CN101979443A - 一种改性白炭黑的生产方法 - Google Patents
一种改性白炭黑的生产方法 Download PDFInfo
- Publication number
- CN101979443A CN101979443A CN2010105049961A CN201010504996A CN101979443A CN 101979443 A CN101979443 A CN 101979443A CN 2010105049961 A CN2010105049961 A CN 2010105049961A CN 201010504996 A CN201010504996 A CN 201010504996A CN 101979443 A CN101979443 A CN 101979443A
- Authority
- CN
- China
- Prior art keywords
- carbon black
- white carbon
- water glass
- modified white
- reaction
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Claims (10)