CN101759981B - 一种不积垢、低散发的聚碳酸酯组合物 - Google Patents
一种不积垢、低散发的聚碳酸酯组合物 Download PDFInfo
- Publication number
- CN101759981B CN101759981B CN 200810207587 CN200810207587A CN101759981B CN 101759981 B CN101759981 B CN 101759981B CN 200810207587 CN200810207587 CN 200810207587 CN 200810207587 A CN200810207587 A CN 200810207587A CN 101759981 B CN101759981 B CN 101759981B
- Authority
- CN
- China
- Prior art keywords
- weight part
- incrustation
- abs
- carbon black
- white carbon
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
Description
组成 | 对照例1 | 实施例1 | 实施例2 | 实施例3 | 实施例4 |
PC-1 | 65 | 20 | 40 | 65 | 95 |
ABS-1 | 35 | 75 | 48 | 25 | 4 |
SMA-1 | 4 | 10 | 3 | ||
环氧树脂-1 | 0.2 | 1 | 2 | 0.8 | |
白炭黑-1 | 0.8 | 1 | 5 | 0.2 | |
抗氧剂 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 |
光稳定剂 | 0.6 | 0.6 | 0.6 | 0.6 | 0.6 |
着色剂 | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 |
测试结果 | 对照例1 | 实施例1 | 实施例2 | 实施例3 | 实施例4 |
弯曲强度(MPa) | 84.2 | 72.1 | 80.1 | 83.6 | 90.4 |
弯曲模量(MPa) | 2180 | 2240 | 2280 | 2310 | 2410 |
缺口冲击强度(J/m) | 620 | 342 | 580 | 626 | 731 |
抗积垢性 | 4 | 2 | 1 | 1 | 1 |
雾化性能(mg) | 1.1 | 0.8 | 0.7 | 0.6 | 0.2 |
组成 | 对照例2 | 对照例3 | 实施例5 | 实施例6 | 实施例7 |
PC-2 | 65 | 65 | 65 | 65 | 65 |
ABS-2 | 33 | 30 | 30 | 30 | |
乳液ABS | 30 | ||||
SMA-2 | 3 | 3 | |||
SMI | 3 | 3 | |||
环氧树脂-2 | 1 | 1 | 1 | 1 | |
白炭黑-2 | 2 | 1 | 1 | 1 | |
白炭黑-3 | 1 | ||||
抗氧剂 | 0.4 | 0.4 | 0.4 | 0.4 | 0.4 |
光稳定剂 | 0.6 | 0.6 | 0.6 | 0.6 | 0.6 |
着色剂 | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 |
测试结果 | 对照例2 | 对照例3 | 实施例5 | 实施例6 | 实施例7 |
弯曲强度(MPa) | 83.7 | 83.7 | 83.6 | 82.7 | 83.6 |
弯曲模量(MPa) | 2340 | 2440 | 2470 | 2460 | 2420 |
缺口冲击强度(J/m) | 567 | 570 | 664 | 710 | 725 |
抗积垢性 | 3 | 4 | 1 | 1 | 1 |
雾化性能(mg) | 1.1 | 2.4 | 0.7 | 0.6 | 0.8 |
Claims (3)