CN102382566A - Uv-超哑光辊涂面漆 - Google Patents
Uv-超哑光辊涂面漆 Download PDFInfo
- Publication number
- CN102382566A CN102382566A CN2011102594782A CN201110259478A CN102382566A CN 102382566 A CN102382566 A CN 102382566A CN 2011102594782 A CN2011102594782 A CN 2011102594782A CN 201110259478 A CN201110259478 A CN 201110259478A CN 102382566 A CN102382566 A CN 102382566A
- Authority
- CN
- China
- Prior art keywords
- mixture
- agent
- ultra
- overpainting
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种UV-超哑光辊涂面漆,该面漆的组分及其重量配比为:100%的UV树脂20%-30%、消泡剂0.1%-0.5%、分散剂1.0%-4%、消光剂10%-18%、填料5%-15%、引发剂3%-8%、流平剂0.1%-1%、防沉剂1%-1.5%,余量为单体;所述100%的UV-树脂为聚氨酯丙烯酸树脂、或改性环氧丙烯酸树脂或它们的混合物;单体为丙烯酸酯类、改性丙烯酸酯类或它们的混合物;本发明表面平整度高、光泽度低、柔和度好,形成的漆膜结构柔韧性好、耐刮擦,能在木家具、木地板等木制品表面形成耐刮擦的保护层,从而对木家具和木地板表面形成持久的保护。
Description
技术领域
本发明涉及一种UV-光固化木器涂料,具体地说是一种哑光或全哑光的UV-辊涂面漆。
背景技术
UV是Ultraviolet (紫外线)的英文缩写,UV漆即紫外光固化漆。普通木板,硅钙板等板材通过上UV漆,再经过UV光固化机干燥而形成的石材板,有亮光表面处理,色泽鲜艳,具有很强的视觉冲击力,耐磨,抗化学性强,使用寿命长,不变色,易清理,是比较理想的板材养护处理工艺。现有的木家具、木地板等木制品表面均采用UV漆即紫外光固化漆养护处理工艺。目前市面上很多的产品都是亮光类型的,但是随着人们审美观点的变化,现在哑光的效果越来越多的受到消费者的青睐,因此哑光的产品也多起来,但是目前光泽度低且表面效果又好的产品几乎没有。
发明内容
为了克服现有技术存在的问题,使面漆的表面平整度高、柔和度好,同时光泽度低,本发明的目的是提供一种UV-超哑光辊涂面漆,该面漆表面平整度高、光泽度低、柔和度好,形成的漆膜结构柔韧性好、耐刮擦,能在木家具、木地板等木制品表面形成耐刮擦的保护层,从而对木家具和木地板表面形成持久的保护。
本发明的目的是通过以下技术方案来实现的:
一种UV-超哑光辊涂面漆,其特征在于:该面漆的组分及其重量配比为:100%的UV树脂 20 %- 30 %、消泡剂 0 . 1 %- 0 . 5 %、分散剂 1 . 0 %- 4%、消光剂10%- 18 %、填料 5%- 15 %、引发剂 3%- 8%、流平剂 0 . 1 % -1 %、防沉剂 1 %- 1.5 %,余量为单体;所述100%的UV-树脂为聚氨酯丙烯酸树脂、或改性环氧丙烯酸树脂或它们的混合物;所述单体为丙烯酸酯类、改性丙烯酸酯类或它们的混合物;所述填料为无机粉类;所述消光剂为有机物改性气相二氧化硅类、气相二氧化硅、消光蜡浆类或它们的混合物。
本发明中,当该面漆的组分中不含消光剂时制得的漆为亮光漆。本发明中,所述消泡剂为不含有机硅聚合物溶液、聚丙烯酸高聚物或它们的混合物;所述分散剂为高分子量嵌段共聚物溶液、改性丙烯酸嵌段共聚物溶液或它们的混合物;所述引发剂剂为芳香酮类、苯偶姻及其衍生物或它们的混合物;所述流平剂为丙烯酸酯共聚物、改性硅氧烷溶液或它们的混合物;所述防沉剂为气相二氧化硅、多元胺酰胺的多元羧酸盐类、改性脲溶液或它们的混合物。所述填料为无机粉类,无机粉类为滑石粉、硅微粉或它们的混合物。
本发明采用改性UV树脂、单体的选择、填料和消光剂的搭配来提高木器面漆的表面平整度、柔和度,同时降低了光泽度。
与现有技术相比,本发明表面平整度高、光泽度低、柔和度好,形成的漆膜结构柔韧性好、耐刮擦,能在木家具、木地板等木制品表面形成耐刮擦的保护层,从而对木家具和木地板表面形成持久的保护。
具体实施方式
下面结合实施例对本发明作进一步的说明。
实施例1
