CN102492913A - 一种热镀用锌锰钛合金 - Google Patents
一种热镀用锌锰钛合金 Download PDFInfo
- Publication number
- CN102492913A CN102492913A CN2011104419364A CN201110441936A CN102492913A CN 102492913 A CN102492913 A CN 102492913A CN 2011104419364 A CN2011104419364 A CN 2011104419364A CN 201110441936 A CN201110441936 A CN 201110441936A CN 102492913 A CN102492913 A CN 102492913A
- Authority
- CN
- China
- Prior art keywords
- zinc
- titanium alloy
- manganese
- manganese titanium
- alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种热镀用锌锰钛合金,锌锰钛合金的重量组份为:Mn 0.5%~2.5%,Ti 0.3%~1.5%,其余为Zn。其制作步骤为加热熔化搅拌均匀、捞渣、浇铸成型,在常温下冷却成型为块状锌锰钛合金。本发明的锌锰钛合金制作工艺简单、制作费用低,锌浴中加入本发明的锌锰钛合金,合金锌浴的流动性好,工件表面镀层厚度均匀、无色差、无圣德林效应、无锌瘤、降低镀层厚度,增强了合金镀层的耐腐蚀性能和机械性能;缩短了热镀时间,降低了生产成本,提高了镀层质量和生产效率。
Description
技术领域
本发明涉及一种热镀用合金,具体涉及一种热镀用锌锰钛合金。
背景技术
目前热镀锌所用锌浴一般都采用锌合金浴。锌合金浴热镀锌镀层,具有优良的抗腐蚀性能,良好的表面质量及优异的结合性能和机械性能。但是对于热镀成分复杂的钢材,热镀锌浴容易产生较多的镀层质量问题,如镀层厚度不均匀、超厚现象、圣德林效应、色差等,虽然采用锌-铝(Zn-Al)系列合金和锌-镍(Zn-Ni)系列合金浴在一定程度上能改进镀层质量,但是这种系列合金浴热镀工艺复杂、费用高、热镀时间长,尤其是对于成分复杂的钢材材质批量热镀锌,镀层合格率低,还会影响生产进度。
发明内容
本发明的目的是要克服上述技术的缺点,提供一种热镀工艺简单、热镀时间短、镀层质量好的热镀用锌锰钛合金。
本发明的热镀用锌锰钛合金,其特征在于:所述的锌锰钛合金的重量组份为:Mn 0.5%~2.5%,Ti 0.3%~1.5%,其余为Zn。
所述的锌锰钛合金的制作步骤如下:
1)熔化:将上述重量组份的Zn、Mn和Ti投入熔锅中加热3~4小时,加热到600℃~700℃,使Zn、Mn和Ti完全熔化成锌锰钛合金溶液并搅拌均匀;
2)捞渣;从熔锅中捞出锌锰钛合金溶液中的渣;
3)浇铸;将无渣的锌锰钛合金溶液倒入浇铸模内,在常温下冷却成型为块状锌锰钛合金。
本发明的锌锰钛合金制作工艺简单、制作费用低,锌浴中加入本发明的锌锰钛合金,合金锌浴的流动性好,工件表面镀层厚度均匀、无色差、无圣德林效应、无锌瘤、降低镀层厚度,增强了合金镀层的耐腐蚀性能和机械性能;缩短了热镀时间,降低了生产成本,提高了镀层质量和生产效率。
附图说明书
图1是本发明的锌锰钛合金制作流程图。
具体实施方式
实施例1
一种热镀用锌锰钛合金,其重量组份为Mn 0.5%;Ti 1.5%;其余量为Zn。
实施例2
一种热镀用锌锰钛合金,其重量组份为Mn 2.5%;Ti 1.5%;其余量为Zn。
实施例3
一种热镀用锌锰钛合金,其重量组份为Mn:0.5%;Ti:0.3%;其余量为Zn。
实施例4
一种热镀用锌锰钛合金,其重量组份为Mn 2.5%;Ti 1.5%;其余量为Zn。
上述实施例的锌锰钛合金的制作步骤如下:
1)熔化;将上述实施例的重量组份的Zn、Mn和Ti投入到中频无芯感应电炉的熔锅中加热3.5小时,加热到650℃,使Zn、Mn和Ti完全熔化成锌锰钛合金溶液并搅拌均匀;
2)捞渣:从熔锅中捞出锌锰钛合金溶液中的渣,将捞出的渣放入渣桶中;
3)浇铸:将温度为650℃的无渣锌锰钛合金熔液到入浇铸模中,在常温下冷却成型为块状锌锰钛合金。
使用时,锌锭∶锌锰钛合金按10~50∶1的比例加入到锌锅中熔化即形成新的锌浴。这种的锌浴流动好,使用这种锌浴热镀成分复杂的钢制工件,热镀质量好、镀层合格率高。
Claims (2)
1.一种热镀用锌锰钛合金,其特征在于:所述的锌锰钛合金的重量组份为:Mn 0.5%~2.5%,Ti 0.3%~1.5%,其余为Zn。
2.根据权利要求1所述的锌锰钛合金,其制作步骤如下:
1)熔化:将上述重量组份的Zn、Mn和Ti投入熔锅中加热3~4小时,加热到600℃~700℃,使Zn、Mn和Ti完全熔化成锌锰钛合金溶液并搅拌均匀;
2)捞渣;从熔锅中捞出锌锰钛合金溶液中的渣;
3)浇铸;将无渣的锌锰钛合金溶液倒入浇铸模内,在常温下冷却成型为块状锌锰钛合金。