CN102168177A - 电解锌阳极泥二氧化锰直接浸出的方法 - Google Patents

电解锌阳极泥二氧化锰直接浸出的方法 Download PDF

Info

Publication number
CN102168177A
CN102168177A CN2011100918132A CN201110091813A CN102168177A CN 102168177 A CN102168177 A CN 102168177A CN 2011100918132 A CN2011100918132 A CN 2011100918132A CN 201110091813 A CN201110091813 A CN 201110091813A CN 102168177 A CN102168177 A CN 102168177A
Authority
CN
China
Prior art keywords
electrolytic zinc
manganese
manganse dioxide
directly
sulfate solution
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011100918132A
Other languages
English (en)
Other versions
CN102168177B (zh
Inventor
梁京宁
张强
杨川丽
张占伟
曹伟
倪恒发
张全胜
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JIYUAN CITY DONGFANG CHEMICAL INDUSTRY Co Ltd
Original Assignee
JIYUAN CITY DONGFANG CHEMICAL INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JIYUAN CITY DONGFANG CHEMICAL INDUSTRY Co Ltd filed Critical JIYUAN CITY DONGFANG CHEMICAL INDUSTRY Co Ltd
Priority to CN201110091813A priority Critical patent/CN102168177B/zh
Publication of CN102168177A publication Critical patent/CN102168177A/zh
Application granted granted Critical
Publication of CN102168177B publication Critical patent/CN102168177B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种电解锌阳极泥二氧化锰直接浸出的方法，具体涉及一种以电解锌阳极泥二氧化锰为原料湿法回收金属锰的电解锌阳极泥二氧化锰直接浸出的方法。本发明的技术方案是这样实现的：把块状和片状二氧化锰原料送入球磨机球磨，二氧化锰原料通过球磨机球磨后，直接进入浆化池进行浆化，对浆化浸出液进行重金属除杂，得到合格的硫酸锰溶液，直接供给电解锌生产厂家，以满足电解锌对锰的要求。由于本发明工艺合理，所以能保证生产出合格的硫酸锰溶液。加之本发明采用的是湿法冶炼回收金属锰的方法，起到了节能减排绿色冶炼的目的。本发明工艺简单、投资少、能耗低。本发明操作简便，因此容易实施和推广。

