CN102190819A - 易脱模的高强度橡胶组合物 - Google Patents
易脱模的高强度橡胶组合物 Download PDFInfo
- Publication number
- CN102190819A CN102190819A CN2010101316342A CN201010131634A CN102190819A CN 102190819 A CN102190819 A CN 102190819A CN 2010101316342 A CN2010101316342 A CN 2010101316342A CN 201010131634 A CN201010131634 A CN 201010131634A CN 102190819 A CN102190819 A CN 102190819A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight parts
- agent
- carbon black
- rubber composition
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供了一种易脱模的高强度橡胶组合物,由下列原料制备而成:丁腈橡胶105重量份、N220炭黑50重量份、N330炭黑10重量份、二辛脂28重量份、硫磺0.8~1重量份、过氧化二异丙苯0.8~1重量份、促进剂2重量份、流动剂2.1重量份、氧化锌5重量份、防老剂3.5~4.5重量份,龟裂防止剂4~5.2重量份、消泡剂8~10重量份、二甲苯麝香2~5重量份、2%水乳化有机硅脱模剂3重量份。本发明的特点是配方更为合理,加工时不易起泡且散发一定芳香气味,且密封耐磨性能好。
Description
技术领域
本发明涉及一种橡胶组合物,尤其是涉及一种具有良好耐磨及脱模性能的橡胶组合物。
背景技术
关于橡胶组合物的配方和制造方法成千上万,根据不同的使用要求往往配有不同的材料配方。目前常用的具有耐侯耐磨性能的常见的一般组分为丁腈橡胶100、N330炭黑65、二丁脂20、硫磺1.8、促进剂2.5、流动剂2、防老剂4、氧化锌5、石蜡1.5-2.5。还有一种组合物为丁腈橡胶100、N330炭黑35、N220炭黑30、二丁脂20、硫磺0.5、过氧化二异丙苯3、促进剂1.5、流动剂2、防老剂4、氧化锌5、石蜡1.5-2.5。这两种组分制成的橡胶制品品质较低,不耐候、不经用、抗疲劳屈挠性低,易龟裂,在用于减震器防尘时质量可靠性不够好。
此前本人申请过一种名称为特种耐磨橡胶组合物的发明专利,其主要技术方案为该橡胶组合物由下列原料制备而成,丁腈橡胶105重量份、N220炭黑55重量份、N330炭黑15重量份、二辛脂30重量份、硫磺0.8~1重量份、过氧化二异丙苯0.8~1重量份、促进剂2重量份、流动剂2.1重量份、氧化锌5重量份、防老剂3.5~4.5重量份,龟裂防止剂4~5.2重量份。该技术在实际生产中有较好的效果,但尚还存在着一定的局限性,主要是生产过程中该橡胶组合物的制造过程制成品表面容易发泡,且该组合物在长期高温使用后有刺激气味。
发明内容
本发明所要解决的问题是提供一种具有加工时不易起泡且散发一定芳香气味,且密封耐磨性能好的橡胶组合物。
为解决上述技术问题,本发明所采用的技术方案是:一种易脱模的高强度橡胶组合物,由下列原料制备而成:丁腈橡胶105重量份、N220炭黑50重量份、N330炭黑10重量份、二辛脂28重量份、硫磺0.8~1重量份、过氧化二异丙苯0.8~1重量份、促进剂2重量份、流动剂2.1重量份、氧化锌5重量份、防老剂3.5~4.5重量份,龟裂防止剂4~5.2重量份、消泡剂8~10重量份、二甲苯麝香2~5重量份、2%水乳化有机硅脱模剂3重量份。
