CN102029250A - Automatic production method of thermal-insulation precoated decorative board - Google Patents
Automatic production method of thermal-insulation precoated decorative board Download PDFInfo
- Publication number
- CN102029250A CN102029250A CN2010105480168A CN201010548016A CN102029250A CN 102029250 A CN102029250 A CN 102029250A CN 2010105480168 A CN2010105480168 A CN 2010105480168A CN 201010548016 A CN201010548016 A CN 201010548016A CN 102029250 A CN102029250 A CN 102029250A
- Authority
- CN
- China
- Prior art keywords
- backing material
- material plate
- insulation
- production method
- automatic production
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an automatic production method of a thermal-insulation precoated decorative board, belonging to processing methods of decorative boards. A full-automatic UV fluorocarbon paint spraying machine controlled by a computer program is used for spraying paint on a substrate. The difference of the color and decorative grains of the colored substrate is smaller, the quality control on the product is stable, and the whole production process adopts a layered coloring mode to reduce the consumption of solvents, thereby lowering the cost. Thus, the product can satisfy the use demands for most construction occasions, is especially suitable for external walls of buildings, and has the effect of thermal insulation.
Description
Technical field
The present invention relates to the processing method of decorative panel, a kind of automatic production method that is incubated prefinished panel of saying so more specifically.
Background technology
The production process of production method of decorative plate is comparatively complicated, and the application of the wall thermal insulation technology of existing popularization great majority has insulation material, promptly on wall decorating veneer, adopt polyurethanes to be called for short polyurethane, materials such as extracellular polymeric, basically all to finish insulation and protection through the multiple working procedure construction material, and in its device operation, the main at present coloring process that adopts generally adopts manual roller coat of colored paint or ready-made in advance colored paint roller coat template to pour into a mould roller coat, automaticity is poor, make its production efficiency low, especially manual roller coat, all there are individual difference in decoration line and color when producing in batches on its decorative panel of producing, make the disqualification rate of product higher, cause cost waste, though and ready-made in advance roller coat template is carried out roller coat and is seemed the individual difference that exists between the decoration line that has solved decorative panel when producing in batches, improved the bulk article uniformity, but adopt and accurately to control what of colored paint in the roller coat template, the color of the decorative panel that uncontrollable its roller coat goes out, use the color of decorative panel still individual difference can occur, so this method does not thoroughly solve existing problem in the decorative panel conventional production methods.
Summary of the invention
The objective of the invention is to solve above-mentioned deficiency, a kind of automaticity height is provided, and the little a kind of automatic production method that is incubated prefinished panel of the product differentiation of producing.
For solving above-mentioned technical problem, the present invention by the following technical solutions:
A kind of automatic production method that is incubated prefinished panel of the present invention is characterized in that: the insulation backing material plate after the processing is operated according to following steps:
Step 1, at first backing material plate is carried out levelling, by roll coating apparatus with UV putty roller coat to substrate, infill panel face injustice guarantees the plate surface evenness, is cured then, the plate face is filled go up putty, plays dry, induration;
Step 2, adopt sealing priming paint roller coat under temperature constant state, make its back side form paint film, play the antiseepage effect at the backing material plate back side;
Step 3, polished in the backing material plate surface, smooth to guarantee, increase coating adhesion;
Step 4, to adopting computer program control on the backing material plate surface after polishing flat, the UV fluorine carbon of modulated good colourity is coated with lacquer under constant temperature, the layering roller coat is to the backing material plate surface, again according to its concrete color classification, adopt ultraviolet light polymerization respectively, UV fluorine carbon lacquer degree is controlled at 20 to 40 microns;
Step 5, in completing steps 2 behind decorative panel back side roller coat sealing priming paint, the control of employing computer program, the UV fluorine carbon of modulated lechery is coated with lacquer under constant temperature, the layering roller coat is to the backing material plate surface, again according to its concrete color classification, adopt suitable ultraviolet light polymerization respectively, obtain the finished product decorative panel after curing is finished.
Further technical scheme is: described method also comprises the steps:
Step 6, with the tack diaphragm, by cylinder film is covered to the plate face, in preventing transportation, installing, produce and scratch and damaged;
Step 7, the finished product decorative panel is cut and deburring according to product specification.
Further technical scheme is: sealing priming paint also needs to solidify after the temperature constant state lower roll is coated in the backing material plate back side in the described step 2: sealing priming paint on the backing material plate back side is fixed and become smooth shape.
Further technical scheme is: in the described step 4 lacquer of the backing material plate surface roller coating UV fluorine carbon after polishing flat is permeated priming paint and curing to its surface spraying before.
Further technical scheme is: to backing material plate surface roller coating UV fluorine carbon lacquer and after solidifying, repeat the operation of a step 4, to reach better coloring effect in the described step 4.
Further technical scheme is: the thickness of the painted UV fluorine of described roller coat carbon lacquer is 30 microns.
Further technical scheme is: described backing material plate is the prefabricated board of cementaceous.