Description

电解锌阳极泥二氧化锰直接浸出的方法
技术领域
本发明涉及一种电解锌阳极泥二氧化锰直接浸出的方法，具体涉及一种以电解锌阳极泥二氧化锰为原料湿法回收金属锰的电解锌阳极泥二氧化锰直接浸出的方法。
背景技术
市场调查发现，全国各个电解锌生产厂都堆积有含有金属锰的阳极泥和清槽、掏槽的含锰结晶渣。长期的堆积不但占据着土地资源而且污染环境和存在安全隐患。传统的锰的冶炼方法以二氧化锰为原料，均是采用火法冶炼，此传统工艺能耗高、投资大，而且易对环境造成污染。迄今为止，尚未见该类冶炼锰的相关技术及专利文献。
发明内容
本发明的目的在于克服现有技术中存在的不足而提供一种以电解锌阳极泥二氧化锰为原料直接浸出回收金属锰的与传统的工艺相比，具有工艺简单、投资少、能耗低、易于操作、易于推广采用的电解锌阳极泥二氧化锰直接浸出的方法。
为实现上述目的，本发明的技术方案是这样实现的:把块状和片状二氧化锰原料送入球磨机球磨，二氧化锰原料通过球磨机球磨后，直接进入浆化池进行浆化，对浆化浸出液进行重金属除杂，得到合格的硫酸锰溶液，直接供给电解锌生产厂家，以满足电解锌对锰的要求。
将球磨后的二氧化锰加入配有硫酸溶液的反应釜中，按照二氧化锰和水的质量比控制浆液的液固比为3:1，硫酸溶液的加入量为二氧化锰质量的1/3，在搅拌反应的过程中缓慢的加入双氧水，加入双氧水是二氧化锰质量的1/3，搅拌反应4h，溶液的PH值控制在2.0～3.0。
在对浆化浸出液进行重金属除杂时，过滤后的硫酸锰溶液的温度控制为55~60℃，PH值为2.0～3.0，缓慢的加入硫化钡试剂，硫化钡试剂的加入量是硫酸锰溶液含锰质量的1/30，进行重金属除杂后得到合格的硫酸锰溶液，经检测合格后进行压滤，合格的溶液可直接去生产MnSO4·H2O成品或供给电解锌生产***补充金属锰。
所用的双氧水为还原剂，其必须在酸性条件下进行反应。
本发明具有如下优点和效果：
1、由于本发明工艺合理，所以能保证生产出合格的硫酸锰溶液。加之本发明采用的是湿法冶炼回收金属锰的方法，起到了节能减排绿色冶炼的目的。
2、本发明工艺简单、投资少、能耗低。
3、本发明操作简便，因此容易实施和推广。
附图说明
图1所示为本发明电解锌阳极泥二氧化锰直接浸出的生产工艺流程图。
具体实施方式：
如图1所示，按照本发明二氧化锰直接浸出法的生产工艺流程图，本发明采取以下步骤获得合格的硫酸锰溶液：
把块状和片状二氧化锰原料送入球磨机球磨，二氧化锰原料通过球磨机球磨后，直接进入浆化池进行浆化，对浆化浸出液进行重金属除杂，得到合格的硫酸锰溶液，直接供给电解锌生产厂家，以满足电解锌对锰的要求。
将球磨后的二氧化锰加入配有硫酸溶液的反应釜中，按照二氧化锰和水的质量比控制浆液的液固比为3:1，硫酸溶液的加入量为二氧化锰质量的1/3，在搅拌反应的过程中缓慢的加入双氧水，加入双氧水是二氧化锰质量的1/3，搅拌反应4h，溶液的PH值控制在2.0～3.0。
在对浆化浸出液进行重金属除杂时，过滤后的硫酸锰溶液的温度控制为55~60℃，PH值为2.0～3.0，缓慢的加入硫化钡试剂，硫化钡试剂的加入量是硫酸锰溶液含锰质量的1/30，进行重金属除杂后得到合格的硫酸锰溶液，经检测合格后进行压滤，合格的溶液可直接去生产MnSO4·H2O成品或供给电解锌生产***补充金属锰。
所用的双氧水为还原剂，其必须在酸性条件下进行反应。
实施例1：将片状和块状的二氧化锰通过球磨机球磨后，直接进入浆化池进行浆化，将球磨后的二氧化锰加入配有硫酸溶液的反应釜中，按照二氧化锰和水的质量比控制浆液的液固比为3:1，硫酸溶液的加入量为二氧化锰质量的1/3，在搅拌反应的过程中缓慢的加入双氧水，加入双氧水是二氧化锰质量的1/3，反应温度严格控制在55~60℃，搅拌反应的过程中缓慢的加入双氧水，搅拌反应4h，溶液的PH控制为2.0～3.0。所得硫酸锰溶液各微量元素如表1所示。
在对浆化浸出液进行重金属除杂时，过滤后的硫酸锰溶液，温度控制为55~60℃，PH值为2.0～3.0，缓慢的加入硫化钡试剂，硫化钡试剂的加入量是硫酸锰溶液含锰质量的1/30，进行重金属除杂后可得到合格的硫酸锰溶液，合格的硫酸锰溶液各个微量元素含量如表2所示，经检测合格后进行压滤，合格的溶液可直接去生产MnSO4·H2O成品或供给电解锌生产***补充金属锰。所用的双氧水为还原剂，其必须在酸性条件下进行反应。
表1为浸出液中各种微量元素的含量：
元素 Mn Zn Fe Pb Cu Co
含量g/L 74.6 0.0335 0.0125 0.025 0.017
表2为硫酸锰溶液净化后微量元素的含量：
元素 Mn Zn Fe Pb Cu Co
含量g/L 67.9 0.0025 0.0005 微量 微量

Claims (4)

1.一种电解锌阳极泥二氧化锰直接浸出的方法，其特征在于：把块状和片状二氧化锰原料送入球磨机球磨，二氧化锰原料通过球磨机球磨后，直接进入浆化池进行浆化，对浆化浸出液进行重金属除杂，得到合格的硫酸锰溶液，直接供给电解锌生产厂家，以满足电解锌对锰的要求。
2.根据权利要求1所述的电解锌阳极泥二氧化锰直接浸出的方法，其特征在于：将球磨后的二氧化锰加入配有硫酸溶液的反应釜中，按照二氧化锰和水的质量比控制浆液的液固比为3:1，硫酸溶液的加入量为二氧化锰质量的1/3，在搅拌反应的过程中缓慢的加入双氧水，加入双氧水是二氧化锰质量的1/3，搅拌反应4h，溶液的PH值控制在2.0～3.0。
3.根据权利要求1所述的电解锌阳极泥二氧化锰直接浸出的方法，其特征在于：在对浆化浸出液进行重金属除杂时，过滤后的硫酸锰溶液的温度控制为55~60℃，PH值为2.0～3.0，缓慢的加入硫化钡试剂，硫化钡试剂的加入量是硫酸锰溶液含锰质量的1/30，进行重金属除杂后得到合格的硫酸锰溶液，经检测合格后进行压滤，合格的溶液可直接去生产MnSO4·H2O成品或供给电解锌生产***补充金属锰。
4. 根据权利要求1所述的电解锌阳极泥二氧化锰直接浸出的方法，其特征在于：所用的双氧水为还原剂，其必须在酸性条件下进行反应。
CN201110091813A 2011-04-13 2011-04-13 电解锌阳极泥二氧化锰直接浸出的方法 Expired - Fee Related CN102168177B (zh)