CN102515702A - Antique art ceramic - Google Patents
Antique art ceramic Download PDFInfo
- Publication number
- CN102515702A CN102515702A CN2011104165391A CN201110416539A CN102515702A CN 102515702 A CN102515702 A CN 102515702A CN 2011104165391 A CN2011104165391 A CN 2011104165391A CN 201110416539 A CN201110416539 A CN 201110416539A CN 102515702 A CN102515702 A CN 102515702A
- Authority
- CN
- China
- Prior art keywords
- antique
- art ceramic
- antique art
- feldspar
- calcite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an antique art ceramic. The blank material of the antique art ceramic comprises the following raw materials: 13-15wt% of feldspar, 15-17wt% of quartz, 18-19wt% of alkali stone, 20-22wt% of Longyan clay, 17-18wt% of kaolin, 2-3wt% of talcum, 2-4wt% of calcite and 6-8wt% of Zuoyun clay; and the antique art ceramic is prepared by sintering through adopting a1300-1320DEG C reduction flame. The blank material of the invention has the advantages of easily available and conveniently prepared formula raw materials, and direct sintering without glazing; and the antique art ceramic has the advantages of gentle color, slight luster, matte texture on the surface, and simplicity and naturalness.
Description
Technical field
The present invention relates to a kind of antique artistic pottery.
Background technology
Along with growth in the living standard, people more and more pursue the enjoyment on the aesthetic feeling to pottery, and the gentle and kind simple and unsophisticated art pottery is liked because of its plain quality receives the human consumer deeply, usually as putting uses such as artwork or flower arrangement vessel.
Copy various decorative patterns when existing antique artistic pottery generally adopts surperficial glazing and make, or adjustment glaze composition, fire and form.These methods all need other brushing glaze, increase process step, also increase production cost simultaneously.
Summary of the invention
The objective of the invention is to the problems referred to above, a kind of new pottery modelled after an antique is provided, do not need glazing to handle, directly can be fired into pottery modelled after an antique to prior art.
The present invention realizes above-mentioned purpose through following technical scheme:
The antique artistic pottery, the blank raw material is: feldspar 13 ~ 15wt%, quartzy 15 ~ 17 wt%, alkali stone 18 ~ 19 wt%, Longyan clay 20 ~ 22 wt%, kaolin 17 ~ 18 wt%, talcum 2 ~ 3 wt%, calcite 2 ~ 4 wt%, Zuoyun soil 6 ~ 8 wt%; Adopt 1300 ℃ ~ 1320 ℃ reducing flames to fire and form.
As a kind of preferred version, the blank raw material is: feldspar 15wt%, and quartzy 16 wt%, alkali stone 18 wt%, Longyan clay 21 wt%, kaolin 18 wt%, talcum 2 wt%, calcite 3 wt%, Zuoyun soil 7 wt% adopt 1310 ℃ of reducing flames to fire and form.
Above-mentioned blank is made into can directly be sent into kiln after the various artistic shapes and burn till.The shuttle-type kiln is preferably adopted in the control of firing atmosphere for the benefit of.
Compared with prior art, blank formulation raw material of the present invention is easy to get, and preparation is convenient, need not glazing and directly fires, and product colour is gentle, and is slightly glossy, and there is frosted texture on the surface, primitive simplicity and nature.
Embodiment
Embodiment 1
Blank porcelain mud raw material: feldspar 15wt%, quartzy 16 wt%, alkali stone 18 wt%, Longyan clay 21 wt%, kaolin 18 wt%, talcum 2 wt%, calcite 3 wt%, Zuoyun soil 7 wt%.Above-mentioned raw materials accurately takes by weighing each component of aforementioned proportion after pulverizing, sieving, add entry and grinding element, is raw material by mass ratio: the mixed of water: grinding element=1:1:1.5; The ball mill of packing into carries out ball milling, and the time is 30 minutes, crosses 180 mesh sieves then; With ball milling separately, elimination part large granular impurity, leave standstill, old 24 hours; Pour blank mud into plaster mould then, after the demoulding, seasoning, further repair again; The shuttle-type kiln is sent in the surface dedusting at last, begins to fire.During product burnt till, heat-up rate should not be too fast, during 800 ~ 900 ℃, should keep good oxidizing atmosphere.Between 1000 ~ 1100 ℃, keep the strongly reducing atmosphere of about 1h, phase out into weakly reducing atmosphere then, during to 1310 ℃, answer the about 8min of constant temperature, cease fire then, naturally cooling.
Embodiment 2
Blank porcelain mud raw material: feldspar 13wt%, quartzy 17 wt%, alkali stone 18 wt%, Longyan clay 22wt%, kaolin 17 wt%, talcum 3 wt%, calcite 2 wt%, Zuoyun soil 8 wt%.Above-mentioned raw materials accurately takes by weighing each component of aforementioned proportion after pulverizing, sieving, add entry and grinding element, is raw material by mass ratio: the mixed of water: grinding element=1:1:1.5; The ball mill of packing into carries out ball milling, and the time is 30 minutes, crosses 180 mesh sieves then; With ball milling separately, elimination part large granular impurity, leave standstill, old 24 hours; Pour blank mud into plaster mould then, after the demoulding, seasoning, further repair again; The shuttle-type kiln is sent in the surface dedusting at last, begins to fire.During product burnt till, heat-up rate should not be too fast, during 800 ~ 900 ℃, should keep good oxidizing atmosphere.Between 1000 ~ 1100 ℃, keep the strongly reducing atmosphere of about 1h, phase out into weakly reducing atmosphere then, during to 1310 ℃, answer the about 10min of constant temperature, cease fire then, naturally cooling.
The product colour that two embodiment methods are fired is gentle, slightly glossy, and there is frosted texture on the surface, all presents antique effect preferably.
Claims (2)
1. an antique artistic pottery is characterized in that the blank raw material is: feldspar 13 ~ 15wt%, quartzy 15 ~ 17 wt%, alkali stone 18 ~ 19 wt%, Longyan clay 20 ~ 22 wt%, kaolin 17 ~ 18 wt%, talcum 2 ~ 3 wt%, calcite 2 ~ 4 wt%, Zuoyun soil 6 ~ 8 wt%; Adopt 1300 ℃ ~ 1320 ℃ reducing flames to fire and form.
2. according to the said antique artistic pottery of claim 1, it is characterized in that the blank raw material is: feldspar 15wt%, quartzy 16 wt%, alkali stone 18 wt%; Longyan clay 21 wt%, kaolin 18 wt%, talcum 2 wt%; Calcite 3 wt%, Zuoyun soil 7 wt% adopt 1310 ℃ of reducing flames to fire and form.