Compared with prior art, the invention has the beneficial effects as follows: backing material plate is sprayed by the full-automatic UV fluorine carbon lacquer flush coater that adopts computer program control, use the color of the backing material plate after painted and decorate the line otherness less, the quality control of product is stable, its whole process of production adopts layer tint to reduce the use of solvent, cost is lower, therefore the product of producing can satisfy the user demand in great majority building place, and by the use of its suitable external wall, and it is with heat insulation effect.
The specific embodiment
Below the present invention is further elaborated.
At first that the explanation of nouns of mentioning among the present invention is as follows:
UV fluorine carbon lacquer: wearability is good, and hardness is big, the decorative paint that weatherability is outstanding, and its adhesive force is good.
Solidify: it is dry gradually that the stand-by period makes its roller coat present liquid lacquer.
Roller coat: adopt the roller of roll coater that UV fluorine carbon lacquer is rolled brushing on the decorative panel panel.
A kind of automatic production method that is incubated prefinished panel provided by the invention, can adopt the cementaceous insulation backing material plate after the processing to operate according to following steps:
Step 1, at first backing material plate is carried out levelling, by roll coating apparatus with UV putty roller coat to substrate, infill panel face injustice guarantees the plate surface evenness, is cured then, the plate face is filled go up putty, plays dry, induration;
Step 2, adopt sealing priming paint roller coat under temperature constant state at the backing material plate back side, make its back side form paint film, play the antiseepage effect, the normal temperature state is waited for down it is solidified then, and then makes the sealing priming paint on the backing material plate back side fixing and smooth;
Step 3, polished in the backing material plate surface, smooth to guarantee, increase coating adhesion;
Step 4, to spraying infiltration priming paint on the backing material plate surface after polishing flat and solidify, adopt computer program control then, the UV fluorine carbon of modulated good colourity is coated with lacquer under constant temperature, the layering roller coat is to the backing material plate surface, again according to its concrete color classification, adopt ultraviolet light polymerization respectively, UV fluorine carbon is coated with lacquer THICKNESS CONTROL at 30 microns; If go for better coloring effect, can repeat once this step.
Step 5, in completing steps 2 behind decorative panel back side roller coat sealing priming paint, the control of employing computer program, the UV fluorine carbon of modulated lechery is coated with lacquer under constant temperature, the layering roller coat is to the backing material plate surface, again according to its concrete color classification, adopt suitable ultraviolet light polymerization respectively, obtain the finished product decorative panel after curing is finished.
Step 6, the tack diaphragm can also be covered film to the plate face by cylinder as required, in preventing transportation, installing, produce and scratch and damaged;
Step 7, can also cut and deburring according to product specification the finished product decorative panel as required, must be used for transportation after the packing deburring is finished and sell.
Claims (7)
1. automatic production method that is incubated prefinished panel is characterized in that: adopt the insulation backing material plate after the processing to operate according to following steps:
Step 1, at first backing material plate is carried out levelling, by roll coating apparatus with UV putty roller coat to substrate, infill panel face injustice guarantees the plate surface evenness, is cured then, the plate face is filled go up putty;
Step 2, adopt sealing priming paint roller coat under temperature constant state, make its back side form paint film at the backing material plate back side;
Step 3, polished in the backing material plate surface, smooth to guarantee;
Step 4, to adopting computer program control on the backing material plate surface after polishing flat, the UV fluorine carbon of modulated good colourity is coated with lacquer under constant temperature, the layering roller coat is to the backing material plate surface, again according to its concrete color classification, adopt ultraviolet light polymerization respectively, UV fluorine carbon is coated with lacquer THICKNESS CONTROL at 20 to 40 microns;
Step 5, in completing steps 2 behind decorative panel back side roller coat sealing priming paint, the control of employing computer program, the UV fluorine carbon of modulated lechery is coated with lacquer under constant temperature, the layering roller coat is to the backing material plate back side, again according to its concrete color classification, adopt suitable ultraviolet light polymerization respectively, obtain the finished product decorative panel after curing is finished.
2. the automatic production method of insulation prefinished panel according to claim 1 is characterized in that:
Described method also comprises the steps:
Step 6, with the tack diaphragm, by cylinder film is covered to the plate face;
Step 7, the finished product decorative panel is cut and deburring according to product specification.
3. the automatic production method of insulation prefinished panel according to claim 1 and 2, it is characterized in that: sealing priming paint also needs to solidify after the temperature constant state lower roll is coated in the backing material plate back side in the described step 2, sealing priming paint on the backing material plate back side is fixed and is become smooth shape.
4. the automatic production method of insulation prefinished panel according to claim 1 and 2 is characterized in that: in the described step 4 lacquer of the backing material plate surface roller coating UV fluorine carbon after polishing flat is permeated priming paint and curing to its surface spraying before.
5. the automatic production method of insulation prefinished panel according to claim 1 and 2 is characterized in that: to backing material plate surface roller coating UV fluorine carbon lacquer and after solidifying, repeat one time step 4 in the described step 4.
6. the automatic production method of insulation prefinished panel according to claim 5 is characterized in that: the thickness of the painted UV fluorine of described roller coat carbon lacquer is 30 microns.
7. the automatic production method of insulation prefinished panel according to claim 1 is characterized in that: described backing material plate is the prefabricated board of cementaceous.