一种本发明所述的UV-超哑光辊涂面漆,其组分及其重量配比为:100%的UV树脂25 %、消泡剂 0 . 5 %、分散剂 4%、消光剂15 %、填料15 %、引发剂 7%、流平剂1 %、防沉剂 1 % ,余量为单体。上述组分中:UV-树脂为聚氨酯丙烯酸树脂、或改性环氧丙烯酸树脂或它们的混合物,如CYTEC、SARTOMER、长兴、三木等生产的;单体为:丙烯酸酯类、改性丙烯酸酯类或它们的混合物,如CYTEC、SARTOMER、长兴、三木等生产的;消泡剂为不含有机硅聚合物溶液、聚丙烯酸高聚物或它们的混合物,如毕克公司生产的BYK055、BYK080A或它们的混合物;分散剂为高分子量嵌段共聚物溶液、改性丙烯酸嵌段共聚物溶液或它们的混合物,如毕克公司生产的BYK164、BYK103或它们的混合物;引发剂剂为芳香酮类、苯偶姻及其衍生物或它们的混合物,如CIBA生产的BP、184、1173或它们的混合物;填料为无机粉类,无机粉类为滑石粉、硅微粉或它们的混合物。。流平剂为丙烯酸酯共聚物、改性硅氧烷溶液或它们的混合物,如毕克公司生产的BYK371、BYK358或它们的混合物;防沉剂为气相二氧化硅、多元胺酰胺的多元羧酸盐类、改性脲溶液或它们的混合物,如毕克公司生产的BYK204;消光剂可采用有机物改性气相二氧化硅类,如美国格雷斯公司生产的 ED80或气相二氧化硅,如DEGUSS公司生产的消光粉OK500;消光蜡浆类,如德谦公司生产的 FA115或它们的混合物。
配制时,将100%的UV-树脂和单体、消泡剂、分散剂、引发剂分散后,加入无机粉料、防沉粉料和消光粉充分分散均匀,最后加入流平剂和防沉剂分散均匀即可。涂装施工时,调节辊涂机的涂装速度和滚轮的夹紧度来控制涂布量;调节恒温水浴槽的温度控制油漆的温度,通过辊涂的方式将漆涂于家具、木地板等木制品表面。
经检测,本发明的UV-超哑光辊涂面漆的主要技术指标如下:
序号 | 检验项目 | 检验结果 | 检验标准 |
1 | 涂膜外观 | 表面平整、光滑 | 目测 |
2 | 附着力 | 0-1 | EN ISO 2409 |
3 | 光泽度 | 5-10° | GB/T9754-1998 |
4 | 抗磨损性能 | ≤0.08 g/100r | GB/T18103-2000 |
本发明表面平整度高、光泽度低、柔和度好,形成的漆膜结构柔韧性好、耐刮擦,能在木家具、木地板等木制品表面形成耐刮擦的保护层,从而对木家具和木地板表面形成持久的保护。
实施例2
又一种本发明所述的UV-辊涂面漆,为哑光漆,与实施例1相比,仅仅是重量配比不同,该哑光漆的组分及其重量配比为:100%的UV树脂 30 %、消泡剂0 . 5 %、分散剂3%、填料5 %、引发剂6%、流平剂1 %、防沉剂1.5 % ,消光剂10 %,余量为单体。
实施例3
又一种本发明所述的UV-辊涂面漆,为哑光漆,与实施例1相比,仅仅是重量配比不同。该哑光漆的组分及其重量配比为:100%的UV树脂20 %、消泡剂0 . 5 %、分散剂 1 %、消光剂16 %、填料 15 %、引发剂 3%、流平剂1 %、防沉剂 1 %,余量为单体。
Claims (7)
1.一种UV-超哑光辊涂面漆,其特征在于:该面漆的组分及其重量配比为:100%的UV树脂 20 %- 30 %、消泡剂 0 . 1 %- 0 . 5 %、分散剂 1 . 0 %- 4%、消光剂10%- 18 %、填料 5%- 15 %、引发剂 3%- 8%、流平剂 0 . 1 % -1 %、防沉剂 1 %- 1.5 %,余量为单体;所述100%的UV-树脂为聚氨酯丙烯酸树脂或改性环氧丙烯酸树脂或它们的混合物;所述单体为丙烯酸酯类、改性丙烯酸酯类或它们的混合物;所述填料为无机粉类;所述消光剂为有机物改性气相二氧化硅类、气相二氧化硅、消光蜡浆类或它们的混合物。
2.根据权利要求1所述的UV-超哑光辊涂面漆,其特征在于:所述消泡剂为不含有机硅聚合物溶液、聚丙烯酸高聚物或它们的混合物。
3.根据权利要求1所述的UV-超哑光辊涂面漆,其特征在于:所述分散剂为高分子量嵌段共聚物溶液、改性丙烯酸嵌段共聚物溶液或它们的混合物。
4.根据权利要求1所述的UV-超哑光辊涂面漆,其特征在于:所述引发剂剂为芳香酮类、苯偶姻及其衍生物或它们的混合物。
5.根据权利要求1所述的UV-超哑光辊涂面漆,其特征在于:所述流平剂为丙烯酸酯共聚物、改性硅氧烷溶液或它们的混合物。
6.根据权利要求1所述的UV-超哑光辊涂面漆,其特征在于:所述防沉剂为气相二氧化硅、多元胺酰胺的多元羧酸盐类、改性脲溶液或它们的混合物。
7.根据权利要求1所述的UV-超哑光辊涂面漆,其特征在于:所述无机粉类为滑石粉、硅微粉或它们的混合物。