow agent;
0.5 part of thickening material;
0.2 part of mould inhibitor;
1.7 parts of membrane-forming agents;
0.8 part of defoamer;
2, environment-friendly type building body of wall interior wall coating according to claim 1, it is characterized in that: emulsion is preferably vinyl acetate between to for plastic-acrylate copolymer emulsion.
3, environment-friendly type building body of wall interior wall coating according to claim 1, it is characterized in that: dispersion agent is preferably T-19.
4, environment-friendly type building body of wall interior wall coating according to claim 1, it is characterized in that: flow agent is preferably T-2020.
5, environment-friendly type building body of wall interior wall coating according to claim 1, it is characterized in that: thickening material is preferably T-17.
6, environment-friendly type building body of wall interior wall coating according to claim 1, it is characterized in that: mould inhibitor is preferably T-75.
7, environment-friendly type building body of wall interior wall coating according to claim 1, it is characterized in that: membrane-forming agent is preferably TX-12.
8, environment-friendly type building body of wall interior wall coating according to claim 1, it is characterized in that: defoamer is preferably T-202.
9, the described environment-friendly type building body of wall of claim 1 production of Interior Wall Paint method, it is characterized in that: component is made slurry and base-material respectively, and slurry and base-material mix, and adding flow agent, thickening material, mould inhibitor, membrane-forming agent, defoamer stir, toning, check finished product warehouse-in.
10, environment-friendly type building body of wall production of Interior Wall Paint method according to claim 9 is characterized in that: slurry: deionized water+titanium dioxide+calcium carbonate superfine powder+ultra-fine medical talc powder stirs and forms base-material: deionized water+emulsion+dispersion agent stirs and forms.