采用以上技术方案,与现有常见的橡胶组合物相比,本发明的显著优点是:
1、配方更为合理。通过配比的调整,将原先的二丁脂改用二辛脂,分子量更大;***调整了过氧化二异丙苯的用量,突破了传统橡胶工艺配方中须由少许硫磺与大量过氧化物相交联的技术限制,基本相同份量的硫磺与过氧化物协同交联使得本组分制成的成品耐臭氧性能明显增强;由于炭黑不仅能提高橡胶制品的强度,并赋予橡胶制品以良好的耐磨耗、耐撕裂、耐热、耐油,延长制品的使用寿命,经多次试验,将全部的N330炭黑换成一定比例的N220炭黑和N330炭黑;由于B10具有较宽的碳数分布和非常合理的直链烷烃与异构烷烃的构成比例,在很宽的温度范围内都能对橡胶制品的臭氧龟裂起到防护作用,合理使用了一定重量份的龟裂防止剂B10能够在制品表面形成物理保护膜,有效防止龟裂产生;在本组分中加入适当量的流动剂等其他助剂,在不影响组分的综合性能的前提下,还有助于改善加工工艺。添加适量的消泡剂,可避免在高温硫化时橡胶制品起泡,使该橡胶组合物的制成品的外表观感更好;加入浓度为2%的水乳化有机硅脱模剂3重量份,其脱模效果最佳;二甲苯麝香是人造麝香的一种,熔点为113摄氏度,可增加橡胶组合物制成品的芳香气味,一定程度上遮盖该组合物在长期高温使用后产生的刺激气味。
2、综合性能明显改善。通过对实施例的综合测定,本发明通过对相关配方的改革和调整,比同类配方的普通橡胶组合物的的耐磨耗、耐撕裂、耐热、密封等性能均有所提升,制成品发生起泡影响外表观感的次数比未调整配方前降低40~50%。
具体实施方式
下面通过实施例进一步说明本发明。
实施例1:丁腈橡胶10.5KG、N220炭黑5KG、N330炭黑1KG、二辛脂2.8KG、硫磺0.1KG、过氧化二异丙苯0.1KG、促进剂0.2KG、流动剂0.21KG、氧化锌0.5KG、防老剂0.35KG,龟裂防止剂B100.4KG,消泡剂0.8KG、二甲苯麝香0.2KG、2%水乳化有机硅脱模剂0.3KG。
实施例2:丁腈橡胶10.5KG、N220炭黑5KG、N330炭黑1KG、二辛脂2.8KG、硫磺0.8KG、过氧化二异丙苯0.08KG、促进剂0.2KG、流动剂0.21KG、氧化锌0.5KG、防老剂0.45KG,龟裂防止剂B100.52KG,消泡剂1KG、二甲苯麝香0.5KG、2%水乳化有机硅脱模剂0.3KG。
实施例3:丁腈橡胶10.5KG、N220炭黑5KG、N330炭黑1KG、二辛脂2.8KG、硫磺0.8KG、过氧化二异丙苯0.08KG、促进剂0.2KG、流动剂0.21KG、氧化锌0.5KG、防老剂0.45KG、龟裂防止剂B100.52KG、消泡剂0.9KG、二甲苯麝香0.4KG、2%水乳化有机硅脱模剂0.3KG。
实施例4:丁腈橡胶10.5KG、N220炭黑5KG、N 330炭黑1KG、气相法白炭黑1.5KG、二辛脂2.8KG、硫磺0.8KG、过氧化二异丙苯0.09KG、促进剂0.2KG、流动剂0.21KG、氧化锌0.5KG、防老剂0.45KG,龟裂防止剂B100.45KG、消泡剂0.8KG、二甲苯麝香0.5KG、2%水乳化有机硅脱模剂0.3KG。
Claims (1)
1.一种易脱模的高强度橡胶组合物,其特征在于由下列原料制备而成:丁腈橡胶105重量份、N220炭黑50重量份、N330炭黑10重量份、二辛脂28重量份、硫磺0.8~1重量份、过氧化二异丙苯0.8~1重量份、促进剂2重量份、流动剂2.1重量份、氧化锌5重量份、2%水乳化有机硅脱模剂3重量份、防老剂3.5~4.5重量份、龟裂防止剂4~5.2重量份、消泡剂8~10重量份、二甲苯麝香2~5重量份。