CN101831809A - 一种制造聚酯双点低温高强度粘合衬布的方法 - Google Patents
一种制造聚酯双点低温高强度粘合衬布的方法 Download PDFInfo
- Publication number
- CN101831809A CN101831809A CN200910068121A CN200910068121A CN101831809A CN 101831809 A CN101831809 A CN 101831809A CN 200910068121 A CN200910068121 A CN 200910068121A CN 200910068121 A CN200910068121 A CN 200910068121A CN 101831809 A CN101831809 A CN 101831809A
- Authority
- CN
- China
- Prior art keywords
- melting point
- point polyester
- low
- cloth
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种制造聚酯双点低温高强度粘合衬布的方法,首先在经过整理的基布上均匀涂布点状的高熔点聚酯胶层;当高熔点聚酯胶还没有完全凝固时,再浇上低熔点聚酯胶粉;然后吸除没有浇到高熔点聚酯胶层上的多余的低熔点聚酯胶粉,最后进行高温定型,即可。本发明的优点是:粘合后可保持面料原有的色泽和光泽,可使面料具有更好的形态稳定性、洗涤尺寸的稳定性、吸湿导湿性和耐碱性,并且解决了服装在日常经过多次洗涤后出现的面料起泡问题。
Description
技术领域:
本发明涉及纺织技术领域,特别涉及一种制造聚酯双点低温高强度粘合衬布的方法。
背景技术:
为了提高服装的质量,目前大部分服装都采用了粘合衬布。粘合衬布是在无纺布、针织布或机织布等基布的单面上以点状设置热熔型粘合树脂而形成的。基布经过精炼、染色、整理加工,使粘合衬布具有手感好、形态稳定、防缩等性能。但是,这种粘合衬布与面料压烫粘合时适应性差,不能保证衬布和面料的互动性,服装经过洗涤后容易发生驳头起泡和“渗胶”的现象,从而影响整个成衣的质量问题。
发明内容:
本发明的目的就在于克服上述现有技术中存在的不足,而提供一种制造聚酯双点低温高强度粘合衬布的方法,该方法可使面料具有更好的形态稳定性、洗涤尺寸的稳定性,并且解决了服装在日常经过多次洗涤后出现的面料起泡和“渗胶”的问题。
本发明的技术方案是:一种制造聚酯双点低温高强度粘合衬布的方法,其特征在于:首先在经过整理的基布上均匀涂布点状的高熔点聚酯胶层;当高熔点聚酯胶还没有完全凝固时,再浇上低熔点聚酯胶粉;然后吸除没有浇到高熔点聚酯胶层上的多余的聚酯胶粉,最后进行高温定型,即可。
上述高熔点聚酯胶的熔点温度在100-120℃之间。
上述低熔点聚酯胶粉的熔点温度在70-80℃之间。
本发明的优点是:本发明的初始模量高、织物有身骨、粘胶不熔于纤维内部、表面粘合力强,胶不渗透面料。在与面料粘合后,可使面料具有更好的形态稳定性、潮湿状态下织物变形小、尺寸稳定性好、织物平滑、粘合后面料悬垂性好、吸湿导湿性好、色泽鲜艳、富有光泽。本发明保持了基布和面料的互动性,大幅度增强面料柔软效果及服装的穿着舒适;具有较好的耐碱性,解决了服装在日常经过多次洗涤后出现的面料起泡问题。
具体实施方式:
一种制造聚酯双点低温高强度粘合衬布的方法,首先在经过整理的基布上均匀涂布点状的熔点温度在100-120℃之间的高熔点聚酯胶层;当高熔点聚酯胶还没有完全凝固时,再浇上熔点温度在70-80℃之间的低熔点聚酯胶粉;然后吸除没有浇到高熔点聚酯胶层上的多余的聚酯胶粉;最后进行高温定型,即可。
本发明采用了两个胶点的不同熔点粘合温度,首先在熔点低的胶点先开始融化,并迅速地粘合在面料纤维上。这时熔点高的另一胶点开始融化,并迅速粘合在熔点低的胶面上,使两种胶点的胶面局部粘合,从而保证了衬布和面料的胶面的粘合力远远大于其它同温胶点的粘合力,达到了基布和面料的互动性,并有效地避免了因胶液透过面料粘合面而渗透到面料表面的现象,使面料表面光亮。同时,因为双胶点的不同粘合熔点粘合面料,保证了服装在日常洗涤时保持永久的粘合效果。
Claims (3)
1.一种制造聚酯双点低温高强度粘合衬布的方法,其特征在于:首先在经过整理的基布上均匀涂布点状的高熔点聚酯胶层;当高熔点聚酯胶还没有完全凝固时,再浇上低熔点聚酯胶粉;然后吸除没有浇到高熔点聚酯胶层上的多余的低熔点聚酯胶粉,最后进行高温定型,即可。
2.根据权利要求1所述的一种制造聚酯双点低温高强度粘合衬布的方法,其特征在于:上述高熔点聚酯胶的熔点温度在100-120℃之间。
3.根据权利要求1所述的一种制造聚酯双点低温高强度粘合衬布的方法,其特征在于:上述低熔点聚酯胶粉的熔点温度在70-80℃之间。