CN101808821A - 交通工具透明体 - Google Patents
交通工具透明体 Download PDFInfo
- Publication number
- CN101808821A CN101808821A CN200880109630A CN200880109630A CN101808821A CN 101808821 A CN101808821 A CN 101808821A CN 200880109630 A CN200880109630 A CN 200880109630A CN 200880109630 A CN200880109630 A CN 200880109630A CN 101808821 A CN101808821 A CN 101808821A
- Authority
- CN
- China
- Prior art keywords
- lamella
- layer
- thickness
- transparent body
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
T | R1 | R2 | |
CIE III,A-2° | 71.56 | 11.31 | 10.41 |
CIE III,C-2° | 71.79 | 11.37 | 10.41 |
ASTM 891,2° | 71.77 | 11.37 | 10.42 |
T | R1 | R2 | |
ISO 9050(280-380T) | 0.02 | 17.62 | 5.01 |
SAE UV(300-400T) | 1.18 | 22.64 | 5.06 |
WINDOWS 4(300-380T) | 0.02 | 20.34 | 4.98 |
T | R1 | R2 | |
ASTM 891(800-2500T) | 2.91 | 82.44 | 59.98 |
T | R1 | R2 | |
SAE T(R)溶胶(E892:300-2500) | 34.40 | 44.29 | 32.74 |
WINDOWS 4 T(R)溶胶(E891:300-4045) | 31.31 | 48.90 | 35.27 |
T | R1 | R2 | ||
CIE III,C-2° | DW | 560.45 | 553.73 | 563.82 |
T | R1 | R2 | ||
Pe | 2.76 | 3.56 | 3.21 | |
Y | 71.79 | 11.37 | 10.41 | |
x | 0.3119 | 0.3107 | 0.3130 | |
y | 0.3247 | 0.3288 | 0.3253 | |
CIE III,D65-2° | Y | 71.82 | 11.38 | 10.40 |
x | 0.3146 | 0.3133 | 0.3161 | |
y | 0.3378 | 0.3419 | 0.3390 | |
CIELAB,D65-10° | L* | 87.84 | 39.99 | 38.33 |
a* | -3.04 | -0.91 | 0.33 | |
b* | 3.88 | 1.18 | 1.05 | |
C* | 4.92 | 1.49 | 1.10 | |
h° | 128.08 | 127.47 | 72.49 |
T | R1 | R2 | |
CIE III,A-2° | 71.78 | 10.58 | 9.68 |
CIE III,C-2° | 72.19 | 10.73 | 9.70 |
T | R1 | R2 | |
ASTM 891,2° | 72.14 | 10.71 | 9.70 |
T | R1 | R2 | |
ISO 9050(280-380T) | 9.83 | 21.03 | 18.85 |
SAE UV(300-400T) | 20.60 | 27.08 | 24.40 |
WINDOWS 4(300-380T) | 12.33 | 24.38 | 21.98 |
T | R1 | R2 | |
ASTM 891(800-2500T) | 2.24 | 84.36 | 64.83 |
T | R1 | R2 | |
SAE T(R)溶胶(E892:300-2500) | 34.83 | 45.64 | 36.13 |
WINDOWS 4 T(R)溶胶(E891:300-4045) | 31.27 | 50.28 | 39.08 |
T | R1 | R2 | ||
CIE III,C-2° | DW | 550.25 | 497.77 | 516.42 |
Pe | 1.90 | 2.71 | 0.53 | |
Y | 72.19 | 10.73 | 9.70 | |
x | 0.3100 | 0.3021 | 0.3087 |
T | R1 | R2 | ||
y | 0.3234 | 0.3208 | 0.3190 | |
CIE III,D65-2° | Y | 72.23 | 10.74 | 9.69 |
x | 0.3125 | 0.3046 | 0.3114 | |
y | 0.3364 | 0.3340 | 0.3317 | |
CIELAB,D65-10° | L* | 88.07 | 38.99 | 37.11 |
a* | -3.30 | -1.25 | 0.97 | |
b* | 2.92 | -1.17 | -1.04 | |
C* | 4.41 | 1.72 | 1.42 | |
h° | 138.50 | 223.16 | 312.87 |
L* | a* | b* | |
CIELAB D65,10° | 34.3 | -2.2 | -1.3 |
CIELAB D65,60° | 45.3 | -0.14 | -0.08 |
T | R1 | R2 | |
CIE III,A-2° | 23.21 | 29.89 | 8.22 |
CIE III,C-2° | 23.15 | 30.90 | 8.38 |
ASTM 891,2° | 23.18 | 30.65 | 8.33 |
T | R1 | R2 | |
ISO 9050(280-380T) | 1.47 | 27.32 | 5.18 |
SAE UV(300-400T) | 4.87 | 36.19 | 6.62 |
WINDOWS 4(300-380T) | 2.01 | 31.57 | 5.35 |
T | R1 | R2 | |
ASTM 891(800-2500T) | 0.10 | 91.86 | 15.31 |
T | R1 | R2 | |
SAE T(R)溶胶(E892:300-2500) | 9.63 | 63.15 | 12.42 |
WINDOWS 4T(R)溶胶(E891:300-4045) | 8.55 | 66.90 | 13.25 |
T | R1 | R2 | ||
CIE III,C-2° | DW | 570.06 | 482.97 | 487.53 |
Pe | 8.26 | 12.03 | 5.75 |
T | R1 | R2 | ||
Y | 23.15 | 30.90 | 8.38 | |
x | 0.3212 | 0.2822 | 0.2955 | |
y | 0.3360 | 0.2987 | 0.3122 | |
CIE III,D65-2。 | Y | 23.13 | 30.89 | 8.36 |
x | 0.3237 | 0.2847 | 0.2983 | |
y | 0.3482 | 0.3127 | 0.3255 | |
CIELAB,D65-10。 | L* | 55.08 | 62.48 | 34.60 |
a* | -1.75 | -3.58 | -1.10 | |
b* | 5.94 | -8.40 | -2.53 | |
C* | 6.19 | 9.13 | 2.76 | |
h° | 106.39 | 246.89 | 246.45 |
Claims (17)