CN102432687A - 制香用改性植物胶的制作工艺 - Google Patents
制香用改性植物胶的制作工艺 Download PDFInfo
- Publication number
- CN102432687A CN102432687A CN2011102471725A CN201110247172A CN102432687A CN 102432687 A CN102432687 A CN 102432687A CN 2011102471725 A CN2011102471725 A CN 2011102471725A CN 201110247172 A CN201110247172 A CN 201110247172A CN 102432687 A CN102432687 A CN 102432687A
- Authority
- CN
- China
- Prior art keywords
- cassava
- tapioca root
- block root
- powder
- curing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种使用木薯制作成制香用改性植物胶的制作工艺,它包括如下步骤:将木薯块根湿料晒干至其含水率小于或者等于10%,得到木薯块根干料;将木薯块根干料加入研磨装置内研磨成木薯块根粉料生料;在搅拌机内加入木薯块根粉料生料与水,搅拌成糊状物;将熟化机的熟化滚筒加热至120~150℃,将糊状物涂敷在熟化机的熟化滚筒上,糊状物的涂敷厚度为1~3mm,熟化时间控制在30~60秒,得到木薯块根粉料熟料;取下熟化机的熟化滚筒的熟化块状物放入研磨装置内研磨成木薯块根粉料熟料。本发明中木薯可大量种植,是可再生资源;植物改性胶的功效和榆皮粉相同;可快速成材;降低了生产成本;节约森林资源。
Description
技术领域
本发明涉及一种公开了制香用改性植物胶的制作工艺,尤其是一种使用木薯制作成制香用改性植物胶的制作工艺。
背景技术
传统佛香、卫生香等制作时,所需的粘合材料是榆皮粉。榆皮粉是由榆树皮晒干粉碎而成。榆树产地主要集中在北方,榆树皮的采集是靠人工削取,费时费力。因榆皮粉加水搅拌后,自身会产生强烈的粘性,是制香的理想材料。榆皮粉与木粉混合搅拌后,可形成粘稠的胶状物,经制香机压制成型烘干后,即可制成佛像、卫生香、薰香等。由于榆皮粉的大量应用,需砍伐大量榆树,森林资源遭到破坏,生态环境失去平衡。
发明内容
本发明的目的是克服现有技术中存在的不足,提供一种可以降低生产成本、节约森林资源的一种制香用改性植物胶的制作工艺。
按照本发明提供的技术方案,所述制香用改性植物胶的制作工艺,其特征在于该制作工艺包括如下步骤:
a、将木薯块根湿料晒干至其含水率小于或者等于10%,得到木薯块根干料;
b、将木薯块根干料加入研磨装置内研磨成120~200目的木薯块根粉料生料;
c、在搅拌机内加入木薯块根粉料生料1~1.5重量份与水5~10重量份,搅拌成糊状物;
d、将熟化机的熟化滚筒加热至120~150℃,将糊状物涂敷在熟化机的熟化滚筒上,糊状物的涂敷厚度为1~3mm,熟化时间控制在30~60秒,得到木薯块根粉料熟料;
e、取下熟化机的熟化滚筒的熟化块状物放入研磨装置内研磨成120~200目的木薯块根粉料熟料。
本发明中木薯可大量种植,是可再生资源;植物改性胶的功效和榆皮粉相同;可快速成材;降低了生产成本;节约森林资源。
具体实施方式
下面结合具体实施例对本发明作进一步说明。
实施例1
一种制香用改性植物胶的制作工艺包括如下步骤:
a、将木薯块根湿料晒干至其含水率小于或者等于10%,得到木薯块根干料;
b、将木薯块根干料加入研磨装置内研磨成120~130目的木薯块根粉料生料;
c、在搅拌机内加入木薯块根粉料生料1千克与水5千克,搅拌成糊状物;
d、将熟化机的熟化滚筒加热至120~122℃,将糊状物涂敷在熟化机的熟化滚筒上,糊状物的涂敷厚度为1mm,熟化时间控制在30~35秒,得到木薯块根粉料熟料;
e、取下熟化机的熟化滚筒的熟化块状物放入研磨装置内研磨成120~130目的木薯块根粉料熟料。
使用这种木薯块根粉料熟料生产得到直径为3.2mm长度为280mm的成品香,该成品香香经测试其抗折强度为71~75g。
实施例2
一种制香用改性植物胶的制作工艺包括如下步骤:
a、将木薯块根湿料晒干至其含水率小于或者等于10%,得到木薯块根干料;
b、将木薯块根干料加入研磨装置内研磨成140~150目的木薯块根粉料生料;
c、在搅拌机内加入木薯块根粉料生料1.3千克与水8千克,搅拌成糊状物;
d、将熟化机的熟化滚筒加热至130~135℃,将糊状物涂敷在熟化机的熟化滚筒上,糊状物的涂敷厚度为1.8mm,熟化时间控制在40秒,得到木薯块根粉料熟料;
e、取下熟化机的熟化滚筒的熟化块状物放入研磨装置内研磨成140~150目的木薯块根粉料熟料。
使用这种木薯块根粉料熟料生产得到直径为2.8mm长度为280mm的成品香,该成品香香经测试其抗折强度为52~56g。
实施例3
一种制香用改性植物胶的制作工艺包括如下步骤:
a、将木薯块根湿料晒干至其含水率小于或者等于10%,得到木薯块根干料;
b、将木薯块根干料加入研磨装置内研磨成190~200目的木薯块根粉料生料;
c、在搅拌机内加入木薯块根粉料生料1.5千克与水10千克,搅拌成糊状物;
d、将熟化机的熟化滚筒加热至145~150℃,将糊状物涂敷在熟化机的熟化滚筒上,糊状物的涂敷厚度为3mm,熟化时间控制在60秒,得到木薯块根粉料熟料;
e、取下熟化机的熟化滚筒的熟化块状物放入研磨装置内研磨成190~200目的木薯块根粉料熟料。
使用这种木薯块根粉料熟料生产得到直径为2.4mm长度为300mm的成品香,该成品香香经测试其抗折强度为32~34g。
本发明中,香条抗折强度测量时,砝码挂在香条的中间处。如长度为280mm的香条,测试时砝码挂在140mm处;如长度为300mm的香条,测试时砝码挂在150mm处。
从以上实施例可以看出,使用木薯块根粉料熟料制作成品香后,成品香的抗折强度与目前使用榆皮粉制作的同规格的香的抗折强度相当,说明木薯块根粉料熟料可以替代榆皮粉进行成品香制作,而且木薯可大量种植,是可再生资源;木薯可快速成材。这样就降低了生产成本,而且节约了森林资源。
Claims (1)
1.一种制香用改性植物胶的制作工艺,其特征在于该制作工艺包括如下步骤:
a、将木薯块根湿料晒干至其含水率小于或者等于10%,得到木薯块根干料;
b、将木薯块根干料加入研磨装置内研磨成120~200目的木薯块根粉料生料;
c、在搅拌机内加入木薯块根粉料生料1~1.5重量份与水5~10重量份,搅拌成糊状物;
d、将熟化机的熟化滚筒加热至120~150℃,将糊状物涂敷在熟化机的熟化滚筒上,糊状物的涂敷厚度为1~3mm,熟化时间控制在30~60秒,得到木薯块根粉料熟料;
e、取下熟化机的熟化滚筒的熟化块状物放入研磨装置内研磨成120~200目的木薯块根粉料熟料。